CN108203284A - Energy-saving, heat-preserving, sound-insulating and environment-friendly building mortar and preparation method thereof - Google Patents

Energy-saving, heat-preserving, sound-insulating and environment-friendly building mortar and preparation method thereof Download PDF

Info

Publication number
CN108203284A
CN108203284A CN201810163366.9A CN201810163366A CN108203284A CN 108203284 A CN108203284 A CN 108203284A CN 201810163366 A CN201810163366 A CN 201810163366A CN 108203284 A CN108203284 A CN 108203284A
Authority
CN
China
Prior art keywords
parts
mixture
energy saving
heat insulating
additive
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201810163366.9A
Other languages
Chinese (zh)
Inventor
王磊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Yakeli New Building Materials Co ltd
Original Assignee
Hefei Yakeli New Building Materials Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Yakeli New Building Materials Co ltd filed Critical Hefei Yakeli New Building Materials Co ltd
Priority to CN201810163366.9A priority Critical patent/CN108203284A/en
Publication of CN108203284A publication Critical patent/CN108203284A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses energy-saving, heat-insulating, sound-insulating and environment-friendly building mortar and a preparation method thereof, wherein the energy-saving, heat-insulating, sound-insulating and environment-friendly building mortar comprises the following raw materials in parts by weight: 20-30 parts of compound cement, 25-35 parts of modified ore filler, 4-8 parts of waterproof adhesion promoter, 20-30 parts of construction waste treatment substance, 8-10 parts of anti-cracking and performance-enhancing additive, 2-4 parts of calcium stearate, 8-10 parts of hollow additive and 20-30 parts of water. The building mortar disclosed by the invention is low in heat conductivity coefficient, good in thermal insulation performance, outstanding in compactness, water-resistant, seepage-proof and excellent in sound insulation performance, and meanwhile, a large amount of building garbage is adopted, so that resources are saved; meanwhile, the raw material components of the invention are safe and reliable, the cost is lower, the raw material source is wide, and the invention has higher practical value and good application prospect.

Description

A kind of energy saving heat insulating sound environment protection architecture mortar and preparation method thereof
Technical field
The present invention relates to building material technical fields, and in particular to a kind of energy saving heat insulating sound environment protection architecture mortar and its system Preparation Method.
Background technology
The essence of building energy conservation is that thermal technology's property of peripheral structure is scientifically and rationally promoted according to the characteristics of Different Climatic Zones Energy.Building heat preservation is to reduce the measure that Indoor environment heat is distributed to outdoor, to creating suitable indoor thermal environment and saving The energy plays an important role.
Various countries are in architectural design and construction, the development and application of new building insulation material, the formulation of Regulation of building energy-saving Done a large amount of work with implement etc., further improved while considerable economic benefit is obtained it is for the survival of mankind from Right environment.Materials for wall dosage shelter has first of construction material under construction, reaches 70%, and traditional wall heat insulation material is deposited Various the defects of and deficiency.As building is to high level development, mitigates the dead weight of materials for wall and improve its heat preservation energy-saving The effect of, thermal insulation mortar is usually coated on wall, thermal insulation mortar is a kind of heat-insulating construction material painted for inner-outer wall, with Light thermal-insulation particle adds the dry powder and mortar being made of other fillers and additive etc., but thermal insulation mortar is sudden and violent as lightweight aggregate Dew in space easily split by water suction, this just needs to set anticracking grout on heat-insulation mortar bed, but existing anticracking grout Effect is poor.In addition, in the market mortar strength performance, impermeability, water absorption rate, can not all meet in construction it is higher will It asks, therefore limits the development of construction.
Invention content
In view of the drawbacks of the prior art, the object of the present invention is to provide a kind of energy saving heat insulating sound environment protection architecture mortars, should Building mortar thermal conductivity factor is low, good heat insulating, and compactness protrudes, and water-fast antiseepage, also excellent sound insulation value uses simultaneously A large amount of building waste, has saved resource;The material component of the present invention is safe and reliable simultaneously, and cost is relatively low, and raw material sources are wide It is general, there is higher practical value and good application prospect.
The present invention solves technical problem and adopts the following technical scheme that:
The present invention provides a kind of energy saving heat insulating sound environment protection architecture mortars, include the raw material of following parts by weight:
Compound 20-30 parts of cement, 25-35 parts of modified ore filler, 4-8 parts of waterproof adhesion promoter, building waste processed material 20-30 Part, crack resistence increase 8-10 parts of additive of property, 2-4 parts of calcium stearate, additive 8-10 parts hollow, 20-30 parts of water.
Preferably, the energy saving heat insulating sound environment protection architecture mortar includes the raw material of following parts by weight:
Compound 25 parts of cement, 30 parts of modified ore filler, 6 parts of waterproof adhesion promoter, 25 parts of building waste processed material, crack resistence increasing property 9 parts of additive, 3 parts of calcium stearate, 9 parts of hollow additive, 25 parts of water.
Preferably, the compounding cement is portland cement, ferrous aluminate cement and high-alumina refractory cement according to weight ratio 5:2:The mixture of 3 compositions.
Preferably, the modified ore filler is:By anorthite, vermiculite, fish-eye stone according to weight ratio 2:1:3 are sent into calcining In stove, 30-40min is calcined under conditions of being 700-800 DEG C in temperature, then crushes and sieves with 100 mesh sieve, then feed the mixture into phase When in the silane coupling agent of the polyvinyl alcohol of its weight 4-6%, 4-6%, in 65-75 DEG C of temperature, speed of agitator 400-600r/ Under min after stirring 15-25min to obtain the final product.
Preferably, the building waste processed material is:Concrete block and brick after building waste is sorted, which are sent into, to be crushed It is crushed in machine, adds in Muffle furnace and calcine 45-55min for 500-600 DEG C in temperature, then be delivered in impact type flour mill and grind Honed 50 mesh sieves to obtain the final product.
Preferably, crack resistence increasing property additive is mineral fibres, glass fibre, steel fibre, ceramic fibre are according to weight Measure ratio 2:3:1:The mixture of 3 compositions.
Preferably, the hollow additive is glass microballoon, ceramic fine bead, coal fly ash hollow micro bead are according to weight ratio 3:2: The mixture of 4 compositions.
Preferably, the waterproof adhesion promoter is acrylic emulsion, waterglass, cellulose ether, chitosan are according to weight ratio 6: 3:2:The mixture of 1 composition.
The present invention also provides a kind of preparation methods of energy saving heat insulating sound environment protection architecture mortar, include the following steps:
Step 1 weighs each component raw material as required;
Step 2, by modified ore filler, building waste processed material, crack resistence increasing property additive, calcium stearate, hollow additive It adds in homogenizer, is stirred 20-30 minutes in the case where speed of agitator is 100-200 r/min and obtain mixture A;
Water, waterproof adhesion promoter are mixed to join in reaction kettle by step 3, and stirring version answers 20-25 points at being 50-60 DEG C in temperature Mixture B is made in clock;
Step 4 will compound and be stirred 10-20 minutes in the mixture A addition blenders that cement is prepared with step 2, and add step The rapid three mixture B prepared, in the case where rotating speed is 200-300r/min, mixing time is 20-30 minutes, and the energy saving guarantor of invention is made Warm sound insulation environment protection architecture mortar.
Preferably, the preparation process of the energy saving heat insulating sound environment protection architecture mortar is:
Step 1 weighs each component raw material as required;
Step 2, by modified ore filler, building waste processed material, crack resistence increasing property additive, calcium stearate, hollow additive It adds in homogenizer, is stirred 25 minutes in the case where speed of agitator is 150r/min and obtain mixture A;
Water, waterproof adhesion promoter are mixed to join in reaction kettle by step 3, and stirring version is answered 22 minutes at being 55 DEG C in temperature, is made Obtain mixture B;
Step 4 will compound and be stirred 15 minutes in the mixture A addition blenders that cement is prepared with step 2, and add step 3 The mixture B of preparation, in the case where rotating speed is 250r/min, mixing time is 25 minutes, and the energy saving heat insulating sound environmental protection that invention is made is built Build mortar.
Compared with prior art, the present invention has following advantageous effect:
(1)The ore filler that a kind of energy saving heat insulating sound environment protection architecture mortar of the present invention uses is mainly anorthite, vermiculite, fish Eyestone is used by its powdered, on the one hand its can to avoid traditional sandstone material water imbibition big, easy dusting, the body in construction Product shrinking percentage it is big the defects of, on the other hand by calcining, it is coupling agent modified so that good can melt between filler and other components It closes, the crack resistence increasing property additive of addition is coordinated to intert and therebetween, forms fine and close lotion, the intensity of mortar is greatly strengthened and prevents Aqueous energy.
(2)A kind of energy saving heat insulating sound environment protection architecture mortar of the present invention employs a large amount of building waste, on the one hand solves It has determined the pollution problem of building waste, has saved resource, realized and recycle, reduced cost, safety and environmental protection, on the other hand By the calcining and grinding to building waste, the cleanliness factor of building waste and agglomerability energy are improved, it can be preferable It is used as mortar aggregate.
(3)The hollow additive that a kind of energy saving heat insulating sound environment protection architecture mortar of the present invention uses is glass microballoon, pottery Porcelain microballon, coal fly ash hollow micro bead, the compound action of a few person's hollow structures of one side can greatly improve the heat-insulating property of mortar, On the other hand it also is able to greatly reduce the propagation of sound, there is preferable soundproof effect
(4)A kind of waterproof adhesion promoter of energy saving heat insulating sound environment protection architecture mortar addition of the present invention is acrylic emulsion, water glass Glass, cellulose ether, chitosan to increase the stickiness of mortar, are formed with the cement gel of adhesive strength, are not easy to cause tilting and oozing Water has good weather-proof, ageing-resistant performance, can effectively play impervious water resistance, while can form space three-dimensional net Shape cross-linked structure can play humidification to cement mortar material.
(5)A kind of crack resistence increasing property additive of energy saving heat insulating sound environment protection architecture mortar addition of the present invention is mainly ore deposit Fibres, glass fibre, steel fibre, ceramic fibre, several persons can be interspersed among each component aggregate, the crack resistance for the mortar for being It can be greatly improved with mechanical property.
(6)A kind of energy saving heat insulating sound environment protection architecture mortar heat conductivity coefficient of the present invention is low, and good heat insulating, compactness is dashed forward Go out, water-fast antiseepage, also excellent sound insulation value, while employ a large amount of building waste, saved resource;The present invention simultaneously Material component it is safe and reliable, cost is relatively low, and raw material sources are extensive, have higher practical value and good application prospect.
Specific embodiment
With reference to specific embodiment, the technical solution in the embodiment of the present invention is clearly and completely described, is shown So, described embodiment is only part of the embodiment of the present invention, instead of all the embodiments.Based on the reality in the present invention Apply example, those of ordinary skill in the art's all other embodiments obtained without making creative work all belong to In the scope of protection of the invention.
Embodiment 1.
A kind of energy saving heat insulating sound environment protection architecture mortar of the present embodiment includes the raw material of following parts by weight:
Compound 20 parts of cement, 25 parts of modified ore filler, 4 parts of waterproof adhesion promoter, 20 parts of building waste processed material, crack resistence increasing property 8 parts of additive, 2 parts of calcium stearate, 8 parts of hollow additive, 20 parts of water.
Compounding cement in the present embodiment is portland cement, ferrous aluminate cement and high-alumina refractory cement according to weight ratio 5:2:The mixture of 3 compositions.
Modified ore filler in the present embodiment is:By anorthite, vermiculite, fish-eye stone according to weight ratio 2:1:3 feedings are forged It burns in stove, calcines 30min under conditions of being 700 DEG C in temperature, then crush and sieve with 100 mesh sieve, then feed the mixture into and be equivalent to The polyvinyl alcohol of its weight 4%, 4% silane coupling agent, in the case where 65 DEG C of temperature, speed of agitator is 400r/min after stirring 15min To obtain the final product.
Building waste processed material in the present embodiment is:Concrete block and brick after building waste is sorted, which are sent into, to be crushed It is crushed in machine, adds in Muffle furnace and calcine 45min for 500 DEG C in temperature, then be delivered to ground 50 in impact type flour mill Mesh sieves to obtain the final product.
Crack resistence increasing property additive in the present embodiment is mineral fibres, glass fibre, steel fibre, ceramic fibre are according to weight Measure ratio 2:3:1:The mixture of 3 compositions.
Hollow additive in the present embodiment is glass microballoon, ceramic fine bead, coal fly ash hollow micro bead are according to weight ratio 3: 2:The mixture of 4 compositions.
Waterproof adhesion promoter in the present embodiment is acrylic emulsion, waterglass, cellulose ether, chitosan are according to weight ratio 6: 3:2:The mixture of 1 composition.
A kind of preparation method of energy saving heat insulating sound environment protection architecture mortar of the present embodiment, includes the following steps:
Step 1 weighs each component raw material as required;
Step 2, by modified ore filler, building waste processed material, crack resistence increasing property additive, calcium stearate, hollow additive It adds in homogenizer, is stirred 20 minutes in the case where speed of agitator is 100 r/min and obtain mixture A;
Water, waterproof adhesion promoter are mixed to join in reaction kettle by step 3, and stirring version is answered 20 minutes at being 50 DEG C in temperature, is made Obtain mixture B;
Step 4 will compound and be stirred 10 minutes in the mixture A addition blenders that cement is prepared with step 2, and add step 3 The mixture B of preparation, in the case where rotating speed is 200r/min, mixing time is 20 minutes, and the energy saving heat insulating sound environmental protection that invention is made is built Build mortar.
Embodiment 2.
A kind of energy saving heat insulating sound environment protection architecture mortar of the present embodiment includes the raw material of following parts by weight:
Compound 30 parts of cement, 35 parts of modified ore filler, 8 parts of waterproof adhesion promoter, 30 parts of building waste processed material, crack resistence increasing property 10 parts of additive, 4 parts of calcium stearate, 10 parts of hollow additive, 30 parts of water.
Compounding cement in the present embodiment is portland cement, ferrous aluminate cement and high-alumina refractory cement according to weight ratio 5:2:The mixture of 3 compositions.
Modified ore filler in the present embodiment is:By anorthite, vermiculite, fish-eye stone according to weight ratio 2:1:3 feedings are forged It burns in stove, calcines 40min under conditions of being 800 DEG C in temperature, then crush and sieve with 100 mesh sieve, then feed the mixture into and be equivalent to The polyvinyl alcohol of its weight 6%, 6% silane coupling agent, in the case where 75 DEG C of temperature, speed of agitator is 600r/min after stirring 25min To obtain the final product.
Building waste processed material in the present embodiment is:Concrete block and brick after building waste is sorted, which are sent into, to be crushed It is crushed in machine, adds in Muffle furnace and calcine 55min for 600 DEG C in temperature, then be delivered to ground 50 in impact type flour mill Mesh sieves to obtain the final product.
Crack resistence increasing property additive in the present embodiment is mineral fibres, glass fibre, steel fibre, ceramic fibre are according to weight Measure ratio 2:3:1:The mixture of 3 compositions.
Hollow additive in the present embodiment is glass microballoon, ceramic fine bead, coal fly ash hollow micro bead are according to weight ratio 3: 2:The mixture of 4 compositions.
Waterproof adhesion promoter in the present embodiment is acrylic emulsion, waterglass, cellulose ether, chitosan are according to weight ratio 6: 3:2:The mixture of 1 composition.
A kind of preparation method of energy saving heat insulating sound environment protection architecture mortar of the present embodiment, includes the following steps:
Step 1 weighs each component raw material as required;
Step 2, by modified ore filler, building waste processed material, crack resistence increasing property additive, calcium stearate, hollow additive It adds in homogenizer, is stirred 30 minutes in the case where speed of agitator is 200 r/min and obtain mixture A;
Water, waterproof adhesion promoter are mixed to join in reaction kettle by step 3, and stirring version is answered 25 minutes at being 60 DEG C in temperature, is made Obtain mixture B;
Step 4 will compound and be stirred 20 minutes in the mixture A addition blenders that cement is prepared with step 2, and add step 3 The mixture B of preparation, in the case where rotating speed is 300r/min, mixing time is 30 minutes, and the energy saving heat insulating sound environmental protection that invention is made is built Build mortar.
Embodiment 3.
A kind of energy saving heat insulating sound environment protection architecture mortar of the present embodiment includes the raw material of following parts by weight:
Compound 25 parts of cement, 30 parts of modified ore filler, 6 parts of waterproof adhesion promoter, 25 parts of building waste processed material, crack resistence increasing property 9 parts of additive, 3 parts of calcium stearate, 9 parts of hollow additive, 25 parts of water.
Compounding cement in the present embodiment is portland cement, ferrous aluminate cement and high-alumina refractory cement according to weight ratio 5:2:The mixture of 3 compositions.
Modified ore filler in the present embodiment is:By anorthite, vermiculite, fish-eye stone according to weight ratio 2:1:3 feedings are forged It burns in stove, calcines 35min under conditions of being 750 DEG C in temperature, then crush and sieve with 100 mesh sieve, then feed the mixture into and be equivalent to The polyvinyl alcohol of its weight 5%, 5% silane coupling agent, in the case where temperature 70 C, speed of agitator is 500r/min after stirring 20min To obtain the final product.
Building waste processed material in the present embodiment is:Concrete block and brick after building waste is sorted, which are sent into, to be crushed It is crushed in machine, adds in Muffle furnace and calcine 50min for 550 DEG C in temperature, then be delivered to ground 50 in impact type flour mill Mesh sieves to obtain the final product.
Crack resistence increasing property additive in the present embodiment is mineral fibres, glass fibre, steel fibre, ceramic fibre are according to weight Measure ratio 2:3:1:The mixture of 3 compositions.
Hollow additive in the present embodiment is glass microballoon, ceramic fine bead, coal fly ash hollow micro bead are according to weight ratio 3: 2:The mixture of 4 compositions.
Waterproof adhesion promoter in the present embodiment is acrylic emulsion, waterglass, cellulose ether, chitosan are according to weight ratio 6: 3:2:The mixture of 1 composition.
A kind of preparation method of energy saving heat insulating sound environment protection architecture mortar of the present embodiment, includes the following steps:
Step 1 weighs each component raw material as required;
Step 2, by modified ore filler, building waste processed material, crack resistence increasing property additive, calcium stearate, hollow additive It adds in homogenizer, is stirred 25 minutes in the case where speed of agitator is 150r/min and obtain mixture A;
Water, waterproof adhesion promoter are mixed to join in reaction kettle by step 3, and stirring version is answered 22 minutes at being 55 DEG C in temperature, is made Obtain mixture B;
Step 4 will compound and be stirred 15 minutes in the mixture A addition blenders that cement is prepared with step 2, and add step 3 The mixture B of preparation, in the case where rotating speed is 250r/min, mixing time is 25 minutes, and the energy saving heat insulating sound environmental protection that invention is made is built Build mortar.
A kind of energy saving heat insulating sound environment protection architecture mortar heat conductivity coefficient of the present invention is low, good heat insulating, and compactness protrudes, Water-fast antiseepage, also excellent sound insulation value, while a large amount of building waste is employed, save resource;Of the invention simultaneously Material component is safe and reliable, and cost is relatively low, and raw material sources are extensive, has higher practical value and good application prospect.
It is obvious to a person skilled in the art that the present invention is not limited to the details of above-mentioned exemplary embodiment, Er Qie In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power Profit requirement rather than above description limit, it is intended that all by what is fallen within the meaning and scope of the equivalent requirements of the claims Variation is included within the present invention.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should It considers the specification as a whole, the technical solutions in each embodiment can also be properly combined, forms those skilled in the art The other embodiment being appreciated that.

Claims (10)

1. a kind of energy saving heat insulating sound environment protection architecture mortar, which is characterized in that include the raw material of following parts by weight:
Compound 20-30 parts of cement, 25-35 parts of modified ore filler, 4-8 parts of waterproof adhesion promoter, building waste processed material 20-30 Part, crack resistence increase 8-10 parts of additive of property, 2-4 parts of calcium stearate, additive 8-10 parts hollow, 20-30 parts of water.
A kind of 2. energy saving heat insulating sound environment protection architecture mortar according to claim 1, which is characterized in that the energy-saving heat preserving Sound insulation environment protection architecture mortar includes the raw material of following parts by weight:
Compound 25 parts of cement, 30 parts of modified ore filler, 6 parts of waterproof adhesion promoter, 25 parts of building waste processed material, crack resistence increasing property 9 parts of additive, 3 parts of calcium stearate, 9 parts of hollow additive, 25 parts of water.
A kind of 3. energy saving heat insulating sound environment protection architecture mortar according to claim 1 or 2, which is characterized in that the compounding Cement is portland cement, ferrous aluminate cement and high-alumina refractory cement according to weight ratio 5:2:The mixture of 3 compositions.
A kind of 4. energy saving heat insulating sound environment protection architecture mortar according to claim 1 or 2, which is characterized in that the modification Ore filler is:By anorthite, vermiculite, fish-eye stone according to weight ratio 2:1:3 are sent into calcining furnace, are 700-800 DEG C in temperature Under conditions of calcine 30-40min, then crush sieve with 100 mesh sieve, then feed the mixture into the polyethylene for being equivalent to its weight 4-6% The silane coupling agent of alcohol, 4-6%, in the case where 65-75 DEG C of temperature, speed of agitator is 400-600r/min after stirring 15-25min to obtain the final product.
A kind of 5. energy saving heat insulating sound environment protection architecture mortar according to claim 1 or 2, which is characterized in that the building Waste disposal is:Concrete block and brick after building waste is sorted, which are sent into pulverizer, to be crushed, and is added in Muffle furnace It is 500-600 DEG C of calcining 45-55min, then be delivered to ground 50 mesh in impact type flour mill and sieve in temperature to obtain the final product.
6. a kind of energy saving heat insulating sound environment protection architecture mortar according to claim 1 or 2, which is characterized in that described to prevent opening Increasing property additive is split for mineral fibres, glass fibre, steel fibre, ceramic fibre is according to weight ratio 2:3:1:The mixture of 3 compositions.
7. a kind of energy saving heat insulating sound environment protection architecture mortar according to claim 1 or 2, which is characterized in that described hollow Additive is glass microballoon, ceramic fine bead, coal fly ash hollow micro bead are according to weight ratio 3:2:The mixture of 4 compositions.
A kind of 8. energy saving heat insulating sound environment protection architecture mortar according to claim 1 or 2, which is characterized in that the waterproof Adhesion promoter is acrylic emulsion, waterglass, cellulose ether, chitosan are according to weight ratio 6:3:2:The mixture of 1 composition.
A kind of 9. method for preparing energy saving heat insulating sound environment protection architecture mortar as claimed in claim 1 or 2, which is characterized in that Include the following steps:
Step 1 weighs each component raw material as required;
Step 2, by modified ore filler, building waste processed material, crack resistence increasing property additive, calcium stearate, hollow additive It adds in homogenizer, is stirred 20-30 minutes in the case where speed of agitator is 100-200 r/min and obtain mixture A;
Water, waterproof adhesion promoter are mixed to join in reaction kettle by step 3, and stirring version answers 20-25 points at being 50-60 DEG C in temperature Mixture B is made in clock;
Step 4 will compound and be stirred 10-20 minutes in the mixture A addition blenders that cement is prepared with step 2, and add step The rapid three mixture B prepared, in the case where rotating speed is 200-300r/min, mixing time is 20-30 minutes, and the energy saving guarantor of invention is made Warm sound insulation environment protection architecture mortar.
10. a kind of preparation method of energy saving heat insulating sound environment protection architecture mortar according to claim 9, which is characterized in that The step is:
Step 1 weighs each component raw material as required;
Step 2, by modified ore filler, building waste processed material, crack resistence increasing property additive, calcium stearate, hollow additive It adds in homogenizer, is stirred 25 minutes in the case where speed of agitator is 150r/min and obtain mixture A;
Water, waterproof adhesion promoter are mixed to join in reaction kettle by step 3, and stirring version is answered 22 minutes at being 55 DEG C in temperature, is made Obtain mixture B;
Step 4 will compound and be stirred 15 minutes in the mixture A addition blenders that cement is prepared with step 2, and add step 3 The mixture B of preparation, in the case where rotating speed is 250r/min, mixing time is 25 minutes, and the energy saving heat insulating sound environmental protection that invention is made is built Build mortar.
CN201810163366.9A 2018-02-27 2018-02-27 Energy-saving, heat-preserving, sound-insulating and environment-friendly building mortar and preparation method thereof Withdrawn CN108203284A (en)