CN101824748A - 一种采用防紫外线整理剂的整理方法 - Google Patents
一种采用防紫外线整理剂的整理方法 Download PDFInfo
- Publication number
- CN101824748A CN101824748A CN 201010139917 CN201010139917A CN101824748A CN 101824748 A CN101824748 A CN 101824748A CN 201010139917 CN201010139917 CN 201010139917 CN 201010139917 A CN201010139917 A CN 201010139917A CN 101824748 A CN101824748 A CN 101824748A
- Authority
- CN
- China
- Prior art keywords
- shirt
- csa
- quality
- sorting
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种采用防紫外线整理剂的整理方法,包括:(1)以SPAN80、Tween80、OP-15按质量比2~5∶2~5∶1混合配制复合乳化剂,再与质量比CSA-1按5~10∶90~95混合配制CSA-1乳液;(2)将CSA-1乳液与硫酸铵、纳米金属氧化物混合配制成整理液;(3)浸渍衬衣或T恤,升温、保温、甩干、烘干后得到防紫外线衬衣或T恤。本发明工艺简单,过程简短,适合大规模生产,整理后的衬衣、T恤能有效的阻挡紫外线,具有防暑、隔热、触感凉爽的性能。
Description
技术领域
本发明属防紫外线衣物的制备领域,特别是涉及一种采用防紫外线整理剂的整理方法。
背景技术
紫外线根据波长分为3部分:UVA(波长315~400nm),UVB(波长280315nm)和UVC(波长185~280nm)。其中UVC能量很高,但几乎完全被臭氧层吸收,不能到达地面;UVB波长较短能量较高,可以穿透皮肤几毫米,使皮肤产生黑色素,出现晒黑和晒斑,如果晒黑和晒斑反复发生,会增加患黑色素瘤的危险。UVA波长较长,能量较低,几乎全部到达地面,它能穿透真皮,使皮肤过早老化,失去弹性,出现皱纹。因此UVA和UVB是紫外线防护的主要目标。上世纪20年代以来,由于碳氟系溶剂和氟利昂的大量使用,地球大气层中臭氧层遭到严重的破坏,使到达地球表面的紫外线不断增加,对环境带来严重危害。因此,防止过量紫外线对人体的伤害成为非常重要的研究课题。
上世纪90年代后,防紫外线织物骤然兴起,其中以日本公司最为突出,他们相继推出具有防紫外线辐射功能的运动服、衬衫、长筒袜、帽子和太阳伞等制品,受到广大消费者的青睐。制备防紫外线衬衣、T恤方法之一是通过在衬衣、T恤上施加一种能反射紫外线或能选择性吸收紫外线的物质。施加这些物质后的衬衣、T恤,对织物各项服用性无不良影响,并达到使用要求,还可以增加织物对紫外线的反射和散射作用,防止透过织物,具有防暑、隔热、触感凉爽的性能。从光学原理上讲,光射到物体上,有一部分在表面反射,部分被物体吸收,其余的则透过物体。经防紫外线辐射屏蔽剂整理的织物,光射到织物上,织物上的紫外线屏蔽剂不是将紫外线反射,就是选择性吸收并将其能量转换成低能而释放,以致将紫外线遮蔽,而另一小部分通过织物的间隙透过织物。
发明内容
本发明所要解决的技术问题是提供一种采用防紫外线整理剂的整理方法。本发明工艺简单,过程简短,适合大规模生产,整理后的衬衣、T恤能有效的阻挡紫外线,具有防暑、隔热、触感凉爽的性能。
本发明的一种采用防紫外线整理剂的整理方法,包括:
(1)以SPAN80、Tween80和OP-15按质量比2~5∶2~5∶1混合配制复合乳化剂,再将复合乳化剂与CSA-1按质量比5~10∶90~95混合配制成所需CSA-1乳液;
(2)将相对T恤或衬衣质量2~5%的CSA-1乳液,相对CSA-1乳液质量10~15%的硫酸铵,相对T恤或衬衣质量0.5~2%的纳米金属氧化物混合均匀,补余量水,配制整理液;
(3)浸渍衬衣或T恤,升温至60~85℃,保温30~45min,甩干、烘干后得到防紫外线衬衣、T恤。
所述步骤(1)中的SPAN80、Tween80和OP-15质量比为4∶5∶1或2∶2∶1。
所述步骤(1)中的复合乳化剂与CSA-1的质量比为10∶90或5∶95。
所述步骤(2)中的CSA-1乳液的质量为相对T恤或衬衣质量的3~3.5%。
所述步骤(2)中的硫酸铵的质量为相对CSA-1乳液质量的10~15%。
所述步骤(2)中的纳米金属氧化物的质量为相对T恤或衬衣质量的1.5%。
所述步骤(2)中的纳米金属氧化物为纳米氧化锌、氧化钛、氧化锆中的一种。
所述步骤(3)中的升温温度为60℃,保温时间为30min。
本发明所使用的防紫外线整理剂为有机酸酐类化合物CSA-1,结构如下:
上海化学试剂采购站提供,也可以自己合成。
有益效果
(1)本发明工艺简单,过程简短,适合大规模生产;
(2)整理后的衬衣、T恤能有效的阻挡紫外线,具有防暑、隔热、触感凉爽的性能。
具体实施方式
下面结合具体实施例,进一步阐述本发明。应理解,这些实施例仅用于说明本发明而不用于限制本发明的范围。此外应理解,在阅读了本发明讲授的内容之后,本领域技术人员可以对本发明作各种改动或修改,这些等价形式同样落于本申请所附权利要求书所限定的范围。
以下实施例中,使用的仪器设备有RY-25012型常温染样机(上海龙灵电子科技有限公司),U3310双光束紫外分光光度仪(日本日立公司),JRJ-300-I剪切乳化搅拌机(上海标本模型厂),UV1000F型织物紫外线测试仪(美国Labshere公司);织物紫外线透过率和UPF值的测定分别按GB/T 18830-2002(纺织品防紫外线性能的评定)测试整理后织物的紫外线透过率(T)和织物的UPF值。
实施例1
以SPAN80:Tween80:OP-15不同比例配制复合乳化剂,制备CSA-1不同浓度的乳液,其结果见表1;
表1
由表1可见,按表1中的6个配方配制的CSA-1乳液可以满足即配即用的要求,其中(5),(3),(4)号配制的乳液稳定相对时间较长。
实施例2
配制整理液:CSA-1乳液(实施例1中的(1)号配方)3.5%(CSA-1的质量对T恤的质量),硫酸铵10%(对CSA-1乳液的质量),加入纳米氧化锌1.5%(相对T恤的质量),补余量水。浸渍T恤→升温60℃,保温30min→甩干→烘干。测定UPF值、UVA透过率、UVB透过率,如表2。
表2
实施例3
配制整理液:CSA-1乳液(实施例1中的(3)号配方)3%(CSA-1的质量对T恤的质量),硫酸铵10%(对CSA-1乳液的质量),加入纳米氧化钛1.5%(相对T恤的质量),
补余量水。浸渍衬衣→升温60℃,保温30min→甩干→烘干。测定UPF值、UVA透过率、UVB透过率,如表3。
表3
实施例4
配制整理液:CSA-1乳液(实施例1中的(5)号配方)3.5%(CSA-1的质量对T恤的质量),硫酸铵10%(对CSA-1乳液的质量),加入纳米氧化锆1.5%(相对T恤的质量),补余量水。浸渍衬衣→升温60℃,保温30min→甩干→烘干。测定UPF值、UVA透过率、UVB透过率,如表4。
表4
Claims (8)
2.根据权利要求1所述的一种采用防紫外线整理剂的整理方法,其特征在于:所述步骤(1)中的SPAN80、Tween80和OP-15的质量比为4∶5∶1或2∶2∶1。
3.根据权利要求1所述的一种采用防紫外线整理剂的整理方法,其特征在于:所述步骤(1)中的复合乳化剂与CSA-1的质量比为10∶90或5∶95。
4.根据权利要求1所述的一种采用防紫外线整理剂的整理方法,其特征在于:所述步骤(2)中的CSA-1乳液的质量为相对T恤或衬衣质量的3~3.5%。
5.根据权利要求1所述的一种采用防紫外线整理剂的整理方法,其特征在于:所述步骤(2)中的硫酸铵的质量为相对CSA-1乳液质量的10~15%。
6.根据权利要求1所述的一种采用防紫外线整理剂的整理方法,其特征在于:所述步骤(2)中的纳米金属氧化物的质量为相对T恤或衬衣质量的1.5%。
7.根据权利要求1或6所述的一种采用防紫外线整理剂的整理方法,其特征在于:所述步骤(2)中的纳米金属氧化物为纳米氧化锌、氧化钛、氧化锆中的一种。
8.根据权利要求1所述的一种采用防紫外线整理剂的整理方法,其特征在于:所述步骤(3)中的升温温度为60℃,保温时间为30min。