CN101876147B - 一种抗菌纺丝油剂 - Google Patents
一种抗菌纺丝油剂 Download PDFInfo
- Publication number
- CN101876147B CN101876147B CN2009101358465A CN200910135846A CN101876147B CN 101876147 B CN101876147 B CN 101876147B CN 2009101358465 A CN2009101358465 A CN 2009101358465A CN 200910135846 A CN200910135846 A CN 200910135846A CN 101876147 B CN101876147 B CN 101876147B
- Authority
- CN
- China
- Prior art keywords
- percent
- antibacterial
- spinning oil
- quaternary ammonium
- ammonium salt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种适于纺丝用的抗菌纺丝油剂,原料组成以重量百分比计,烷基二甲基羟乙基季铵盐5-15%,烷基二甲基季铵盐5-15%,聚乙二醇脂肪酸酯8-16%,烷基酚聚氧乙烯醚5-10%,脂肪醇聚氧乙烯醚5-10%,聚乙二醇1-5%,化妆品用酚及其衍生物杀菌剂0.05-0.25%,化妆品用季铵盐类杀菌剂0.05-0.25%,去离子水加至100%,在反应釜里搅拌均匀,温度为常温,即制得油剂成品。其中油剂中的总活性物含量35-55%。总上油率为0.3-0.8wt%。
Description
背景技术
无纺布广泛用于卫生巾、纸尿裤等一次性卫生用品的贴肤面料。目前制造无纺布(热轧或热风)的主要原料是聚丙烯(PP)或聚丙烯/聚乙烯双组分短纤等。生产上述短纤时必须使用纺丝油剂,以便达到抗静电、润滑、润湿、渗透、集束的效果,可赋予纤维良好的平滑性和抱合性,手感柔软、滑爽,使得纤维的动静摩擦系数适当,可纺性好。
传统短纤及其无纺布通常含0.5~3.0wt%的水份,在使用于与身体接触的一次性卫生用品时极易滋生病菌,甚而造成消费者的“二次污染”。
为了抑制细菌滋生,现有技术中提出了制造抗菌纤维,目前制造抗菌纤维的常用方法有:
1.纺丝时加入银系抗菌母粒。但是上述方法的特点是:1)纤维颜色不稳定,易变黑;2)对酵母菌的抑制效果相对较差;3)抗菌效果永久而且纤维耐洗,但是价格昂贵,用于一次性卫生用品使得成本提高,造成资源浪费。例如CN1297496A中公开了一种含抗微生物剂的皮芯聚酯纤维,其中可将银系抗菌物质与母粒按适当比例掺混,然后通过螺杆挤压机进行纺丝,获得抗菌纤维。
2.对纤维进行改性,例如对聚丙烯腈改性(AB抗菌防臭纤维)。CN87100231A中公开了一种抗菌防臭纤维织物,其特征在于对腈纶纤维进行改性,它是在腈纶纤维的第一单体丙烯腈上复合铜离子,在第三单体衣康酸或丙烯磺酸钠上复合C↓[23]H↓[25]N↓[2]↑[+]基团。但是其特点是:1)墨绿色限制;2)生产工艺复杂;3)抗菌效果永久而且纤维耐洗,但是价格昂贵,用于一次性卫生用品使得成本提高,造成资源浪费。
发明内容
本发明所要解决的技术问题是为了克服现有技术中的上述缺陷,提出一种抗菌纺丝油剂,其适用于合成纤维纺丝的生产过程。其中该油剂中具有抗菌组分。其在纺丝过程中使用,其中生产出的合成纤维为短纤,所述短纤适于用作一次性卫生用品的贴肤无纺布。该油剂具有优异的抗静电性、柔软性、适宜的平滑性、抱合性,同时使得生产出来的纤维具有抗菌效果。
本发明解决上述技术问题采用的技术方案为:一种适于纺丝用的抗菌纺丝油剂,原料组成以重量百分比计,烷基二甲基羟乙基季铵盐5-15%,烷基二甲基季铵盐5-15%,聚乙二醇脂肪酸酯8-16%,烷基酚聚氧乙烯醚5-10%,脂肪醇聚氧乙烯醚5-10%,聚乙二醇1-5%,化妆品用酚及其衍生物杀菌剂0.05-0.25%,化妆品用季铵盐类杀菌剂0.05-0.25%,去离子水加至100%,在反应釜里搅拌均匀,温度为常温,即制得油剂成品。其中油剂中的总活性物含量35-55%。
通过试验证明该油剂不但具有优良的纺丝功能,而且还具有特殊的抗菌功能,取得了双重效果。
该油剂适于棉型短纤,尤其适于亲水性合成纤维短纤,其中合成纤维例如为聚丙烯(PP)短纤、聚丙烯/聚乙烯(PP/PE)复合短纤和/或聚酯/聚乙烯(PET/PE)复合短纤,但是上述仅仅是举例说明,而并非对本发明的限制。由使用上述抗菌纺丝油剂纺出的短纤可制备成抗菌无纺布,可将上述抗菌无纺布用于一次性卫生用品,达到良好的抑菌效果。
生产短纤的生产工艺为常规的传统工艺。
附图1:工艺流程图。
其流程为树脂熔练→喷丝、上油→静置润湿→上油、拉伸→卷曲→烘干→切断→包装。
只是纺丝过程中使用的油剂为本发明申请的抗菌纺丝油剂,纺丝过程中控制总上油率为0.3-0.8wt%。
化妆品用酚及其衍生物杀菌剂有:4-氯-3,5-二甲苯酚、4-氯-3-甲酚、四溴邻甲苯酚、二氯苯氧氯酚、溴氯双酚等。
化妆品用季铵盐类杀菌剂有:烷基三甲基溴化铵、苯扎氯铵、氯苄乙铵、十二烷基二甲基乙苯氧乙基溴化铵、十四烷基2-甲基吡啶溴化物等。
经试验证明,使用本发明申请的抗菌纺丝油剂生产出的纤维具有如下的抗菌特点:
1.抗菌力强:20分钟抑菌率≥90%。
2.抗菌谱广:对化脓菌、肠道感染菌、酵母菌有明显效果。
3.有效期长:抗菌有效期2年以上。
4.安全性好:对皮肤及阴道黏膜均无刺激,不会引起皮肤变态反应。
5.成本低廉:成本同比降低5%以下。
6.由于纤维具有明显持久的抗菌效果,因此当由上述纤维制备成的无纺布用于一次性卫生用品时,能够达到抗菌效果,有效防止“二次污染”。
具体实施方式
实施例1:
原料组成以重量百分比计,烷基二甲基羟乙基季铵盐5%,烷基二甲基季铵盐5%,聚乙二醇脂肪酸酯8%,烷基酚聚氧乙烯醚5%,脂肪醇聚氧乙烯醚5%,聚乙二醇1%,化妆品用酚及其衍生物杀菌剂0.05%,化妆品用季铵盐类杀菌剂0.05%,去离子水加至100%。
实施例2:
原料组成以重量百分比计,烷基二甲基羟乙基季铵盐15%,烷基二甲基季铵盐15%,聚乙二醇脂肪酸酯16%,烷基酚聚氧乙烯醚10%,脂肪醇聚氧乙烯醚10%,聚乙二醇5%,化妆品用酚及其衍生物杀菌剂0.25%,化妆品用季铵盐类杀菌剂0.25%,去离子水加至100%,在反应釜里搅拌均匀,温度为常温,即制得油剂成品。
实施例3:
原料组成以重量百分比计,十八烷基二甲基羟乙基季铵硝酸盐12%,十二烷基二甲基溴化铵8%,脂肪酸聚氧乙烯(10)酯10%,聚乙二醇(400)3%,烷基酚聚氧乙烯(4)醚2%,烷基酚聚氧乙烯(9)醚8%,脂肪醇聚氧乙烯(10)醚6%,三氯生0.2%,苯扎氯铵0.1%,去离子水加至100%。以上常温下混合、搅拌均匀,即得油剂成品。
同时应该指出的上,上述仅仅是举例说明,而并非对本发明的限制。本发明的范围并不限于上述具体实施例,而是在不脱离本发明精神实质下的各种变型、变化和替换仍落入本发明的保护范围内。
Claims (4)
1.一种抗菌纺丝油剂,其适用于合成纤维纺丝的生产过程,其中该抗菌纺丝油剂中具有抗菌组分,该抗菌纺丝油剂的原料组成以重量百分比计,烷基二甲基羟乙基季铵盐为5-15%,烷基二甲基季铵盐为5-15%,聚乙二醇脂肪酸酯为8-16%,烷基酚聚氧乙烯醚为5-10%,脂肪醇聚氧乙烯醚为5-10%,聚乙二醇为1-5%,化妆品用酚及其衍生物杀菌剂为0.05-0.25%,其中化妆品用酚及其衍生物杀菌剂选自于:4-氯-3,5-二甲苯酚、4-氯-3-甲酚、四溴邻甲苯酚、二氯苯氧氯酚或溴氯双酚,化妆品用季铵盐类杀菌剂为0.05-0.25%,其中化妆品用季铵盐类杀菌剂选自于:烷基三甲基溴化铵、苯扎氯铵、氯苄乙铵、十二烷基二甲基乙苯氧乙基溴化铵或十四烷基2-甲基吡啶溴化物,去离子水加至100%,在反应釜里搅拌均匀,温度为常温,即制得油剂成品。
2.根据权利要求1所述的抗菌纺丝油剂,其中该抗菌纺丝油剂的总上油率为0.3-0.8wt%。
3.根据权利要求1所述的抗菌纺丝油剂,其中生产出的合成纤维为短纤,所述短纤适于用作一次性卫生用品的贴肤无纺布。
4.根据权利要求1所述的抗菌纺丝油剂,其中合成纤维为聚丙烯短纤、聚丙烯/聚乙烯复合短纤和/或聚酯/聚乙烯复合短纤。