CN102010217B - 钢包热喷涂用喷涂料 - Google Patents
钢包热喷涂用喷涂料 Download PDFInfo
- Publication number
- CN102010217B CN102010217B CN 201010609961 CN201010609961A CN102010217B CN 102010217 B CN102010217 B CN 102010217B CN 201010609961 CN201010609961 CN 201010609961 CN 201010609961 A CN201010609961 A CN 201010609961A CN 102010217 B CN102010217 B CN 102010217B
- Authority
- CN
- China
- Prior art keywords
- ladle
- purity
- spray paint
- alumine
- mgo
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种钢包热喷涂用喷涂料，可有效解决钢包热喷涂修补的问题技术方案是，该喷涂料是由以下重量百分比计的：中档镁砂65-85％，高铝矾土5-15％，矾土基尖晶石5-15％，结合剂2-10％，增塑剂1-5％混合均匀制成；所说的中档镁砂为MgO，纯度≥90％；高铝矾土为Al2O3，纯度≥80％；矾土基尖晶石为Al2O3，纯度≥70％或MgO，纯度≥26％；所说的结合剂为水合氧化铝、磷酸盐、水玻璃、铝溶胶的一种或两种以上的组合；所说的增塑剂为膨润土或粘土等，本发明是一种镁质喷涂料，可在钢包使用间隙通过热喷涂施工对钢包包衬进行修补，使钢包使用寿命长，吨钢耐材消耗低，经济和社会效益巨大。
Description
一、技术领域
本发明涉及涂料，特别是一种钢包热喷涂用喷涂料。
二、背景技术
为了保证钢包使用效果，钢包喷涂修补是常有之事。常规喷涂料只能用于冷态喷补，需要将钢包暂停使用，自然冷却(通常要2-3天)之后才能进行修补作业。而钢包再次投入生产时，需要预先烘烤至1000-1400℃。整个过程周期很长，既延误生产又耗费能源。因此，喷涂料的改进和创新势在必行。
三、发明内容
针对上述情况，为克服现有技术之缺陷，本发明之目的就是提供一种钢包热喷涂用喷涂料，可有效解决钢包热喷涂修补的问题。
本发明解决的技术方案是，该喷涂料是由以下重量百分比计的：中档镁砂65-85％，高铝矾土5-15％，矾土基尖晶石5-15％，结合剂2-10％，增塑剂1-5％混合均匀制成；所说的中档镁砂为MgO，纯度≥90％；高铝矾土为Al2O3，纯度≥80％；矾土基尖晶石为Al2O3，纯度≥70％或MgO，纯度≥26％(尖晶石——镁的铝酸盐，化学式MgO·Al2O3；矾土基尖晶石：以高铝矾土为主要原料生产的尖晶石。其指标一般以MgO和Al2O3各自的含量表示)；所说的结合剂为水合氧化铝、磷酸盐、水玻璃、铝溶胶的一种或两种以上的组合；所说的增塑剂为膨润土或粘土等。
本发明是一种镁质喷涂料，可在钢包使用间隙通过热喷涂施工对钢包包衬进行修补，使钢包使用寿命长，吨钢耐材消耗低，经济和社会效益巨大。
四、具体实施方式
以下结合实施例对本发明的具体实施方式作详细说明。
实施例1
本发明在具体实施中可采用以下重量百分比计的：中档镁砂65％，高铝矾土15％，矾土基尖晶石15％，结合剂4％，增塑剂1％混合在一起，由搅拌机搅拌均匀制成。
实施例2
本发明在具体实施中还可采用以下重量百分比计的：中档镁砂70％，高铝矾土10％，矾土基尖晶石10％，结合剂6％，增塑剂4％混合在一起，由搅拌机搅拌均匀制成。
实施例3
本发明在具体实施中还可采用以下重量百分比计的：中档镁砂78％，高铝矾土8％，矾土基尖晶石8％，结合剂4％，增塑剂2％混合在一起，由搅拌机搅拌均匀制成。
实施例4
本发明在具体实施中还可采用以下重量百分比计的：中档镁砂68％，高铝矾土11％，矾土基尖晶石11％，结合剂7％，增塑剂3％混合在一起，由搅拌机搅拌均匀制成。
在实施例1-4中，所称的中档镁砂、高铝矾土、矾土基尖晶石、结合剂和增塑剂同发明内容部分中给出的组分相同，不再一一列举。
本发明的喷涂料可以直接对1000℃以上的钢包包衬进行喷涂修补，使钢包寿命增加4～6倍，大大降低了吨钢耐材消耗，可节约吨钢耐材50％以上(注：如有不妥，请给出准确的节约量)。本发明喷涂料经测试，质量好，其测试指标如下表：
本发明效果之好是未曾预料到的，是发明人经科学研究和实验，并对实践总结后作出的创造性劳动的结晶，是钢包喷涂上的创新，经济价值和技术价值巨大。
Claims (5)
1.一种钢包热喷涂用喷涂料，其特征在于，是由以下重量百分比计的：中档镁砂65-85%，高铝矾土5-15%，矾土基尖晶石5-15%，结合剂2-10%，增塑剂1-5%混合均匀制成；
所述的中档镁砂为MgO，纯度≥90%；高铝矾土为Al2O3，纯度≥80%；矾土基尖晶石为Al2O3，纯度≥70%或MgO，纯度≥26%；所述的结合剂为水合氧化铝、磷酸盐、水玻璃、铝溶胶的一种或两种以上的组合；所述的增塑剂为膨润土或粘土。
2.根据权利要求1所述的钢包热喷涂用喷涂料，其特征在于，是由以下重量百分比计的：中档镁砂65%，高铝矾土15%，矾土基尖晶石15%，结合剂4%，增塑剂1%混合在一起，由搅拌机搅拌均匀制成。
3.根据权利要求1所述的钢包热喷涂用喷涂料，其特征在于，是由以下重量百分比计的：中档镁砂70%，高铝矾土10%，矾土基尖晶石10%，结合剂6%，增塑剂4%混合在一起，由搅拌机搅拌均匀制成。
4.根据权利要求1所述的钢包热喷涂用喷涂料，其特征在于，是由以下重量百分比计的：中档镁砂78%，高铝矾土8%，矾土基尖晶石8%，结合剂4%，增塑剂2%混合在一起，由搅拌机搅拌均匀制成。
5.根据权利要求1所述的钢包热喷涂用喷涂料，其特征在于，是由以下重量百分比计的：中档镁砂68%，高铝矾土11%，矾土基尖晶石11%，结合剂7%，增塑剂3%混合在一起，由搅拌机搅拌均匀制成。