CN101871245A - Roofing heat insulating bricks and preparation method thereof - Google Patents
Roofing heat insulating bricks and preparation method thereof Download PDFInfo
- Publication number
- CN101871245A CN101871245A CN 201010205798 CN201010205798A CN101871245A CN 101871245 A CN101871245 A CN 101871245A CN 201010205798 CN201010205798 CN 201010205798 CN 201010205798 A CN201010205798 A CN 201010205798A CN 101871245 A CN101871245 A CN 101871245A
- Authority
- CN
- China
- Prior art keywords
- heat insulating
- insulating bricks
- cement
- cement concrete
- eps
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses roofing heat insulating bricks and a preparation method thereof. The roofing heat insulating bricks consist of cement concrete, a polystyrene EPS foam board, a polystyrene XPS extruded sheet and an acrylic adhesive or an acrylic interfacial agent, wherein the EPS and the XPS are adhered to the cement concrete by using the acrylic adhesive or the acrylic interfacial agent. The roofing heat insulating bricks have the advantages of: 1, good heat insulating effect; 2, long service life; 3, constant heat insulating effect; 4, light weight; 5, simple and convenient construction and low cost; and 6, energy conservation.
Description
Technical field
The present invention relates to a kind of heat-barrier material and preparation method thereof, specifically is a kind of roofing heat insulating bricks and preparation method thereof.
Background technology
Be used at present build that terrace is heat insulation, insulation normally the building terrace erect one deck precast plate or on terrace layer overlay slag and cement mortar, these two kinds of method heat-barrier materials are heavy and effect is undesirable.
Summary of the invention
For overcoming the deficiencies in the prior art, it is lighter to the invention provides a kind of weight, roofing heat insulating bricks of heat insulation, high insulating effect and preparation method thereof.
The technical scheme that the present invention solves the problems of the technologies described above is:
1. roofing heat insulating bricks, it is made of cement concrete, polystyrene (EPS) cystosepiment or polystyrene XPS extruded sheet and acroleic acid binding agent or interfacial agents; With acroleic acid binding agent or acrylic acid interfacial agents EPS or XPS are bonded on the cement concrete.
Above-mentioned cement concrete is that cement, sand, water are by weight forming cement: sand: water=1: 0～8: 0.1～2.
2. the preparation method of roofing heat insulating bricks may further comprise the steps:
(1) is sprayed at the top layer of EPS or XPS with acroleic acid binding agent or acrylic acid interfacial agents;
(2) cement concrete is cement, sand, a water composition by weight, cement: sand: water=1: 0～8: 0.1～2, through mechanical agitation;
(3) cement concrete is injected mould, then vibrations;
(4) EPS or XPS are put into mould, the top layer and the cement concrete of spraying acroleic acid binding agent or acrylic acid interfacial agents are pressed close to, the pressurization vibrations;
(5) demoulding then is a roofing heat insulating bricks.
3. the purposes of above-mentioned roofing heat insulating bricks: be used to build that terrace is heat insulation, insulation or decorate.
Advantage of the present invention is:
1. good heat-insulation effect.The coefficient of thermal conductivity of this product is 0.028w/ (m.k), the coefficient of thermal conductivity of steel concrete is 1.74w/ (m.k), learn thus: the coefficient of thermal conductivity of steel concrete is 58 times of this product coefficient of thermal conductivity, be the thermal resistance that the thermal resistance of this product is equivalent to 1.74 meters steel concrete, we can imagine the effect of heat insulation of this product thus.After the building terrace was spread this product, the top layer room temperature reached consistent with other floor room temperature.
2. long service life.Common foam is very easy to be aging under ultraviolet direct irradiation, and EPS of this product or XPS have added age resister when making, and is covered by cement concrete, can reach the same long application life with architecture noumenon.
3. the effect of heat insulation that constancy is arranged.Once there was the common foam of human to make isolation layer, think when just carrying out that effect is all right, but the foam water absorption rate of Yin Putong is very high, and water was heat carrier, so through a period of time, foam suction back effect of heat insulation has just died down.EPS of this product or XPS (foam body) water absorption rate has only 2.9% (GB is 0.041), so the effect of heat insulation constancy.
4. lightweight.This product has only 20 kilograms for every square metre, is convenient to carrying, construction, never influences the load of architecture noumenon.
5. easy construction, cost are low.During the construction of this product, only need directly be adhered to terrace and get final product with the cementing agent water distribution mud of special use, visible saving of labor material saving, cost is low.
6. energy-conservation.Behind this production insulating,, play insulation effect winter again, so can save air conditioning electricity about 50% owing to greatly reduce interior temperature summer.
Description of drawings
Fig. 1 is a main TV structure schematic diagram of the present invention.
Fig. 2 is a perspective view of the present invention.
Among the figure: EPS or XPS 1, cementing agent or interfacial agents 2, cement concrete 3.
The specific embodiment
Below in conjunction with accompanying drawing and one embodiment of the invention the present invention is described in detail.But need to prove that embodiment does not constitute the restriction to the claimed scope of the present invention.
As depicted in figs. 1 and 2, be sprayed at the top layer of EPS or XPS with acroleic acid binding agent or acrylic acid interfacial agents, cement concrete is injected mould, and then put into EPS or XPS, will be tightly bonding after cement concrete solidifies with EPS or XPS, form roofing heat insulating bricks.
Make the step of roofing heat insulating bricks:
(1) is sprayed at the top layer of EPS or XPS with acrylic acid wherein a kind of cementing agent or interfacial agents.
(2) cement concrete is cement, sand, a water composition by weight, cement: sand: water=1: 0～8: 0.1～2, and through mechanical agitation.
(3) cement concrete is injected mould, then vibrations.
(4) EPS or XPS are put into mould, the top layer and the cement concrete of spraying acroleic acid binding agent or acrylic acid interfacial agents are pressed close to, the pressurization vibrations.
(5) demoulding then is a roofing heat insulating bricks.
Product of the present invention is used for: the building terrace is heat insulation, insulation, decorate.
Claims (4)
1. a roofing heat insulating bricks is characterized in that, it is made of cement concrete, polystyrene (EPS) cystosepiment or polystyrene XPS extruded sheet and acroleic acid binding agent or interfacial agents; With acroleic acid binding agent or acrylic acid interfacial agents EPS or XPS are bonded on the cement concrete.
2. roofing heat insulating bricks according to claim 1 is characterized in that, described cement concrete is that cement, sand, water are by weight forming cement: sand: water=1: 0～8: 0.1～2.
3. the preparation method of a roofing heat insulating bricks is characterized in that, may further comprise the steps:
(1) is sprayed at the top layer of EPS or XPS with acroleic acid binding agent or acrylic acid interfacial agents;
(2) cement concrete is cement, sand, a water composition by weight, cement: sand: water=1: 0～8: 0.1～2, through mechanical agitation;
(3) cement concrete is injected mould, then vibrations;
(4) EPS or XPS are put into mould, the top layer and the cement concrete of spraying acroleic acid binding agent or acrylic acid interfacial agents are pressed close to, the pressurization vibrations;
(5) demoulding then is a roofing heat insulating bricks.
4. a kind of roofing heat insulating bricks according to claim 1 is characterized in that, the purposes of described roofing heat insulating bricks: be used to build that terrace is heat insulation, insulation or decorate.