CN101845282A - Components of armyworm adhesive and method for preparing same - Google Patents
Components of armyworm adhesive and method for preparing same Download PDFInfo
- Publication number
- CN101845282A CN101845282A CN201010013602A CN201010013602A CN101845282A CN 101845282 A CN101845282 A CN 101845282A CN 201010013602 A CN201010013602 A CN 201010013602A CN 201010013602 A CN201010013602 A CN 201010013602A CN 101845282 A CN101845282 A CN 101845282A
- Authority
- CN
- China
- Prior art keywords
- adhesive
- armyworm
- csm
- eva
- mineral oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an armyworm adhesive, which comprises the following components of: ethylene vinyl acetate (EVA), chlorosulfonated polyethylene (CSM), polymerized rosin, hydrogenated rosin, an anti-aging agent D, mineral oil, vaseline and kaolin. The armyworm adhesive has the advantages of innocuity to natural enemies, high environmental compatibility, high selectivity, broad insecticide spectrum, non residue, and obvious effect of preventing and controlling aphid, trialeurodes vaporariorum, lithocolletis ringoniella mats and male liriomyza during mating and breeding and the like. The armyworm adhesive is mainly suitable for adhering pests in agriculture, and adhering mosquitoes and flies, and the like at home.
Description
Technical field
The present invention relates to chemical technology field, relate in particular to a kind of composition and preparation method of insect adhesive.This insect adhesive is applicable to the sticking insect of agricultural, the sticking mosquitos and flies of family etc.
Background technology
The current environment problem has become the focus of International Politics, and control is polluted, and the protection environment has become the important standard of conduct of international co-operation.Along with the fast development of agricultural, using in a large number of agrochemicals goods and materials causes the contaminated situation in farmland very severe, and the abuse of chemical pesticide causes " 3R " problem increasingly serious, has seriously hindered the development of organic products and nuisanceless cause.It is influenced to cause agricultural product quality to arrive, and the agricultural-food of some areas are subjected to more serious pollution, because of edible contaminated food causes the incident of the poisoning end that appears in the newspapers repeatly.Therefore, the development pollution-less agriculture is protection and the needs that improve agroecological environment." green barrier " of international in addition food, agricultural-food (relevant, market) trade also makes China's tradition export of farm produce be faced with serious threat and challenge.Therefore, utilize biological pesticide and modern insecticidal technology to become the certainty of social development.
Particularly in recent years, mini pest such as sucking pest aphid, aleyrodid, the Liriomyza class since its reproductivity strong, be easy to generate characteristics such as resistance, General Medicine is difficult to control, and this class pest transmitted virus disease increases the weight of the generation of field virus disease, the serious harm plant growth.How to utilize new Prevention Technique, carrying out pollution-less agriculture production is one of problem of primary solution at present, and a ring important in the pollution-less agriculture technical system is exactly will carry out promoting the use of nuisanceless production technology in product.Therefore, utilize the characteristics such as taxis of yellow, phototaxis, chemotaxis of Agricultural pests, develop efficient, novel desinsection instrument, have characteristics such as environmentally safe, pollution-free, more help improving the agricultural product quality and the market competitiveness.
Existing insect adhesive is relatively poor to the viscosity of insect, and is particularly especially poor to the male liriomyza bryoniae prevention effect in aphid, Trialeurodes vaporariorum Westwood, plutella xylostella and the mating breeding.
Summary of the invention
At the problems referred to above, the objective of the invention is to a kind of insect adhesive, relatively poor to solve this insect adhesive of the prior art to the viscosity of insect, the problem of the male liriomyza bryoniae prevention effect difference in particularly especially aphid, Trialeurodes vaporariorum Westwood, plutella xylostella and mating being bred.
To achieve these goals, technical scheme of the present invention is as follows:
Insect adhesive is characterized in that, includes following component:
EVA (ethene-vinyl acetate) 30-40 part;
CSM (chlorosulfonated polyethylene) 10-20 part;
Polymerized rosin 5-10 part;
Staybelite 5-10 part;
Antioxidant D (N-phenyl-2-naphthylamines) 1-5 part;
Mineral oil 10-15 part;
Vaseline 5-10 part;
Kaolin 5-10 part; More than be mass ratio.
A kind of preparation method of insect adhesive is characterized in that, may further comprise the steps:
1) behind the adding mineral oil, it is heated to 130 ℃-140 ℃, adds EVA, CSM in proportion, stir then, until abundant dissolving;
2) add polymerized rosin, staybelite, stir, fully after the dissolving, be evacuated to no bubble;
3) be cooled to 70 ℃-80 ℃, add anti-aging agent, Vaseline then;
4) material kaolin is added in adding at last, and being incubated to tackiness agent does not have bubble.
During use, the surface that insect adhesive of the present invention is directly spread upon adhering sheet (yellow plate, fiber board etc.) gets final product.
Beneficial effect of the present invention is:
1, the present invention have harmless to natural enemy, with good, the characteristics such as selectivity is strong, insecticidal spectrum is wide, noresidue of environmentally compatible.
2, the present invention is especially remarkable to the male liriomyza bryoniae prevention effect in aphid, Trialeurodes vaporariorum Westwood, plutella xylostella and the mating breeding.
The present invention mainly is applicable to the sticking insect of agricultural, the sticking mosquitos and flies of family etc.
Embodiment
For technique means, creation characteristic that the present invention is realized, reach purpose and effect is easy to understand, below further set forth the present invention.
Embodiment 1:
Insect adhesive, the component that it is formed and the mass ratio of each component are as follows:
36 parts of EVA (ethene-vinyl acetate);
15 parts of CSM (chlorosulfonated polyethylene);
8 parts of polymerized rosines;
8 parts of staybelites;
3 parts of antioxidant Ds;
14 parts in mineral oil;
8 parts in Vaseline;
8 parts of kaolin.
The preparation method of this insect adhesive may further comprise the steps:
1) behind the adding mineral oil, it is heated to 130 ℃, adds EVA, CSM in proportion, stir then, until abundant dissolving;
2) add polymerized rosin, staybelite, stir, fully after the dissolving, be evacuated to no bubble;
3) be cooled to 70 ℃, add anti-aging agent, Vaseline then;
4) material kaolin is added in adding at last, and being incubated to tackiness agent does not have bubble.
Embodiment 2
Insect adhesive, the component that it is formed and the mass ratio of each component are as follows:
40 parts of EVA (ethene-vinyl acetate);
20 parts of CSM (chlorosulfonated polyethylene);
6 parts of polymerized rosines;
6 parts of staybelites;
2 parts of antioxidant Ds;
15 parts in mineral oil;
5 parts in Vaseline;
6 parts of kaolin.
The preparation method of this insect adhesive may further comprise the steps:
1) behind the adding mineral oil, it is heated to 140 ℃, adds EVA, CSM in proportion, stir then, until abundant dissolving;
2) add polymerized rosin, staybelite, stir, fully after the dissolving, be evacuated to no bubble;
3) be cooled to 80 ℃, add anti-aging agent, Vaseline then;
4) material kaolin is added in adding at last, and being incubated to tackiness agent does not have bubble.
Embodiment 3
Difference between present embodiment and the embodiment 1 is, the mass ratio difference between the each component of insect adhesive.
Insect adhesive, the component that it is formed and the mass ratio of each component are as follows:
35 parts of EVA (ethene-vinyl acetate);
15 parts of CSM (chlorosulfonated polyethylene);
8 parts of polymerized rosines;
8 parts of staybelites;
3 parts of antioxidant Ds;
14 parts in mineral oil;
8 parts in Vaseline;
9 parts of kaolin.
The preparation method of this insect adhesive may further comprise the steps:
1) behind the adding mineral oil, it is heated to 130 ℃, adds EVA, CSM in proportion, stir then, until abundant dissolving;
2) add polymerized rosin, staybelite, stir, fully after the dissolving, be evacuated to no bubble;
3) be cooled to 70 ℃, add anti-aging agent, Vaseline then;
4) material kaolin is added in adding at last, and being incubated to tackiness agent does not have bubble.
During use, the surface that insect adhesive of the present invention is directly spread upon adhering sheet (yellow plate, fiber board etc.) gets final product.
With the yellow plate of insect sticker is example, and insect adhesive is directly spread upon the two sides of yellow plate, gets the glue-line surface at insect adhesive then and pastes one deck waterproofing membrane, be i.e. the yellow plate of the insect sticker of system.Time spent tears waterproofing membrane off and gets final product.The yellow plate of this insect sticker can be 50 ℃ of insulations 30 days down, and gummosis is less than 1mm, it is hung on outdoor, two months no catabiosis.
The yellow plate of insect sticker field result of use test: for example in the apple orchard, June before spiraea aphid generation alate is migrated the phase 10 was fixed in the orchard with yellow plate, the plate face that makes yellow plate is towards parallel with the tree row, the suspension height of yellow plate and tree crown are fair, and each processing is established containing adult of 30,40,50 blocks of three different yellow plates and sent out device to containing a latter stage, hangs about 10 days, take off yellow plate, investigate yellow plate, spiraea aphid quantity is added up, and insecticidal effect is estimated.
Field experiment is the result show, as shown in table 1, yellow plate just has good trapping effect to spiraea aphid, the yellow plate of specification minimum preventive effect to spiraea aphid under least density has reached 64.9%-76.5%, has arrived 84.5%-87.6% in yellow plate preventive effect to spiraea aphid under the highest density of specification maximum.
The yellow plate of table 1 is to the experimental result of preventing and treating of apple spiraea aphid
More than show and described ultimate principle of the present invention, principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in the foregoing description and the specification sheets is principle of the present invention; the present invention also has various changes and modifications without departing from the spirit and scope of the present invention, and these changes and improvements all fall in the claimed scope of the present invention.The protection domain that the present invention requires is defined by appending claims and equivalent thereof.
Claims (3)
1. insect adhesive is characterized in that, includes following component:
EVA 30-40 part;
CSM 10-20 part;
Polymerized rosin 5-10 part;
Staybelite 5-10 part;
Antioxidant D 1-5 part;
Mineral oil 10-15 part;
Vaseline 5-10 part;
Kaolin 5-10 part; More than be mass ratio.
2. the preparation method of an insect adhesive is characterized in that, may further comprise the steps:
1) behind the adding mineral oil, it is heated, add EVA, CSM then in proportion, stir then, until abundant dissolving;
2) add polymerized rosin, staybelite, stir, fully after the dissolving, be evacuated to no bubble;
3) be cooled to 70 ℃-80 ℃, add anti-aging agent, Vaseline then;
4) material kaolin is added in adding at last, and being incubated to tackiness agent does not have bubble.
3. the preparation method of insect adhesive according to claim 2 is characterized in that, before adding EVA, CSM, earlier mineral oil is heated to 130 ℃-140 ℃.