CN104449033A - Environment-friendly heat-resistant printing ink and preparation method thereof - Google Patents
Environment-friendly heat-resistant printing ink and preparation method thereof Download PDFInfo
- Publication number
- CN104449033A CN104449033A CN201410558308.8A CN201410558308A CN104449033A CN 104449033 A CN104449033 A CN 104449033A CN 201410558308 A CN201410558308 A CN 201410558308A CN 104449033 A CN104449033 A CN 104449033A
- Authority
- CN
- China
- Prior art keywords
- environment
- friendly type
- ink
- fumed silica
- solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses environment-friendly heat-resistant printing ink and a preparation method thereof. The environment-friendly heat-resistant printing ink comprises the following components in parts by weight: 28-32 parts of methyl methacrylate, 24-26 parts of polyurethane, 14-16 parts of nano-fumed silica, 7-9 parts of a chelating agent, 4-6 parts of a slipping agent and 14-16 parts of a solvent. The environment-friendly heat-resistant printing ink disclosed by invention has the effects of resisting high temperature, protecting base layer printing ink, and preventing adhesion between printed materials and adhesion between coatings; the grade of the printed materials can be improved; and meanwhile, the environment-friendly heat-resistant printing ink has the characteristics of being non-toxic, safe, environment-friendly, sanitary and the like.
Description
Technical field
The present invention relates to a kind of environment-friendly type thermostable ink and preparation method thereof, belong to paint field.
Background technology
Environment-friendly type thermostable ink is methyl methacrylate; urethane; the material such as nano fumed silica and auxiliary agent forms; and there is the aqueous gluing body of certain degree of mobilization; through being uniformly mixed; printed matter heatproof can be made more than 180 DEG C after printing drying on the substrate, playing the effect of protection basic unit ink, anti, is a kind of novel functional printing environment-friendly material.
Summary of the invention
The object of the present invention is to provide a kind of environment-friendly type thermostable ink and preparation method thereof; The brush product of high temperature resistant ink of the present invention are used to have high temperature resistant; Protection basic unit ink, prevents between printed matter and is coated with the inter-adhesive effect of interlayer; There is the features such as nontoxic, safety, environmental protection, health simultaneously.
The present invention adopts following technical scheme:
Environment-friendly type thermostable ink, the weight part of its constitutive material is: methyl methacrylate 28-32, urethane 24-26, nano fumed silica 14-16, sequestrant 7-9, smooth agent 4-6 and solvent 14-16.
Environment-friendly type thermostable ink, the weight part of its constitutive material is: methyl methacrylate 30, urethane 25, nano fumed silica 15, sequestrant 8, smooth agent 5 and solvent 15.
Described solvent is ethanol or ethyl ester; Described sequestrant is one or more in polyacrylic acid, toxilic acid, amino trimethylammonium phosphonic acids, ethylene diamine tetra methylene phosphonic acid, Amino Trimethylene Phosphonic Acid; Described smooth agent is methyl-silicone oil, dimethyl silicone oil, polyacrylic acid ester cpds, modified polyacrylate, polydimethylsiloxane, the one of polysiloxane-polyether copolymer or mixture.
The preparation method of environment-friendly type thermostable ink, comprises the following steps:
(1) take each raw material by the weight part of constitutive material, first solvent is dropped into dispersion cylinder, start and stir, rotating speed 300 revs/min;
(2) methyl methacrylate and urethane are added in dispersion cylinder successively, stir 30 minutes;
(3) after step (2) is fully uniformly mixed, add nano fumed silica, after nano fumed silica is wetting, rotating speed is promoted to 1500 revs/min, stirs 50 minutes;
(4) add smooth agent more in step (3), stir and can obtain after 10 minutes;
(5) dispersing speed is adjusted to 100 revs/min, slowly adds sequestrant, stir 120 minutes.
Beneficial effect of the present invention:
The brush product of high temperature resistant ink of the present invention are used to have high temperature resistant; Protection basic unit ink, prevents between printed matter and is coated with the inter-adhesive effect of interlayer; There is the features such as nontoxic, safety, environmental protection, health simultaneously.
The technical problem that the present invention solves:
(1) when disperseing nano fumed silica, utilizing high-shear to make it get back to primary granule as far as possible, improving ink transparency.
(2) the strict sequestrant that controls adds dispersing speed, avoids high speed dispersion to destroy chelant stability.
(3) when controlling to disperse, ink temperature is not higher than 45 DEG C, prevents ink from producing crosslinking reaction.
Embodiment
Embodiment 1: environment-friendly type thermostable ink, the weight part (kg) of its constitutive material is: methyl methacrylate 30, urethane 25, nano fumed silica 15, sequestrant 8, smooth agent 5 and solvent 15.
Described solvent is ethanol or ethyl ester; Described sequestrant is one or more in polyacrylic acid, toxilic acid, amino trimethylammonium phosphonic acids, ethylene diamine tetra methylene phosphonic acid, Amino Trimethylene Phosphonic Acid; Described smooth agent is methyl-silicone oil, dimethyl silicone oil, polyacrylic acid ester cpds, modified polyacrylate, polydimethylsiloxane, the one of polysiloxane-polyether copolymer or mixture.
The preparation method of environment-friendly type thermostable ink, comprises the following steps:
(1) take each raw material by the weight part of constitutive material, first solvent is dropped into dispersion cylinder, start and stir, rotating speed 300 revs/min
(2) methyl methacrylate and urethane are added in dispersion cylinder successively, stir 30 minutes;
(3) after step (2) is fully uniformly mixed, add nano fumed silica, after nano fumed silica is wetting, rotating speed is promoted to 1500 revs/min, stirs 50 minutes;
(4) add smooth agent more in step (3), stir and can obtain after 10 minutes;
(5) dispersing speed is adjusted to 100 revs/min, slowly adds sequestrant, stir 120 minutes.
The performance data of environment-friendly type thermostable ink of the present invention:
Physical index:
Viscosity: 40 "; Scrape sample viscosity: 19 " (zhan2# cup inspection viscosity); Solid content: 50%.
Sanitary index:
Arsenic: 0.52ppm, lead: 0.35ppm, mercury: 0 ppm, chromium: 0.84ppm and nickel: 0.45ppm.
Claims (6)
1. an environment-friendly type thermostable ink, is characterized in that the weight part of its constitutive material is: methyl methacrylate 28-32, urethane 24-26, nano fumed silica 14-16, sequestrant 7-9, smooth agent 4-6 and solvent 14-16.
2. environment-friendly type thermostable ink according to claim 1, is characterized in that the weight part of its constitutive material is: methyl methacrylate 30, urethane 25, nano fumed silica 15, sequestrant 8, smooth agent 5 and solvent 15.
3. environment-friendly type thermostable ink according to claim 1, is characterized in that: described solvent is ethanol or ethyl ester.
4. a preparation method for environment-friendly type thermostable ink as claimed in claim 1, is characterized in that comprising the following steps:
(1) take each raw material by the weight part of constitutive material, first solvent is dropped into dispersion cylinder, start and stir, rotating speed 300 revs/min;
(2) methyl methacrylate and urethane are added in dispersion cylinder successively, stir 30 minutes;
(3) after step (2) is fully uniformly mixed, add nano fumed silica, after nano fumed silica is wetting, rotating speed is promoted to 1500 revs/min, stirs 50 minutes;
(4) add smooth agent more in step (3), stir and can obtain after 10 minutes;
(5) dispersing speed is adjusted to 100 revs/min, slowly adds sequestrant, stir 120 minutes.
5. environment-friendly type thermostable ink according to claim 1, is characterized in that: described sequestrant is one or more in polyacrylic acid, toxilic acid, amino trimethylammonium phosphonic acids, ethylene diamine tetra methylene phosphonic acid, Amino Trimethylene Phosphonic Acid.
6. environment-friendly type thermostable ink according to claim 1, is characterized in that: described smooth agent is methyl-silicone oil, dimethyl silicone oil, polyacrylic acid ester cpds, modified polyacrylate, polydimethylsiloxane, the one of polysiloxane-polyether copolymer or mixture.