CN106517931A - Rockwool waterproof heat-preserving heat-insulating mortar - Google Patents
Rockwool waterproof heat-preserving heat-insulating mortar Download PDFInfo
- Publication number
- CN106517931A CN106517931A CN201610856935.9A CN201610856935A CN106517931A CN 106517931 A CN106517931 A CN 106517931A CN 201610856935 A CN201610856935 A CN 201610856935A CN 106517931 A CN106517931 A CN 106517931A
- Authority
- CN
- China
- Prior art keywords
- parts
- rock wool
- water
- heat insulation
- proof heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a rockwool waterproof heat-preserving heat-insulating mortar. The rockwool waterproof heat-preserving heat-insulating mortar is prepared from the following raw materials in parts by weight: 400 to 500 parts of cement, 40 to 50 parts of leftovers of rockwool, 100 to 120 parts of glass beads, 8 to 12 parts of blast furnace slag, 4 to 8 parts of sodium tetraborate, 3 to 5 parts of potassium dihydrogen phosphate, 5 to 7 parts of clay, 1 to 3 parts of sodium oleate, 4 to 8 parts of a composite filling material, 8 to 12 parts of a redispersible latex powder, 1.5 to 2.5 parts of methylcellulose, 8 to 10 parts of a waterproofing agent, 1 to 3 parts of wood fiber and 1 to 3 parts of polypropylene fiber. The mortar provided by the invention has the advantages of excellent water resistance, waterproofness, impermeability, heat-preserving heat-insulating properties, chemical corrosion resistance and weather resistance, high strength, strong adhesion force, fire prevention, flame retardance, and no occurrence of problems like cracking and falling-off; meanwhile, the mortar is simple, convenient, safe and reliable to construct, has low cost, and can be extensively applied to projects of heat preservation, heat insulation, water prevention and the like for interior and exterior walls of buildings.
Description
Technical field
The present invention relates to building material technical field, specifically a kind of rock wool water-proof heat insulation mortar.
Background technology
Into after 21 century, Urbanization in China is developed rapidly, and the thing followed is that energy consumption acutely increases, building, work
Industry, traffic are three big fields of China's power consumption, and what wherein building accounted for Chinese total energy consumption is close to 30%, it is contemplated that the year two thousand twenty building it is complete
Energy consumption accounts for the 50% of whole society's total energy consumption, and wherein exterior-wall heat insulation, thermal insulation of roof, door and window radiating accounts for the 50% of house energy waste,
As can be seen here, winter heating, cooling in summer energy waste are very big.
At present, on market existing building thermal-insulation energy-saving material technically basic development is ripe, in heat-insulating property
It may be said that having basically reached power conservation requirement.From the point of view of the service condition of more than ten years, there is resistance in these insulation materials and heat insulation system
Combustion property poor, easy firing, service life is short, it is easy to fall off damaged, easy to crack the shortcomings of, these shortcomings are brought much to modern building
Hidden danger.Many effect mortars are, with various light materials as aggregate, with cement as gelating material, to admix some property-modifying additives, Jing lifes
Produce enterprise stirring mixing and made by a kind of premixing dry powder and mortar, for construct building surface a kind of construction material.With low
Continuous improvement of the continuous popularization and people of carbocyclic ring guarantor and building energy conservation to living environment comfortableness demand, many effect mortars are got over
Attract widespread attention to get over, the research of many effect mortars of China is more in recent years, it is existing in Practical Project a lot
With, but compared with developed countries, which also exists, and water proofing property is poor, and water absorption rate is big, the easy moisture absorption, and seep water easy to crack, thermal insulation separation thermal effect
Really undesirable the problems such as.
The content of the invention
It is an object of the invention to provide a kind of rock with the features such as high waterproof, high-efficiency insulated, effectively insulating and environmental protection
Cotton water-proof heat insulation mortar.
The present invention solves the technical scheme of technical problem：
A kind of rock wool water-proof heat insulation mortar, is made up of the raw material of following weight：
Cement 400-500 parts, rock wool leftover bits and pieces 40-50 parts, glass bead 100-120 parts, blast-furnace cinder 8-12 parts, sodium tetraborate
4-8 parts, potassium dihydrogen phosphate 3-5 parts, potter's clay 5-7 parts, enuatrol 1-3 parts, compounded mix 4-8 parts, redispersable latex powder 8-12
Part, methylcellulose 1.5-2.5 parts, waterproofing agent 8-10 parts, wood fibre 1-3 parts, polypropylene fibre 1-3 parts.
Preferably, above-mentioned rock wool water-proof heat insulation mortar, is made up of the raw material of following weight：
450 parts of cement, 45 parts of rock wool leftover bits and pieces, 110 parts of glass bead, 10 parts of blast-furnace cinder, 6 parts of sodium tetraborate, biphosphate
4 parts of potassium, 6 parts of potter's clay, 2 parts of enuatrol, 6 parts of compounded mix, 10 parts of redispersable latex powder, 2 parts of methylcellulose, waterproofing agent 9
Part, 2 parts of wood fibre, 2 parts of polypropylene fibre.
The cement is common portland cement, the one kind in sulphate aluminium cement.
Described compounded mix, is prepared by the raw materials in：Meerschaum 10-12 parts, Vermiculitum 8-10 parts, shale
20-30 parts, gangue 8-12 parts, Kaolin 10-12 parts, boron mud 8-10 part, spent pulping liquor 25-35 parts, plant ash 4-8 parts, receive
Rice Ludox 18-20 parts, citric acid 1-2 parts, sugar calcium 2-4 part, nano-silicon nitride 3-5 parts, jade powder 4-6 part；Preferably, it is described
Compounded mix, be prepared by the raw materials in：11 parts of meerschaum, 9 parts of Vermiculitum, 25 parts of shale, 10 parts of gangue, kaolinite
11 parts of soil, 9 parts of boron mud, 30 parts of spent pulping liquor, 6 parts of plant ash, 19 parts of Nano silica sol, 1.5 parts of citric acid, sugar calcium 3 part, nanometer
4 parts of silicon nitride, 5 parts of jade powder.
The preparation method of described compounded mix is：A. by shale, gangue, Kaolin and boron mud mix homogeneously, crush
100-120 mesh sieves are crossed, spent pulping liquor and citric acid is subsequently adding, ball milling 20-30min, pelletize, particle diameter are 0.3-0.4mm, 100-
Dry at 120 DEG C, then the high-temperature roasting 1-2h at 1150-1250 DEG C, it is cooled to room temperature standby；B. meerschaum and Vermiculitum are mixed
It is uniform to be placed in after being cooled to room temperature in hydrochloric acid solution after 650-700 DEG C of temperature lower calcination 2-3h, heating in water bath to 70-80 DEG C,
Insulation 30-40min, filters, and with distilled water by residue washing to neutrality, dries, crushed 200-300 mesh sieves, and be subsequently adding sugar
Calcium, nano-silicon nitride and jade powder, mixed at high speed 20-30min are standby；C. take Nano silica sol to stir, add step A
Obtained granule, high-speed stirred 8-10min add compound obtained in plant ash and step B, high-speed stirred 10-12min,
Drying compounded mix；
The waterproofing agent, is prepared by the raw materials in：It is by zinc stearate 3-5 parts, calcium stearate 2-4 parts, Zinc Oxide
4-6 parts, sodium bicarbonate 1-3 parts, cross-linking agent 0.1-0.3 parts.
The preparation method of above-mentioned rock wool water-proof heat insulation mortar, comprises the steps：
（1）10-12h is soaked in taking hydrochloric acid solution of the rock wool leftover bits and pieces in concentration for 10-12%, take out, deionized water wash, dry
Dry, pulverizing crosses 250-350 mesh sieves, adds attapulgite equivalent to its weight 1-2%, the shitosan of 1-2%, the benzene of 3-5%
Acrylic emulsion, pelletize after mixing, balling-up particle diameter obtain modified rock wool leftover bits and pieces granule in 0.8-1mm, standby；
（2）Modified rock wool leftover bits and pieces granule, cement, glass bead and blast-furnace cinder are mixed by weight, in 300-400 turn/
Divide the lower 3-5min that stirs to take out, add remaining whole raw material mixing and mix thoroughly, 80-100 turn/min at the uniform velocity stirs 20-30min, most
The material three-roll grinder being stirred is ground into 1-2h afterwards, is obtained final product after packaging.
The using method of above-mentioned rock wool water-proof heat insulation mortar is：By mortar and the ratio of water by weight 1: 1.3-1.5
Example, after stirring can use.
The invention has effective effect that：Mortar of the present invention has excellent resistance to water, water proofing property, impermeability, insulation
Property, chemical resistance and weatherability, and intensity is high, and adhesive force is strong, fire protection flame retarding, is not in cracking and the problems such as come off,
Adhesion strength is high, and early strength improves fast, hence it is evident that better than common mortar, improves efficiency of construction；Meanwhile, easy construction, completely
It is reliable, it is with low cost, can be widely used for the engineerings such as insulation, the waterproof of building inside and outside wall.
Specific embodiment
The present invention is further described with reference to embodiments, but the invention is not limited in these embodiments.
Embodiment 1
A kind of rock wool water-proof heat insulation mortar, is made up of the raw material of following weight：
Cement 400kg, rock wool leftover bits and pieces 40kg, glass bead 100kg, blast-furnace cinder 8kg, sodium tetraborate 4kg, potassium dihydrogen phosphate
3kg, potter's clay 5kg, enuatrol 1kg, compounded mix 4kg, redispersable latex powder 8kg, methylcellulose 1.5kg, waterproofing agent
8kg, wood fibre 1kg, polypropylene fibre 1kg.
The cement is common portland cement.
Described compounded mix, is prepared by the raw materials in：Meerschaum 10kg, Vermiculitum 8kg, shale 20kg, coal
Spoil 8kg, Kaolin 10kg, boron mud 8kg, spent pulping liquor 25kg, plant ash 4kg, Nano silica sol 18kg, citric acid 1kg, sugar
Calcium 2kg, nano-silicon nitride 3kg, jade powder 4kg.
The preparation method of described compounded mix is：A. by shale, gangue, Kaolin and boron mud mix homogeneously, crush
100 mesh sieves are crossed, spent pulping liquor and citric acid is subsequently adding, ball milling 20min, pelletize, particle diameter are 0.3mm, are dried at 100 DEG C, then
At 1150 DEG C, high-temperature roasting h, is cooled to room temperature standby；B. meerschaum and Vermiculitum mix homogeneously are forged at a temperature of 650 DEG C
2h is burnt, is placed in after being cooled to room temperature in hydrochloric acid solution, heating in water bath is incubated 30min to 70 DEG C, filters, with distilled water by filtering residue
Wash to neutrality, 200 mesh sieves were crushed in drying, be subsequently adding sugar calcium, nano-silicon nitride and jade powder, mixed at high speed 20min,
It is standby；C. take Nano silica sol to stir, add granule obtained in step A, high-speed stirred 8min to add plant ash and step
Compound obtained in rapid B, high-speed stirred 10min, drying compounded mix；
The waterproofing agent, is prepared by the raw materials in：Be by zinc stearate 3kg, calcium stearate 2kg, Zinc Oxide 4kg,
Sodium bicarbonate 1kg, cross-linking agent 0.1kg.
The preparation method of above-mentioned rock wool water-proof heat insulation mortar, comprises the steps：
（1）Take rock wool leftover bits and pieces and 10h is soaked in the hydrochloric acid solution that concentration is 10%, take out, deionized water wash, drying, mill
Powder, crosses 250 mesh sieves, adds attapulgite equivalent to its weight 1%, 1% shitosan, 3% styrene-acrylic emulsion, makes after mixing
Grain, balling-up particle diameter obtains modified rock wool leftover bits and pieces granule in 0.8mm, standby；
（2）Modified rock wool leftover bits and pieces granule, cement, glass bead and blast-furnace cinder are mixed by weight, under 300 revs/min
Stirring 3min takes out, and adds remaining whole raw material mixing and mixes thoroughly, 80 turns/min at the uniform velocity stirs 20min, will finally be stirred
Material three-roll grinder grinds 1h, obtains final product after packaging.
The using method of above-mentioned rock wool water-proof heat insulation mortar is：By mortar and water by weight 1: 1.3 ratio, stir
Use by after mixing uniformly.
Embodiment 2
A kind of rock wool water-proof heat insulation mortar, is made up of the raw material of following weight：
Cement 450kg, rock wool leftover bits and pieces 45kg, glass bead 110kg, blast-furnace cinder 10kg, sodium tetraborate 6kg, biphosphate
Potassium 4kg, potter's clay 6kg, enuatrol 2kg, compounded mix 6kg, redispersable latex powder 10kg, methylcellulose 2kg, waterproofing agent
9kg, wood fibre 2kg, polypropylene fibre 2kg.
The cement is general sulphate aluminium cement.
Described compounded mix, is prepared by the raw materials in：Meerschaum 11kg, Vermiculitum 9kg, shale 25kg, coal
Spoil 10kg, Kaolin 11kg, boron mud 9kg, spent pulping liquor 30kg, plant ash 6kg, Nano silica sol 19kg, citric acid
1.5kg, sugar calcium 3kg, nano-silicon nitride 4kg, jade powder 5kg.
The preparation method of described compounded mix is：A. by shale, gangue, Kaolin and boron mud mix homogeneously, crush
110 mesh sieves are crossed, spent pulping liquor and citric acid is subsequently adding, ball milling 25min, pelletize, particle diameter are 0.35mm, are dried at 110 DEG C, then
At 1200 DEG C, high-temperature roasting 1.5h, is cooled to room temperature standby；B. by meerschaum and Vermiculitum mix homogeneously at a temperature of 675 DEG C
Calcining 2.5h, is placed in after being cooled to room temperature in hydrochloric acid solution, and heating in water bath is incubated 35min to 75 DEG C, filters, will with distilled water
Residue washing was crushed 250 mesh sieves, was subsequently adding sugar calcium, nano-silicon nitride and jade powder, mixed at high speed to neutrality, drying
25min, it is standby；C. take Nano silica sol to stir, add granule obtained in step A, high-speed stirred 9min to add vegetation
Ash and compound obtained in step B, high-speed stirred 11min, drying compounded mix；
The waterproofing agent, is prepared by the raw materials in：It is by zinc stearate 4kg, calcium stearate 3kg parts, Zinc Oxide
5kg, sodium bicarbonate 2kg, cross-linking agent 0.2kg.
The preparation method of above-mentioned rock wool water-proof heat insulation mortar, comprises the steps：
（1）Take rock wool leftover bits and pieces and 11h is soaked in the hydrochloric acid solution that concentration is 11%, take out, deionized water wash, drying, mill
Powder, crosses 300 mesh sieves, adds attapulgite equivalent to its weight 1.5%, 1.5% shitosan, 4% styrene-acrylic emulsion, mixes
Pelletize afterwards, balling-up particle diameter obtain modified rock wool leftover bits and pieces granule in 0.9mm, standby；
（2）Modified rock wool leftover bits and pieces granule, cement, glass bead and blast-furnace cinder are mixed by weight, under 350 revs/min
Stirring 4min takes out, and adds remaining whole raw material mixing and mixes thoroughly, 90 turns/min at the uniform velocity stirs 25min, will finally be stirred
Material three-roll grinder grinds 1.5h, obtains final product after packaging.
The using method of above-mentioned rock wool water-proof heat insulation mortar is：By mortar and water by weight 1: 1.4 ratio, stir
Use by after mixing uniformly.
Embodiment 3
A kind of rock wool water-proof heat insulation mortar, is made up of the raw material of following weight：
Cement 500kg, rock wool leftover bits and pieces 50kg, glass bead 120kg, blast-furnace cinder 12kg, sodium tetraborate 8kg, biphosphate
Potassium 5kg, potter's clay 7kg, enuatrol 3kg, compounded mix 8kg, redispersable latex powder 12kg, methylcellulose 2.5kg, waterproofing agent
10kg, wood fibre 3kg, polypropylene fibre 3kg.
The cement is common portland cement.
Described compounded mix, is prepared by the raw materials in：Meerschaum 12kg, Vermiculitum 10kg, shale 30kg, coal
Spoil 12kg, Kaolin 12kg, boron mud 10kg, spent pulping liquor 35kg, plant ash 8kg, Nano silica sol 20kg, citric acid 2kg,
Sugar calcium 4kg, nano-silicon nitride 5kg, jade powder 6kg.
The preparation method of described compounded mix is：A. by shale, gangue, Kaolin and boron mud mix homogeneously, crush
120 mesh sieves are crossed, spent pulping liquor and citric acid is subsequently adding, ball milling 30min, pelletize, particle diameter are 0.4mm, are dried at 120 DEG C, then
At 1250 DEG C, high-temperature roasting 2h, is cooled to room temperature standby；B. meerschaum and Vermiculitum mix homogeneously are forged at a temperature of 700 DEG C
3h is burnt, is placed in after being cooled to room temperature in hydrochloric acid solution, heating in water bath is incubated 40min to 80 DEG C, filters, with distilled water by filtering residue
Wash to neutrality, 300 mesh sieves were crushed in drying, be subsequently adding sugar calcium, nano-silicon nitride and jade powder, mixed at high speed 30min,
It is standby；C. take Nano silica sol to stir, add step A obtained in granule, high-speed stirred 10min, add plant ash and
Compound obtained in step B, high-speed stirred 12min, drying compounded mix；
The waterproofing agent, is prepared by the raw materials in：Be by zinc stearate 5kg, calcium stearate 4kg, Zinc Oxide 6kg,
Sodium bicarbonate 3kg, cross-linking agent 0.3kg.
The preparation method of above-mentioned rock wool water-proof heat insulation mortar, comprises the steps：
（1）Take rock wool leftover bits and pieces and 12h is soaked in the hydrochloric acid solution that concentration is 12%, take out, deionized water wash, drying, mill
Powder, crosses 350 mesh sieves, adds attapulgite equivalent to its weight 2%, 2% shitosan, 5% styrene-acrylic emulsion, makes after mixing
Grain, balling-up particle diameter obtains modified rock wool leftover bits and pieces granule in 1mm, standby；
（2）Modified rock wool leftover bits and pieces granule, cement, glass bead and blast-furnace cinder are mixed by weight, under 400 revs/min
Stirring 5min takes out, and adds remaining whole raw material mixing and mixes thoroughly, and 100 turns/min at the uniform velocity stirs 30min, will finally be stirred
Material three-roll grinder grinding 2h, obtain final product after packaging.
The using method of above-mentioned rock wool water-proof heat insulation mortar is：By mortar and water by weight 1: 1.5 ratio, stir
Use by after mixing uniformly.
Above example only to illustrate technical scheme, rather than a limitation；Although with reference to the foregoing embodiments
The present invention has been described in detail, it will be understood by those within the art that：Which still can be to aforementioned each enforcement
Technical scheme described in example is modified, or carries out equivalent to which part technical characteristic；And these modification or
Replace, do not make the essence of appropriate technical solution depart from the spirit and scope of various embodiments of the present invention technical scheme.
Claims (9)
1. a kind of rock wool water-proof heat insulation mortar, is characterized in that：It is made up of the raw material of following weight：
Cement 400-500 parts, rock wool leftover bits and pieces 40-50 parts, glass bead 100-120 parts, blast-furnace cinder 8-12 parts, sodium tetraborate
4-8 parts, potassium dihydrogen phosphate 3-5 parts, potter's clay 5-7 parts, enuatrol 1-3 parts, compounded mix 4-8 parts, redispersable latex powder 8-12
Part, methylcellulose 1.5-2.5 parts, waterproofing agent 8-10 parts, wood fibre 1-3 parts, polypropylene fibre 1-3 parts.
2. rock wool water-proof heat insulation mortar according to claim 1, is characterized in that：By the raw material of following weight
Make：
450 parts of cement, 45 parts of rock wool leftover bits and pieces, 110 parts of glass bead, 10 parts of blast-furnace cinder, 6 parts of sodium tetraborate, biphosphate
4 parts of potassium, 6 parts of potter's clay, 2 parts of enuatrol, 6 parts of compounded mix, 10 parts of redispersable latex powder, 2 parts of methylcellulose, waterproofing agent 9
Part, 2 parts of wood fibre, 2 parts of polypropylene fibre.
3. rock wool water-proof heat insulation mortar according to claim 1, is characterized in that：The cement is common Portland water
One kind in mud, sulphate aluminium cement.
4. rock wool water-proof heat insulation mortar according to claim 1, is characterized in that：Described compounded mix, by following
The raw material of weight portion is made：Meerschaum 10-12 parts, Vermiculitum 8-10 parts, shale 20-30 parts, gangue 8-12 parts, Kaolin 10-
12 parts, boron mud 8-10 part, spent pulping liquor 25-35 parts, plant ash 4-8 parts, Nano silica sol 18-20 parts, citric acid 1-2 parts, sugar
Calcium 2-4 parts, nano-silicon nitride 3-5 parts, jade powder 4-6 part.
5. rock wool water-proof heat insulation mortar according to claim 1, is characterized in that：Described compounded mix, by following
The raw material of weight portion is made：11 parts of meerschaum, 9 parts of Vermiculitum, 25 parts of shale, 10 parts of gangue, 11 parts of Kaolin, 9 parts of boron mud, paper
30 parts of pulp waste, 6 parts of plant ash, 19 parts of Nano silica sol, 1.5 parts of citric acid, 3 parts of sugar calcium, 4 parts of nano-silicon nitride, jade powder 5
Part.
6. the rock wool water-proof heat insulation mortar according to claim 3 or 4, is characterized in that：The system of described compounded mix
Preparation Method is：
A. by shale, gangue, Kaolin and boron mud mix homogeneously, 100-120 mesh sieves were crushed, be subsequently adding spent pulping liquor and
Citric acid, ball milling 20-30min, pelletize, particle diameter are to dry at 0.3-0.4mm, 100-120 DEG C, then the height at 1150-1250 DEG C
Warm roasting 1-2h, is cooled to room temperature standby；
B. meerschaum and Vermiculitum mix homogeneously are placed in into hydrochloric acid after 650-700 DEG C of temperature lower calcination 2-3h after being cooled to room temperature
In solution, heating in water bath is incubated 30-40min to 70-80 DEG C, filters, and with distilled water by residue washing to neutrality, dries, crushes
200-300 mesh sieves are crossed, sugar calcium, nano-silicon nitride and jade powder is subsequently adding, mixed at high speed 20-30min is standby；
C. take Nano silica sol to stir, add step A obtained in granule, high-speed stirred 8-10min, add plant ash and
Compound obtained in step B, high-speed stirred 10-12min, drying compounded mix.
7. rock wool water-proof heat insulation mortar according to claim 1, is characterized in that：The waterproofing agent, by following weight
The raw material of part is made：It is by zinc stearate 3-5 parts, calcium stearate 2-4 parts, Zinc Oxide 4-6 part, sodium bicarbonate 1-3 parts, cross-linking agent
0.1-0.3 parts.
8. the preparation method of rock wool water-proof heat insulation mortar according to claim 1, is characterized in that：Specifically include as follows
Step：
（1）10-12h is soaked in taking hydrochloric acid solution of the rock wool leftover bits and pieces in concentration for 10-12%, take out, deionized water wash, dry
Dry, pulverizing crosses 250-350 mesh sieves, adds attapulgite equivalent to its weight 1-2%, the shitosan of 1-2%, the benzene of 3-5%
Acrylic emulsion, pelletize after mixing, balling-up particle diameter obtain modified rock wool leftover bits and pieces granule in 0.8-1mm, standby；
（2）Modified rock wool leftover bits and pieces granule, cement, glass bead and blast-furnace cinder are mixed by weight, in 300-400 turn/
Divide the lower 3-5min that stirs to take out, add remaining whole raw material mixing and mix thoroughly, 80-100 turn/min at the uniform velocity stirs 20-30min, most
The material three-roll grinder being stirred is ground into 1-2h afterwards, is obtained final product after packaging.
9. the using method of rock wool water-proof heat insulation mortar according to claim 1, is characterized in that：Mortar is pressed with water
Weight compares 1: 1.3-1.5 ratio, after stirring by use.