CN101863650A - 石灰竹浆纤维增强硅酸钙板 - Google Patents

石灰竹浆纤维增强硅酸钙板 Download PDF

Info

Publication number
CN101863650A
CN101863650A CN 201010197118 CN201010197118A CN101863650A CN 101863650 A CN101863650 A CN 101863650A CN 201010197118 CN201010197118 CN 201010197118 CN 201010197118 A CN201010197118 A CN 201010197118A CN 101863650 A CN101863650 A CN 101863650A
Authority
CN
China
Prior art keywords
lime
bamboo pulp
calcium silicate
pulp fiber
silicate board
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 201010197118
Other languages
English (en)
Other versions
CN101863650B (zh
Inventor
宋实勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LIUZHOU GUIREN BUILDING MATERIAL CO Ltd
Original Assignee
LIUZHOU GUIREN BUILDING MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LIUZHOU GUIREN BUILDING MATERIAL CO Ltd filed Critical LIUZHOU GUIREN BUILDING MATERIAL CO Ltd
Priority to CN201010197118XA priority Critical patent/CN101863650B/zh
Publication of CN101863650A publication Critical patent/CN101863650A/zh
Application granted granted Critical
Publication of CN101863650B publication Critical patent/CN101863650B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种石灰竹浆纤维增强硅酸钙板，涉及一种建筑材料，该石灰竹浆纤维增强硅酸钙板，它由如下组分及其重量百分比配比组成：石灰竹浆纤维6％～12％；玻璃纤维1％～3％；石灰15％～20％；石英35％～60％；普通硅酸盐水泥20％～30％；膨胀珍珠岩1％～2％。由于采用上述原料组分及其重量百分比配比而成的石灰竹浆纤维增强硅酸钙板，具有强度高、成本低、外形美观，更环保的有益效果。

Description

石灰竹浆纤维增强硅酸钙板
技术领域
本发明涉及一种建筑材料，特别是一种纤维增强硅酸钙板。
背景技术
纤维增强硅酸钙板因具有密度低、防火、隔音性强、防腐防潮、强度高等优点，因此被广泛应用于各类建筑中，现有的纤维增强硅酸钙板，分含石棉和无石棉两种。生产现有含石棉的纤维增强硅酸钙板，使用的增强纤维主要为废旧牛皮纸、玻璃纤维、石棉等，其它原料为CaO、SiO2、膨胀珍珠岩及普通硅酸盐水泥等。通过碎纸磨浆-石棉松解-制浆-流浆真空脱水-成型脱模-蒸压反应-烘干-磨边-成品等工序制成。该已有技术使用的纤维为纸纤维、玻璃纤维、石棉，其中纸纤维原料为牛皮纸，市场来源为废旧的水泥袋及进口美国废纸。原料价钱高、杂质多、污染严重，并且要经过碎纸磨浆才能使用，加工过程耗电大，工序复杂。另外，由于目前造纸厂在造纸制浆时使用的纤维软化剂为氢氧化钠(NaOH)，所生产的纸浆中含Na+，使用这种纸浆纤维生产纤维增强硅酸钙板，在蒸压反应过程中Na+会抢先与Si+反应生成Na2SiO3，使得制成的纤维增强硅酸钙板的强度低，且外观呈黑斑，不能使用或影响使用。
发明内容
本发明的目的是提供一种强度高且外形美的石灰竹浆纤维增强硅酸钙板。
为达到上述发明目的本发明采用的技术方案是：一种竹浆纤维增强硅酸钙板，它由如下组分及其重量百分比配比组成：石灰竹浆纤维6％～12％；玻璃纤维1％～3％；石灰15％～20％；石英35％～60％；普通硅酸盐水泥20％～30％；膨胀珍珠岩1％～2％。
其中所述石灰竹浆纤维为用石灰水浸泡过的竹纤维。
其中各组分及其重量百分比为：石灰竹浆纤维7.48％；玻璃纤维2.16％；石灰17.27％；石英46.04％；普通硅酸盐水泥25.9％；膨胀珍珠岩1.15％。
由于采用上述原料组分及重量百分比配比而成的石灰竹浆纤维硅酸钙板具有以下有益效果。
1.强度高
本发明之石灰竹浆纤维增强硅酸钙板，由于采用石灰竹浆纤维中的竹纤维代替传统纤维增强硅酸钙板中的纸纤维，且以石灰(CaO)作为竹纤维的软化剂，制得的竹浆中含有Ca+，由于未使用普通纸浆，因此浆液中不含Na+，在石灰竹浆与其它材料结合形成纤维增强硅酸钙板反应过程中Ca+参加了化学反应，增加了纤维增强硅酸钙板中Ca+浓度，使生产出来的纤维增强硅酸钙板更加坚硬，达到高强度的要求。
2.外形美观
本发明之石灰竹浆纤维增强硅酸钙板，由于使用石灰竹浆而未使用常规纸浆，石灰竹浆中不含Na+，在板的形成中没有Na2SiO3，生成，因此形成的纤维增强硅酸钙板无黑斑，外形更美观。
3.成本低、更环保
本发明之石灰竹浆增强硅酸钙板，由于使用石灰竹浆纤维代替传统硅酸钙板中的增强纤维，原料价格低，杂质少，在生产过程中真空脱水回收的废水可循环利用，废水中的Ca+到了完全利用，且使用石灰竹浆纤维可取消石棉的使用，生产的是100％的无棉板，成本低、更环保。
具体实施方式
实施例一：
本发明石灰竹浆纤维增强硅酸钙板，它由如下组分及其重量百分比配比组成：石灰竹浆纤维7.48％；玻璃纤维2.16％；石灰17.27％；石英46.04％；普通硅酸盐水泥25.9％；膨胀珍珠岩1.15％。所述石灰竹浆纤维为用石灰水浸泡过的竹纤维，在用石灰水浸泡竹纤维形成的混合物石灰竹浆中：石灰的重量百分比为2％，竹纤维的重量百分比为8％。
现以配制6立方米混合料(总重量6600公斤)为例。首先配制石灰竹浆，备料：竹纤维52公斤、石灰13公斤、水585公斤，并将石灰与水混合形成598公斤石灰水。再准备玻璃纤维15公斤、石灰120公斤、石英320公斤、普通硅酸盐水泥180公斤、膨胀珍珠岩8公斤、水5307公斤。
在制作时，先制作石灰竹浆，首先将竹块(竹纤维)打成碎片，用石灰水(即上述配得的598公斤石灰水)浸泡15-20天使竹块软化，然后将竹块磨制成竹浆形成650公斤的石灰竹浆，再将已备好的玻璃纤维15公斤、石灰120公斤、石英320公斤、膨胀珍珠岩8公斤、普通硅酸盐水泥180公斤、水5307公斤与上述650公斤的石灰竹浆混合，后投入搅拌机中充分搅拌均匀形成混合浆料，再经过流浆-真空脱水-成型-静养脱模-蒸压反应-烘干-磨边-成品。即可形成本发明石灰竹浆纤维增强硅酸钙板。在流浆真空脱水时，所收集的废水可用于下一次的石灰竹浆及混合浆料的补充用水循环。成型时的边角废料可回收重新搅拌使用。
以下表1为按上述原料配比制成的石灰竹浆纤维增强硅酸钙板(规格为2240×1220mm×10mm)物理力学性能指标检测结果。
表1：物理力学性能指标检测结果
从以上数据可以看出，本发明石灰竹浆纤维增强硅酸钙板的抗折强度、含水率、湿胀率、热导率、热收缩率、耐火极限及隔声量等均优于一般普通硅酸钙板。
以下表2为本发明石灰竹浆纤维增强硅酸钙板实施例二至实施例五各原料组分及其重量百分比。
表2：实施例二至实施例五各原料组分及其重量百分比
Figure GDA0000022224790000051
按照实施例二至实施例五所述各原料及其重量百分比配比的石灰竹浆纤维增强硅酸钙板，除各原料的重量百分比稍有不同，其配置过程与实施例一基本相同，在此不在再重复叙述，其配制得到的石灰竹浆纤维增强硅酸钙板也能达到实施例一所述效果。当然本发明石灰竹浆纤维增强硅酸钙板原料配比也不限于上述实施例，只要在本发明范围内所做变换均属于本发明的范畴。

Claims (3)

1.一种石灰竹浆纤维增强硅酸钙板，其特征在于，它由如下组分及其重量百分比配比组成：石灰竹浆纤维6％～12％；玻璃纤维1％～3％；石灰15％～20％；石英35％～60％；普通硅酸盐水泥20％～30％；膨胀珍珠岩1％～2％。
2.如权利要求1所述的石灰竹浆纤维增强硅酸钙板，其特征在于，所述石灰竹浆纤维为用石灰水浸泡过的竹纤维。
3.如权利要求2所述的石灰竹浆纤维增强硅酸钙板，其特征在于，各组分及其重量百分比为：石灰竹浆纤维7.48％；玻璃纤维2.16％；石灰17.27％；石英46.04％；普通硅酸盐水泥25.9％；膨胀珍珠岩1.15％。
CN201010197118XA 2010-06-10 2010-06-10 石灰竹浆纤维增强硅酸钙板 Expired - Fee Related CN101863650B (zh)