CN102019269A - 一种玻璃钢制品的分色喷涂工艺 - Google Patents
一种玻璃钢制品的分色喷涂工艺 Download PDFInfo
- Publication number
- CN102019269A CN102019269A CN201010510751XA CN201010510751A CN102019269A CN 102019269 A CN102019269 A CN 102019269A CN 201010510751X A CN201010510751X A CN 201010510751XA CN 201010510751 A CN201010510751 A CN 201010510751A CN 102019269 A CN102019269 A CN 102019269A
- Authority
- CN
- China
- Prior art keywords
- glass fiber
- color
- fiber reinforced
- spraying
- coating resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于玻璃钢领域,具体涉及一种玻璃钢制品的分色喷涂工艺,其方案主要包括以下步骤:首先在模具上粘贴一层纸膜,然后在纸膜上喷涂一种颜色胶衣层,接着将需要喷涂另一种颜色的胶衣层区域内的纸膜撕去,然后在模具整个区域内喷涂另一种颜色胶衣层,待胶衣层在常温下凝胶后,在胶衣层上铺设树脂玻璃纤维层,高温下固化成型,之后常温下冷却后起模,撕去纸膜即得产品。通过以上技术方案,玻璃钢制品表面的不同颜色区域间分界清楚,同时不同颜色区域的分界处无明显对接痕。
Description
技术领域
本发明属于玻璃钢领域,具体涉及一种玻璃钢制品的分色喷涂工艺。
背景技术
目前在玻璃钢领域,大部分玻璃钢产品表面的分色喷涂,都是在需要不同颜色的区域内喷涂相应颜色的胶衣层。然而这种喷涂方式易造成不同颜色区域间的分界线模糊不清。
发明内容
本发明的目的是提供一种玻璃钢制品的分色喷涂工艺,保证产品不同颜色区域间的分界清晰。
为实现上述目的,本发明采用了以下技术方案,一种玻璃钢制品的分色喷涂工艺,主要包括以下步骤:
a、在模具上粘贴一层纸膜;
b、在纸膜上喷涂一种颜色胶衣层
c、将需要喷涂另一种颜色胶衣层区域内的纸膜撕去;
d、在模具整个区域内喷涂另一种颜色胶衣层
e、待胶衣层在常温下凝胶后,在胶衣层上铺设树脂玻璃纤维层;
f、高温下固化成型;
g、常温下冷却后起模,撕去纸膜即得产品。
通过以上技术方案,玻璃钢制品表面的不同颜色区域间分界清楚同时不同颜色区域的分界处无明显对接痕。
附图说明
图1是步骤b的层状结构示意图;
图2是步骤c的层状结构示意图;
图3是步骤d的层状结构示意图;
图4是步骤e的层状结构示意图;
图5是产品的层状结构示意图。
具体实施方式
一种玻璃钢制品的表面处理方法,主要包括以下步骤:
a、在模具上粘贴一层纸膜;
b、在纸膜上喷涂一种颜色胶衣层,如图1所示;
c、将需要喷涂另一种颜色胶衣层区域内的纸膜撕去,这样也就连同纸膜上的胶衣层也一起除去,如图2所示;
d、在模具整个区域内喷涂另一种颜色胶衣层,并将前一种颜色胶衣层覆盖。这样就在与模具接合面上得到两种颜色的胶衣层,如图3所示;
e、待胶衣层在常温下凝胶后,在胶衣层上铺设树脂玻璃纤维层,如图4所示;
f、高温下固化成型;
g、常温下冷却后起模,撕去纸膜即得包括两种不同颜色的产品,如图5所示。
所述固化成型温度为60℃-70℃,固化成型时间为3-4小时。
所述胶衣层在常温下的凝胶时间为20-30分钟,达到果冻状的半固化状态。
实施例1中,固化成型温度为60℃时,固化成型时间为4小时;固化成型温度为65℃时,固化成型时间为3.5小时,固化成型温度为70℃时,固化成型时间为3小时。
Claims (3)
1.一种玻璃钢制品的分色喷涂工艺,主要包括以下步骤:
a、在模具上粘贴一层纸膜;
b、在纸膜上喷涂一种颜色胶衣层;
c、将需要喷涂另一种颜色胶衣层区域内的纸膜撕去;
d、在模具整个区域内喷涂另一种颜色胶衣层;
e、待胶衣层在常温下凝胶后,在胶衣层上铺设树脂玻璃纤维层;
f、高温下固化成型;
g、常温下冷却后起模,撕去纸膜即得产品。
2.根据权利要求1所述的一种玻璃钢制品的分色喷涂工艺,其特征在于:所述固化成型温度为60℃-70℃,固化成型时间为3-4小时。
3.根据权利要求1所述的一种玻璃钢制品的分色喷涂工艺,其特征在于:所述胶衣层在常温下的凝胶时间为20℃-30℃。