CN101885602A - 高强度硅钙渣陶粒及其制备方法 - Google Patents

高强度硅钙渣陶粒及其制备方法 Download PDF

Info

Publication number
CN101885602A
CN101885602A CN 201010228825 CN201010228825A CN101885602A CN 101885602 A CN101885602 A CN 101885602A CN 201010228825 CN201010228825 CN 201010228825 CN 201010228825 A CN201010228825 A CN 201010228825A CN 101885602 A CN101885602 A CN 101885602A
Authority
CN
China
Prior art keywords
dregs
calcium silicon
high intensity
preparation
calcium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201010228825
Other languages
English (en)
Inventor
李侠
张金山
赵俊梅
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Inner Mongolia University of Science and Technology
Original Assignee
Inner Mongolia University of Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Inner Mongolia University of Science and Technology filed Critical Inner Mongolia University of Science and Technology
Priority to CN 201010228825 priority Critical patent/CN101885602A/zh
Publication of CN101885602A publication Critical patent/CN101885602A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种高强度硅钙渣陶粒及其制备方法，属于材料领域。本发明包括下列原料按重量百分比计：粉煤灰30-45％，硅钙渣15-55％，粘土5-15％，硫铁矿渣5-10％，其余为水。制备方法如下，上述原料粉碎，粒径不大于1mm，且小于200目的含量大于70％，将上述粉碎后物料充分混合；造球；自然晾干后的球体进行烧结，烧结温度：1000-1100℃，保温：15-60min。本发明由于采用固体废弃物粉煤灰及硅钙渣为主要原料，制备出的陶粒不仅强度高，而且还解决了工业固体废弃物对环境的污染、对土地资源的占用等问题，为高铝粉煤灰提铝后的产物硅钙渣的利用提供了一条新途径，可有效解决硅钙渣的综合利用问题。

Description

高强度硅钙渣陶粒及其制备方法
技术领域
发明涉及一种高强度硅钙渣陶粒及其制备方法，属于材料领域。
背景技术
高强陶粒配制的混凝土有着许多优良的性能，与普通混凝土相比，高强陶粒混凝土密度更低，保温隔热、耐磨、抗震、吸音性能更好，而且强度也可以更高。因此高强陶粒混凝土的应用将越来越广泛。经国内外几十年生产实践证明，根据各地资源条件不同，可分别采用黏土、页岩、粉煤灰或其他固体废弃物生产陶粒。此种生产高强陶粒方法，使用的黏土、页岩等不可再生资源较多，浪费不可再生资源严重。
发明内容
本发明的目的在于提供一种利用固体废弃物生产高强度硅钙渣陶粒及其制备方法。
技术解决方案：高强度硅钙渣陶粒包括下列原料按重量百分比计，粉煤灰30-45％，硅钙渣15-55％，粘土5-15％，硫铁矿渣5-10％，其余为水。
高强度硅钙渣陶粒的制备方法，将粉煤灰、硅钙渣、粘土、硫铁矿渣粉碎，粒径不大于1mm，且小于200目的含量大于70％，将上述粉碎后物料充分混合；采用人工模拟造球盘进行造球；自然晾干后的球体进行烧结，烧结温度：1000-1100℃，保温：15-60min。
本发明采用粉煤灰及硅钙渣为主要原料，硅钙渣为粉煤灰提取氧化铝后的固体废弃物，用粉煤灰添加硅钙渣生产陶粒不仅可以提高陶粒的强度，而且可以充分利用粉煤灰和硅钙渣这两种固体废弃物，不仅解决了工业固体废弃物对环境的污染、对土地资源的占用等问题，而且为高铝粉煤灰提铝后的产物硅钙渣的利用提供了一条新途径，可有效解决硅钙渣的综合利用问题。
具体实施方式
实施例1
制备2吨高强度硅钙渣陶粒的制备：取粉煤灰800Kg，硅钙渣800Kg，粘土200Kg，硫铁矿渣200Kg粉碎，粒径不大于1mm，且小于200目的含量大于70％，将上述物料混合，混合后的物料与水充分混合搅拌，固液质量比为3∶2，采用人工模拟造球盘进行造球；自然晾干后的球体进行烧结，烧结温度：1050℃，保温：25min。
陶粒工业试验产品性能检测见表1。
表1工业试验的高强硅钙渣陶粒性能
Figure BSA00000193875800021
用上述配方及工艺生产的高强硅钙渣陶粒代替混凝土中的石子配制陶粒混凝土，试验结果见表2.表2中编号1-0和2-0为普通混凝土；1-1和2-1为用高强度硅钙渣陶粒配制的混凝土。
表二用石子配制的普通混凝土和用陶粒配制的混凝土试验对比
Figure BSA00000193875800022
注：陶粒颗粒级配为5～15mm。

Claims (2)

1.高强度硅钙渣陶粒，其特征在于，包括下列原料按重量百分比计，粉煤灰30-45％，硅钙渣15-55％，粘土5-15％，硫铁矿渣5-10％，其余为水。
2.高强度硅钙渣陶粒的制备方法，其特征在于，将粉煤灰、硅钙渣、粘土、硫铁矿渣粉碎，粒径不大于1mm，且小于200目的含量大于70％，将上述粉碎后物料充分混合；采用人工模拟造球盘进行造球；自然晾干后的球体进行烧结，烧结温度：1000-1100℃，保温：15-60min。
CN 201010228825 2010-07-03 2010-07-03 高强度硅钙渣陶粒及其制备方法 Pending CN101885602A (zh)