CN101891502A - Method for manufacturing peacock glaze - Google Patents
Method for manufacturing peacock glaze Download PDFInfo
- Publication number
- CN101891502A CN101891502A CN 201010251361 CN201010251361A CN101891502A CN 101891502 A CN101891502 A CN 101891502A CN 201010251361 CN201010251361 CN 201010251361 CN 201010251361 A CN201010251361 A CN 201010251361A CN 101891502 A CN101891502 A CN 101891502A
- Authority
- CN
- China
- Prior art keywords
- glaze
- frit
- fusion cake
- peacock
- ball
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a method for manufacturing a peacock glaze. The method is characterized in that: a fusion cake and a glaze are manufactured according to a given formula, wherein the fusion cake comprises borax, potassium feldspar and quartz; and the glaze comprises potassium feldspar, steel and stock, zinc oxide, bentonite, quartz, cobalt oxide and chrome red. The method comprises the following steps of: grinding the components of the fusion cake by a dry method at the temperature of 1,250 DEG C to form the fusion cake for later use; ball-milling the components of the glaze by a wet method, selecting a ratio of material to spheres to water of 1: 2: 0.5, adding 5 percent of clay into complete glaze, and screening the mixture with a 250-mesh screen, wherein the screening residue is less than 0.3; taking the crushed fusion cake and the ball-milled screened glaze, adjusting the fusion cake and the glaze to the same concentration according to a Baume degree, namely adjusting fusion cake and the glaze to form slurry of 40 to 50 Baume degrees, then mixing and stirring the fusion cake and the glaze in a ratio of 1:1-1.8, performing wet ball milling, and screening the glaze with a 325-mesh screen; and obtaining the peacock glaze when the Baume degree is 40 to 50. The obtained glaze has bright surface, natural peacock feather-like patterns, bright color and excellent visual effect.
Description
Technical field
The present invention relates to a kind of making method of peacock glaze
Background technology
In ceramic industry, pottery, porcelain overglaze color and luster, pattern directly have influence on the attractive in appearance of product and user's favorable rating, thereby, the more apparent prominent position of the allotment of glaze, the base substrate of same moulding often produces Different Effects because of the different visions to the human consumer of overglaze, people like the porcelain beautiful design, prefer decorative pattern as the peacock plumes plumage of nature, the porcelain of visual decorative effect; The beauty of peacock plumes plumage makes us gasp in admiratioing, if it is decorated on household china, people can be appreciated whenever and wherever possible, and that is full of endless joy naturally.
Summary of the invention
The objective of the invention is to prepare and a kind ofly can in 1180-1196 ℃ of quick roller kiln, burn till the peacock glaze that glaze reaches the same glaze chromatic effect with the peacock plumes plumage.
The present invention develops respectively by two glaze of major-minor, and remix imposes on the base and burns till; Promptly by given formulated glaze, metal oxide by RO and R2O and R2O3 and RO2 makes orchid, purple, Huang, ash, green transparency enamel, join again and opaque glaze, preparation by a certain percentage, modulation 40～50 degree Beaume concentration promptly get glaze slip, get and go into kiln after specific composition base substrate adopts glaze spraying, burn till fast 1180～1195 ℃ of oxidizing atmospheres, gained glaze light has decorative pattern as the peacock plumes plumage of nature, decorative effect is unexpected, and decorative daily-use porcelain effect is splendid.
Concrete technical scheme is as follows:
1, by following prescription batching one by one,
A, frit (main glaze) are got the raw materials ready by following prescription:
Borax 40～60%, potassium felspar sand 15～30%, quartzy 20～40%;
B, glaze (secondary glaze) are got the raw materials ready by following prescription:
Potassium felspar sand 20～35%, steel stone 15～25%, zinc oxide 10～20%,
Wilkinite 5～10%, quartz 10～20%, cobalt oxide 0.5～1.5%,
Chrome red 10～20%;
Each component percentage composition sum is 100%;
2, make frit: above-mentioned frit (main glaze) batching is carried out 1250 ℃ of dry grindings, and to make frit standby;
3, ball milling sieves: above-mentioned glaze (secondary glaze) batching is adopted wet ball grinding, selected material: ball: water=1: 2: 0.5 also adds 5% clay in 100% glaze (secondary glaze), 250 mesh sieves, tail over less than 0.3 standby;
4, modulation: get the glaze (secondary glaze) that above-mentioned frit (main glaze) crushed material and ball milling sieve, transfer to same concentrations by degree Beaume, be that furnishing concentration is 40～50 degree Beaume slurries, be that 1: 1～1.8 proportionings are puddled modulation by frit and glaze proportioning then, the glaze that carries out again behind the wet ball grinding is crossed 325 mesh sieves, tails over less than 0.5; Degree Beaume is 40～50 promptly.
Above-mentioned gained glaze is when using (glazing), and the glaze layer thickness on the base substrate is controlled to be 0.8-1.2mm; Go in the quick roller kiln and burn till in 1180～1196 ℃; Gained glaze light has decorative pattern as the peacock plumes plumage of nature, and coloured and dazzling, visual effect is splendid.
Embodiment
Get the raw materials ready by following prescription
A, frit (main glaze) are got the raw materials ready by following prescription:
Borax 50%, potassium felspar sand 20%, quartzy 30%;
B, glaze (secondary glaze) are got the raw materials ready by following prescription:
Potassium felspar sand 28% steel stone 21% zinc oxide 14% wilkinite 7%
Quartzy 14% cobalt oxide, 1% chrome red 15%
Each component percentage composition sum is 100%;
(2), make frit (main glaze): above-mentioned frit batching is carried out 1250 ℃ of dry grindings, and to make frit standby;
(3), ball milling sieves: above-mentioned glaze (secondary glaze) batching is adopted wet ball grinding, selected material: ball: water=1: 2: 0.5 also adds 5% clay in 100% glaze, cross 250 mesh sieves, tails over less than 0.3 standby;
(4), modulation: get the glaze (secondary glaze) that above-mentioned frit (main glaze) crushed material and ball milling sieve, transfer to same concentrations by degree Beaume, be that furnishing concentration is 46 degree Beaume slurries, proportioning by major and minor glaze is that 1: 0.8 proportioning is puddled then, the glaze that carries out again behind the wet ball grinding is crossed 325 mesh sieves, tails over less than 0.5; Degree Beaume is 46 promptly, glazing on base substrate, and the thick 1.2mm of glaze burns till for 1185 ℃ at roller kiln fast, just can obtain the splendid purple profit of effect and desire---peacock glaze.Gained glaze light has decorative pattern as the peacock plumes plumage of nature, and coloured and dazzling, visual effect is splendid.
Claims (1)
1. the making method of a peacock glaze, it comprises the modulation of sieving of prescription batching-making frit-ball milling; It is characterized in that:
(1) prescription batching
A, frit are got the raw materials ready by following prescription:
Borax 40～60%, potassium felspar sand 15～30%, quartzy 20～40%;
B, glaze are got the raw materials ready by following prescription:
Potassium felspar sand 20～35%, steel stone 15～25%, zinc oxide 10～20%,
Wilkinite 5～10%, quartz 10～20%, cobalt oxide 0.5～1.5%,
Chrome red 10～20%;
Each component percentage composition sum is 100%;
(2), make frit: above-mentioned frit batching is carried out 1250 ℃ of dry grindings, and to make frit standby;
(3), ball milling sieves: above-mentioned glaze batching is adopted wet ball grinding, selected material: ball: water=1:2:0.5 also adds 5% clay in 100% glaze, cross 250 mesh sieves, tails over less than 0.3 standby;
(4), modulation: get the glaze that above-mentioned frit powder minces and sieves with ball milling, transfer to same concentrations by degree Beaume, promptly furnishing concentration is 40～50 degree Beaume slurries separately, be that 1: 1～1.8 proportionings are puddled modulation by frit and glaze proportioning then, the glaze that carries out again behind the wet ball grinding is crossed 325 mesh sieves, tails over less than 0.5; Degree Beaume is 40～50 promptly.