CN101791785A - 一种可调整硬度级别的金刚石磨块 - Google Patents

一种可调整硬度级别的金刚石磨块 Download PDF

Info

Publication number
CN101791785A
CN101791785A CN 201010127496 CN201010127496A CN101791785A CN 101791785 A CN101791785 A CN 101791785A CN 201010127496 CN201010127496 CN 201010127496 CN 201010127496 A CN201010127496 A CN 201010127496A CN 101791785 A CN101791785 A CN 101791785A
Authority
CN
China
Prior art keywords
diamond
rubbing block
cryolite
block
hardness level
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 201010127496
Other languages
English (en)
Other versions
CN101791785B (zh
Inventor
沈衡平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2010101274960A priority Critical patent/CN101791785B/zh
Publication of CN101791785A publication Critical patent/CN101791785A/zh
Application granted granted Critical
Publication of CN101791785B publication Critical patent/CN101791785B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种可调整硬度级别的金刚石磨块，包括胎体粉料、碳粒和金刚石，其特征是所述胎体粉料中添加有冰晶石(Na3AlF6)。本发明的金刚石磨块的特点是采用了一种特殊材料冰晶石(Na3AlF6)。冰晶石是一种络合物、溶点为1025℃微溶于水，烧结时(850℃以下)不分解。在磨削时由于高速磨擦受磨削热和阻力作用，在大量水的作用下促成其分解，使得金属胎体的机械强度和耐磨性能发生改变，因此可以改变金刚石的自锐性，达到调整金刚石磨块硬度级别的目的，使金刚石磨块既有切削力，又有一定的耐磨性。本金刚石磨块可以满足不同瓷砖、石材材质在不同机型设备上对抛光的要求，提高生产效率和降低成本。

Description

一种可调整硬度级别的金刚石磨块
技术领域
本发明属于陶瓷、石材等抛光材料，具体涉及一种可调整硬度级别的金刚石磨块。
背景技术
磨块是陶瓷、石材端面抛光的主要工具，抛光分：粗、中、细三段。传统抛光用磨块是指：用氧化镁作结合剂、氯化镁作调和剂、碳化硅作磨料，自然固化而成。粗、中段磨块使用寿命在2小时左右，精磨段磨块使用寿命在3-8小时之间，存在消耗大，更换次数多，环境污染大等缺点。
金刚石磨块主要用于粗段的磨削，取代部分普通磨块。它是用胎体粉料(包括铜、铁、镍、锌、锡、锰、钛、铝、铬、钴等金属粉料)作结合剂，人造金刚石作磨料，将它们混合后通过高温低压烧结而成，其耐磨性是普通磨块的100倍左右。
由于陶瓷、石材产品种类繁多，对于抛光各有不同要求，生产线必须根据产品的不同随时需要不同硬度级别的磨块。现有的金刚石磨块，由于其品种规格单一，硬度级别不能调整，无法适应各种板材和各种机型磨削的不同要求，达不到正常使用的目的，使得生产效率不高，成本增加。
发明内容
针对上述问题，本发明的目的是提供一种可调整硬度级别的金刚石磨块，这种金刚石磨块可以适应不同瓷砖、石材材质对抛光的要求，提高抛光生产效率和降低成本。
实现本发明目的采用的技术方案是：本发明的可调整硬度级别的金刚石磨块，包括胎体粉料、碳粒和金刚石，其特征是所述胎体粉料中添加有冰晶石(Na3AlF6)；其组分的质量百分比含量为：
胎体粉料80-94％，冰晶石2-10％，碳粒1-10％，金刚石2.6-4.0％；
所述胎体粉料为：
Fe-Cu-663Cu-Ni；
Fe-Cu-Sn；
Fe-Cu-Sn-Ti；
Fe-Cu-Sn-Mn；
Fe-Cu-Sn-Al；
Fe-Cu-663Cu-Al-Ni；
Fe-Cu-Sn-Al-Zn-Ni；
Fe-Cu-Al-Sn-Zn-Pb-Ni。
本发明的金刚石磨块的特点是采用了一种特殊材料冰晶石(Na3AlF6)。冰晶石是一种络合物、溶点为1025℃微溶于水，烧结时(850℃以下)不分解。在磨削时由于高速磨擦受磨削热和阻力作用，在大量水的作用下促成其分解，使得金属胎体的机械强度和耐磨性能发生改变，因此可以改变金刚石的自锐性，达到调整金刚石磨块硬度级别的目的，使金刚石磨块既有切削力，又有一定的耐磨性。冰晶石的含量越高，金刚石磨块的硬度级别越低。碳粒可以起到部分替代冰晶石的作用。
本发明的金刚石磨块可以根据不同瓷砖、石材材质在不同机型设备上对抛光的要求，通过添加或减少冰晶石的含量来调节金刚石磨块的硬度级别，以满足生产的需要，提高生产效率和降低成本。目前，本发明产品经在七个陶瓷厂家，二十多条抛光线上试用仅一年时间，便完全取代了“46#、54#、60#、80#、100#、120#、150#180#的粗段普通磨块。
下面结合实施例详细说明本发明技术方案。
具体实施方式
可调整硬度级别的金刚石磨块采用的不同配方(质量％)如下：
可调整硬度级别的金刚石磨块可按现有方法进行制作，其步骤包括：
1、配料：
按上述实施例的配方配料，其中金刚石选用低品级(JR1和JR2)，根据磨块的号数采用单号或混合JR1+JR2使用，金刚石粒度从80目-320目；
2、混合：
用混料机将步骤1的配料混合搅拌；
3、冷压：
按普通磨块的基本尺寸设计冷压模，压胎尺寸为：164×62×17(mm)，厚度中心点为17mm，顶面为弧形，结构采用面层加底层，配料作为面层，用量550-600g/每个，底层采用：铜、铁、锡合金粉，用量为250-350g/每个，模压制成冷压胎体；
4、烧结：
将冷压胎体用电加热炉进行烧结成半成品；
5、组装
在半成品底层钻孔，将其固定在塑料卡座上即成成品磨块。
成品磨块的规格分：46#、54#、60#、80#、100#、120#、150#、180#。硬度级别分四个，如100#A、100#B、100#C、100#D，A级硬度最高，D级硬度最低，各级别的金刚石磨块在抛光机上的磨削时间都可控制在110-170小时以内。

Claims (1)

1.一种可调整硬度级别的金刚石磨块，包括胎体粉料、碳粒和金刚石，其特征是所述胎体粉料中添加有冰晶石；其组分的质量百分比含量为：
胎体粉料80-94％，冰晶石2-10％，碳粒1-10％，金刚石2.6-4.0％；
所述胎体粉料为：
Fe-Cu-663Cu-Ni；
Fe-Cu-Sn；
Fe-Cu-Sn-Ti；
Fe-Cu-Sn-Mn；
Fe-Cu-Sn-Al；
Fe-Cu-663Cu-Al-Ni；
Fe-Cu-Sn-Al-Zn-Ni；
Fe-Cu-Al-Sn-Zn-Pb-Ni。
CN2010101274960A 2010-03-19 2010-03-19 一种可调整硬度级别的金刚石磨块 Expired - Fee Related CN101791785B (zh)