KR20030042216A - functional paint using a natural material and method for manufacturing that paint - Google Patents

functional paint using a natural material and method for manufacturing that paint Download PDF

Info

Publication number
KR20030042216A
KR20030042216A KR1020010072877A KR20010072877A KR20030042216A KR 20030042216 A KR20030042216 A KR 20030042216A KR 1020010072877 A KR1020010072877 A KR 1020010072877A KR 20010072877 A KR20010072877 A KR 20010072877A KR 20030042216 A KR20030042216 A KR 20030042216A
Authority
KR
South Korea
Prior art keywords
powder
raw
natural materials
clay
paint
Prior art date
Application number
KR1020010072877A
Other languages
Korean (ko)
Inventor
박영배
Original Assignee
박영배
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 박영배 filed Critical 박영배
Priority to KR1020010072877A priority Critical patent/KR20030042216A/en
Publication of KR20030042216A publication Critical patent/KR20030042216A/en

Abstract

PURPOSE: Provided are a functional coating using a natural material which reduces environmental pollution, is not easily discolored after coating, and facilitates anti-corrosion, anti-microbial and anti-moisture functions, as well as far-infrared emitting function, and a method for producing the same. CONSTITUTION: The functional coating comprises 40-50 wt% of clay powder, 5-10 wt% of raw ore powder for pigment, 20-25 wt% of water, and 20-30 wt% of acrylic resin. The clay powder and raw ore powder are crushed so as to have a particle size of 325-1200 mesh. 5-10 wt% of pyrophyllite powder or a mixture of 5-7 wt% of pyrophyllite powder and 2-5 wt% of carbon powder is used as the raw ore powder.

Description

천연 물질을 이용한 기능성 도료 및 그의 제조방법{functional paint using a natural material and method for manufacturing that paint}Functional paint using a natural material and method for manufacturing that paint}

본 발명은 천연 물질을 이용한 기능성 도료 및 그의 제조방법에 관한 것으로, 특히 원적외선을 방사하는 백토 분체를 주원료로 하고, 안료용 돌가루, 물 및 아크릴 수지를 적정비율로 혼합하여, 탈취, 항균 및 내구성을 증진시키는 천연 물질을 이용한 기능성 도료 및 그의 제조방법에 관한 것이다.The present invention relates to a functional paint using a natural material and a method for manufacturing the same, in particular, the clay powder which emits far infrared rays as a main raw material, by mixing the stone powder, water and acrylic resin for pigment in an appropriate ratio, deodorization, antibacterial and durability It relates to a functional paint using a natural material to enhance the and a method for producing the same.

일반적으로 백토는 벤토나이트라고도 하며, 몬모릴로나이트를 주성분으로 하고, 여기에 교상규산(膠狀硅酸)이 혼합된 것이다. 백색 또는 담갈색·담녹색이고 산성반응을 나타낸다. 산성백토는 원토도 흡착성과 탈색성이 강한데, 황산으로 가열 처리하면 한층 그 성능이 향상된다. 이것을 활성백토고 하여, 석유 ·유지류의 정제·탈색 등에 사용된다. 또 여러 가지 촉매와 흡습성을 이용하여 건조제로서 사용된다Generally, the clay is also called bentonite, and the main component is montmorillonite, and the mixed silicic acid is mixed therein. White or light brown, light green and acidic reaction. Acid clay has strong adsorption and decolorization, and its performance is further improved by heating with sulfuric acid. It is used as activated white soil and is used for purification and decolorization of petroleum and oils and fats. It is also used as a desiccant utilizing various catalysts and hygroscopicity

또한, 백토는 마그네슘, 칼륨, 알루미늄, 셀렌, 게르마늄, 칼슘 등이 함유되어 있고, 인체에 유익한 5-20㎛의 원적외선 파장이 90% 이상 방사되는 광물질이다.In addition, the clay is a mineral containing magnesium, potassium, aluminum, selenium, germanium, calcium, and the like, and the 90-5 far infrared wavelength of 5-20 μm beneficial to the human body is emitted.

건축물의 내장 또는 외장의 착색시에 사용되는 도료는 수성 도료와 유성 도료가 사용되는 데, 이 들 도료는 석유에서 추출한 화학물질과 안료 및 화학 접착제를 이용하여 제조된 화학 유기질 도료로서, 이들은 독성과 악취가 있어 도장 작업시 인체의 건강을 해칠 수 있으며, 쉽게 분해되지 않아 환경을 오염시키는 문제점이 있었다. 또한, 도장후 쉽게 탈색하여 1~2년후에 재 도장하게 됨으로써 자원을 낭비하는 문제점이 있었다.The paints used for coloring interiors or exteriors of buildings are water-based and oil-based paints, which are chemical organic paints made from petroleum-derived chemicals, pigments and chemical adhesives. There is a bad smell can harm the health of the human body during painting work, there was a problem that does not decompose easily pollute the environment. In addition, there is a problem in wasting resources by being easily discolored after painting and repainting after 1-2 years.

본 발명은 상기의 문제점을 해소하기 위하여 발명된 것으로, 원적외선을 방출하며 항균 탈취에 탁월한 효능을 인정받은 백토에 납석, 청석, 카본등 안료용 돌가루를 첨가하고 물과 접착용 아크릴 수지를 혼합하여 천연물질 만으로 건축물의 내장 및 외장에 사용되는 도료를 제조하여 도장 작업시에 인체의 건강을 해칠 위험 및 천연물에 의하여 환경 오염을 경감시키고, 도장후 쉽게 탈색되지 않음은 물론 무독, 무취와 부식방지 및 항균, 항습과 원적외선 방출 작용을 도모하는 천연 물질을 이용한 기능성 도료 및 그의 제조방법을 제공하는 데 그 목적이 있다.The present invention has been invented to solve the above problems, by adding a powder of feldspar, blue stone, carbon, etc. to the clay, which is far infrared and emits far infrared rays and is recognized for its excellent antibacterial deodorization, by mixing water and an acrylic resin for adhesion. By manufacturing paints used for interior and exterior of buildings with only natural materials, it reduces the environmental pollution by natural materials and the risk of harming human health during painting work, and does not discolor easily after painting, as well as preventing toxic, odorless and corrosion. It is an object of the present invention to provide a functional coating using a natural material that promotes antibacterial, moisture and far-infrared radiation and a method for producing the same.

이와 같은 목적을 달성하기 위한 본 발명은,The present invention for achieving such an object,

중량 %로 백토 분체 40-50%와 안료용 원석분체 5-10%, 물 20-25% 및 아크릴 수지 20-30%로 구성되며, 백토분체는 325 - 1200메쉬로 분쇄하고, 안료용 원석 분체는 325 - 1200메쉬로 분쇄됨을 특징으로 한다.By weight%, it consists of 40-50% of clay powder, 5-10% of raw gem powder, 20-25% of water and 20-30% of acrylic resin, and the clay is pulverized into 325-1200 mesh, and the raw gem powder for pigment Is characterized in that it is ground to 325-1200 mesh.

이하 본 발명의 바람직한 실시예를 상세히 설명하면 다음과 같다.Hereinafter, the preferred embodiment of the present invention will be described in detail.

본 발명은 백토 분체 40-50wt%와, 안료용 돌가루 5-10wt%와, 물 20-25wt%과 아크릴 수지 20-30wt%의 비율로 혼합한다.The present invention is mixed with 40-50wt% clay powder, 5-10wt% pigment stone, 20-25wt% water and 20-30wt% acrylic resin.

이를 위하여 먼저 백토원석을 분쇄기에 투입하여 325 - 1200메쉬로 분쇄하고, 안료용으로 사용되는 납석, 카본, 옥, 청석 및 적벽돌의 원료인 붉은 흙인 일명 뱅가라의 원석을 필요한 색상에 따라 분쇄기에 투입하여 325 - 1200메쉬로 분쇄한다.To do this, first, the white clay is put into the grinder and pulverized into 325-1200 mesh, and the raw material of so-called Bangara, which is a raw material of lead stone, carbon, jade, blue stone and red brick, used for pigments, is mixed into the grinder according to the required color. And grind to 325-1200 mesh.

그리고, 분쇄기에서 분쇄된 백토 분체 40-50wt%와 안료용 돌가루 5-10wt%, 그리고, 물 20-25wt%과 아크릴 수지 20-30wt%를 혼합기에 넣고 혼합하게 된다.Then, 40-50 wt% of the clay powder pulverized in the crusher, 5-10wt% of the pigment stone powder, and 20-25wt% of water and 20-30wt% of the acrylic resin are mixed in a mixer.

실시예Example

여기서, 본 발명에 의하여 제조되는 도료가 미색을 가지게 하기 위하여 백토 분체 40-50wt%에 안료용 돌가루로 분쇄된 납석가루 5-10wt%를 혼합하고, 여기에 물 20-25wt% 및 아크릴 수지 20-30wt%를 첨가한 후 이를 고르게 혼합하여 제조하며, 도료가 베이지색을 가지게 하기 위하여 백토 분체 40-50wt%에 안료용 돌가루로 분쇄된 납석가루 5-7wt% 및 분쇄된 카본가루 2-5wt%를 혼합하고, 여기에 물 20-25wt% 및 아크릴 수지 20-30wt%를 첨가한 후 이를 고르게 혼합하여 제조한다.Here, in order to make the paint produced by the present invention have a off-white color, 40-10 wt% of clay powder is mixed with 5-10 wt% of feldspar powder pulverized with pigment stone, and 20-25 wt% of water and acrylic resin 20 It is prepared by adding -30wt% and mixing it evenly.To make the paint have beige color, 5-7wt% of feldspar powder and 2-5wt pulverized carbon powder in 40-50wt% of clay powder. % Is mixed and 20-25 wt% of water and 20-30 wt% of acrylic resin are added thereto, followed by evenly mixing.

또한, 본 발명에 의하여 제조되는 도료가 회색을 가지게 하기 위하여 백토 분체 40-50wt%에 안료용 돌가루로 분쇄된 카본가루 5-10wt%를 혼합하고, 여기에 물 20-25wt% 및 아크릴 수지 20-30wt%를 첨가한 후 이를 고르게 혼합하여 제조하며, 도료가 연녹색을 가지게 하기 위하여 백토 분체 40-50wt%에 안료용 돌가루로 분쇄된 옥가루 5-10wt%를 혼합하고, 여기에 물 20-25wt% 및 아크릴 수지 20-30wt%를 첨가한 후, 이를 고르게 혼합하여 제조한다.In addition, in order to make the paint produced according to the present invention have a gray color, 40-10 wt% of clay powder is mixed with 5-10 wt% of carbon powder pulverized with pigment stone, and 20-25 wt% of water and acrylic resin 20 It is prepared by adding -30wt% and mixing it evenly.To make the paint light green, 40-50wt% of clay powder is mixed with 5-10wt% pulverized jade powder with pigment stone powder and 20-25wt of water % And 20-30 wt% of acrylic resin are added and then mixed evenly.

본 발명에 의하여 제조되는 도료가 연하늘색을 가지게 하기 위하여 백토 분체 40-50wt%에 안료용 돌가루로 분쇄된 청석가루 5-10wt%를 혼합하고. 여기에 물 20-25wt% 및 아크릴 수지 20-30wt%를 첨가하여 이를 고르게 혼합하여 제조하며, 도료가 보라색을 가지게 하기 위하여 백토 분체 40-50wt%에 안료용 돌가루로 분쇄된 뱅가라 가루 5-7wt% 및 분쇄된 청석가루 2-5wt%를 혼합하고, 여기에 물 20-25wt% 및 아크릴 수지 20-30wt%를 첨가하여 이를 고르게 혼합한다.In order to make the paint prepared in accordance with the present invention have light blue color, 5-10 wt% of blue clay powder pulverized with pigment stone powder is mixed with 40-50 wt% of clay powder. It is prepared by adding 20-25wt% of water and 20-30wt% of acrylic resin and mixing it evenly.Bangara powder 5-pulverized with pigment stone in 40-50wt% of white clay powder to make the paint purple. 7 wt% and crushed blue powder 2-5 wt% are mixed, and 20-25 wt% of water and 20-30 wt% of acrylic resin are added and mixed evenly.

제조되는 안료가 핑크색을 가지게 하기 위하여 백토 분체 40-50wt%에 안료용 돌가루로 적벽돌의 원료로 사용되는 붉은 흙인 일명 뱅가라 가루를 5-10wt%로 혼합하고, 여기에 물 20-25wt% 및 아크릴 수지 20-30wt%를 첨가한 후 이를 고르게 혼합하여 제조한다.In order to make the pigment to have a pink color, 5-50 wt% of clay powder, which is used as a raw material for red brick, is mixed with 40-50wt% of clay powder, and 5-10wt% of water, and 20-25wt% of water And 20-30wt% acrylic resin is added and then mixed evenly to prepare.

또한, 제조되는 안료가 백색을 가지게 하기 위하여 백토 분체 40-50wt%에 안료용 돌가루로 백토 가루를 5-10wt%로 혼합하고, 여기에 물 20-25wt% 및 아크릴 수지 20-30wt%를 첨가한 후 이를 고르게 혼합하여 제조하며, 제조되는 도료가 국방색을 가지게 하기 위하여 백토 분체 40-50wt%에 안료용 돌가루로 납석 가루 5-7wt% 및 분쇄된 청석가루 2-5wt%를 혼합하고, 여기에 물 20-25wt% 및 아크릴 수지 20-30wt%를 첨가하고 이를 고르게 혼합하여 제조한다.In addition, in order to make the pigment to have a white color of white clay powder 40-50wt% of clay powder mixed with 5-10wt% of pigment powder, 20-25wt% of water and 20-30wt% of acrylic resin are added thereto. After mixing evenly, to prepare the paint to have a defense color, mix clay powder 5-7wt% and crushed cyanite powder 2-5wt% with pigment stone powder to 40-50wt% of clay powder. 20-25 wt% of water and 20-30 wt% of an acrylic resin are added thereto, and the mixture is evenly mixed.

이와 같이 만들어진 백토 및 안료용 돌가루와 물을 주원료로 한 도료는 기존 화학도료에서 발생하는 자극적인 냄새와 신나 등을 전혀 사용할 필요가 없고, 도장 작업시 인체에 무해하며, 광물질이 주원료이므로 콘크리트, 시멘트에 내재되어 있는 강알칼리성분을 흡수 중화시켜주는 작용을 하게 된다.As a main raw material made of clay and water for clay and pigment, the paint does not need to use any irritating odors and thinners generated from existing chemical paints. It absorbs and neutralizes strong alkalis inherent in cement.

아울러 뛰어난 접착성분으로 흡착력이 강하며 특히, 원적외선 방출이 증대되어 화학도료에서 나온 암모니아 냄새를 전혀 발생시키지 않는다.In addition, it has a strong adhesive force with an excellent adhesive component, and in particular, far-infrared emission is increased so that it does not generate any ammonia odor from the chemical paint.

그리고 본 발명의 도료에서 발산하는 원적외선은 공기를 음이온화 하여 양이온을 중화시켜 탈취기능을 함으로 향균, 항습 작용을 하여 이끼나 균류의 서식을 차단시킨다.And far-infrared rays emanating from the paint of the present invention, by anionizing the air to neutralize the cation and deodorizing function to act as antibacterial, anti-humidity to block the habitat of moss or fungus.

또한 천연 접착제가 배합되어 무독, 무취, 표면의 압착에 의한 방수 및 부식방지, 화학도료에 비해 두꺼운 피막 층을 형성하여 균질 현상을 예방하는 등 천연 원료를 이용한 도료로 친 환경적인 도료이다.In addition, it is a environmentally friendly paint that uses natural raw materials such as non-toxic, odorless, waterproof and corrosion resistant by pressing the surface, and forming a thick film layer compared to chemical paints to prevent homogeneous phenomenon.

상술한 바와 같이, 본 발명에 따른 천연 물질을 이용한 기능성 도료 및 그의 제조방법은 백토에 납석, 청석, 카본등 안료용 돌가루를 첨가하고 물과 접착용 아크릴 수지를 혼합하여 천연물질 만으로 건축물의 내장 및 외장에 사용되는 도료를 제조하여 도장 작업시에 인체의 건강을 해칠 위험 및 천연물에 의하여 환경 오염을 경감시키고, 도장후 쉽게 탈색되지 않음은 물론 무독, 무취와 부식방지 및 항균, 항습과 원적외선 방출 작용을 도모하는 효과가 있다.As described above, the functional paint using the natural material according to the present invention and the manufacturing method thereof is added to the clay stone, such as feldspar, blue stone, carbon, etc. to the clay, and mixed with water and adhesive acrylic resin, the interior of the building only with natural materials Manufacture paints used for exteriors and exteriors to reduce environmental pollution by the risk of harming human health during painting and natural products, not easily discolored after painting, as well as non-toxic, odorless and corrosion prevention, antibacterial, moisture and far infrared It is effective to promote the action.

이상에서 첨부된 도면을 참조하여 본 발명의 바람직한 실시예를 상세히 설명하였으나, 본 발명은 이에 한정되는 것이 아니며 본 발명의 기술적 사상의 범위내에서 당업자에 의해 그 개량이나 변형이 가능하다.Although the preferred embodiments of the present invention have been described in detail with reference to the accompanying drawings, the present invention is not limited thereto and may be improved or modified by those skilled in the art within the scope of the technical idea of the present invention.

Claims (12)

중량 %로 백토 분체 40-50%와 안료용 원석분체 5-10%, 물 20-25% 및 아크릴 수지 20-30%로 구성되는 천연 물질을 이용한 기능성 도료.Functional paint using natural materials composed of 40-50% of clay powder, 5-10% of raw stone powder for pigment, 20-25% of water, and 20-30% of acrylic resin. 제 1 항에 있어서, 상기 백토분체는 325 - 1200메쉬로 분쇄하고, 안료용 원석 분체는 325 - 1200메쉬로 분쇄됨을 특징으로 하는 천연 물질을 이용한 기능성 도료.The functional paint using natural materials according to claim 1, wherein the white clay powder is pulverized to 325-1200 mesh, and the raw gemstone powder for pigment is pulverized to 325-1200 mesh. 제 1 항에 있어서, 상기 안료용 원석 분체로는 납석가루 5-10wt%가 사용되는 것을 특징으로 하는 천연 물질을 이용한 기능성 도료.2. The functional coating using natural materials according to claim 1, wherein 5-10 wt% of feldspar powder is used as the raw gemstone powder for pigments. 제 1 항에 있어서, 상기 안료용 원석 분체로는 납석가루 5-7wt% 및 카본 가루 2-5wt%가 혼합 사용되는 것을 특징으로 하는 천연 물질을 이용한 기능성 도료.2. The functional coating using natural materials according to claim 1, wherein the raw stone powder for pigment is mixed with 5-7 wt% of feldspar powder and 2-5 wt% of carbon powder. 제 1 항에 있어서, 상기 안료용 원석 분체로는 카본 가루 5-10wt%가 사용되는 것을 특징으로 하는 천연 물질을 이용한 기능성 도료.The functional coating using natural materials according to claim 1, wherein 5-10 wt% of carbon powder is used as the raw gemstone powder for pigments. 제 1 항에 있어서, 상기 안료용 원석 분체로는 옥가루 5-10wt%가 사용되는 것을 특징으로 하는 천연 물질을 이용한 기능성 도료.The functional paint using natural materials according to claim 1, wherein 5-10 wt% of jade powder is used as the raw gemstone powder. 제 1 항에 있어서, 상기 안료용 원석 분체로는 청석가루 5-10wt%가 사용되는 것을 특징으로 하는 천연 물질을 이용한 기능성 도료.2. The functional coating using natural materials according to claim 1, wherein 5-10 wt% of cyanite is used as the raw gemstone powder. 제 1 항에 있어서, 상기 안료용 원석분체로는 뱅가라 가루 5-7wt% 및 청석가루 2-5wt%가 혼합 사용되는 것을 특징으로 하는 천연 물질을 이용한 기능성 도료.According to claim 1, wherein the raw powder for pigments functional coatings using natural materials, characterized in that 5-7wt% of Bangara powder and 2-5wt% of cyanite powder are mixed and used. 제 1 항에 있어서, 상기 안료용 원석 분체로는 뱅가라 가루 5-10wt%가 사용되는 것을 특징으로 하는 천연 물질을 이용한 기능성 도료.2. The functional coating using natural materials according to claim 1, wherein 5-10 wt% of bengal powder is used as the raw material for pigments. 제 1 항에 있어서, 상기 안료용 원석분체로는 백토 가루를 5-10wt%가 사용되는 것을 특징으로 하는 천연 물질을 이용한 기능성 도료.The functional coating using natural materials according to claim 1, wherein 5-10 wt% of clay powder is used as the raw gemstone powder. 제 1 항에 있어서, 상기 안료용 원석분체로는 납석 가루 5-7wt% 및 청석가루 2-5wt%가 혼합 사용되는 것을 특징으로 하는 천연 물질을 이용한 기능성 도료.The method of claim 1, wherein the raw material for pigment is a functional coating using a natural material, characterized in that 5-7wt% of feldspar powder and 2-5wt% of cyanite powder are mixed and used. 백토원석을 분쇄기에 투입하여 325 - 1200메쉬로 분쇄하고, 안료용 원석을 을 필요한 색상에 따라 분쇄기에 투입하여 325 - 1200메쉬로 분쇄하는 단계; 및Putting white clay into a grinder to grind it to 325-1200 mesh, and putting the raw material for pigment into a grinder according to the required color to grind it to 325-1200 mesh; And 분쇄기에서 분쇄된 백토 분체 40-50wt%와 안료용 원석가루 5-10wt%, 물 20-25wt%과 아크릴 수지 20-30wt%를 혼합기에 투입하여 일정시간 혼합하여 제조되는천연 물질을 이용한 기능성 도료의 제조방법40-50wt% of the clay powder pulverized in the crusher, 5-10wt% of the raw gemstone powder, 20-25wt% of the water and 20-30wt% of the acrylic resin were added to the mixer and mixed for a certain time. Manufacturing method
KR1020010072877A 2001-11-22 2001-11-22 functional paint using a natural material and method for manufacturing that paint KR20030042216A (en)