CN108485410A - A kind of storage tank watery anti-corrosion insulating mold coating and preparation method thereof - Google Patents
A kind of storage tank watery anti-corrosion insulating mold coating and preparation method thereof Download PDFInfo
- Publication number
- CN108485410A CN108485410A CN201810413512.9A CN201810413512A CN108485410A CN 108485410 A CN108485410 A CN 108485410A CN 201810413512 A CN201810413512 A CN 201810413512A CN 108485410 A CN108485410 A CN 108485410A
- Authority
- CN
- China
- Prior art keywords
- parts
- storage tank
- mold coating
- insulating mold
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of storage tank watery anti-corrosion insulating mold coatings.It counts in parts by weight, it is composed of the following components：35 45 parts of lotion, water：15 30 parts, 15 parts of wetting dispersing agents, 15 parts of nano titanium dioxide paste liquid, 0.5 1 parts of antifoaming agent, 15 parts of hydrophobing agent, 5 10 parts of anticorrosive, 28 parts of coalescents, 0.5 5 parts of thickeners, 0.3 5 parts of levelling agents, 0.1 0.3 parts of pH adjusting agents, 10 22 parts of reflective thermal-insulating heat-barrier material, 5 15 parts of pigment, 12 30 parts of fillers, 0.1 0.3 parts of biocide mildewcide compositions.The present invention increases the use function of coating on the basis of insulation, so that coating is had self-cleaning, hydrophobicity, anticorrosive property, is a kind of composite multifunction type coating.
Description
Technical field
The present invention relates to a kind of technologies and preparation method thereof of storage tank watery anti-corrosion insulating mold coating.
Background technology
Insulating moulding coating plays that heat-reflecting heat-insulating, heat radiation be heat-insulated or heat insulation heat preservation energy-saving effect as a kind of heat-insulated means
Fruit has not insignificant social and economic implications to industry with civilian.To the research origin of insulating moulding coating in aircraft temperature control
Needs, then use it in petroleum industry, achieve good cooling-down effect, reduce the volatilization of oil product, ensure that storage
The safety of tank.Traditional insulating moulding coating only has simple function, does not meet the requirement of economic environmental protection.The product of the present invention is one
Kind have efficiently, thin layer, heat-insulation and heat-preservation, decoration, anti-corrosion, electrically isolate from integrated novel anticorrosion reflecting heat insulation paint, coating
The three-dimensional network hollow-core construction to be linked together by closing microballon, such nano-hollow ceramic microsphere can be formed in body surface
The still air group for folding folder one by one, that is, heat-insulation and heat-preservation unit one by one are formd between microballon.The heat reflection of coating
Rate is 85% or more, can largely reflect infrared ray, prevent infrared ray from being heated to object, the thermal coefficient of coating is
0.04W/m.K can effectively inhibit radiant heat and the heat conduction of the sun and infrared ray, heat-insulation and heat-preservation to inhibit efficiency up to 85% left side
It is right.
Invention content
The present invention mainly develops a kind of technology of preparing of storage tank watery anti-corrosion insulating mold coating.Purpose is for petrochemical industry
Storage tank, metal Roof etc. provide a kind of watery anti-corrosion insulating mold coating.
A kind of storage tank watery anti-corrosion insulating mold coating, is counted in parts by weight, composed of the following components：
35-45 parts of lotion, water：15-30 parts, 1-5 parts of wetting dispersing agents, 1-5 parts of nano titanium dioxide paste liquid, 0.5-1 parts
Antifoaming agent, 1-5 parts of hydrophobing agent, 5-10 parts of anticorrosive, 2-8 parts of coalescents, 0.5-5 parts of thickeners, 0.3-5 parts of streams
Flat agent, 0.1-0.3 parts of pH adjusting agents, 10-22 parts of reflective thermal-insulating heat-barrier material, 5-15 parts of pigment, 12-30 parts of fillers,
0.1-0.3 parts of biocide mildewcide compositions.
The nano titanium dioxide paste liquid is composed of the following components：
Nano-titanium dioxide:Dispersant：The mass ratio of propylene glycol methyl ether acetate is 1.0：0.1-0.2:2-3.
The wetting dispersing agent be BYK-180, BYK-190, TEGO750, TEGO 715, EFKA4530, EFKA 6225,
It is one or more in ELEMENTIS FA620, W-518.
The antifoaming agent is TEGO 902W, TEGO815, BYK024, BYK 094, in ELEMENTIS DF7010, W052
It is one or more；
The levelling agent is one or both of SLIP-AYD FS444, BYK-3440.
The hydrophobing agent is one or both of TEGO phobe1000, Synthro-pel PA.
The anticorrosive is one or both of HALOX 430JM, 515 HALOX.
The reflective thermal-insulating heat-barrier material be Solaproof SP-105C, Hollow Glass H40 hollow glass micropearls,
It is one or more in AKZO 920DE40.
The lotion is Celanese VAE lotion CP-143, ROHM AND HAAS PR-71K, and east joins one in chemical industry BA-2902
Kind is a variety of.
The filler is one or more in calcined kaolin, talcum powder, barium sulfate, alumina silicate.
Include the following steps：
1) preparation of nano titanium dioxide paste liquid
By nano-titanium dioxide:Dispersant：The mass ratio of propylene glycol methyl ether acetate is 1：0.1-0.2:The proportioning of 2-3 is mixed
Nano-beads mill processing 3-8 times, 100 nanometers of fineness ＜ is carried out after conjunction, and nano slurry is made；
2) preparation of storage tank watery anti-corrosion insulating mold coating
By lotion, water, nano titanium dioxide paste liquid, wetting dispersing agent, antifoaming agent, pigment, filler, anticorrosive, pH value
Conditioning agent is prepared according to the above ratio, by 800-1000rpm be dispersed with stirring fineness be 60 microns hereinafter, be added coalescents,
Reflective thermal-insulating heat-barrier material, thickener, levelling agent, hydrophobing agent, biocide mildewcide are prepared into storage tank watery anti-corrosion thermal insulation separation
Hot coating.
Advantages of the present invention：
The present invention prepares nano titanium dioxide paste using nano particle surface modifying technology, then they and lotion, face are filled out
Material, insulation auxiliary agent etc. are matched in proportion is prepared into watery anti-corrosion insulating mold coating.The paint has excellent adhesive force, soft
Good toughness, water resistance, ageing-resistant, wet-heat resisting, exposes heat and Frozen-thawed cycled, anticorrosion, surfacing, usage amount at insulation
The features such as low, using water as decentralized medium, non-environmental-pollution, safety and environmental protection.
Specific implementation mode
Embodiment 1：
Storage tank watery anti-corrosion insulating mold coating of the present invention is mono-component aqueous coating, is counted in parts by weight, specifically
Formula is as follows：
(alumina silicate, talcum powder, kaolin=1 in filler:1:1 weight ratio)
800-1000rpm is dispersed with stirring to 60 microns of fineness ＜, is added：
Watery anti-corrosion insulating mold coating is made.
Wherein, nano titanium dioxide paste liquid is prepared as：
By nano-titanium dioxide:Dispersant：The mass ratio of propylene glycol methyl ether acetate is 1：0.1-0.2:The proportioning of 2-3 is mixed
Nano-beads mill processing 3-8 times, 100 nanometers of fineness ＜ is carried out after conjunction, and nano slurry is made.
Claims (10)
1. a kind of storage tank watery anti-corrosion insulating mold coating, it is characterised in that：It counts in parts by weight, by following components group
At：
35-45 parts of lotion, water：15-30 parts, 1-5 parts of wetting dispersing agents, 1-5 parts of nano titanium dioxide paste liquid, 0.5-1 parts of defoamings
Agent, 1-5 parts of hydrophobing agent, 5-10 parts of anticorrosive, 2-8 parts of coalescents, 0.5-5 parts of thickeners, 0.3-5 parts of levellings
Agent, 0.1-0.3 parts of pH adjusting agents, 10-22 parts of reflective thermal-insulating heat-barrier material, 5-15 parts of pigment, 12-30 parts of fillers, 0.1-
0.3 part of biocide mildewcide composition.
2. watery anti-corrosion insulating mold coating described in accordance with the claim 1, it is characterised in that：The nano titanium dioxide paste
Liquid is composed of the following components：
Nano-titanium dioxide:Dispersant：The mass ratio of propylene glycol methyl ether acetate is 1.0：0.1-0.2:2-3.
3. storage tank described in accordance with the claim 1 watery anti-corrosion insulating mold coating, it is characterised in that：The wetting and dispersing
Agent is BYK-180, BYK-190, TEGO750, TEGO 715, EFKA4530, EFKA 6225, ELEMENTIS FA620, W-518
In it is one or more.
4. storage tank described in accordance with the claim 1 watery anti-corrosion insulating mold coating, it is characterised in that：The antifoaming agent is
TEGO 902W, TEGO815, BYK024, BYK 094, it is one or more in ELEMENTIS DF7010, W052；
The levelling agent is one or both of SLIP-AYD FS444, BYK-3440.
5. storage tank described in accordance with the claim 1 watery anti-corrosion insulating mold coating, it is characterised in that：The hydrophobing agent is
One or both of TEGO phobe1000, Synthro-pel PA.
6. storage tank described in accordance with the claim 1 watery anti-corrosion insulating mold coating, it is characterised in that：The anticorrosive
For one or both of HALOX 430JM, 515 HALOX.
7. storage tank described in accordance with the claim 1 watery anti-corrosion insulating mold coating, it is characterised in that：The reflective thermal-insulating
Heat-barrier material is Solaproof SP-105C, Hollow Glass H40 hollow glass micropearls, one kind in AKZO 920DE40
Or it is a variety of.
8. storage tank described in accordance with the claim 1 watery anti-corrosion insulating mold coating, it is characterised in that：The lotion is plug
Nice VAE lotion CP-143, ROHM AND HAAS PR-71K are drawn, it is one or more in the connection chemical industry BA-2902 of east.
9. storage tank described in accordance with the claim 1 watery anti-corrosion insulating mold coating, it is characterised in that：The filler is to forge
It burns one or more in kaolin, talcum powder, barium sulfate, alumina silicate.
10. a kind of any storage tank preparation methods of watery anti-corrosion insulating mold coating of claim 1-9, feature
It is：Include the following steps：
1) preparation of nano titanium dioxide paste liquid
By nano-titanium dioxide:Dispersant：The mass ratio of propylene glycol methyl ether acetate is 1：0.1-0.2:After the proportioning mixing of 2-3
It carries out nanometer bead mill to handle 3-8 times, 100 nanometers of fineness ＜, nano slurry is made；
2) preparation of storage tank watery anti-corrosion insulating mold coating
Lotion, water, nano titanium dioxide paste liquid, wetting dispersing agent, antifoaming agent, pigment, filler, anticorrosive, pH value are adjusted
Agent is prepared according to the above ratio, is dispersed with stirring fineness by 800-1000rpm as 60 microns hereinafter, coalescents, reflection is added
Heat preserving and insulating material, thickener, hydrophobing agent, levelling agent, biocide mildewcide are prepared into the painting of storage tank watery anti-corrosion insulation
Material.