- thinner
- polyaniline
- mixture
- coating mixture
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Links
Images
Landscapes
- Paints Or Removers (AREA)
- Application Of Or Painting With Fluid Materials (AREA)
Abstract
The invention discloses an aluminum silver wall decorative material comprising a metal substrate. Three layers of paint are sprayed on the surface of the metal substrate. The method for manufacturing the aluminum silver wall decorative material comprises the following steps: (1) substrate making: processing steel plates into a decorative plate according to the requirement; and (2) paint spraying: firstly spraying priming paint on the surface of the substrate, then spraying middle paint on the priming paint and finally spraying finish paint on the middle paint. The invention has the characteristics that the aluminum silver wall decorative plate has long service time, low production cost, good processing performance and no pollution to the environment.
Description
Technical field
The present invention relates to a kind of curtain wall decoration material and manufacture craft, specifically a kind of aluminum silver wall decoration material and manufacturing process thereof.
Background technology
Existing building curtain wall decoration material has curtain wall, and aluminum facade etc., but the reflective severity of curtain wall produce light pollution, aluminum facade cost of production height to environment.
Also have proposition to make curtain wall with iron plate, but how the antirust problem of iron plate solving, is crucial.If plating mode is passed through in the protection on iron plate surface; comprise zinc-plated, chromium plating, cadmium plating etc.; electroplating technology not only needs a large amount of strong acid, highly basic, heavy metal solution and harmful chemicals, and they can produce environment pollution and human health is constituted harm in production procedure.
Summary of the invention
The objective of the invention is to develop a kind of aluminum silver wall decoration material and manufacturing process thereof.
What the present invention will solve is that existing a kind of curtain wall decoration plate pollutes heavy and the high problem of cost of production.
Aluminum silver wall decoration material of the present invention, comprise metal substrate, be coated with three layers of paint on the surface of this metal substrate, be followed successively by priming paint, middle japanning and finish paint from inside to outside, it is characterized in that at described priming paint be the aluminum paste anti-corrosion primer, middle japanning is for containing the bi-component thick-slurry type anticorrosive polyaniline lacquer of epoxy resin, fluorocarbon resin, aluminium paste, and finish paint is the fluorine-carbon-aluminum powder finish paint.Metal substrate is that thickness is the 0.5-1.5mm steel plate.
The manufacturing process of aluminum silver wall decoration material of the present invention is characterized in that this technology comprises: 1) substrate manufacture, be processed into decorative panel on request to steel plate;
2) paint spraying, at first at the surface of substrate spraying priming paint, japanning in the spraying on priming paint then, at last in be coated with and paint spray paint;
The spraying of described priming paint comprises: A component and B component stir well even after, mix with 10: 1 part by weight, static again slaking 30 minutes adds proper amount of diluting then, sprays after transferring to working viscosity;
Japanning spraying comprises in described: C component and B component stir well even after, mix with 8: 1 part by weight, static again slaking 30 minutes adds proper amount of diluting then, sprays after transferring to working viscosity;
The spraying of described finish paint comprises: D component and B component stir well even after, mix with 15: 1 part by weight, static again slaking 30 minutes adds proper amount of diluting then, sprays after transferring to working viscosity;
Described C component prepares as follows: by weight percentage, get the epoxy resin of 20-40%, the fluorocarbon resin of 10-20%, the color stuffing of 40-70%, all the other are thinner, mix after each coating mixture, after adding the thinner grinding again, handle, get the C component at last with ultrasonic wave;
Described epoxy resin is a kind of in epoxide modified thermoplasticity acrylic acid resin, the epoxide modified acrylic acid resin;
The thinner consumption that adds is: in weight portion, and the thinner that adds 0.4-0.6 part in 1 part of coating mixture; The thinner that is added is a kind of in own fat, fourth fat or the dimethylbenzene;
Color stuffing is selected polyaniline and aluminum paste mixture for use, or selects the mixture of polyaniline, aluminum paste and metal dust for use, or selects the mixture of polyaniline, aluminum paste and lead-free pigment for use;
Described D component prepares as follows: by weight percentage, get the fluorocarbon resin of 30-60%, the color stuffing of 40-70%, after the mixing coating mixture, add again after thinner grinds, handle with ultrasonic wave, at last the D component;
The thinner consumption that adds is: in weight portion, and the thinner that adds 0.4-0.6 part in 1 part of coating mixture; The thinner that is added is a kind of in own fat, fourth fat or the dimethylbenzene;
Advantage of the present invention is: the aluminum silver wall decorative panel that the present invention produces is long service time, and cost of production is low, and good processability can not pollute environment..
Description of drawings
Fig. 1 is the structural representation of metal substrate of the present invention.
The specific embodiment
The present invention is described further below in conjunction with drawings and Examples.
Aluminum silver wall decoration material of the present invention comprises metal substrate 1.The surface of metal substrate 1 comprises the external surface and the inner surface of substrate.External surface sprays priming paint 4, middle japanning 3 and finish paint 2 from inside to outside successively.Inner surface sprays priming paint 5, middle japanning 6 and finish paint 7 from inside to outside successively.At described priming paint is the aluminum paste anti-corrosion primer, and middle japanning is to contain the bi-component thick-slurry type anticorrosive polyaniline of epoxy resin, fluorocarbon resin, aluminium paste lacquer, and finish paint is the fluorine-carbon-aluminum powder finish paint.Metal substrate is that thickness is the 0.5-1.0mm steel plate.
The manufacturing process of aluminum silver wall decoration material of the present invention is characterized in that this technology comprises: 1) substrate manufacture, be processed into decorative panel on request to steel plate;
2) paint spraying, at first at the surface of substrate spraying priming paint, japanning in the spraying on priming paint then, at last in be coated with and paint spray paint;
The spraying of described priming paint comprises: A component and B component stir well even after, mix with 10: 1 part by weight, static again slaking 30 minutes adds proper amount of diluting then, sprays after transferring to working viscosity;
Japanning spraying comprises in described: C component and B component stir well even after, mix with 8: 1 part by weight, static again slaking 30 minutes adds proper amount of diluting then, sprays after transferring to working viscosity;
The spraying of described finish paint comprises: D component and B component stir well even after, mix with 15: 1 part by weight, static again slaking 30 minutes adds proper amount of diluting then, sprays after transferring to working viscosity;
Described A component prepares as follows: by weight percentage, get the epoxy resin of 30-60%, the color stuffing of 40-70%, after the mixing coating mixture, add again after thinner grinds, handle with ultrasonic wave, at last the A component;
Described epoxy resin is a kind of in epoxide modified thermoplasticity acrylic acid resin, the epoxide modified acrylic acid resin;
The thinner consumption that adds is: in weight portion, and the thinner that adds 0.4-0.6 part in 1 part of coating mixture; The thinner that is added is a kind of in own fat, fourth fat or the dimethylbenzene;
Described B component is general curing compound, and the B component comprises the N3390 or the N75 curing compound of Bayer, and described N75 curing compound is to be the aliphatic polymeric isocyanate of base-material with hexamethylene diisocyanate (HDI).
Described color stuffing is selected polyaniline and aluminum paste mixture for use, or selects the mixture of polyaniline, aluminum paste and metal dust for use, or selects the mixture of polyaniline, aluminum paste and lead-free pigment for use.
In the described coating mixture, color stuffing is selected polyaniline and aluminum paste mixture for use, and wherein the aluminum paste consumption accounts for the 10-30% of coating mixture, and the polyaniline consumption accounts for the 5-10% of coating mixture, and all the other are thinner.
In the described coating mixture, color stuffing is selected polyaniline, aluminum paste and metal powder mixture for use, and wherein the aluminum paste consumption accounts for the 10-30% of coating mixture, and the polyaniline consumption accounts for the 8-10% of coating mixture, the metal dust consumption accounts for coating mixture less than 10%, and all the other are thinner.
Described grinding is meant color stuffing is dissolved among the TMDA, is cured back and epoxy resin mixed grinding.
Described C component prepares as follows: by weight percentage, get the epoxy resin of 20-40%, the fluorocarbon resin of 10-20%, the color stuffing of 30-40%, dimethylbenzene 10-30%, mix after each coating mixture, after adding the thinner grinding again, handle, get the C component at last with ultrasonic wave;
Described epoxy resin is a kind of in epoxide modified thermoplasticity acrylic acid resin, the epoxide modified acrylic acid resin;
The thinner consumption that adds is: in weight portion, and the thinner that adds 0.4-0.6 part in 1 part of coating mixture; The thinner that is added is a kind of in own fat, fourth fat or the dimethylbenzene;
Color stuffing is selected polyaniline and aluminum paste mixture for use, or selects the mixture of polyaniline, aluminum paste and metal dust for use, or selects the mixture of polyaniline, aluminum paste and lead-free pigment for use;
Select polyaniline and aluminum paste mixture for use as color stuffing, wherein the aluminum paste consumption accounts for the 10-30% of coating mixture, and the polyaniline consumption accounts for the 8-10% of coating mixture; All the other are thinner.
Select polyaniline, aluminum paste and metal powder mixture for use as color stuffing, wherein the aluminum paste consumption accounts for the 10-30% of coating mixture, and the polyaniline consumption accounts for the 5-10% of coating mixture, and the metal dust consumption accounts for coating mixture less than 30%.
Described D component prepares as follows: by weight percentage, the fluorocarbon resin of 30-60%, the color stuffing of 30-40%, all the other are thinner.After the mixing coating mixture, add again after thinner grinds, handle with ultrasonic wave, at last the D component;
The thinner consumption that adds is: in weight portion, and the thinner that adds 0.4-0.6 part in 1 part of coating mixture; The thinner that is added is a kind of in own fat, fourth fat or the dimethylbenzene.
Claims (10)
1. aluminum silver wall decoration material, comprise metal substrate, be coated with three layers of paint on the surface of this metal substrate, be followed successively by priming paint, middle japanning and finish paint from inside to outside, it is characterized in that at described priming paint be the aluminum paste anti-corrosion primer, middle japanning is for containing the bi-component thick-slurry type anticorrosive polyaniline lacquer of epoxy resin, fluorocarbon resin, aluminium paste, and finish paint is the fluorine-carbon-aluminum powder finish paint.
2. aluminum silver wall decoration material according to claim 1 is characterized in that metal substrate is that thickness is the 0.5-1.5mm steel plate.
3. the manufacturing process of aluminum silver wall decoration material according to claim 1 is characterized in that this technology comprises: 1) substrate manufacture, be processed into decorative panel on request to steel plate; 2) paint spraying, at first at the surface of substrate spraying priming paint, japanning in the spraying on priming paint then, at last in be coated with and paint spray paint;
The spraying of described priming paint comprises: A component and B component stir well even after, mix with 10: 1 part by weight, static again slaking 30 minutes adds proper amount of diluting then, sprays after transferring to working viscosity;
Japanning spraying comprises in described: C component and B component stir well even after, mix with 8: 1 part by weight, static again slaking 30 minutes adds proper amount of diluting then, sprays after transferring to working viscosity;
The spraying of described finish paint comprises: D component and B component stir well even after, mix with 15: 1 part by weight, static again slaking 30 minutes adds proper amount of diluting then, sprays after transferring to working viscosity.
4. the manufacturing process of aluminum silver wall decoration material according to claim 3, it is characterized in that described A component prepares as follows: by weight percentage, get the epoxy resin of 30-60%, the color stuffing of 30-40%, all the other are thinner, after the mixing coating mixture, add again after thinner grinds, handle with ultrasonic wave, get the A component at last;
Described epoxy resin is a kind of in epoxide modified thermoplasticity acrylic acid resin, the epoxide modified acrylic acid resin;
The thinner consumption that adds is: in weight portion, and the thinner that adds 0.4-0.6 part in 1 part of coating mixture; The thinner that is added is a kind of in own fat, fourth fat or the dimethylbenzene;
Described B component is general curing compound, and the B component comprises the N3390 or the N75 curing compound of Bayer, and described N75 curing compound is to be the aliphatic polymeric isocyanate of base-material with hexamethylene diisocyanate (HDI).
5. the manufacturing process of aluminum silver wall decoration material according to claim 4, it is characterized in that described described color stuffing selects polyaniline and aluminum paste mixture for use, or select the mixture of polyaniline, aluminum paste and metal dust for use, or select the mixture of polyaniline, aluminum paste and lead-free pigment for use.
6. the manufacturing process of aluminum silver wall decoration material according to claim 4, it is characterized in that in the described coating mixture, color stuffing is selected polyaniline and aluminum paste mixture for use, wherein the aluminum paste consumption accounts for the 10-30% of coating mixture, the polyaniline consumption accounts for the 8-10% of coating mixture, and all the other are thinner.
7. the manufacturing process of aluminum silver wall decoration material according to claim 4, it is characterized in that in the described coating mixture, color stuffing is selected polyaniline, aluminum paste and metal powder mixture for use, wherein the aluminum paste consumption accounts for the 20-30% of coating mixture, the polyaniline consumption accounts for the 5-10% of coating mixture, and the metal dust consumption accounts for coating mixture less than 30%.
8. the manufacturing process of aluminum silver wall decoration material according to claim 4 is characterized in that described grinding is meant color stuffing is dissolved among the TMDA, is cured back and epoxy resin mixed grinding.
9. the manufacturing process of aluminum silver wall decoration material according to claim 3, it is characterized in that described C component prepares as follows: by weight percentage, get the epoxy resin of 20-40%, the fluorocarbon resin of 10-20%, the color stuffing of 30-40%, all the other are thinner, get coating mixture after mixing each, after adding the thinner grinding again, handle, get the C component at last with ultrasonic wave;
Described epoxy resin is a kind of in epoxide modified thermoplasticity acrylic acid resin, the epoxide modified acrylic acid resin;
The thinner consumption that adds is: in weight portion, and the thinner that adds 0.4-0.6 part in 1 part of coating mixture; The thinner that is added is a kind of in own fat, fourth fat or the dimethylbenzene;
Color stuffing is selected polyaniline and aluminum paste mixture for use, or selects the mixture of polyaniline, aluminum paste and metal dust for use, or selects the mixture of polyaniline, aluminum paste and lead-free pigment for use;
Select polyaniline and aluminum paste mixture for use as color stuffing, wherein the aluminum paste consumption accounts for the 10-30% of coating mixture, and the polyaniline consumption accounts for the 8-10% of coating mixture, and all the other are thinner;
Select polyaniline, aluminum paste and metal powder mixture for use as color stuffing, wherein the aluminum paste consumption accounts for the 20-30% of coating mixture, and the polyaniline consumption accounts for the 5-10% of coating mixture, and the metal dust consumption accounts for coating mixture less than 30%.
10. the manufacturing process of aluminum silver wall decoration material according to claim 3, it is characterized in that described D component prepares as follows: by weight percentage, get the fluorocarbon resin of 30-60%, the color stuffing of 30-40%, all the other are thinner, after the mixing coating mixture, add again after thinner grinds, handle with ultrasonic wave, get the D component at last;
The thinner consumption that adds is: in weight portion, and the thinner that adds 0.4-0.6 part in 1 part of coating mixture; The thinner that is added is a kind of in own fat, fourth fat or the dimethylbenzene.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN2010102216534A CN101906860B (en) | 2010-07-09 | 2010-07-09 | Aluminum silver wall decoration material and manufacturing process thereof |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN2010102216534A CN101906860B (en) | 2010-07-09 | 2010-07-09 | Aluminum silver wall decoration material and manufacturing process thereof |
Publications (2)
Publication Number | Publication Date |
---|---|
CN101906860A true CN101906860A (en) | 2010-12-08 |
CN101906860B CN101906860B (en) | 2012-11-07 |
Family
ID=43262434
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
CN2010102216534A Active CN101906860B (en) | 2010-07-09 | 2010-07-09 | Aluminum silver wall decoration material and manufacturing process thereof |
Country Status (1)
Country | Link |
---|---|
CN (1) | CN101906860B (en) |
Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN2804234Y (en) * | 2005-06-27 | 2006-08-09 | 深圳市明远氟涂料有限公司 | Anti-crack F-carbon painting structure |
CN101298530A (en) * | 2008-06-19 | 2008-11-05 | 深圳市广田环保涂料有限公司 | Fluorine carbon silver powder baking finish and preparation thereof, special diluting agent and use method thereof |
CN101314684A (en) * | 2008-06-18 | 2008-12-03 | 深圳市广田环保涂料有限公司 | Single-component fluorine-carbon-aluminum powder baking varnish, preparation, special thinning agent and use method thereof |
WO2009030120A1 (en) * | 2007-09-05 | 2009-03-12 | Yijin Chen | A decorative panel for wall |
CN101531852A (en) * | 2009-04-13 | 2009-09-16 | 湖南湘江涂料集团有限公司 | Spraying type fluorocarbon metallic paint and application thereof in aluminium alloy sections of buildings |
CN201367699Y (en) * | 2009-02-26 | 2009-12-23 | 江阴天虹板业有限公司 | Outer wall granite vein aluminum-plastic composite board |
-
2010
- 2010-07-09 CN CN2010102216534A patent/CN101906860B/en active Active
Patent Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN2804234Y (en) * | 2005-06-27 | 2006-08-09 | 深圳市明远氟涂料有限公司 | Anti-crack F-carbon painting structure |
WO2009030120A1 (en) * | 2007-09-05 | 2009-03-12 | Yijin Chen | A decorative panel for wall |
CN101314684A (en) * | 2008-06-18 | 2008-12-03 | 深圳市广田环保涂料有限公司 | Single-component fluorine-carbon-aluminum powder baking varnish, preparation, special thinning agent and use method thereof |
CN101298530A (en) * | 2008-06-19 | 2008-11-05 | 深圳市广田环保涂料有限公司 | Fluorine carbon silver powder baking finish and preparation thereof, special diluting agent and use method thereof |
CN201367699Y (en) * | 2009-02-26 | 2009-12-23 | 江阴天虹板业有限公司 | Outer wall granite vein aluminum-plastic composite board |
CN101531852A (en) * | 2009-04-13 | 2009-09-16 | 湖南湘江涂料集团有限公司 | Spraying type fluorocarbon metallic paint and application thereof in aluminium alloy sections of buildings |
Also Published As
Publication number | Publication date |
---|---|
CN101906860B (en) | 2012-11-07 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CN104098996B (en) | A kind of nano compound polyurethane aircraft coating and preparation method thereof | |
CN103952072B (en) | A kind of polyurethane water-proof paint and preparation method thereof | |
CN101469248A (en) | Bicomponent polyurethane coating and preparation thereof | |
CN104148258A (en) | Fluorocarbon aluminum panel manufacturing technique | |
CN101831233A (en) | Method for preparing green low-carbon special anticorrosive coating | |
CN101671515A (en) | Anticorrosive coating for concrete structure reinforcing bars and preparation method thereof | |
TWI572743B (en) | Application of coating pretreating agent and coating type coating method for coating type coating | |
CN103397324B (en) | A kind of multifunction phosphide liquid and its production and use | |
CN104004448A (en) | Single-component cathodic electrophoretic coating for automotive primer | |
CN111205717A (en) | High-hardness silver flashing baking paint and preparation method thereof | |
CN104109428A (en) | 3C1B-enabled wet-on-wet white primer surfacer and preparation method thereof | |
CN108080239B (en) | Preparation method of environment-friendly powder coating color-coated sheet | |
CN101906860B (en) | Aluminum silver wall decoration material and manufacturing process thereof | |
CN105951024A (en) | Preparation method for composite coating on surface of protective guard | |
CN104559598A (en) | Heat-resistant corrosion-resistant noise-reduction water-base paint and preparation method thereof | |
CN103275600B (en) | A kind of true mineral varnish of true stone metallic plate and the manufacturing process of this true stone metallic plate | |
CN103351797B (en) | Poly-Radix Asparagi industrial coating and preparation method and application | |
CN105860744A (en) | High-salt spray resistance one-component quick-drying grey epoxy primer and preparation method thereof | |
CN105665262A (en) | Coating wet-spraying wet process for engineering machinery | |
CN104629586A (en) | Roasting-free energy-saving high salt spray resistant epoxy primer and preparation method thereof | |
CN104789104B (en) | Hydroxyl group-containing polyurethane acrylate copolymer aqueous industrial paint with high mechanical performances | |
JP2017179261A (en) | Primer coating for solvent-based metal, metal material with thin film and precoat metal material | |
CN101210148B (en) | Fast preparation of nano environmental protection chemical coating liquid and using method thereof | |
CN103113813A (en) | Hydraulic steel-structure anticorrosion anti-aging high-polymer nano modified coating material | |
CN104109425A (en) | Fluorocarbon resin finishing paint and method utilizing fluorocarbon resin to improve anticorrosion performance of steel fiber concrete |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
C06 | Publication | ||
PB01 | Publication | ||
C10 | Entry into substantive examination | ||
SE01 | Entry into force of request for substantive examination | ||
C14 | Grant of patent or utility model | ||
GR01 | Patent grant | ||
PE01 | Entry into force of the registration of the contract for pledge of patent right | ||
PE01 | Entry into force of the registration of the contract for pledge of patent right |
Denomination of invention: An aluminum silver curtain wall decoration material and its manufacturing process Effective date of registration: 20201231 Granted publication date: 20121107 Pledgee: Agricultural Bank of China Limited by Share Ltd. Jiaxing science and Technology Branch Pledgor: JIAXING ZHONGFA METAL SURFACE PROC Co.,Ltd. Registration number: Y2020330001370 |