CN101906860B - Aluminum silver wall decoration material and manufacturing process thereof - Google Patents
Aluminum silver wall decoration material and manufacturing process thereof Download PDFInfo
- Publication number
- CN101906860B CN101906860B CN2010102216534A CN201010221653A CN101906860B CN 101906860 B CN101906860 B CN 101906860B CN 2010102216534 A CN2010102216534 A CN 2010102216534A CN 201010221653 A CN201010221653 A CN 201010221653A CN 101906860 B CN101906860 B CN 101906860B
- Authority
- CN
- China
- Prior art keywords
- component
- diluent
- polyaniline
- mixture
- coating mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses an aluminum silver wall decorative material comprising a metal substrate. Three layers of paint are sprayed on the surface of the metal substrate. The method for manufacturing the aluminum silver wall decorative material comprises the following steps: (1) substrate making: processing steel plates into a decorative plate according to the requirement; and (2) paint spraying: firstly spraying priming paint on the surface of the substrate, then spraying middle paint on the priming paint and finally spraying finish paint on the middle paint. The invention has the characteristics that the aluminum silver wall decorative plate has long service time, low production cost, good processing performance and no pollution to the environment.
Description
Technical field
The present invention relates to a kind of curtain wall decoration material and manufacture craft, specifically a kind of aluminum silver wall decoration material and manufacturing process thereof.
Background technology
Existing structure curtain wall decoration material has glass curtain wall, and aluminum facade etc., but the reflective severity of glass curtain wall produce light pollution to environment, and the aluminum facade production cost is high.
Also have proposition to make curtain wall with iron plate, but how the antirust problem of iron plate solving, is crucial.If plating mode is passed through in the protection on iron plate surface; Comprise zinc-plated, chromium plating, cadmium plating etc.; Electroplating technology not only needs a large amount of strong acid, highly basic, heavy metal solution and harmful chemicals, and they can produce environmental pollution and human health is constituted harm in production procedure.
Summary of the invention
The objective of the invention is to develop a kind of aluminum silver wall decoration material and manufacturing process thereof.
What the present invention will solve is that existing a kind of curtain wall decoration plate pollutes heavy and the high problem of production cost.
Aluminum silver wall decoration material of the present invention; Comprise metal substrate; Be coated with three layers of paint on the surface of this metal substrate, be followed successively by priming paint, middle japanning and finish paint from inside to outside, it is characterized in that at described priming paint be the aluminum paste anti-corrosion primer; Middle japanning is for containing the bi-component thick-slurry type anticorrosive polyaniline lacquer of epoxy resin, fluorocarbon resin, aluminium paste, and finish paint is the fluorine-carbon-aluminum powder finish paint.Metal substrate is that thickness is the 0.5-1.5mm steel plate.
The manufacturing process of aluminum silver wall decoration material of the present invention is characterized in that this technology comprises: 1) substrate manufacture, be processed into decorative panel to steel plate on request;
2) paint spraying, spraying priming paint at first on the surface of substrate, japanning in the spraying on priming paint then, at last in be coated with and paint spray paint;
The spraying of described priming paint comprises: A component and B component stir well spare after, mix with 10: 1 part by weight, static again slaking 30 minutes adds proper amount of diluting then, sprays after transferring to working viscosity;
Japanning spraying comprises in described: C component and B component stir well spare after, mix with 8: 1 part by weight, static again slaking 30 minutes adds proper amount of diluting then, sprays after transferring to working viscosity;
The spraying of described finish paint comprises: D component and B component stir well spare after, mix with 15: 1 part by weight, static again slaking 30 minutes adds proper amount of diluting then, sprays after transferring to working viscosity;
Described C component prepares as follows: by weight percentage, get the epoxy resin of 20-40%, the fluorocarbon resin of 10-20%; The color stuffing of 40-70%, all the other are diluent, mix after each coating mixture; After adding the diluent grinding again, use ultrasonic Treatment, get the C component at last;
Described epoxy resin is a kind of in epoxide modified thermoplasticity acrylic acid resin, the epoxide modified acrylic acid resin;
The diluent consumption that adds is: in weight portion, and the diluent that adds 0.4-0.6 part in 1 part of coating mixture; The diluent that is added is a kind of in own fat, fourth fat or the xylenes;
Color stuffing is selected polyaniline and aluminum paste mixture for use, or selects the mixture of polyaniline, aluminum paste and metal dust for use, or selects the mixture of polyaniline, aluminum paste and lead-free pigment for use;
Described D component prepares as follows: by weight percentage, get the fluorocarbon resin of 30-60%, the color stuffing of 40-70%, after the mixing coating mixture, add again after diluent grinds, use ultrasonic Treatment, at last must the D component;
The diluent consumption that adds is: in weight portion, and the diluent that adds 0.4-0.6 part in 1 part of coating mixture; The diluent that is added is a kind of in own fat, fourth fat or the xylenes;
Advantage of the present invention is: the aluminum silver wall decorative panel that the present invention produces is long service time, and production cost is low, and good processability can not pollute environment..
Description of drawings
Fig. 1 is the structural representation of metal substrate of the present invention.
The specific embodiment
Below in conjunction with accompanying drawing and embodiment the present invention is done further explanation.
Aluminum silver wall decoration material of the present invention comprises metal substrate 1.The surface of metal substrate 1 comprises the outer surface and the inner surface of substrate.Outer surface sprays priming paint 4, middle japanning 3 and finish paint 2 from inside to outside successively.Inner surface sprays priming paint 5, middle japanning 6 and finish paint 7 from inside to outside successively.At described priming paint is the aluminum paste anti-corrosion primer, and middle japanning is to contain the bi-component thick-slurry type anticorrosive polyaniline of epoxy resin, fluorocarbon resin, aluminium paste lacquer, and finish paint is the fluorine-carbon-aluminum powder finish paint.Metal substrate is that thickness is the 0.5-1.0mm steel plate.
The manufacturing process of aluminum silver wall decoration material of the present invention is characterized in that this technology comprises: 1) substrate manufacture, be processed into decorative panel to steel plate on request;
2) paint spraying, spraying priming paint at first on the surface of substrate, japanning in the spraying on priming paint then, at last in be coated with and paint spray paint;
The spraying of described priming paint comprises: A component and B component stir well spare after, mix with 10: 1 part by weight, static again slaking 30 minutes adds proper amount of diluting then, sprays after transferring to working viscosity;
Japanning spraying comprises in described: C component and B component stir well spare after, mix with 8: 1 part by weight, static again slaking 30 minutes adds proper amount of diluting then, sprays after transferring to working viscosity;
The spraying of described finish paint comprises: D component and B component stir well spare after, mix with 15: 1 part by weight, static again slaking 30 minutes adds proper amount of diluting then, sprays after transferring to working viscosity;
Described A component prepares as follows: by weight percentage, get the epoxy resin of 30-60%, the color stuffing of 40-70%, after the mixing coating mixture, add again after diluent grinds, use ultrasonic Treatment, at last must the A component;
Described epoxy resin is a kind of in epoxide modified thermoplasticity acrylic acid resin, the epoxide modified acrylic acid resin;
The diluent consumption that adds is: in weight portion, and the diluent that adds 0.4-0.6 part in 1 part of coating mixture; The diluent that is added is a kind of in own fat, fourth fat or the xylenes;
Described B component is general curing agent, and the B component comprises the N3390 or the N75 curing agent of Bayer, and described N75 curing agent is to be the aliphatic polymeric isocyanate of base-material with hexamethylene diisocyanate (HDI).
Described color stuffing is selected polyaniline and aluminum paste mixture for use, or selects the mixture of polyaniline, aluminum paste and metal dust for use, or selects the mixture of polyaniline, aluminum paste and lead-free pigment for use.
In the described coating mixture, color stuffing is selected polyaniline and aluminum paste mixture for use, and wherein the aluminum paste consumption accounts for the 10-30% of coating mixture, and the polyaniline consumption accounts for the 5-10% of coating mixture, and all the other are diluent.
In the described coating mixture; Color stuffing is selected polyaniline, aluminum paste and metal powder mixture for use, and wherein the aluminum paste consumption accounts for the 10-30% of coating mixture, and the polyaniline consumption accounts for the 8-10% of coating mixture; The metal dust consumption accounts for coating mixture less than 10%, and all the other are diluent.
Described grinding is meant and is dissolved in color stuffing among the TMDA, is cured back and epoxy resin mixed grinding.
Described C component prepares as follows: by weight percentage, get the epoxy resin of 20-40%, the fluorocarbon resin of 10-20%; The color stuffing of 30-40%, xylenes 10-30%, mix after each coating mixture; After adding the diluent grinding again, use ultrasonic Treatment, get the C component at last;
Described epoxy resin is a kind of in epoxide modified thermoplasticity acrylic acid resin, the epoxide modified acrylic acid resin;
The diluent consumption that adds is: in weight portion, and the diluent that adds 0.4-0.6 part in 1 part of coating mixture; The diluent that is added is a kind of in own fat, fourth fat or the xylenes;
Color stuffing is selected polyaniline and aluminum paste mixture for use, or selects the mixture of polyaniline, aluminum paste and metal dust for use, or selects the mixture of polyaniline, aluminum paste and lead-free pigment for use;
Select polyaniline and aluminum paste mixture for use like color stuffing, wherein the aluminum paste consumption accounts for the 10-30% of coating mixture, and the polyaniline consumption accounts for the 8-10% of coating mixture; All the other are diluent.
Select polyaniline, aluminum paste and metal powder mixture for use like color stuffing, wherein the aluminum paste consumption accounts for the 10-30% of coating mixture, and the polyaniline consumption accounts for the 5-10% of coating mixture, and the metal dust consumption accounts for coating mixture less than 30%.
Described D component prepares as follows: by weight percentage, the fluorocarbon resin of 30-60%, the color stuffing of 30-40%, all the other are diluent.After the mixing coating mixture, add again after diluent grinds, use ultrasonic Treatment, at last must the D component;
The diluent consumption that adds is: in weight portion, and the diluent that adds 0.4-0.6 part in 1 part of coating mixture; The diluent that is added is a kind of in own fat, fourth fat or the xylenes.
Claims (9)
1. aluminum silver wall decoration material; Comprise metal substrate; Be coated with three layers of paint on the surface of this metal substrate, be followed successively by priming paint, middle japanning and finish paint from inside to outside, it is characterized in that at described priming paint be the aluminum paste anti-corrosion primer; Middle japanning is for containing the bi-component thick-slurry type anticorrosive polyaniline lacquer of epoxy resin, fluorocarbon resin, aluminium paste, and finish paint is the fluorine-carbon-aluminum powder finish paint.
2. aluminum silver wall decoration material according to claim 1 is characterized in that metal substrate is that thickness is the 0.5-1.5mm steel plate.
3. the manufacturing process of aluminum silver wall decoration material according to claim 1 is characterized in that this technology comprises: 1) substrate manufacture, be processed into decorative panel to steel plate on request; 2) paint spraying, spraying priming paint at first on the surface of substrate, japanning in the spraying on priming paint then, at last in be coated with and paint spray paint;
The spraying of described priming paint comprises: A component and B component stir well spare after, mix with 10: 1 part by weight, static again slaking 30 minutes adds proper amount of diluting then, sprays after transferring to working viscosity;
Japanning spraying comprises in described: C component and B component stir well spare after, mix with 8: 1 part by weight, static again slaking 30 minutes adds proper amount of diluting then, sprays after transferring to working viscosity;
The spraying of described finish paint comprises: D component and B component stir well spare after, mix with 15: 1 part by weight, static again slaking 30 minutes adds proper amount of diluting then, sprays after transferring to working viscosity;
Described A component prepares as follows: by weight percentage, get the epoxy resin of 30-60%, the color stuffing of 30-40%, all the other are diluent, after the mixing coating mixture, add again after diluent grinds, use ultrasonic Treatment, at last must the A component;
Described B component is general curing agent;
Described C component prepares as follows: by weight percentage, get the epoxy resin of 20-40%, the fluorocarbon resin of 10-20%; The color stuffing of 30-40%, all the other are diluent, get coating mixture after the mixing; After adding the diluent grinding again, use ultrasonic Treatment, get the C component at last;
Described D component prepares as follows: by weight percentage, get the fluorocarbon resin of 30-60%, the color stuffing of 30-40%, all the other are diluent, after the mixing coating mixture, add again after diluent grinds, use ultrasonic Treatment, at last must the D component.
4. the manufacturing process of aluminum silver wall decoration material according to claim 3 is characterized in that the epoxy resin described in the described A component is a kind of in epoxide modified thermoplasticity acrylic acid resin, the epoxide modified acrylic acid resin;
The diluent consumption that adds in the A component is: in weight portion, add the diluent of 0.4-0.6 part in 1 part of coating mixture; The diluent that is added is a kind of in own fat, fourth fat or the xylenes;
Described B component comprises the N3390 or the N75 curing agent of Bayer, and described N75 curing agent is to be the aliphatic polymeric isocyanate of base-material with the hexamethylene diisocyanate.
5. the manufacturing process of aluminum silver wall decoration material according to claim 4; It is characterized in that color stuffing is selected polyaniline and aluminum paste mixture for use in the described A component; Or select the mixture of polyaniline, aluminum paste and metal dust for use, or select the mixture of polyaniline, aluminum paste and lead-free pigment for use.
6. the manufacturing process of aluminum silver wall decoration material according to claim 4; It is characterized in that in the coating mixture in the described A component; Color stuffing is selected polyaniline and aluminum paste mixture for use; Wherein the aluminum paste consumption accounts for the 10-30% of coating mixture, and the polyaniline consumption accounts for the 8-10% of coating mixture, and all the other are diluent.
7. the manufacturing process of aluminum silver wall decoration material according to claim 4; It is characterized in that in the described A component in the coating mixture; Color stuffing is selected polyaniline, aluminum paste and metal powder mixture for use; Wherein the aluminum paste consumption accounts for the 20-30% of coating mixture, and the polyaniline consumption accounts for the 5-10% of coating mixture, and the metal dust consumption accounts for coating mixture less than 30%.
8. the manufacturing process of aluminum silver wall decoration material according to claim 3 is characterized in that the epoxy resin described in the described C component is a kind of in epoxide modified thermoplasticity acrylic acid resin, the epoxide modified acrylic acid resin;
The diluent consumption that adds in the C component is: in weight portion, add the diluent of 0.4-0.6 part in 1 part of coating mixture; The diluent that is added is a kind of in own fat, fourth fat or the xylenes;
Color stuffing is selected polyaniline and aluminum paste mixture for use in the C component, or selects the mixture of polyaniline, aluminum paste and metal dust for use, or selects the mixture of polyaniline, aluminum paste and lead-free pigment for use;
Select polyaniline and aluminum paste mixture for use like color stuffing, wherein the aluminum paste consumption accounts for the 10-30% of coating mixture, and the polyaniline consumption accounts for the 8-10% of coating mixture, and all the other are diluent;
Select polyaniline, aluminum paste and metal powder mixture for use like color stuffing, wherein the aluminum paste consumption accounts for the 20-30% of coating mixture, and the polyaniline consumption accounts for the 5-10% of coating mixture, and the metal dust consumption accounts for coating mixture less than 30%.
9. the manufacturing process of aluminum silver wall decoration material according to claim 3 is characterized in that the diluent consumption that adds in the described D component is: in weight portion, and the diluent that adds 0.4-0.6 part in 1 part of coating mixture; The diluent that is added is a kind of in own fat, fourth fat or the xylenes.