CN101913820A - Heat-preserving decorative mortar and preparation method thereof - Google Patents
Heat-preserving decorative mortar and preparation method thereof Download PDFInfo
- Publication number
- CN101913820A CN101913820A CN2010102307764A CN201010230776A CN101913820A CN 101913820 A CN101913820 A CN 101913820A CN 2010102307764 A CN2010102307764 A CN 2010102307764A CN 201010230776 A CN201010230776 A CN 201010230776A CN 101913820 A CN101913820 A CN 101913820A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat
- preserving
- decorative mortar
- preserving decorative
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to heat-preserving decorative mortar which comprises the following components in parts by weight: 180-220 parts of cement, 30-70 parts of fly ash, 560-600 parts of sand, 70-100 parts of heavy calcium carbonate, 30-60 parts of heat-preserving aggregate, 3-9 parts of bentonite, 4-8 parts of wood fiber, 2-7 parts of water repellent, 2-5 parts of alkalization inhibitor, 0.5-4 parts of cellulose ether, 6-15 parts of rubber powder and 1-30 parts of pigment. A preparation method thereof comprises the following steps of: firstly uniformly mixing the cement, the fly ash, the sand, the heavy calcium carbonate, the bentonite, the wood fiber, the water repellent, the alkalization inhibitor, the cellulose ether, the rubber powder and the pigment, subsequently adding the heat-preserving aggregate, and then mechanically and uniformly mixing to prepare the heat-preserving decorative mortar. The invention has the advantages of heat preservation, heat insulation, strong hydrophobic property, environmental protection, no pollution, and the like.
Description
Technical field
The present invention relates to a kind of material of construction, relate in particular to a kind of mortar of exterior wall finish, also possess heat-preserving decorative mortar of heat insulating effect and preparation method thereof when utilizing heat preserving aggregate to make it play decoration function more specifically to a kind of.
Background technology
Decoration mortar has obtained using widely in last century Europe exterior wall finish system, has replaced the only selection that coating and face brick become finish coat with its excellent characteristic.Its deadweight is lighter than face brick, increased the security of outer wall structure of building, and can be by selecting the template of different graphic, instrument, impose and drag, roll, scrape, turn round pressure, the different operating method such as rub, metope is changed embossing, ripple, various pattern such as wood grain, can form multiple texture, the effect of color and texture, expressive force is abundant, artistic feeling is strong, can with physical environment, architectural style and historical sites more ideally merge, though decoration mortar is not long in the history of China, because of it has above advantage, so obtained development fast in nearly 2 years at home.Particularly present country has formulated the development strategy of " low-carbon economy ", and a large amount of waste polyurethane foams that exist in fields such as refrigerator manufacturing, piping insulation, freezer construction, equipment packages have caused " yellow strain ", if can utilize it fully, just can turn waste into wealth, solve its pollution problem to environment, and can cut down the consumption of energy, reduce pollution relatively, reduce discharging, for " low-carbon economy " makes contributions.
Through searching for relevant scientific and technical literature data discovery both at home and abroad, though prior art has solved mortar accumulation of salt in the surface soil problem, improved endurance quality etc., do not have the heat insulating effect, on exterior-wall heat insulation and reducing energy consumption engineering, exist limitation.
Summary of the invention
Technical problem to be solved by this invention is to overcome above-mentioned deficiency; a kind of cheap heat-preserving decorative mortar that is suitable for large public building and covil construction and preparation method thereof is provided; with cement, flyash is gelling material; serving as the insulation light skeletal through the polyurathamc foam beads of fragmentation or through the compound material that the polyurathamc foam beads and the expanded and vitrified small ball of fragmentation mixes; mix multiple additives and pigment, make have heat insulating, good permeability, strong, the environment friendly and pollution-free heat-preserving decorative mortar of hydrophobic nature.
Technical scheme of the present invention: a kind of heat-preserving decorative mortar, its component and weight content are as follows:
180～220 parts of cement, 30～70 parts in flyash, 560～600 parts in sand,
70～100 parts of dry powders, 30～60 parts of heat preserving aggregates, 3～9 parts of wilkinites,
4～8 parts of wood fibres, 2～7 parts of hydrophober, 2～5 parts in accumulation of salt in the surface soil inhibitor,
0.5～4 part of ether of cellulose, 6～15 parts of rubber powders, 1～30 part of pigment.
Described heat preserving aggregate is that polyurathamc foam unit dry weight is less than 60kg/m through the polyurathamc foam beads of fragmentation or the compound material that mixes through the polyurathamc foam beads and the expanded and vitrified small ball of fragmentation
3, thermal conductivity is less than 0.025W/mK, the expanded and vitrified small ball unit dry weight is less than 120kg/m
3, thermal conductivity is less than 0.048W/mK.Described cement is normal silicate 42.5 cement or white silicate 42.5 cement.Described flyash is I level or II level flyash.Described sand is through cleaning the natural sand of oven dry or quartz sand.Described pigment is iron oxide pigment.Described rubber powder is the redispersable latex powder of the one or more combination in the multipolymer of vinyl acetate and tertiary ethylene carbonate or ethene or acrylate.Described hydrophober is organosilicon moisture repellent.Described accumulation of salt in the surface soil inhibitor is a kind of extraordinary resin base powder that accumulation of salt in the surface soil phenomenon produces that is used for suppressing.The preparation method of above-mentioned heat-preserving decorative mortar: at first cement, flyash, sand, dry powder, wilkinite, wood fibre, hydrophober, accumulation of salt in the surface soil inhibitor, ether of cellulose, rubber powder and pigment are mixed, subsequently heat preserving aggregate is added, evenly make by mechanically mixing again.
The present invention compared with prior art has following beneficial effect: 1, by adding heat preserving aggregate, utilize material self unit weight low, the advantage of low heat conduction is used for reducing the deadweight of material, reduces the thermal conductivity of material, improves its thermal property; 2, by adding high molecular polymers such as hydrophober, accumulation of salt in the surface soil inhibitor, ether of cellulose, rubber powder, make mortar have certain flexibility, can guarantee under the situation of repeated deformation, can not occur fatigure failure, produce the crack.And the mortar internal structure is changed, improve the effect of hole, micromolecular water vapour molecule can freely be passed through, and macromolecular water molecules can't see through, thereby strengthen the hydrophobic function of mortar, suppress the phenomenon of the accumulation of salt in the surface soil; 3, select for use inorganic oxide iron pigment to mix colours, the color fastness that guarantees material is fugitive color not by force.
The main performance index of heat-preserving decorative mortar all detects according to JC/T1024-2007, and detected value sees the following form:
Embodiment
Embodiment 1: a kind of heat-preserving decorative mortar, its component and weight content are as follows: 180 parts of board normal silicate 42.5 cement that reach the clouds, 70 parts in flyash, 560 parts in sand, 70 parts of dry powders, 9 parts of 60 parts of polyurathamc foam beads, wilkinites through fragmentation, 4 parts of TECHNOCEL 1004-7N wood fibres, 2 parts of Elotex SEAL80 hydrophober, 5 parts in Elotex ERA100 accumulation of salt in the surface soil inhibitor, 15 parts of Bermocoll M30 ether of cellulose 4 part, watts gram VINNAPAS 5044N rubber powders, 1 part of Shanghai one product S110 ferric oxide red colorant.
Embodiment 2: a kind of heat-preserving decorative mortar, its component and weight content are as follows: 200 parts of white silicate 42.5 cement, 50 parts in flyash, 580 parts in sand, 80 parts of dry powders, 5 parts of 40 parts of 30 parts of polyurathamc foam beads, expanded and vitrified small balls, wilkinites through fragmentation, 4 parts of TECHNOCEL 1004-7N wood fibre 5 part, watts gram SILRES Powder D (69051VP) hydrophober, 3 parts in Elotex ERA100 accumulation of salt in the surface soil inhibitor, 2 parts of Bermocoll M30 ether of cellulose, 10 parts of Elotex FX7000 rubber powders, 15 parts of Shanghai one product S930 ferric oxide yellow pigments.
Embodiment 3: a kind of heat-preserving decorative mortar, its component and weight content are as follows: 220 parts of board normal silicate 42.5 cement that reach the clouds, 40 parts in flyash, 600 parts in sand, 100 parts of dry powders, 3 parts of 40 parts of 20 parts of polyurathamc foam beads, expanded and vitrified small balls, wilkinites through fragmentation, 8 parts of TECHNOCEL 1004-7N wood fibres, 7 parts of Elotex SEAL80 hydrophober, 2 parts in Elotex ERA100 accumulation of salt in the surface soil inhibitor, 6 parts of Bermocoll M30 ether of cellulose 0.5 part, watt gram VINNAPAS 5044N rubber powders, 30 parts of Shanghai one product S340 black iron oxide pigments.
Embodiment 4: a kind of heat-preserving decorative mortar, its component and weight content are as follows: 210 parts of white silicate 42.5 cement, 55 parts in flyash, 595 parts in sand, 75 parts of dry powders, 30 parts of polyurathamc foams, 7 parts of wilkinites, 6 parts of TECHNOCEL 1004-7N wood fibre 6 part, watts gram SILRES Powder D (69051VP) hydrophober, Elotex ERA100 accumulation of salt in the surface soil inhibitors 4 part, 3 parts of Bermocoll M30 ether of cellulose, 15 parts of Elotex FX7000 rubber powders, 20 parts of Shanghai one product S960 ferric oxide orange pigment.
Embodiment 5: a kind of heat-preserving decorative mortar, its component and weight content are as follows: 220 parts of white silicate 42.5 cement, 30 parts in flyash, 570 parts in sand, 90 parts of dry powders, 55 parts of polyurathamc foams, 6.5 parts of wilkinites, 5 parts of ECHNOCEL 1004-7N wood fibres, 3 parts of Elotex SEAL80 hydrophober, Elotex ERA100 accumulation of salt in the surface soil inhibitors 4 part, 2.5 parts of Bermocoll M30 ether of cellulose, 12 parts of Shanxi D S WF-06 rubber powders, 18 parts of Shanghai one product S868 iron oxide brown pigment.
The preparation method of the foregoing description: at first cement, flyash, sand, dry powder, wilkinite, wood fibre, hydrophober, accumulation of salt in the surface soil inhibitor, ether of cellulose, rubber powder and pigment are mixed; add with the polyurathamc foam or with compound material that expanded and vitrified small ball mixes subsequently; even by mechanically mixing once more, treat that mortar converts water at building-site and stir to use.
Claims (10)
1. heat-preserving decorative mortar is characterized in that its component and weight content are as follows:
180～220 parts of cement, 30～70 parts in flyash, 560～600 parts in sand,
70～100 parts of dry powders, 30～60 parts of heat preserving aggregates, 3～9 parts of wilkinites,
4～8 parts of wood fibres, 2～7 parts of hydrophober, 2～5 parts in accumulation of salt in the surface soil inhibitor,
0.5～4 part of ether of cellulose, 6～15 parts of rubber powders, 1～30 part of pigment.
2. heat-preserving decorative mortar according to claim 1; it is characterized in that described heat preserving aggregate is that polyurathamc foam unit dry weight is less than 60kg/m through the polyurathamc foam beads of fragmentation or the compound material that mixes through the polyurathamc foam beads and the expanded and vitrified small ball of fragmentation
3, thermal conductivity is less than 0.025W/mK, the expanded and vitrified small ball unit dry weight is less than 120kg/m
3, thermal conductivity is less than 0.048W/mK.
3. heat-preserving decorative mortar according to claim 1 is characterized in that described cement is normal silicate 42.5 cement or white silicate 42.5 cement.
4. heat-preserving decorative mortar according to claim 1 is characterized in that described flyash is I level or II level flyash.
5. heat-preserving decorative mortar according to claim 1 is characterized in that described sand is through cleaning the natural sand of oven dry or quartz sand.
6. heat-preserving decorative mortar according to claim 1 is characterized in that described pigment is iron oxide pigment.
7. heat-preserving decorative mortar according to claim 1 is characterized in that described rubber powder is the redispersable latex powder of the one or more combination in the multipolymer of vinyl acetate and tertiary ethylene carbonate or ethene or acrylate.
8. heat-preserving decorative mortar according to claim 1 is characterized in that described hydrophober is organosilicon moisture repellent.
9. heat-preserving decorative mortar according to claim 1 is characterized in that described accumulation of salt in the surface soil inhibitor is a kind of extraordinary resin base powder that accumulation of salt in the surface soil phenomenon produces that is used for suppressing.
10. method for preparing the heat-preserving decorative mortar of claim 1 art, it is characterized in that at first cement, flyash, sand, dry powder, wilkinite, wood fibre, hydrophober, accumulation of salt in the surface soil inhibitor, ether of cellulose, rubber powder and pigment being mixed, subsequently heat preserving aggregate is added, evenly make by mechanically mixing again.