CN101955696B - Attapulgite window screen paint with function of eradicating mosquitoes - Google Patents

Abstract

The invention discloses attapulgite window screen paint with the function of eradicating mosquitoes. The essential points of the technical scheme are that the attapulgite window screen paint with the function of eradicating mosquitoes comprises paste attapulgite clay, pyrethrum, marigold, mint, garlic, molasses, sucrose fatty acid ester, super absorbent resin, methyl paraben, propyl paraben and deionized water. The attapulgite window screen paint with the function of eradicating mosquitoes is prepared by the following steps of: stirring the mixed material of the paint; crushing and pulping to form a mixture; inputting the mixture into a multifunctional colloid mill for grinding to obtain a paste mixture; and canning to obtain the finished product of the attapulgite window screen paint with the function of eradicating mosquitoes. When mosquitoes sniff the smell of the attapulgite window screen paint with the function of eradicating mosquitoes, the mosquitoes which do not like the smell fly away from the window screen, and the mosquitoes which like the smell directly throw on the attapulgite window screen paint with the function of eradicating mosquitoes for entering to the inside of a room and are stuck by the attapulgite window screen paint with the function of eradicating mosquitoes. Pesticide in the paint can quickly eradicate the mosquitoes. The attapulgite window screen paint with the function of eradicating mosquitoes is applicable to eradicating the mosquitoes and other pests.

Description

Attapulgite kill mosquito window screening coating

Technical field

The present invention relates to mosquitocide, be specifically related to a kind of Attapulgite kill mosquito window screening coating.

Background technology

Be the most rampant movable season of mosquito summer, and skin understand " red born of the same parents " after by mosquito bite, and is not only ugly but also very itch incomparably; The skin so the allergy of scratching where it itches are common phenomena, and more dangerous is that mosquito has a large amount of poisonous germs on one's body, brings some fearful transmissible disease to human body; Mosquito has had a strong impact on people's orthobiosis and sleep; Be detrimental to health, eliminating mosquito is to guarantee human health, avoids the key of pathophoresis.

Be to adopt aerosol bomb, electric mosquito repellent, mosquito repellent liquid and mosquito-repellent perfume to eliminate mosquito at present mostly; Sterilant can cause people's chronic poisoning; Acute poisoning symptoms such as dizzy, nauseating take place, and aerial fog pesticide and insecticidal emulsifiable concentrate adopt the higher solvent of toxicity, contact the function that these solvents can damage hemopoietic system for a long time; The burning-point of most of aerial fog pesticides is all very low, causes fire easily.

Can mosquito be completely cut off outdoor with screen window, still, screen window can only passively be kept away mosquito can not kill mosquitoes, also has chemical industry synthetic sterilant is sprayed on the screen window, and practical effect is also bad, and the parasiticidal while also has influence on people's health.

Summary of the invention

The objective of the invention is to overcome weak point in the prior art, a kind of Attapulgite kill mosquito window screening coating is provided.

Attapulgite kill mosquito window screening coating is made up of paste attapulgite clay, pyrethrum, Flower of Aztec Marigold, peppermint, garlic, molasses, fatty acid cane sugar ester, High hydrophilous resin, Tegosept M, propylben and deionized water.After the batching of Attapulgite kill mosquito window screening coating stirred, pulverize making beating and be mixture, mixture is imported to grind in the multi-functional colloid mill be paste mixture, canned is the finished product of Attapulgite kill mosquito window screening coating.

The attapulgite clay soil property is fine and smooth, smooth surface, and quality is lighter; Be viscosity and plasticity-when moist; Its viscosity can reach more than the 3000mPas, helps the bonding between the raw material, and paste attapulgite clay is a kind of thixotropy and the special good natural magnesium aluminium silicate gel of gumminess; It is neutral that the pH value is, and the viscosity of attapulgite clay, absorption property and sticking power all are greatly improved.Paste attapulgite clay adds in the coating solution, under external force stirs, forms stable not stratified gelinite fast, and viscosity and thixotropy are preferably arranged.

Contain pyrethrin and cinerin in the flower of pyrethrum, pyrethrin is claimed pyrethrin again, is a kind of environment-friendly pesticide, after mosquito contact pyrethrum, will neural paralysis, and poison and dead.Between the autumn in summer, to pluck being about to open pyrethrum flower, dry back is subsequent use.

Flower of Aztec Marigold is the annual herb flowers, and plant branches and leaves foul smelling flavor so be " smelly chrysanthemum " again, selects for use fresh flower and branches and leaves subsequent use.

Peppermint is a kind of fragrant crop that extraordinary economic worth is arranged, and has special fragrance, pungent sense and cool sense.Select for use fresh peppermint branches and leaves subsequent use.

Garlic is a per nnial herb, and underground bulb distinguish is divided into purple skin kind and white skin kind by the color of the leather difference.It is peppery to distinguish the flavor of, and irritating smell is arranged.

Pyrethrum, Flower of Aztec Marigold, peppermint and garlic all are that mosquito dislikes approaching smell.

Molasses are that sugar refinery is in the sugaring process; The mother liquor that syrup is left after concentrating, impurity is more, but has special fragrance; Mosquito is liked the fragrance of molasses; Molasses also help covering the smell that mosquito dislikes in the Attapulgite waterproof kill mosquito window screening coating simultaneously, and attracting mosquitoes contact window screening is killed by the pyrethrum in the Attapulgite kill mosquito window screening coating.

Fatty acid cane sugar ester aqueous solution toughness, and wettability is arranged, be a kind of emulsifying agent, quality improver and preservation agent, help preventing Attapulgite kill mosquito window screening paint aging.

The water regain of High hydrophilous resin is big, can reach hundreds of times even thousands of times of sole mass, and absorption speed is fast, can in the several seconds, generate gel, and water retention property is good.

Tegosept M has the broad-spectrum antibacterial effect, to Gram-positive, and negative bacteria, yeast and mould have very strong restraining effect, and the low and safety economy of working concentration uses validity period long.Tegosept M is compatible with various chemical substances easily, and the composite use of Tegosept M and propylben is to reach better preservative effect.

The present invention is achieved through following technical proposals:

1, the batching of Attapulgite kill mosquito window screening coating is made up of following component by weight percentage: paste attapulgite clay 15～45%, pyrethrum 10～45%, Flower of Aztec Marigold 2～10%, peppermint 1～8%, garlic 1～6%, molasses 1～6%, fatty acid cane sugar ester 0.1～1%, High hydrophilous resin 0.01～1%, Tegosept M 0.01～0.5%, propylben 0.01～0.5% and deionized water 5～35%.

The production technique of said paste attapulgite clay is: (1) selects for use Attapulgite sludge slurry to be body material, and Attapulgite sludge slurry is made up of following component by weight percentage: attapulgite clay 15～35% and water 65～85%; (2) sodium is handled: Attapulgite sludge slurry is transported in the stirrer, stirs after adding sodium hydroxide, be transported in the sodium pond ageing 1～7 day through the Attapulgite sludge slurry after stirring; The sodium batching is made up of following component by weight percentage: Attapulgite sludge slurry 95～99.5% and sodium hydroxide 0.5～5%; (3) acidification: Attapulgite sludge slurry after the sodium is transported in the stirrer, stirs after adding concentration and be 98% sulfuric acid, be transported in the acidulated pool ageing 1～3 day through the Attapulgite sludge slurry after stirring; The acidifying batching is made up of following component by weight percentage: Attapulgite sludge slurry 92～99.5% after the sodium and concentration are 98% sulfuric acid 0.5～8%; (4) washing and sieve decon: the slurry of the Attapulgite sludge after the acidifying is transported in the settling tank, soaks, dash with air pump and turn over; The sieve decon; Post precipitation is emitted soaked in water, and the slurry transportation of post precipitation is arrived in the finished product pond, and the mud of post precipitation is paste attapulgite clay; The washing batching is made up of following component by weight percentage: Attapulgite sludge slurry 25～65% and water 35～75% after the acidifying; Paste attapulgite clay is made up of following component by weight percentage: attapulgite clay 5～40% and water 60～95%.

Above-mentioned production technique is to adopt " production technique of paste attapulgite clay " in application on August 25th, 2008 by the inventor, and the Chinese patent publication number is: CN101348257, open day: on January 21st, 2009.

2, the working method of Attapulgite kill mosquito window screening coating: 1. the batching of Attapulgite kill mosquito window screening coating is added and carry out in the stirrer after stirring at low speed mixes; Pulverizing making beating in the input pulverizing hollander is the mixture of Attapulgite kill mosquito window screening coating; The speed control of stirrer is at 500～800 rev/mins; The stirring at low speed time was controlled at 5～15 minutes, and the speed control of pulverizing hollander is at 2500～3000 rev/mins; The purpose of stirring at low speed is that various batchings are stirred, and helps pulverizing the works better of hollander; 2. the mixture that 1. step is obtained is imported to grind in the multi-functional colloid mill and is paste mixture; Particle fineness is less than 0.025 millimeter; The speed control of multi-functional colloid mill is at 2900 rev/mins, with paste mixture canned be the finished product of Attapulgite kill mosquito window screening coating.

Pyrethrum, Flower of Aztec Marigold, peppermint and garlic in the Attapulgite kill mosquito window screening coating proportioning do not need water to carry out the production technique of soaking and extracting effective ingredient; But adopt the production technique of directly pulverizing making beating and grinding; Make full use of whole effective ingredients in the raw material; Do not have waste sludge discharge, not only practiced thrift production cost, also improved the quality of Attapulgite kill mosquito window screening coating greatly.

Attapulgite kill mosquito window screening paint adhesion is good, and it is high to kill mosquito efficient, and have anticorrosion, fresh-keeping, preserve moisture and characteristics that the kill mosquito validity period is long.

Smell the smell of Attapulgite kill mosquito window screening coating when mosquito after; The mosquito that dislikes this smell can fly away away from window screening; Like the mosquito of this smell, in the ability inlet chamber, can directly pounce on the Attapulgite kill mosquito window screening coating; By the adhesion of Attapulgite kill mosquito window screening coating institute, the sterilant in the coating is killed mosquito fast.

The method of use of Attapulgite kill mosquito window screening coating: on window screening, brushing once can keep 35～45 days kill mosquito validity period with Attapulgite kill mosquito window screening coating direct brushing, and the kill mosquito rate is greater than 98%.

Attapulgite kill mosquito window screening coating does not destroy the eubiosis to the toxicological harmless of people and animals poultry, and no resistance, but natural degradation are free from environmental pollution.

Attapulgite kill mosquito window screening coating is applicable to kill mosquitoes and other insect.

Embodiment

Below in conjunction with embodiment the present invention is done further description:

1, the batching of Attapulgite kill mosquito window screening coating is made up of following component by weight percentage: paste attapulgite clay 35%, pyrethrum 24%, Flower of Aztec Marigold 8%, peppermint 6%, garlic 3%, molasses 3.2%, fatty acid cane sugar ester 0.2%, High hydrophilous resin 0.5%, Tegosept M 0.06%, propylben 0.04% and deionized water 20%.

2, the working method of Attapulgite kill mosquito window screening coating: 1. the batching of Attapulgite kill mosquito window screening coating is added and carry out in the stirrer after stirring at low speed mixes; Pulverizing making beating in the input pulverizing hollander is the mixture of Attapulgite kill mosquito window screening coating; The speed control of stirrer is at 600 rev/mins; The stirring at low speed time was controlled at 10 minutes, and the speed control of pulverizing hollander is at 2800 rev/mins; The purpose of stirring at low speed is that various batchings are stirred, and helps pulverizing the works better of hollander; 2. the mixture that 1. step is obtained is imported to grind in the multi-functional colloid mill and is paste mixture; Particle fineness is less than 0.025 millimeter; The speed control of multi-functional colloid mill is at 2900 rev/mins, with paste mixture canned be the finished product of Attapulgite kill mosquito window screening coating.

Claims (1)

1. Attapulgite kill mosquito window screening coating; It is characterized in that the batching of Attapulgite kill mosquito window screening coating is made up of following component by weight percentage: paste attapulgite clay 15～45%, pyrethrum 10～45%, Flower of Aztec Marigold 2～10%, peppermint 1～8%, garlic 1～6%, molasses 1～6%, fatty acid cane sugar ester 0.1～1%, High hydrophilous resin 0.01～1%, Tegosept M 0.01～0.5%, propylben 0.01～0.5% and deionized water 5～35%;

The working method of said Attapulgite kill mosquito window screening coating: 1. the batching of Attapulgite kill mosquito window screening coating is added and carry out in the stirrer after stirring at low speed mixes; Pulverizing making beating in the input pulverizing hollander is the mixture of Attapulgite kill mosquito window screening coating; The speed control of stirrer is at 500～800 rev/mins; The stirring at low speed time was controlled at 5～15 minutes, and the speed control of pulverizing hollander is at 2500～3000 rev/mins; 2. the mixture that 1. step is obtained is imported to grind in the multi-functional colloid mill and is paste mixture; Particle fineness is less than 0.025 millimeter; The speed control of multi-functional colloid mill is at 2900 rev/mins, with paste mixture canned be the finished product of Attapulgite kill mosquito window screening coating;

The production technique of said paste attapulgite clay is: (1) selects for use Attapulgite sludge slurry to be body material, and Attapulgite sludge slurry is made up of following component by weight percentage: attapulgite clay 15～35% and water 65～85%; (2) sodium is handled: Attapulgite sludge slurry is transported in the stirrer, stirs after adding sodium hydroxide, be transported in the sodium pond ageing 1～7 day through the Attapulgite sludge slurry after stirring; The sodium batching is made up of following component by weight percentage: Attapulgite sludge slurry 95～99.5% and sodium hydroxide 0.5～5%; (3) acidification: Attapulgite sludge slurry after the sodium is transported in the stirrer, stirs after adding concentration and be 98% sulfuric acid, be transported in the acidulated pool ageing 1～3 day through the Attapulgite sludge slurry after stirring; The acidifying batching is made up of following component by weight percentage: Attapulgite sludge slurry 92～99.5% after the sodium and concentration are 98% sulfuric acid 0.5～8%; (4) washing and sieve decon: the slurry of the Attapulgite sludge after the acidifying is transported in the settling tank, soaks, dash with air pump and turn over; The sieve decon; Post precipitation is emitted soaked in water, and the slurry transportation of post precipitation is arrived in the finished product pond, and the mud of post precipitation is paste attapulgite clay; The washing batching is made up of following component by weight percentage: Attapulgite sludge slurry 25～65% and water 35～75% after the acidifying; Paste attapulgite clay is made up of following component by weight percentage: attapulgite clay 5～40% and water 60～95%.