CN105801063A - Light-weight, heat-insulating and environment-friendly composite wall building material - Google Patents

Light-weight, heat-insulating and environment-friendly composite wall building material Download PDF

Info

Publication number
CN105801063A
CN105801063A CN201610148666.0A CN201610148666A CN105801063A CN 105801063 A CN105801063 A CN 105801063A CN 201610148666 A CN201610148666 A CN 201610148666A CN 105801063 A CN105801063 A CN 105801063A
Authority
CN
China
Prior art keywords
construction
environment
parts
lightweight
friendly type
Prior art date
Application number
CN201610148666.0A
Other languages
Chinese (zh)
Inventor
韩旭霞
Original Assignee
韩旭霞
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 韩旭霞 filed Critical 韩旭霞
Priority to CN201610148666.0A priority Critical patent/CN105801063A/en
Publication of CN105801063A publication Critical patent/CN105801063A/en

Abstract

The invention discloses a light-weight, heat-insulating and environment-friendly composite wall building material.The building coating is prepared from cellulose, carbon fiber particles, rubber particles, plant particles, low-density polyethylene resin, organosilicon-modified epoxy resin, calcium carbonate, magnesium oxide, magnesium silicate, magnesium calcium carbonate, calcium borate, nanosized silica, light-weight ceramic, EVA redispersable rubber powder and the like.The building wall coating has the advantages of being high in breaking strength and compressive strength, has the effects of heat preservation and sound insulation, is low in heat conductivity coefficient and good in energy-saving effect, and has the good waterproof effect.The obtained wall material is portable, low in cost, free of pollution and environmentally friendly, energy consumption and the production cost are greatly reduced, and the material can be widely applied to building construction.

Description

A kind of lightweight, heat insulation, environment-friendly type combined wall construction material
Technical field
The present invention relates to a kind of construction timber material formula and preparation method thereof, be specifically related to a kind of lightweight, heat insulation, environment-friendly type combined wall construction material.
Background technology
Along with the development of various countries' process of industrialization, the Fossil fuel that the earth is available for human use is day by day exhausted, and the outlet of worldwide energy crisis only has two, notes saving the energy while tapping a new source of energy.Building energy consumption proportion in the whole energy resource consumption of the mankind is very high, therefore building energy conservation is the fundamental way solving energy problem of China, and building energy conservation the most effective method is to use heat preserving and insulating material.At architectural reasonable employing heat preserving and insulating material, it is possible to reduce the consumption of construction material, improve the industrialization degree of construction, accompanied by substantial power saving.The heat preserving and insulating material originally used under construction, is mainly based upon and improves comfortable for living degree, nowadays have been transferred to energy-conservation above.Use building heat preservation heat-barrier material that the residential level of alleviating energy crisis and the raising people is significant.
The wide range that novel construction material includes, has insulation material, heat-barrier material, high-strength material, the material etc. that can breathe to broadly fall into new material.Construction material is the general designation of the material used in civil engineering and architectural engineering.
Construction material can be divided into structural material, ornament materials and some proprietary material.Structural material includes timber, bamboo wood, stone material, cement, concrete, metal, brick and tile, pottery, glass, engineering plastics, composite etc.;Ornament materials includes various coating, paint, coating, veneer, assorted ceramic tile, has the glass etc. of special-effect;Proprietary material refers to for waterproof, protection against the tide, anticorrosion, fire prevention, fire-retardant, sound insulation, heat insulation, insulation, sealing etc..
At present, clay class that building field uses and the wall body building material being gellant with cement, although it has the advantages such as intensity height, good endurance, but its unit weight is big, and sound insulation, heat-proof quality are poor so that it is range of application is restricted.Also exist simultaneously high cost source and fuel, complex process, very easily to environment.The construction material quality made loosely, insufficient strength, and the raw material storage having is little, by the restriction of regional condition, is not suitable for large-scale production.
Summary of the invention
Goal of the invention: the present invention is directed to deficiency of the prior art, it is proposed to a kind of have rupture strength and a high feature of comprcssive strength, and there is effect of insulation, sound insulation, its heat conductivity is low, good energy-conserving effect, and has good waterproof effect;The materials for wall material prepared is light, with low cost, and environmental protection, it is greatly saved the consumption of the energy and production cost, it is possible to be widely used for the lightweight in construction, heat insulation, environment-friendly type combined wall construction material and preparation method.
Technical scheme: a kind of lightweight, heat insulation, environment-friendly type combined wall construction material of the present invention, the component including following mass parts forms:
nullCellulose 5-10 part,Carbon fiber particles 10-15 part,Rubber grain 20-25 part,Plant granule 20-30 part,Ldpe resin 15-40 part,Modifying epoxy resin by organosilicon 5-8 part,Calcium carbonate 5-15 part,Magnesium oxide 0.5-2 part,Magnesium silicate 0.6-0.8 part,Magnesium calcium carbonate 10-15 part,Calcium pyroborate 5-8 part,Nano silicon oxide 5-10 part,Light ceramics 5-10 part,EVA re-dispersible glue powder 1.5-1.7 part,Pumex 15-35 part,Peat soil 3-5 part,Cement 20-55 part,Quick lime 8-12 part,Feldspar powder 5-10 part,Flyash 35-45 part,Poly-4-methyl-1-pentene 7-12 part,Polystyrolsulfon acid 5-9 part,Butyl rubber 7-11 part,Heat stabilizer 1-3 part,Waterproofing agent 0.3-0.8 part,Toughener 1-3 part,Foaming agent 0.1-1 part,Cross-linking agent 0.1-0.5 part,Silylation hydrophober 0.2-0.3 part、Wetting agent 2.3-2.5 part、Additive 1-2 part.
Further, described plant granule be after the plant tissue such as wheat straw or corn stalk is pulverized particle diameter at the granule of 10-30mm.
Further, described cellulose is that methylcellulose, hydroxypropyl methyl cellulose, hydroxyethyl cellulose are according to the 1-3:1-2:1-2 mixture formed.
Further, described wetting agent is succinic acid dibutyl ester sodium sulfonate is 1:15 with its weight ratio of sodium alkyl sulfonate.
Further, described additive is ethylene-vinyl acetate c emulsion with calcium carbonate according to the 2-3:1-2 mixture formed.
Further, described heat stabilizer is zinc stearate.
Further, described waterproofing agent is inorganic aluminate.
Further, described toughener is EP rubbers, and foaming agent is carbon black, and cross-linking agent is cumyl peroxide.
The preparation method that the invention also discloses a kind of lightweight, heat insulation, environment-friendly type combined wall construction material, comprises the steps:
(1) take Pumex according to proportioning raw materials, peat soil, cement, quick lime, feldspar powder, flyash, light ceramics, magnesium silicate are sufficiently mixed in batch mixer, pulverize and make uniform compound A;
(2) carry out being sufficiently mixed in batch mixer uniformly according to proportioning raw materials extracting cellulose, carbon fiber particles, rubber grain, plant granule, ldpe resin, modifying epoxy resin by organosilicon, calcium carbonate, magnesium oxide, magnesium calcium carbonate, Calcium pyroborate, nano silicon oxide, prepare compound B;
(3) above-mentioned compound A and compound B is sufficiently mixed, and places 24-48 hour;
(4) in foam material pond, add the water of the 40-60% producing construction material weight, then pass into steam heating 13-15h, control water temperature 50-75 DEG C, the compound of above-mentioned steps (3) is added, is uniformly mixing to obtain mixed liquor A;
(5) EVA re-dispersible glue powder, poly-4-methyl-1-pentene, polystyrolsulfon acid, butyl rubber, heat stabilizer, waterproofing agent, toughener, foaming agent, cross-linking agent, silylation hydrophober, wetting agent mixing are taken according to proportioning raw materials, add the water of remaining weight, uniform in stirrer for mixing, make uniform mixed liquid B;
(6) by mixed liquor A and B mix homogeneously, steam is passed into heating, makes temperature of liquid reach 85-90 DEG C, add additive, must not have suspended impurity, reach transparent till;
(7) gained mixture repressurization being shaped, moulding pressure is 16MPa-24MPa, and pressing time is 5-8h, places 6-18h, obtain combined wall construction material after cooling.
Beneficial effect: building wall paint provided by the invention, it has rupture strength and a high feature of comprcssive strength, and has effect of insulation, sound insulation, and its heat conductivity is low, good energy-conserving effect, and has good waterproof effect;The materials for wall material prepared is light, with low cost, and environmental protection, it is greatly saved the consumption of the energy and production cost, it is possible to be widely used in construction.
Detailed description of the invention
Below in conjunction with specific embodiment, the invention will be further described:
Embodiment 1
A kind of lightweight, heat insulation, environment-friendly type combined wall construction material, the component including following mass parts forms:
Cellulose 5 parts, carbon fiber particles 10 parts, rubber grain 20 parts, plant granule 20 parts, ldpe resin 15 parts, modifying epoxy resin by organosilicon 5 parts, calcium carbonate 5 parts, magnesium oxide 0.5 part, magnesium silicate 0.6 part, magnesium calcium carbonate 10 parts, Calcium pyroborate 5 parts, nano silicon oxide 5 parts, light ceramics 5 parts, EVA re-dispersible glue powder 1.5 parts, Pumex 15 parts, peat soil 3 parts, cement 20 parts, quick lime 8 parts, feldspar powder 5 parts, 35 parts of flyash, poly-4-methyl-1-pentene 7 parts, polystyrolsulfon acid 5 parts, butyl rubber 7 parts, heat stabilizer 1 part, waterproofing agent 0.3 part, toughener 1 part, foaming agent 0.1 part, cross-linking agent 0.1 part, silylation hydrophober 0.2 part, wetting agent 2.3 parts, additive 1 part.
Further, described plant granule be after the plant tissue such as wheat straw or corn stalk is pulverized particle diameter at the granule of 10-30mm.
Further, described cellulose is that methylcellulose, hydroxypropyl methyl cellulose, hydroxyethyl cellulose are according to the 1:1:1 mixture formed.
Further, described wetting agent is succinic acid dibutyl ester sodium sulfonate is 1:15 with its weight ratio of sodium alkyl sulfonate.
Further, described additive is ethylene-vinyl acetate c emulsion with calcium carbonate according to the 2:1 mixture formed.
Further, described heat stabilizer is zinc stearate.
Further, described waterproofing agent is inorganic aluminate.
Further, described toughener is EP rubbers, and foaming agent is carbon black, and cross-linking agent is cumyl peroxide.
The preparation method that the invention also discloses a kind of lightweight, heat insulation, environment-friendly type combined wall construction material, comprises the steps:
(1) take Pumex according to proportioning raw materials, peat soil, cement, quick lime, feldspar powder, flyash, light ceramics, magnesium silicate are sufficiently mixed in batch mixer, pulverize and make uniform compound A;
(2) carry out being sufficiently mixed in batch mixer uniformly according to proportioning raw materials extracting cellulose, carbon fiber particles, rubber grain, plant granule, ldpe resin, modifying epoxy resin by organosilicon, calcium carbonate, magnesium oxide, magnesium calcium carbonate, Calcium pyroborate, nano silicon oxide, prepare compound B;
(3) above-mentioned compound A and compound B is sufficiently mixed, and places 24 hours;
(4) in foam material pond, add the water of to produce construction material weight 40%, then pass into steam heating 13-15h, control water temperature 50 DEG C, the compound of above-mentioned steps (3) is added, is uniformly mixing to obtain mixed liquor A;
(5) EVA re-dispersible glue powder, poly-4-methyl-1-pentene, polystyrolsulfon acid, butyl rubber, heat stabilizer, waterproofing agent, toughener, foaming agent, cross-linking agent, silylation hydrophober, wetting agent mixing are taken according to proportioning raw materials, add the water of remaining 60% weight, uniform in stirrer for mixing, make uniform mixed liquid B;
(6) by mixed liquor A and B mix homogeneously, steam is passed into heating, makes temperature of liquid reach 85 DEG C, add additive, must not have suspended impurity, reach transparent till;
(7) gained mixture repressurization being shaped, moulding pressure is 16MPa, and pressing time is 5h, places 6h, obtain combined wall construction material after cooling.
Embodiment 2
A kind of lightweight, heat insulation, environment-friendly type combined wall construction material, the component including following mass parts forms:
Cellulose 10 parts, carbon fiber particles 15 parts, rubber grain 25 parts, plant granule 30 parts, ldpe resin 40 parts, modifying epoxy resin by organosilicon 8 parts, calcium carbonate 15 parts, magnesium oxide 2 parts, magnesium silicate 0.8 part, magnesium calcium carbonate 15 parts, Calcium pyroborate 8 parts, nano silicon oxide 10 parts, light ceramics 10 parts, EVA re-dispersible glue powder 1.7 parts, Pumex 35 parts, peat soil 5 parts, cement 55 parts, quick lime 12 parts, feldspar powder 10 parts, 45 parts of flyash, poly-4-methyl-1-pentene 12 parts, polystyrolsulfon acid 9 parts, butyl rubber 11 parts, heat stabilizer 3 parts, waterproofing agent 0.8 part, toughener 3 parts, foaming agent 1 part, cross-linking agent 0.5 part, silylation hydrophober 0.3 part, wetting agent 2.5 parts, additive 2 parts.
Further, described plant granule be after the plant tissue such as wheat straw or corn stalk is pulverized particle diameter at the granule of 10-30mm.
Further, described cellulose is that methylcellulose, hydroxypropyl methyl cellulose, hydroxyethyl cellulose are according to the 3:2:2 mixture formed.
Further, described wetting agent is succinic acid dibutyl ester sodium sulfonate is 1:15 with its weight ratio of sodium alkyl sulfonate.
Further, described additive is ethylene-vinyl acetate c emulsion with calcium carbonate according to the 3:2 mixture formed.
Further, described heat stabilizer is zinc stearate.
Further, described waterproofing agent is inorganic aluminate.
Further, described toughener is EP rubbers, and foaming agent is carbon black, and cross-linking agent is cumyl peroxide.
The preparation method that the invention also discloses a kind of lightweight, heat insulation, environment-friendly type combined wall construction material, comprises the steps:
(1) take Pumex according to proportioning raw materials, peat soil, cement, quick lime, feldspar powder, flyash, light ceramics, magnesium silicate are sufficiently mixed in batch mixer, pulverize and make uniform compound A;
(2) carry out being sufficiently mixed in batch mixer uniformly according to proportioning raw materials extracting cellulose, carbon fiber particles, rubber grain, plant granule, ldpe resin, modifying epoxy resin by organosilicon, calcium carbonate, magnesium oxide, magnesium calcium carbonate, Calcium pyroborate, nano silicon oxide, prepare compound B;
(3) above-mentioned compound A and compound B is sufficiently mixed, and places 24-48 hour;
(4) in foam material pond, add the water of to produce construction material weight 60%, then pass into steam heating 15h, control water temperature 75 DEG C, the compound of above-mentioned steps (3) is added, is uniformly mixing to obtain mixed liquor A;
(5) EVA re-dispersible glue powder, poly-4-methyl-1-pentene, polystyrolsulfon acid, butyl rubber, heat stabilizer, waterproofing agent, toughener, foaming agent, cross-linking agent, silylation hydrophober, wetting agent mixing are taken according to proportioning raw materials, add the water of remaining weight, uniform in stirrer for mixing, make uniform mixed liquid B;
(6) by mixed liquor A and B mix homogeneously, steam is passed into heating, makes temperature of liquid reach 90 DEG C, add additive, must not have suspended impurity, reach transparent till;
(7) gained mixture repressurization being shaped, moulding pressure is 24MPa, and pressing time is 8h, places 18h, obtain combined wall construction material after cooling.
Embodiment 3
A kind of lightweight, heat insulation, environment-friendly type combined wall construction material, the component including following mass parts forms:
Cellulose 7 parts, carbon fiber particles 12 parts, rubber grain 22 parts, plant granule 25 parts, ldpe resin 30 parts, modifying epoxy resin by organosilicon 6 parts, calcium carbonate 10 parts, magnesium oxide 1 part, magnesium silicate 0.7 part, magnesium calcium carbonate 12 parts, Calcium pyroborate 6 parts, nano silicon oxide 7 parts, light ceramics 7 parts, EVA re-dispersible glue powder 1.6 parts, Pumex 25 parts, peat soil 4 parts, cement 35 parts, quick lime 10 parts, feldspar powder 7 parts, 40 parts of flyash, poly-4-methyl-1-pentene 9 parts, polystyrolsulfon acid 7 parts, butyl rubber 9 parts, heat stabilizer 2 parts, waterproofing agent 0.5 part, toughener 2 parts, foaming agent 0.5 part, cross-linking agent 0.3 part, silylation hydrophober 0.25 part, wetting agent 2.4 parts, additive 1.5 parts.
Further, described plant granule be after the plant tissue such as wheat straw or corn stalk is pulverized particle diameter at the granule of 10-30mm.
Further, described cellulose is that methylcellulose, hydroxypropyl methyl cellulose, hydroxyethyl cellulose are according to the 2:1:1 mixture formed.
Further, described wetting agent is succinic acid dibutyl ester sodium sulfonate is 1:15 with its weight ratio of sodium alkyl sulfonate.
Further, described additive is ethylene-vinyl acetate c emulsion with calcium carbonate according to the 2:1 mixture formed.
Further, described heat stabilizer is zinc stearate.
Further, described waterproofing agent is inorganic aluminate.
Further, described toughener is EP rubbers, and foaming agent is carbon black, and cross-linking agent is cumyl peroxide.
The preparation method that the invention also discloses a kind of lightweight, heat insulation, environment-friendly type combined wall construction material, comprises the steps:
(1) take Pumex according to proportioning raw materials, peat soil, cement, quick lime, feldspar powder, flyash, light ceramics, magnesium silicate are sufficiently mixed in batch mixer, pulverize and make uniform compound A;
(2) carry out being sufficiently mixed in batch mixer uniformly according to proportioning raw materials extracting cellulose, carbon fiber particles, rubber grain, plant granule, ldpe resin, modifying epoxy resin by organosilicon, calcium carbonate, magnesium oxide, magnesium calcium carbonate, Calcium pyroborate, nano silicon oxide, prepare compound B;
(3) above-mentioned compound A and compound B is sufficiently mixed, and places 36 hours;
(4) in foam material pond, add the water of to produce construction material weight 50%, then pass into steam heating 13-15h, control water temperature 65 DEG C, the compound of above-mentioned steps (3) is added, is uniformly mixing to obtain mixed liquor A;
(5) EVA re-dispersible glue powder, poly-4-methyl-1-pentene, polystyrolsulfon acid, butyl rubber, heat stabilizer, waterproofing agent, toughener, foaming agent, cross-linking agent, silylation hydrophober, wetting agent mixing are taken according to proportioning raw materials, add the water of remaining weight, uniform in stirrer for mixing, make uniform mixed liquid B;
(6) by mixed liquor A and B mix homogeneously, steam is passed into heating, makes temperature of liquid reach 87 DEG C, add additive, must not have suspended impurity, reach transparent till;
(7) gained mixture repressurization being shaped, moulding pressure is 20MPa, and pressing time is 6.5h, places 12h, obtain combined wall construction material after cooling.
Building wall paint provided by the invention, it has rupture strength and a high feature of comprcssive strength, and has effect of insulation, sound insulation, and its heat conductivity is low, good energy-conserving effect, and has good waterproof effect;The materials for wall material prepared is light, with low cost, and environmental protection, it is greatly saved the consumption of the energy and production cost, it is possible to be widely used in construction.
The above, it it is only presently preferred embodiments of the present invention, not the present invention is done any pro forma restriction, although the present invention is disclosed above with preferred embodiment, but it is not limited to the present invention, any those skilled in the art, without departing within the scope of technical solution of the present invention, when the technology contents of available the disclosure above makes a little change or is modified to the Equivalent embodiments of equivalent variations, in every case it is the content without departing from technical solution of the present invention, according to any simple modification that above example is made by the technical spirit of the present invention, equivalent variations and modification, all still fall within the scope of technical solution of the present invention.

Claims (8)

1. a lightweight, heat insulation, environment-friendly type combined wall construction material, it is characterised in that: include the component composition of following mass parts:
nullCellulose 5-10 part,Carbon fiber particles 10-15 part,Rubber grain 20-25 part,Plant granule 20-30 part,Ldpe resin 15-40 part,Modifying epoxy resin by organosilicon 5-8 part,Calcium carbonate 5-15 part,Magnesium oxide 0.5-2 part,Magnesium silicate 0.6-0.8 part,Magnesium calcium carbonate 10-15 part,Calcium pyroborate 5-8 part,Nano silicon oxide 5-10 part,Light ceramics 5-10 part,EVA re-dispersible glue powder 1.5-1.7 part,Pumex 15-35 part,Peat soil 3-5 part,Cement 20-55 part,Quick lime 8-12 part,Feldspar powder 5-10 part,Flyash 35-45 part,Poly-4-methyl-1-pentene 7-12 part,Polystyrolsulfon acid 5-9 part,Butyl rubber 7-11 part,Heat stabilizer 1-3 part,Waterproofing agent 0.3-0.8 part,Toughener 1-3 part,Foaming agent 0.1-1 part,Cross-linking agent 0.1-0.5 part,Silylation hydrophober 0.2-0.3 part、Wetting agent 2.3-2.5 part、Additive 1-2 part.
2. a kind of lightweight, heat insulation, environment-friendly type combined wall construction material according to claim 1, it is characterised in that: described plant granule be after the plant tissue such as wheat straw or corn stalk is pulverized particle diameter at the granule of 10-30mm.
3. a kind of lightweight, heat insulation, environment-friendly type combined wall construction material according to claim 1, it is characterised in that: described cellulose is that methylcellulose, hydroxypropyl methyl cellulose, hydroxyethyl cellulose are according to the 1-3:1-2:1-2 mixture formed.
4. a kind of lightweight, heat insulation, environment-friendly type combined wall construction material according to claim 1, it is characterised in that: described wetting agent is succinic acid dibutyl ester sodium sulfonate is 1:15 with its weight ratio of sodium alkyl sulfonate.
5. a kind of lightweight, heat insulation, environment-friendly type combined wall construction material according to claim 1, it is characterised in that: described additive be ethylene-vinyl acetate c emulsion with calcium carbonate according to the 2-3:1-2 mixture formed.
6. a kind of lightweight, heat insulation, environment-friendly type combined wall construction material according to claim 1, it is characterised in that: described heat stabilizer is zinc stearate.
7. a kind of lightweight, heat insulation, environment-friendly type combined wall construction material according to claim 1, it is characterised in that: described waterproofing agent is inorganic aluminate.
8. a kind of lightweight, heat insulation, environment-friendly type combined wall construction material according to claim 1, it is characterised in that: described toughener is EP rubbers, and foaming agent is carbon black, and cross-linking agent is cumyl peroxide.
CN201610148666.0A 2016-03-16 2016-03-16 Light-weight, heat-insulating and environment-friendly composite wall building material CN105801063A (en)