CN103496878B - High workability mortar king - Google Patents

High workability mortar king Download PDF

Info

Publication number
CN103496878B
CN103496878B CN201310383780.8A CN201310383780A CN103496878B CN 103496878 B CN103496878 B CN 103496878B CN 201310383780 A CN201310383780 A CN 201310383780A CN 103496878 B CN103496878 B CN 103496878B
Authority
CN
China
Prior art keywords
sodium
powder
mortar
dry
workability
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310383780.8A
Other languages
Chinese (zh)
Other versions
CN103496878A (en
Inventor
王传福
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhanjiang Qiaofeng building materials Co., Ltd
Original Assignee
王传福
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 王传福 filed Critical 王传福
Priority to CN201310383780.8A priority Critical patent/CN103496878B/en
Publication of CN103496878A publication Critical patent/CN103496878A/en
Application granted granted Critical
Publication of CN103496878B publication Critical patent/CN103496878B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a kind of high workability mortar king, be made up of the raw material of following weight part: fly ash in electric power plant 80-90, dry powder 10-20, modified talc powder 5-10, methylcellulose gum 2-3, polyoxyethylenated alcohol sodium sulfate 3-4, HS-2 moisturizing lubricant 1.5-2.5, sodium lauryl sulphate 2-3, sodium abietate 1-2.Mortar king of the present invention has excellent workability, mortar bonding strength can be significantly improved, thus raising block smears efficiency, reduce and land the use of ash, cement and lime putty, reduce construction cost, overcome the problems such as layering, hollowing, cracking, drop simultaneously, and there is good water-retentivity, frost resistance, impermeability and moistureproof and mildewproof performance, the cement products such as mortar, motar, sand-cement slurry, asbestos tile, hollow brick, thistle board of various industry, covil construction can be widely used in.

Description

High workability mortar king
Technical field
The present invention relates to a kind of high workability mortar king, belong to technical field of concrete additives.
Background technology
Mortar king is that one is commonly called as, and have people to be also its rock essence, cement fluidizer etc., it is that one acts in agglutinate (cement), in order to improve the material of sand-cement slurry performance, replaces the lime in concrete, reduces the cement consumption in mortar.Mortar king range of product is innumerable in the market, and quality is uneven especially, because its workability is poor, causes the phenomenons such as rendering layer layering, hollowing, cracking.
Summary of the invention
The object of the invention is to for the deficiencies in the prior art, provide a kind of high workability mortar king, it can improve mortar bonding power, overcomes the problems such as layering, hollowing, cracking, drop
The technical solution used in the present invention is as follows:
A kind of high workability mortar king, is made up of the raw material of following weight part: fly ash in electric power plant 80-90, dry powder 10-20, modified talc powder 5-10, methylcellulose gum 2-3, polyoxyethylenated alcohol sodium sulfate 3-4, HS-2 moisturizing lubricant 1.5-2.5, sodium lauryl sulphate 2-3, sodium abietate 1-2;
The preparation method of described modified talc powder is as follows: take talcum powder by weight 4-8:2-3:1-2:1, wilkinite, jade powder, boron mud mixes, add the trolamine of 1-2%, the sodium polyacrylate of 2-3%, the calcium lignin sulphonate of 1-2%, vinyl three ('beta '-methoxy oxyethyl group) silane of 0.5-1%, 2000-3000rpm speed lapping 10-15min, dry, pulverize, cross 400-500 mesh sieve, then add appropriate water making beating and make the slurries that concentration is 40-50%, add the Sodium dodecylbenzene sulfonate of 2-3%, the polyvinylpyrrolidone of 3-5%, the organosilicon crylic acid latex of 4-8%, the butyl of 0.5-1%, the Lauryl Alcohol ester of 1-2%, stir 1-2h, filter, dry, pulverize porphyrize, cross 300-400 mesh sieve.
Preferably, a kind of high workability mortar king, is made up of the raw material of following weight part: fly ash in electric power plant 80, dry powder 10, modified talc powder 10, methylcellulose gum 2, polyoxyethylenated alcohol sodium sulfate 3, HS-2 moisturizing lubricant 2, sodium lauryl sulphate 2.5, sodium abietate 1;
The preparation method of described modified talc powder is as follows: take talcum powder by weight 8:3:2:1, wilkinite, jade powder, boron mud mixes, add the trolamine of 2%, the sodium polyacrylate of 3%, the calcium lignin sulphonate of 2%, vinyl three ('beta '-methoxy oxyethyl group) silane of 1%, 3000rpm speed lapping 15min, dry, pulverize, cross 400 mesh sieves, then add appropriate water making beating and make the slurries that concentration is 40%, add the Sodium dodecylbenzene sulfonate of 3%, the polyvinylpyrrolidone of 4%, the organosilicon crylic acid latex of 8%, the butyl of 1%, the Lauryl Alcohol ester of 2%, stir 2h, filter, dry, pulverize porphyrize, cross 300 mesh sieves.
Preparation method: above-mentioned raw materials is added horizontal mixer and stir 20-40 minute, packing, gets product.
During use, according to the mixing mortar of the ratio 0.3-0.5% of cement weight.
Beneficial effect of the present invention:
Mortar king of the present invention has excellent workability, mortar bonding strength can be significantly improved, thus raising block smears efficiency, reduce and land the use of ash, cement and lime putty, reduce construction cost, overcome the problems such as layering, hollowing, cracking, drop simultaneously, and there is good water-retentivity, frost resistance, impermeability and moistureproof and mildewproof performance, the cement products such as mortar, motar, sand-cement slurry, asbestos tile, hollow brick, thistle board of various industry, covil construction can be widely used in.
Embodiment
A kind of high workability mortar king, is made up of the raw material of following weight (kg): fly ash in electric power plant 80, dry powder 10, modified talc powder 10, methylcellulose gum 2, polyoxyethylenated alcohol sodium sulfate 3, HS-2 moisturizing lubricant 2, sodium lauryl sulphate 2.5, sodium abietate 1;
The preparation method of described modified talc powder is as follows: take talcum powder by weight 8:3:2:1, wilkinite, jade powder, boron mud mixes, add the trolamine of 2%, the sodium polyacrylate of 3%, the calcium lignin sulphonate of 2%, vinyl three ('beta '-methoxy oxyethyl group) silane of 1%, 3000rpm speed lapping 15min, dry, pulverize, cross 400 mesh sieves, then add appropriate water making beating and make the slurries that concentration is 40%, add the Sodium dodecylbenzene sulfonate of 3%, the polyvinylpyrrolidone of 4%, the organosilicon crylic acid latex of 8%, the butyl of 1%, the Lauryl Alcohol ester of 2%, stir 2h, filter, dry, pulverize porphyrize, cross 300 mesh sieves.
Preparation method: above-mentioned raw materials is added horizontal mixer and stir 30 minutes, packing, get product.
During use, according to the mixing mortar of the ratio 0.4% of cement weight.
Mortar king salient features of the present invention is as follows:
Density (kg/ cube) >=1800;
Compressive strength rate (%) 7d:105,28d:121;
Delamination degree (mm)≤30;
Time of coagulation poor (min)-60 ~+90;
Shrinkage ratio (%)≤5;
Anti-freezing property circulates 15 times: mass loss rate (%)≤5, loss of strength rate (%)≤10.

Claims (2)

1. a high workability mortar king, it is characterized in that, be made up of the raw material of following weight part: fly ash in electric power plant 80-90, dry powder 10-20, modified talc powder 5-10, methylcellulose gum 2-3, polyoxyethylenated alcohol sodium sulfate 3-4, HS-2 moisturizing lubricant 1.5-2.5, sodium lauryl sulphate 2-3, sodium abietate 1-2;
The preparation method of described modified talc powder is as follows: take talcum powder by weight 4-8:2-3:1-2:1, wilkinite, jade powder, boron mud mixes, add the trolamine of 1-2%, the sodium polyacrylate of 2-3%, the calcium lignin sulphonate of 1-2%, vinyl three ('beta '-methoxy oxyethyl group) silane of 0.5-1%, 2000-3000rpm speed lapping 10-15min, dry, pulverize, cross 400-500 mesh sieve, then add appropriate water making beating and make the slurries that concentration is 40-50%, add the Sodium dodecylbenzene sulfonate of 2-3%, the polyvinylpyrrolidone of 3-5%, the organosilicon crylic acid latex of 4-8%, the butyl of 0.5-1%, the Lauryl Alcohol ester of 1-2%, stir 1-2h, filter, dry, pulverize porphyrize, cross 300-400 mesh sieve.
2. a kind of high workability mortar king according to claim 1, it is characterized in that, be made up of the raw material of following weight part: fly ash in electric power plant 80, dry powder 10, modified talc powder 10, methylcellulose gum 2, polyoxyethylenated alcohol sodium sulfate 3, HS-2 moisturizing lubricant 2, sodium lauryl sulphate 2.5, sodium abietate 1;
The preparation method of described modified talc powder is as follows: take talcum powder by weight 8:3:2:1, wilkinite, jade powder, boron mud mixes, add the trolamine of 2%, the sodium polyacrylate of 3%, the calcium lignin sulphonate of 2%, vinyl three ('beta '-methoxy oxyethyl group) silane of 1%, 3000rpm speed lapping 15min, dry, pulverize, cross 400 mesh sieves, then add appropriate water making beating and make the slurries that concentration is 40%, add the Sodium dodecylbenzene sulfonate of 3%, the polyvinylpyrrolidone of 4%, the organosilicon crylic acid latex of 8%, the butyl of 1%, the Lauryl Alcohol ester of 2%, stir 2h, filter, dry, pulverize porphyrize, cross 300 mesh sieves.
CN201310383780.8A 2013-08-29 2013-08-29 High workability mortar king Active CN103496878B (en)