CN107337407A - A kind of water-proof heat insulation mortar and preparation method thereof - Google Patents
A kind of water-proof heat insulation mortar and preparation method thereof Download PDFInfo
- Publication number
- CN107337407A CN107337407A CN201710589028.7A CN201710589028A CN107337407A CN 107337407 A CN107337407 A CN 107337407A CN 201710589028 A CN201710589028 A CN 201710589028A CN 107337407 A CN107337407 A CN 107337407A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- powder
- heat insulation
- proof heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of water-proof heat insulation mortar, include the component of following parts by weight：30 50 parts of cement, 20 30 parts of swelling perlite powder, 20 30 parts of quartz sand powder, 10 30 parts of vermiculite power, 10 20 parts of nano titanium oxide, 5 15 parts of diatomite, 15 25 parts of light calcined magnesia, 5 10 parts of mica powder, 28 parts of light ceramic, 5 15 parts of sodium lignin sulfonate, 38 parts of hollow glass bead, modified 60 80 parts of 5 15 parts of charcoal powder, 4 10 parts of dodecyl sodium sulfate, 3 10 parts of reinforcing fiber, 26 parts of inserts, 15 parts of polycarboxylate water-reducer, 38 parts of waterproofing agent and water.The water-proof heat insulation mortar of the present invention has the characteristics that high waterproof, high-efficiency insulated, effectively insulating, good flame resistance and environmental protection, can be widely used for the engineerings such as insulation, the waterproof of building inside and outside wall.
Description
Technical field
The present invention relates to building material technical field, and in particular to a kind of water-proof heat insulation mortar and preparation method thereof.
Background technology
With the increasing of China environmental protection dynamics and the implementation of the strategy of sustainable development, people's environmental resource protection meaning
Know and gradually strengthen, building energy conservation receives more and more attention with environmental protection.
Into after 21 century, Urbanization in China rapid development, the thing followed is that energy consumption acutely increases, building, work
Industry, traffic are three big fields of China's power consumption, wherein building account for Chinese total energy consumption close to 30%, it is contemplated that the year two thousand twenty building it is complete
Energy consumption accounts for the 50% of whole society's total energy consumption, and wherein exterior-wall heat insulation, thermal insulation of roof, door and window radiating accounts for the 50% of house energy waste,
As can be seen here, winter heating, cooling in summer energy waste are very big.
At present, technically basic development is ripe for the existing building thermal-insulation energy-saving material of in the market, in heat-insulating property
It may be said that power conservation requirement is basically reached.From the point of view of the service condition of more than ten years, there is resistance in these insulation materials and heat insulation system
The poor, easy firing of combustion property, the shortcomings of service life is short, easy to fall off damaged, easy to crack, these shortcomings are brought much to modern building
Hidden danger.More effect mortars are using various light materials as aggregate, using cement as gelating material, some property-modifying additives are admixed, through life
Production enterprise is stirred and a kind of manufactured premixing dry powder and mortar, for constructing a kind of construction material on building surface.With low
Carbocyclic ring protects the continuous improvement of continuous popularization and people to living environment comfortableness demand with building energy conservation, and more effect mortars are got over
More to attract widespread attention, the research of the more effect mortars in China is more in recent years, existing in Practical Project a lot
With, but compared with developed countries, it is also poor there is water proofing property, and water absorption rate is big, the easy moisture absorption, and seep water easy to crack, thermal insulation separation thermal effect
The problems such as fruit is undesirable.
The content of the invention
It is an object of the invention to overcome above-mentioned the deficiencies in the prior art, there is provided a kind of water-proof heat insulation mortar and its system
Preparation Method, the water-proof heat insulation mortar have the characteristics that high waterproof, high-efficiency insulated, effectively insulating, good flame resistance and environmental protection, full
Sufficient construction industry can be widely used for the engineerings such as insulation, the waterproof of building inside and outside wall to mortar performance index request.
The present invention is in order to solve the above technical problems, adopt the following technical scheme that：
A kind of water-proof heat insulation mortar, include the component of following parts by weight：Cement 30-50 parts, swelling perlite powder 20-30
Part, quartz sand powder 20-30 parts, vermiculite power 10-30 parts, nano titanium oxide 10-20 parts, diatomite 5-15 parts, light calcined magnesia
15-25 parts, mica powder 5-10 parts, light ceramic 2-8 parts, sodium lignin sulfonate 5-15 parts, hollow glass bead 3-8 parts, modification
Charcoal powder 5-15 parts, dodecyl sodium sulfate 4-10 parts, reinforcing fiber 3-10 parts, inserts 2-6 parts, polycarboxylate water-reducer 1-5
Part, waterproofing agent 3-8 parts and water 60-80 parts.
Preferably, 40 parts of the cement, 25 parts of swelling perlite powder, 25 parts of quartz sand powder, 20 parts of vermiculite power, nano-silica
Change 15 parts of titanium, 10 parts of diatomite, 20 parts of light calcined magnesia, 7.5 parts of mica powder, 5 parts of light ceramic, 10 parts of sodium lignin sulfonate,
5.5 parts of hollow glass bead, modified 10 parts of charcoal powder, 7 parts of dodecyl sodium sulfate, 6 parts of reinforcing fiber, 4 parts of inserts, poly- carboxylic
70 parts of sour 3 parts of water reducer, 5.5 parts of waterproofing agent and water.
Preferably, the cement is portland cement.
Preferably, the preparation method of the modified charcoal powder is：The ring equivalent to its weight 1-3% will be added in charcoal powder
Oxygen soybean oil, 0.5-2% silane coupler and appropriate water, stir 20-30min at 30-50 DEG C, take out, place into concentration
To soak 10-12h in 8-10% sodium chloride solution, take out, drying, produce.
Preferably, the reinforcing fiber is polypropylene fibre, carboxylic propyl methocel and cellulose ether according to mass ratio
For 1:1:1 mixture.
Preferably, the inserts is made up of the raw material of following parts by weight：Kaolin 2-5 parts, sepiolite 1-3 parts, water magnesium
Stone flour 0.5-2.5 parts and dolomite dust 0.2-0.8 parts.
A kind of preparation method of water-proof heat insulation mortar, comprises the following steps：
（1）By the cement of the parts by weight, swelling perlite powder, quartz sand powder, vermiculite power, nano titanium oxide, diatomite,
It is levigate in light calcined magnesia, mica powder, light ceramic, hollow glass bead, modified charcoal powder ball mill, then levigate is mixed
Powder is closed to pour into agitator tank；
（2）Sodium lignin sulfonate, dodecyl sodium sulfate are added into agitator tank according to the parts by weight, reinforcing fiber, is filled out
Charge, polycarboxylate water-reducer, waterproofing agent and water, are heated to 40-60 DEG C, stir, and produce water-proof heat insulation mortar.
Preferably, the step（1）In also include：Levigate powder is crossed into 100-200 mesh sieves.
Preferably, the step（2）In stir condition：20-30min is stirred with 200-300r/min.
Compared with prior art, the present invention has following beneficial effect：The water-proof heat insulation mortar of the present invention has
The features such as high waterproof, high-efficiency insulated, effectively insulating, good flame resistance and environmental protection, meet that construction industry, can to mortar performance index request
The engineerings such as insulation, the waterproof of building inside and outside wall are widely used in, concrete condition is as follows：
（1）The water-proof heat insulation mortar of the present invention, with cement, swelling perlite powder, quartz sand powder, vermiculite power, nano-silica
Change titanium, diatomite, light calcined magnesia, mica powder, light ceramic, hollow glass bead, want composition based on modified charcoal powder, and lead to
It is auxiliary to cross addition sodium lignin sulfonate, dodecyl sodium sulfate, reinforcing fiber, inserts, polycarboxylate water-reducer, waterproofing agent and water etc.
Co-ingredients, then it is aided with the techniques such as grinding distribution, mixing so that the water-proof heat insulation mortar environmental friendliness and no harm of preparation, protect
Warm good heat-insulation effect, fire-proof and water-proof excellent performance, it disclosure satisfy that construction industry to mortar performance index request, has before preferably applying
Scape；
（2）The water-proof heat insulation mortar of the present invention has excellent water resistance, water proofing property, impermeability, heat insulation property, resistance toization
Corrosivity and weatherability are learned, and intensity is high, adhesive force is strong, fire protection flame retarding, the problems such as being not in cracking and come off, meanwhile, apply
Work is easy, and completely reliable, cost is cheap, can be widely used for the engineerings such as insulation, the waterproof of building inside and outside wall；
（3）Primary raw material in the present invention is made up of inorganic material, utilizes inorganic material high intensity, anticorrosive, fire-retardant, resistance to old
The characteristics such as change, service life length so that water-proof heat insulation mortar of the invention has preferable heat-insulating property and fire protecting performance,
Simultaneously by the tight seamless heat-insulation layer formed between inorganic material, it on the one hand can reduce heat and scatter and disappear, on the other hand may be used
To play preferable waterproof effect, inorganic material is environmentally friendly material in addition so that water-proof heat insulation sand of the invention
Environmental protection and public nuisance free is starched, meets green building material requirement.
Embodiment
With reference to specific embodiment, the present invention is expanded on further.These embodiments are merely to illustrate the present invention and not had to
In limitation the scope of the present invention.
Embodiment 1
A kind of water-proof heat insulation mortar, include the component of following parts by weight：40 parts of cement, 25 parts of swelling perlite powder, stone
25 parts of sand powder, 20 parts of vermiculite power, 15 parts of nano titanium oxide, 10 parts of diatomite, 20 parts of light calcined magnesia, 7.5 parts of mica powder,
5 parts of light ceramic, 10 parts of sodium lignin sulfonate, 5.5 parts of hollow glass bead, modified 10 parts of charcoal powder, dodecyl sodium sulfate 7
Part, 6 parts of reinforcing fiber, 4 parts of inserts, 3 parts of polycarboxylate water-reducer, 5.5 parts of waterproofing agent and 70 parts of water.
Wherein, the cement is portland cement.
Wherein, the preparation method of the modified charcoal powder is：It is big equivalent to the epoxy of its weight 2% by being added in charcoal powder
Soya-bean oil, 1.3% silane coupler and appropriate water, 25min is stirred at 40 DEG C, taken out, place into the sodium chloride that concentration is 9%
11h is soaked in solution, is taken out, drying, is produced.
Wherein, the reinforcing fiber is that polypropylene fibre, carboxylic propyl methocel and cellulose ether are according to mass ratio
1:1:1 mixture.
Wherein, the inserts is made up of the raw material of following parts by weight：4 parts of kaolin, 2 parts of sepiolite, brucite powder 1.5
0.5 part of part and dolomite dust.
A kind of preparation method of water-proof heat insulation mortar, comprises the following steps：
（1）By the cement of the parts by weight, swelling perlite powder, quartz sand powder, vermiculite power, nano titanium oxide, diatomite,
It is levigate in light calcined magnesia, mica powder, light ceramic, hollow glass bead, modified charcoal powder ball mill, then levigate is mixed
Powder is closed to pour into agitator tank；
（2）Sodium lignin sulfonate, dodecyl sodium sulfate are added into agitator tank according to the parts by weight, reinforcing fiber, is filled out
Charge, polycarboxylate water-reducer, waterproofing agent and water, 50 DEG C are heated to, is stirred, produce water-proof heat insulation mortar.
Preferably, the step（1）In also include：Levigate powder is crossed into 150 mesh sieves.
Preferably, the step（2）In stir condition：25min is stirred with 250r/min.
Embodiment 2
A kind of water-proof heat insulation mortar, include the component of following parts by weight：30 parts of cement, 20 parts of swelling perlite powder, stone
It is 20 parts of sand powder, 10 parts of vermiculite power, 10 parts of nano titanium oxide, 5 parts of diatomite, 15 parts of light calcined magnesia, 5 parts of mica powder, light
2 parts of matter haydite, 5 parts of sodium lignin sulfonate, 3 parts of hollow glass bead, modified 5 parts of charcoal powder, 4 parts of dodecyl sodium sulfate, increasing
Strong 60 parts of 3 parts of fiber, 2 parts of inserts, 1 part of polycarboxylate water-reducer, 3 parts of waterproofing agent and water.
Wherein, the cement is portland cement.
Wherein, the preparation method of the modified charcoal powder is：It is big equivalent to the epoxy of its weight 1% by being added in charcoal powder
Soya-bean oil, 0.5% silane coupler and appropriate water, 20min is stirred at 30 DEG C, taken out, place into the sodium chloride that concentration is 8%
10h is soaked in solution, is taken out, drying, is produced.
Wherein, the reinforcing fiber is that polypropylene fibre, carboxylic propyl methocel and cellulose ether are according to mass ratio
1:1:1 mixture.
Wherein, the inserts is made up of the raw material of following parts by weight：2 parts of kaolin, 1 part of sepiolite, brucite powder 0.5
0.2 part of part and dolomite dust.
A kind of preparation method of water-proof heat insulation mortar, comprises the following steps：
（1）By the cement of the parts by weight, swelling perlite powder, quartz sand powder, vermiculite power, nano titanium oxide, diatomite,
It is levigate in light calcined magnesia, mica powder, light ceramic, hollow glass bead, modified charcoal powder ball mill, then levigate is mixed
Powder is closed to pour into agitator tank；
（2）Sodium lignin sulfonate, dodecyl sodium sulfate are added into agitator tank according to the parts by weight, reinforcing fiber, is filled out
Charge, polycarboxylate water-reducer, waterproofing agent and water, 40 DEG C are heated to, is stirred, produce water-proof heat insulation mortar.
Wherein, the step（1）In also include：Levigate powder is crossed into 100 mesh sieves.
Wherein, the step（2）In stir condition：20min is stirred with 200r/min.
Embodiment 3
A kind of water-proof heat insulation mortar, include the component of following parts by weight：50 parts of cement, 30 parts of swelling perlite powder, stone
30 parts of sand powder, 30 parts of vermiculite power, 20 parts of nano titanium oxide, 15 parts of diatomite, 25 parts of light calcined magnesia, 10 parts of mica powder,
8 parts of light ceramic, 15 parts of sodium lignin sulfonate, 8 parts of hollow glass bead, modified 15 parts of charcoal powder, dodecyl sodium sulfate 10
Part, 10 parts of reinforcing fiber, 6 parts of inserts, 5 parts of polycarboxylate water-reducer, 8 parts of waterproofing agent and 80 parts of water.
Wherein, the cement is portland cement.
Wherein, the preparation method of the modified charcoal powder is：It is big equivalent to the epoxy of its weight 3% by being added in charcoal powder
Soya-bean oil, 2% silane coupler and appropriate water, 30min is stirred at 50 DEG C, taken out, place into the sodium chloride that concentration is 10%
12h is soaked in solution, is taken out, drying, is produced.
Wherein, the reinforcing fiber is that polypropylene fibre, carboxylic propyl methocel and cellulose ether are according to mass ratio
1:1:1 mixture.
Wherein, the inserts is made up of the raw material of following parts by weight：5 parts of kaolin, 3 parts of sepiolite, brucite powder 2.5
0.8 part of part and dolomite dust.
A kind of preparation method of water-proof heat insulation mortar, comprises the following steps：
（1）By the cement of the parts by weight, swelling perlite powder, quartz sand powder, vermiculite power, nano titanium oxide, diatomite,
It is levigate in light calcined magnesia, mica powder, light ceramic, hollow glass bead, modified charcoal powder ball mill, then levigate is mixed
Powder is closed to pour into agitator tank；
（2）Sodium lignin sulfonate, dodecyl sodium sulfate are added into agitator tank according to the parts by weight, reinforcing fiber, is filled out
Charge, polycarboxylate water-reducer, waterproofing agent and water, 60 DEG C are heated to, is stirred, produce water-proof heat insulation mortar.
Wherein, the step（1）In also include：Levigate powder is crossed into 200 mesh sieves.
Wherein, the step（2）In stir condition：30min is stirred with 300r/min.
Described above is only the preferred embodiment of the present invention, and protection scope of the present invention is not limited merely to above-mentioned implementation
Example, all technical schemes belonged under thinking of the present invention belong to protection scope of the present invention.It should be pointed out that for the art
Those of ordinary skill for, some improvements and modifications without departing from the principles of the present invention, these improvements and modifications
It should be regarded as protection scope of the present invention.
Claims (9)
1. a kind of water-proof heat insulation mortar, it is characterised in that include the component of following parts by weight：Cement 30-50 parts, expansion
Crushed crude pearlite 20-30 parts, quartz sand powder 20-30 parts, vermiculite power 10-30 parts, nano titanium oxide 10-20 parts, diatomite 5-15
Part, light calcined magnesia 15-25 parts, mica powder 5-10 parts, light ceramic 2-8 parts, sodium lignin sulfonate 5-15 parts, hollow vitreous are micro-
Pearl 3-8 parts, modified charcoal powder 5-15 parts, dodecyl sodium sulfate 4-10 parts, reinforcing fiber 3-10 parts, inserts 2-6 parts, poly- carboxylic
Sour water reducer 1-5 parts, waterproofing agent 3-8 parts and water 60-80 parts.
2. water-proof heat insulation mortar according to claim 1, it is characterised in that 40 parts of the cement, expanded perlite
25 parts of powder, 25 parts of quartz sand powder, 20 parts of vermiculite power, 15 parts of nano titanium oxide, 10 parts of diatomite, 20 parts of light calcined magnesia, cloud
7.5 parts of female powder, 5 parts of light ceramic, 10 parts of sodium lignin sulfonate, 5.5 parts of hollow glass bead, modified 10 parts of charcoal powder, 12
70 parts of 7 parts of sodium alkyl sulfonate, 6 parts of reinforcing fiber, 4 parts of inserts, 3 parts of polycarboxylate water-reducer, 5.5 parts of waterproofing agent and water.
3. water-proof heat insulation mortar according to claim 1, it is characterised in that the cement is portland cement.
4. water-proof heat insulation mortar according to claim 1, it is characterised in that the preparation method of the modified charcoal powder
For：Epoxidized soybean oil equivalent to its weight 1-3%, 0.5-2% silane coupler and appropriate water will be added in charcoal powder,
20-30min is stirred at 30-50 DEG C, is taken out, places into the sodium chloride solution that concentration is 8-10% and soaks 10-12h, take out, dry
It is dry, produce.
5. water-proof heat insulation mortar according to claim 1, it is characterised in that the reinforcing fiber is that polypropylene is fine
Dimension, carboxylic propyl methocel and cellulose ether are 1 according to mass ratio:1:1 mixture.
6. water-proof heat insulation mortar according to claim 1, it is characterised in that the inserts is by following parts by weight
Raw material is made：Kaolin 2-5 parts, sepiolite 1-3 parts, brucite powder 0.5-2.5 parts and dolomite dust 0.2-0.8 parts.
A kind of 7. preparation method of water-proof heat insulation mortar according to claim any one of 1-6, it is characterised in that bag
Include following steps：
（1）By the cement of the parts by weight, swelling perlite powder, quartz sand powder, vermiculite power, nano titanium oxide, diatomite,
It is levigate in light calcined magnesia, mica powder, light ceramic, hollow glass bead, modified charcoal powder ball mill, then levigate is mixed
Powder is closed to pour into agitator tank；
（2）Sodium lignin sulfonate, dodecyl sodium sulfate are added into agitator tank according to the parts by weight, reinforcing fiber, is filled out
Charge, polycarboxylate water-reducer, waterproofing agent and water, are heated to 40-60 DEG C, stir, and produce water-proof heat insulation mortar.
8. the preparation method of water-proof heat insulation mortar according to claim 7, the step（1）In also include：Will mill
Thin powder crosses 100-200 mesh sieves.
9. the preparation method of water-proof heat insulation mortar according to claim 7, the step（2）In stir bar
Part：20-30min is stirred with 200-300r/min.