CN101913780A - 具有双层减反射涂层的太阳能电池组件封装玻璃 - Google Patents

具有双层减反射涂层的太阳能电池组件封装玻璃 Download PDF

Info

Publication number
CN101913780A
CN101913780A CN 201010242347 CN201010242347A CN101913780A CN 101913780 A CN101913780 A CN 101913780A CN 201010242347 CN201010242347 CN 201010242347 CN 201010242347 A CN201010242347 A CN 201010242347A CN 101913780 A CN101913780 A CN 101913780A
Authority
CN
China
Prior art keywords
solar cell
antireflection coatings
double
dereflection
cell component
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201010242347
Other languages
English (en)
Inventor
林金锡
林书铨
唐敦乙
王国祥
丁怀欣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGZHOU ALMADEN STOCK Co Ltd
Original Assignee
CHANGZHOU ALMADEN STOCK Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGZHOU ALMADEN STOCK Co Ltd filed Critical CHANGZHOU ALMADEN STOCK Co Ltd
Priority to CN 201010242347 priority Critical patent/CN101913780A/zh
Publication of CN101913780A publication Critical patent/CN101913780A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种太阳能电池，特别涉及一种具有双层减反射涂层的太阳能电池组件封装玻璃，用于太阳能电池组件的制造。本发明是具有双层减反射涂层的太阳能电池组件封装玻璃包括压花超白玻璃基板(1)，还包括有设置在压花超白玻璃基板(1)上面的第一减反射涂层(2)，在第一减反射涂层(2)上面还设置有第二减反射涂层(3)。本发明好处是：(1)透光率和功率增加量更高。在双层减反射涂层共同作用下，本发明透光性达到95％以上，用本发明封装出来的太阳能电池组件其功率增加量达到2.5％以上，最高可增加到3.5％，具有更高的功率增加量，本发明极大地提高了太阳能电池组件光电转换效率；(2)性价比高，使用成本降低。

Description

具有双层减反射涂层的太阳能电池组件封装玻璃
技术领域
本发明涉及一种太阳能电池，特别涉及一种具有双层减反射涂层的太阳能电池组件封装玻璃，用于太阳能电池组件的制造。
背景技术
太阳能电池目前已得到了广泛的应用，做为一种绿色、环保的清洁新能源，太阳能电池具有广阔的发展空间。公知的晶体硅太阳能电池组件的光电转换效率主要由太阳能电池组件中的晶体硅太阳能电池片的效率来决定。随着人们对电池片制作技术的不断改进，电池片的光电转换效率也在不断提高，电池片的光电转化效率目前已达到了较高的值，在现有技术的基础上将电池片的效率再提高已非常困难。提高太阳能电池组件的另外一个方法是增加照射到电池片上的光的强度，而太阳能电池封装时都必须要用到一块盖板玻璃，在电池片组件上面盖上盖板玻璃，当阳光入射时一定会阻挡入射的太阳光，使得入射进来的光线在盖板玻璃的上下表面被反射和被玻璃吸收，通过提高玻璃盖板的性能来提高太阳光能的有效利用率是一个很好的办法。目前性能较好的、也是普遍采用的盖板玻璃是超白压花玻璃，超白压花玻璃一面是光滑平面，一面是压花面，在太阳能电池组件封装时，将超白压花玻璃的光滑平面一面朝外，即朝向太阳一侧，将压花层一面朝里，即朝向太阳能电池片一侧的，这种超白压花玻璃的含铁量低，压花层上的花纹形状有多种形状，折射性较普通超白玻璃要好，但超白压花玻璃的透过率也不会超过91.5％，致使8.5％左右的阳光仍未得到利用，这8.5％左右的阳光也是非常巨大的能源，这造成太阳能的利用率的降低，使用成本增加。要提高阳光的透过率的方法很多，可以通过改变组成玻璃的成份来减少对阳光的吸收，还可以在盖板玻璃上涂覆单层膜，来减少光线的反射量。目前在玻璃表面涂覆单层膜来增加透过率的方法被普遍使用，在压花超白玻璃基板上面设置一层反射涂层，这层反射涂层设置在压花超白玻璃基板的非压花面上，但是这种涂覆单层减反射膜层的玻璃的透过率一般低于94％，再想提高已非常困难，而且在使用具有涂覆单层减反射膜层的盖板玻璃后封装出来的太阳能组件的功率增加量一般在1.5％～1.8％。若涂层的质量不高，则功率增加量只有百分之零点几，甚至增加量为零。这些加了单层减反射膜层的盖板玻璃，透光性还不是很理想。因而，要想更大地提高太阳能电池组件封装玻璃的透光率一直是一个技术难题。
发明内容
本发明的目的是针对现有技术的不足，提供一种透光性更高、能使太阳能组件的功率增加量更高、使用成本低的具有双层减反射涂层的太阳能电池组件封装玻璃。
实现上述目的的技术方案是：一种具有双层减反射涂层的太阳能电池组件封装玻璃，包括压花超白玻璃基板，还包括有设置在压花超白玻璃基板上面的第一减反射涂层，在第一减反射涂层上面还设置有第二减反射涂层。
进一步，所述的第二减反射涂层材料为纳米二氧化硅。
进一步，所述的第二减反射涂层厚度为50nm～200nm。
进一步，所述的第一减反射涂层材料为纳米二氧化钛、纳米二氧化锆或纳米三氧化二铝中的任意一种。
进一步，所述的第一减反射涂层的厚度为20nm～150nm。
采用本发明的技术方案，具有以下优点：(1)透光率和功率增加量更高。本发明在现有的压花超白玻璃基板上面的第一减反射涂层上面还设置有第二减反射涂层。本发明具有双层反射涂层，在本发明双层减反射涂层的共同作用下，本发明的透光率大大增加，透光性更高，达到95％以上，用本发明的盖板玻璃封装出来的太阳能电池组件其功率增加量达到2.5％以上，最高可增加到3.5％，具有更高的功率增加量，本发明极大地提高了太阳能电池组件的光电转换效率。本发明在大规模生产的条件下，透光率和功率增加量会更高；(2)性价比高，使用成本低。本发明由于具有双层反射涂层，制作成本增加的不多，但使本发明的性能大大提高，因而性价比高，使用成本大大降低。
附图说明
附图为本发明的结构示意图。
具体实施方式
下面通过实施例对本发明作进一步详细的说明。
实施例一
如附图所示，一种具有双层减反射涂层的太阳能电池组件封装玻璃，包括压花超白玻璃基板1，还包括有涂覆在压花超白玻璃基板1上面的第一减反射涂层2，压花超白玻璃基板1的a面是压花面，b面是非压花面，第一减反射涂层2设置在压花超白玻璃基板1的非压花面上，在第一减反射涂层2上面还涂覆设置有第二减反射涂层3。第一减反射涂层2材料为纳米级的二氧化钛，第一减反射涂层2的厚度为20nm。第二减反射涂层3材料为纳米级的二氧化硅，第二减反射涂层3厚度为120nm。
实施例二
如附图所示，一种具有双层减反射涂层的太阳能电池组件封装玻璃，包括压花超白玻璃基板1，还包括有涂覆在压花超白玻璃基板1上面的第一减反射涂层2，压花超白玻璃基板1的a面是压花面，b面是非压花面，第一减反射涂层2设置在压花超白玻璃基板1的非压花面上，在第一减反射涂层2上面还涂覆设置有第二减反射涂层3。第一减反射涂层2材料为纳米级的二氧化锆，第一减反射涂层2的厚度为65nm。第二减反射涂层3材料为纳米级的二氧化硅，第二减反射涂层3厚度为95nm。
实施例三
如附图所示，一种具有双层减反射涂层的太阳能电池组件封装玻璃，包括压花超白玻璃基板1，还包括有涂覆在压花超白玻璃基板1上面的第一减反射涂层2，压花超白玻璃基板1的a面是压花面，b面是非压花面，第一减反射涂层2设置在压花超白玻璃基板1的非压花面上，在第一减反射涂层2上面还涂覆设置有第二减反射涂层3。第一减反射涂层2材料为纳米级的三氧化二铝，第一减反射涂层2的厚度为70nm。第二减反射涂层3材料为纳米级的二氧化硅，第二减反射涂层3厚度为50nm。
实施例四
如附图所示，本实施例与实施例一基本相同，不同的是第一减反射涂层2的厚度为100nm，第二减反射涂层3厚度为150nm。
实施例五
如附图所示，本实施例与实施例二基本相同，不同的是第一减反射涂层2的厚度为120nm，第二减反射涂层3厚度为185nm。
实施例六
如附图所示，本实施例与实施例三基本相同，不同的是第一减反射涂层2的厚度为150nm，第二减反射涂层3厚度为200nm。
本发明制作时，在压花超白玻璃基板1的非压花面上先涂覆第一减反射涂层2，然后在反射涂层2上面涂覆上第二减反射涂层3。第一减反射涂层2和第二减反射涂层3涂覆时按要求的厚度和材料涂覆。
除上述实施例外，第一减反射涂层2材料还可以选择二氧化钛、二氧化锆或三氧化二铝中的任意两种或三种的混合物，第一减反射涂层2和第二减反射涂层3根据所选材料性能对二者的涂层厚度做相应的调整即可。
本发明的实施例很多，无法穷举，凡采用等同替换或等效替换形成的技术方案均属于发明要求保护的范围。

Claims (5)

1.一种具有双层减反射涂层的太阳能电池组件封装玻璃，包括压花超白玻璃基板(1)，还包括有设置在压花超白玻璃基板(1)上面的第一减反射涂层(2)，其特征在于：在第一减反射涂层(2)上面还设置有第二减反射涂层(3)。
2.根据权利要求1所述的具有双层减反射涂层的太阳能电池组件封装玻璃，其特征在于：所述的第二减反射涂层(3)材料为纳米二氧化硅。
3.根据权利要求1所述的具有双层减反射涂层的太阳能电池组件封装玻璃，其特征在于：所述的第二减反射涂层(3)厚度为50nm～200nm。
4.根据权利要求1所述的具有双层减反射涂层的太阳能电池组件封装玻璃，其特征在于：所述的第一减反射涂层(2)材料为纳米二氧化钛、纳米二氧化锆或纳米三氧化二铝中的任意一种。
5.根据权利要求1所述的具有双层减反射涂层的太阳能电池组件封装玻璃，其特征在于：所述的第一减反射涂层(2)的厚度为20nm～150nm。
CN 201010242347 2010-08-02 2010-08-02 具有双层减反射涂层的太阳能电池组件封装玻璃 Pending CN101913780A (zh)