CN102030562A - 裂瓷修补新技术 - Google Patents
裂瓷修补新技术 Download PDFInfo
- Publication number
- CN102030562A CN102030562A CN2009101774244A CN200910177424A CN102030562A CN 102030562 A CN102030562 A CN 102030562A CN 2009101774244 A CN2009101774244 A CN 2009101774244A CN 200910177424 A CN200910177424 A CN 200910177424A CN 102030562 A CN102030562 A CN 102030562A
- Authority
- CN
- China
- Prior art keywords
- senior
- ceramics
- feitian
- chapped
- spray
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种裂瓷修补新技术,属于陶瓷生产工艺技术领域。本发明解决的技术问题所采取的技术方案包括以下操作:磨平,补平,打磨,喷漆,打磨,调配,喷漆,入窑八大主要工艺。本技术修补的裂瓷品质与原瓷一样,经久耐用,永不褪色,色泽鲜艳,同时具有环保卫生,节约资源,降低成本的有益效果。
Description
技术领域
本发明涉及陶瓷生产工艺技术领域,特别是涉及一种裂瓷修补新技术。
背景技术
随着生活水平的提高,座便器已是人们日常不可缺少的生活用品,在得到广泛应用的同时,也存在开裂现象严重的致命缺陷,常因此,一件成千上万元的陶瓷产品便整体报废,实在可惜。
现有的克服开裂的主要措施有:1、提高入窑坯体的质量;2、控制坯体入窑水分在2%以下;3、控制预热升温速度,适当减少冷却风量;4、坯体厚薄均匀,配件的大小与粘结部要恰当,粘接用泥料中要加10%-15%的釉料,以略为降低熔化温度,使配件与主体熔结在一起。然而,这些措施,均能起到减少出现开裂现象,其作用甚小,不能从根本上克服裂瓷这一问题。
发明内容
本发明的目的在于克服上述现有技术中的不足之处,提供一种裂瓷修补新技术。
本发明所要解决的技术问题是通过以下技术方案来实现的:
(1)用手磨机把开裂部位磨平;
(2)用10%的高级原子灰配好,补平,经过一个小时高级原子灰自然晾干;
(3)用280目的砂纸打磨平至光滑即可;
(4)配15%的高级福田底漆喷上补好的部位,经过三至四小时自然晾干;
(5)用500目的砂纸打磨平至光滑即可;
(6)用一个口杯加入20%的SW面油、10%SW主剂、10%SW面油固定剂、10%的高级福田稀释剂调配好,再用另一口杯加入20%的莱顺双组份268高浓度清漆、10%SW主剂、10%SW面油固化剂、10%高级福田稀释剂调配好与原陶瓷颜色一致;
(7)用喷枪喷入补好部位,厚度喷在2.5mm~4.5mm;
(8)放入专业烤窑里烤上110度~130度,出窑后由专业检验人员检验。
相对于现有技术,本发明的有益效果是:
1、使裂瓷变废为宝,降低生产成本。
2、环保卫生,节约资源。避免裂瓷污染环境,防止陶瓷土过度开采。
3、本技术修补的裂瓷品质与原瓷一样,经久耐用,永不褪色,色泽鲜艳。
具体实施方式
一种裂瓷修补新技术,包括磨平,补平,打磨,喷漆,打磨,调配,喷漆,入窑八大主要工艺,操作过程如下:
(1)用手磨机把开裂部位磨平;
(2)用10%的高级原子灰配好,补平,经过一个小时高级原子灰自然晾干;
(3)用280目的砂纸打磨平至光滑即可;
(4)配15%的高级福田底漆喷上补好的部位,经过三至四小时自然晾干;
(5)用500目的砂纸打磨平至光滑即可;
(6)用一个口杯加入20%的SW面油、10%SW主剂、10%SW面油固定剂、10%的高级福田稀释剂调配好,再用另一口杯加入20%的莱顺双组份268高浓度清漆、10%SW主剂、10%SW面油固化剂、10%高级福田稀释剂调配好与原陶瓷颜色一致;
(7)用喷枪喷入补好部位,厚度喷在2.5mm~4.5mm;
(8)放入专业烤窑里烤上110度~130度,出窑后由专业检验人员检验。
Claims (1)
1.一种裂瓷修补新技术,其特征包括以下步骤:
(1)用手磨机把开裂部位磨平;
(2)用10%的高级原子灰配好,补平,经过一个小时高级原子灰自然晾干;
(3)用280目的砂纸打磨平至光滑即可;
(4)配15%的高级福田底漆喷上补好的部位,经过三至四小时自然晾干;
(5)用500目的砂纸打磨平至光滑即可;
(6)用一个口杯加入20%的SW面油、10%SW主剂、10%SW面油固定剂、10%的高级福田稀释剂调配好,再用另一口杯加入20%的莱顺双组份268高浓度清漆、10%SW主剂、10%SW面油固化剂、10%高级福田稀释剂调配好与原陶瓷颜色一致;
(7)用喷枪喷入补好部位,厚度喷在2.5mm~4.5mm;
(8)放入专业烤窑里烤上110度~130度,出窑后由专业检验人员检验。