CN101760077B - 水性二苯基乙烯纸杯柔版油墨及其制备方法 - Google Patents
水性二苯基乙烯纸杯柔版油墨及其制备方法 Download PDFInfo
- Publication number
- CN101760077B CN101760077B CN200910214444.4A CN200910214444A CN101760077B CN 101760077 B CN101760077 B CN 101760077B CN 200910214444 A CN200910214444 A CN 200910214444A CN 101760077 B CN101760077 B CN 101760077B
- Authority
- CN
- China
- Prior art keywords
- percent
- aqueous
- mixture
- diphenyl
- flexographic printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开一种水性二苯基乙烯纸杯柔版墨,其组分及制备方法为:先将苯乙烯丙烯酸树脂碱溶性树脂30~40%、水15~20%、有机颜料10~25%、硅烷类消泡剂0.2~0.5%、水性氯甲基/甲基异噻唑啉酮混合体防腐剂0.1~0.3%、有机硅分散剂0.3~0.6%进行混合;再用砂磨机将混合物A磨至细度为5μm~10μm的混合物,接着加入苯乙烯-丙烯酸共聚成膜半自交联型乳液30~40%、非成膜性硬性苯乙烯-丙烯酸共聚乳液5~10%、聚四氟乙烯蜡2~4%、氟碳有机硅流平剂0.3~0.8%、硅油0.2~0.5%、乙醇胺0.2~0.5%、丙二醇1~3%并充分搅拌均匀,最后制得产物。本产品具有良好的附着力、抗磨性和抗冻性,另外该产品具有耐酸、耐碱、耐水、耐温、耐光的特性,并且也无毒性,应用前景十分广泛。
Description
技术领域
本发明涉及印刷油墨领域,具体涉及一种水性二苯基乙烯(DPE)纸杯柔版油墨及其制备方法。
背景技术
随着人民生活水平的提高,对食品包装也提出了更高的要求,油墨在包装中格外引人关注。油墨作为印刷材料,应满足各种不同的功能要求,如无毒、耐热、耐寒、耐溶剂、耐油、耐摩擦等。国际公认食品印刷所用油墨必须遵守无转移的原则;食品包装物内表面印刷时不得使用常规油墨;承印厂商必须确保印刷后油墨中的溶剂全部挥发,并达到应用行业的相应标准,而纸杯属于食品包装的一种。
由于国家环保意识的加强,为了符合绿色包装的需要,要求包装产品安全、卫生,对环境保护有良好的适应性,能节约资源。纸杯的生产和使用正好符合国家环保政策,用纸杯代替一次性塑料杯减少了“白色污染”,纸杯的方便卫生价廉性是代替其他器皿广泛占有市场的关键。纸杯主要分为DPE和单PE的纸杯。
目前我国DPE纸杯主要使用溶剂型油墨,该类油墨无论是制造和使用技术都已成熟,虽然这种油墨的印刷适性优良,印后加工性能好、干燥快,但含有大量有害溶剂,如苯、甲苯、二甲苯等,苯超标的话就会引起癌症,特别是血液系统疾病。此外,油墨中的重金属如汞、铅、砷等含量也对人体存在极大的危害。溶剂油墨在干燥过程中排放出的有机化合物、异丙醇的挥发气体等均对人体有害,纸杯属于人口接触产品,容易将上述的各种化学物质随液体一起带入体内影响身体健康。因此,油墨的重金属、溶剂残留必须达到卫生安全性能指标,符合食品卫生法和相应的食品包装卫生标准。
DPE纸杯对油墨要求较高,主要因为水性油墨印刷的基材是聚乙烯(PE)膜,PE膜的附着力一般不好,所以对油墨的配方要求比较高.对油墨的要求体现在:附着力好,干燥快,耐磨,防水,抗冻,这几方面的要求比较高,所以油墨的配方对树脂,色粉,添加剂的选择上的限制有一定的难度.单PE对油墨的要求不算高,因为单PE水性油墨是印刷在纸张上的,所以对油墨的附着力和干燥方面要求不高,一般水墨都可做到。用于纸杯的印刷油墨要求印刷的牢度要好,印刷品有良好耐酸、耐碱、耐水、耐温、耐光性,不会因这些因素的作用发生褪色、变色、脱落现象;另印刷品要有良好的耐刮性。
有鉴于此,本发明在经过一系列的研究和试验的基础上,主要解决普通水性油墨在DPE纸杯上不耐水、附着力差、干燥慢、不抗冻、易堵网的问题,本案由此产生。
发明内容
本发明的目的在于提供一种水性二苯基乙烯(DPE)纸杯柔版油墨,以解决普通水性油墨在DPE纸杯上不耐水、附着力差、干燥慢、不抗冻、易堵网的问题。
为了实现此目的,本发明的解决方案如下:
水性二苯基乙烯纸杯柔版油墨,按重量百分比由以下组分组成:
所述有机颜料选自酞菁蓝BGS、联苯胺黄GR、永固黄2GS或永固桃红FBB中的至少一种。
该水性二苯基乙烯纸杯柔版油墨的制备方法如下:
先将苯乙烯丙烯酸树脂碱溶性树脂、水、有机颜料、硅烷类消泡剂、水性氯甲基/甲基异噻唑啉酮混合体防腐剂、有机硅分散剂进行混合,得混合物A;再用砂磨机将混合物A磨至细度为5μm~lOμm的混合物粉末B,接着往混合物粉末B加入苯乙烯-丙烯酸共聚成膜半自交联型乳液、非成膜性硬性苯乙烯-丙烯酸共聚乳液、聚四氟乙烯蜡、氟碳有机硅流平剂、硅油、乙醇胺、丙二醇并充分搅拌均匀,最后制得产物。
本发明以水为主要溶剂,具有良好的附着力、抗磨性和抗冻性,另外该产品具有耐酸、耐碱、耐水、耐温、耐光的特性。并且也无毒性。具有良好的使用性能,应用前景十分广泛。
具体实施方式
下面结合实例对本发明作进一步的描述。
实施例1
一种水性二苯基乙烯纸杯柔版油墨;包括以重量百分比计的30%苯乙烯-丙烯酸共聚成膜半自交联型乳液、10%苯乙烯丙烯酸树脂碱溶性树脂、5%非成膜性硬性苯乙烯-丙烯酸共聚乳液、0.3%有机硅分散剂、0.2%硅烷类消泡剂、0.2%硅油、0.2%MEA、1%丙二醇、0.1%水性氯甲基/甲基异噻唑啉酮(CMI/MI)混合体防腐剂、2%聚四氟乙烯蜡、0.3%氟碳有机硅流平剂、15%有机颜料、15%水。
制备方法:先将上述量的苯乙烯丙烯酸树脂碱溶性树脂、水、有机颜料、硅烷类消泡剂、水性氯甲基/甲基异噻唑啉酮(CMI/MI)混合体防腐剂、有机硅分散剂进行混合,得混合物A;再用砂磨机将混合物A磨至细度为10μm的混合物粉末B,接着往混合物粉末B加入苯乙烯-丙烯酸共聚成膜半自交联型乳液、非成膜性硬性苯乙烯-丙烯酸共聚乳液、聚四氟乙烯蜡、氟碳有机硅流平剂、硅油、乙醇胺、丙二醇并充分搅拌均匀,最后制得产物。
实施例2
一种水性二苯基乙烯纸杯柔版油墨;包括以重量百分比计的35%苯乙烯-丙烯酸共聚成膜半自交联型乳液、15%苯乙烯丙烯酸树脂碱溶性树脂、10%非成膜性硬性苯乙烯-丙烯酸共聚乳液、0.4%有机硅分散剂聚氧乙烯醚、0.3%硅烷类消泡剂乳化硅油、0.3%硅油、0.3%MEA、1%丙二醇、0.2%水性氯甲基/甲基异噻唑啉酮(CMI/MI)混合体防腐剂、3%聚四氟乙烯蜡、0.5%氟碳有机硅流平剂、20%有机颜料、17%水。
制备方法同实施例1,其中不同点在于混合物粉末B的细度为6μm,防水性稍提高,水洗后少许脱色,附着力达到4级,滑爽性稍有提高,滑度角达20度,抗磨性稍有改善,可耐磨21b,100次。
实施例3
一种水性二苯基乙烯纸杯柔版油墨;包括以重量百分比计的40%苯乙烯-丙烯酸共聚成膜半自交联型乳液、15%苯乙烯丙烯酸树脂碱溶性树脂、8%非成膜性硬性苯乙烯-丙烯酸共聚乳液、0.6%有机硅分散剂聚氧乙烯醚、0.5%硅烷类消泡剂乳化硅油、0.5%硅油、0.5%MEA、3%丙二醇、0.3%水性氯甲基/甲基异噻唑啉酮(CMI/MI)混合体防腐剂、4%聚四氟乙烯蜡、0.8%氟碳有机硅流平剂、25%有机颜料、20%水。
制备方法同实施例1,其中不同点在于混合物粉末B的细度达到5μm,抗水性能最佳,水洗后不脱色,附着力优异可达到5级,色泽饱满,转印性强,滑爽性提高,滑度角达15度,抗磨性提高,可耐磨21b,400次。
通过上述配方和方法制备的水性二苯基乙烯(DPE)纸杯柔版油墨解决了普通水性油墨在DPE纸杯上不耐水、附着力差、干燥慢、不抗冻、易堵网的问题,具有具有良好的附着力、抗磨性和抗冻性,具有耐酸、耐碱、耐水、耐温、耐光的特性,并且无毒性,应用前景广泛。
可以理解,在本产品制备过程中很多细节的变化是可能的,但这并不因此违背本发明的范围和精神,任何所属技术领域的普通技术人员对其所做的适当变化,皆应视为不脱离本发明专利的范畴。
Claims (4)
1.水性二苯基乙烯纸杯柔版油墨,其特征在于按重量百分比由以下组分组成:
2.如权利要求1所述的水性二苯基乙烯纸杯柔版油墨,其特征在于:所述有机颜料选自酞菁蓝BGS、联苯胺黄GR、永固黄2GS或永固桃红FBB中的至少一种。
3.如权利要求1所述的水性二苯基乙烯纸杯柔版油墨,其特征在于:所述有机硅分散剂为有机硅分散剂聚氧乙烯醚,所述硅烷类消泡剂为乳化硅油。
4.如权利要求l或2或3所述的水性二苯基乙烯纸杯柔版油墨,其特征在于:其制备方法如下:先将苯乙烯丙烯酸树脂碱溶性树脂、水、有机颜料、硅烷类消泡剂、水性氯甲基/甲基异噻唑啉酮混合体防腐剂、有机硅分散剂进行混合,得混合物A;再用砂磨机将混合物A磨至细度为5μm~10μm的混合物粉末B,接着往混合物粉末B加入苯乙烯-丙烯酸共聚成膜半自交联型乳液、非成膜性硬性苯乙烯-丙烯酸共聚乳液、聚四氟乙烯蜡、氟碳有机硅流平剂、硅油、乙醇胺、丙二醇并充分搅拌均匀,最后制得产物。