CN102020922B - Water-based single component container primer - Google Patents
Water-based single component container primer Download PDFInfo
- Publication number
- CN102020922B CN102020922B CN2010106167325A CN201010616732A CN102020922B CN 102020922 B CN102020922 B CN 102020922B CN 2010106167325 A CN2010106167325 A CN 2010106167325A CN 201010616732 A CN201010616732 A CN 201010616732A CN 102020922 B CN102020922 B CN 102020922B
- Authority
- CN
- China
- Prior art keywords
- water
- agent
- container
- single component
- based single
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a water-based single component container primer which comprises anticorrosive emulsion, zinc phosphate, aluminum tripolyphosphate, carbon black, dispersing agent, antifoaming agent, multifunctional assistant, anti-flash anti-dust agent, film forming assistant, thickener and deionized water. Compared with the traditional solvent-type container paint, the water-based single component container primer has quite low volatile organic matter content, greatly enhanced environment friendliness and fast drying speed of the film, thus completely satisfying the requirement of the container production line on high rhythmic production efficiency.
Description
Technical field
The present invention relates to the coating manufacturing in the chemical industry field, relate to a kind of manufacturing technology of priming paint of the single-component water-based matched coating to freight container.
Background technology
At present, world's freight container YO is 3,200,000 twenty-feet equivalent units, and year needs about 300,000 tons of coating, is worth about 5,000,000,000 yuan.The coating container that uses in the world wide is essentially solvent based coating.Solvent based coating is the conventional variety that in the freight container anticorrosive construction, obtains extensively, uses for a long time, and through experiment adjustment repeatedly, workability that it is outstanding and antiseptic property obtain checking in container production and use.It is conventional as follows supporting:
| Casing is outside | Box house | |
| The solvent-borne type epoxy zinc rich primer | 30μm | 30μm |
| Finish paint in the solvent-borne type epoxy | 50μm | |
| Solvent-borne type epoxy intermediate coat | 50μm | |
| The solvent-type acrylic finish paint | 40μm | |
| Amount to | 120μm | 80μm |
But since the environmental problem and the flammable potential safety hazard of the contaminative of solvent-borne type coating container, the degree of progress speed that makes the development of water-based coating container.It has higher technology content water-borne coatings, and will progressively in industry, obtain promoting.
Summary of the invention
The invention solves the pollution problem and the potential safety hazard of existing solvent-borne type coating container, developed water-based case of new generation and coated with lacquer---water-based mono-component coating container, the content of description of the invention are the priming paint of water-based mono-component coating container.
Water-based mono-component coating container technology adopts the corollary system of aqueous one-component freight container priming paint and aqueous one-component freight container finish paint (the aqueous one-component freight container finish paint referring to our unit has applied for is designated hereinafter simply as our unit's finish paint) twice application.Aqueous one-component freight container priming paint has excellent antiseptic property and sticking power.It is as follows supporting:
| Casing is outside | Box house | |
| Aqueous one-component freight container priming paint | 50μm | 50μm |
| Aqueous one-component freight container finish paint | 50μm | 50μm |
| Amount to | 100μm | 100μm |
Supporting than the conventional solvent type, its advantage is at feature of environmental protection enhanced simultaneously, has reduced application road number one time, and as onepot coating, has simplified construction technology greatly.
Water-based mono-component priming paint weight percent prescription and production technique thereof are following:
1. weight percent prescription
| Raw material | Weight ratio (%) |
| Deionized water | 10.0-13.0 |
| Dispersion agent | 1.0-1.5 |
| Skimmer | 0.2-0.5 |
| Multifunctional assistant | 0.2-0.4 |
| Carbon black | 2.0-3.0 |
| Zn phosphate | 10.0-12.0 |
| Aluminium triphosphate | 6.0-8.0 |
| Anticorrosion emulsion | 60.0-65.0 |
| The agent of anti-sudden strain of a muscle rust | 0.4-0.6 |
| Film coalescence aid | 2.0-3.5 |
| Thickening material | 0.2-0.5 |
2. ME
After the deionized water weighing; Be put in stainless steel or the enamel stirred pot, under condition of stirring, add dispersion agent, skimmer and multifunctional assistant, add pigment and anticorrosive packing then; Adopt high speed dispersor or sand milling or three roller five equilibriums to be casually arranged with and be equipped with, will be ground to spreading mass and require fineness.
Will above ready-made slurry join in the anticorrosion emulsion, being lower than under 1000 rev/mins the stirring state, add film coalescence aid and thickening material then, the after-filtration that stirs packing is through dispatch from the factory after the assay was approved.
3. starting material
Employed starting material are the commercially available prod: dispersant B YK190, skimmer 024, thickening material BYK425 are German BYK Company products; Multifunctional assistant AMP95 is a U.S. Mykrolis Corp product; Anticorrosion emulsion PR-71K is a U.S. Rhom and Hass product; Anti-sudden strain of a muscle rust agent Sodium Nitrite is a home made article; Film coalescence aid DPNB is the LG-DOW Company products.
Adopt the made water-based mono-component freight container of the present invention priming paint to cooperate the The performance test results of water-based mono-component freight container finish paint (our unit's finish paint) corollary system following:
| Test item | Requirement | Detected result | Examination criteria |
| Salt fog resistance | ≥600h | 600h passes through | GB/T1771-1991 |
| Water tolerance | ≥600h | 600h passes through | GB/T?1733-93 |
| Sticking power (cross-hatching) (level) | ≤1 | 0 | GB/T?9286 |
| Shock-resistance (cm) | ≥50 | 50 pass through | GB/T?1732-93 |
Products obtained therefrom satisfies existing coating container requirement.
Embodiment
The present invention can realize through following instance:
The specific embodiment prescription is tabulated as follows:
(following content is weight ratio)
ME adopts aforementioned priming paint ME.
Adopt the made water-based mono-component freight container of above instance priming paint to cooperate the The performance test results of water-based mono-component freight container finish paint (our unit's finish paint) corollary system following:
| Test item | Requirement | Detected result | Examination criteria |
| Salt fog resistance | ≥600h | 600h passes through | GB/T1771-1991 |
| Water tolerance | ≥600h | 600h passes through | GB/T?1733-93 |
| Sticking power (cross-hatching) (level) | ≤1 | 0 | GB/T?9286 |
| Shock-resistance (cm) | ≥50 | 50 pass through | GB/T?1732-93 |
Claims (1)
1. the aqueous one-component freight container priming paint of an environment-friendly type, its characteristic is following:
The content of each component is following by weight:
Deionized water 10.0-13.0,
Dispersion agent 1.0-1.5,
Skimmer 0.2-0.5,
Multifunctional assistant 0.2-0.4,
Carbon black 2.0-3.0,
Zn phosphate 10.0-12.0,
Aluminium triphosphate 6.0-8.0,
Anticorrosion emulsion 60.0-65.0,
The agent 0.4-0.6 of anti-sudden strain of a muscle rust,
Film coalescence aid 2.0-3.5,
Thickening material 0.2-0.5,
Wherein, described dispersion agent is the BYK190 dispersion agent of German BYK company;
Described skimmer is the BYK024 skimmer of German BYK company;
Described multifunctional assistant is the AMP95 multifunctional assistant of U.S. Mykrolis Corp;
The anticorrosion emulsion of PR-71K that described anticorrosion emulsion is a U.S. Rhom and Hass;
Described anti-sudden strain of a muscle rust auxiliary agent is a Sodium Nitrite;
Described film coalescence aid is the DPNB film coalescence aid of LG-DOW company;
Described thickening material is the BYK425 thickening material of German BYK company.