CN101758369A - 钛及钛合金法兰加工工艺 - Google Patents

钛及钛合金法兰加工工艺 Download PDF

Info

Publication number
CN101758369A
CN101758369A CN200910254410A CN200910254410A CN101758369A CN 101758369 A CN101758369 A CN 101758369A CN 200910254410 A CN200910254410 A CN 200910254410A CN 200910254410 A CN200910254410 A CN 200910254410A CN 101758369 A CN101758369 A CN 101758369A
Authority
CN
China
Prior art keywords
titanium
titanium alloy
ingot
thickness
flange
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN200910254410A
Other languages
English (en)
Other versions
CN101758369B (zh
Inventor
常荣波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2009102544108A priority Critical patent/CN101758369B/zh
Publication of CN101758369A publication Critical patent/CN101758369A/zh
Application granted granted Critical
Publication of CN101758369B publication Critical patent/CN101758369B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种钛及钛合金法兰加工工艺，其按照如下步骤实施：在中空钛锭或钛合金锭表面包厚度不大于0.8mm的铜板，并焊接固定；包裹铜板的中空钛锭或钛合金锭加热至500度以上，通过挤压机挤压成为管型坯料；管型坯料按法兰的厚度通过线切割或者带锯切片，通过精加工---检验---成品。本发明针对宇航标准法兰的生产，提高标准的同时，达到降低生产成本，减少加工环节，节约加工时间，显著提高经济效益的目的。

Description

钛及钛合金法兰加工工艺
技术领域
本发明属于金属材料加工技术领域，特别是稀贵金属制品的加工工艺。
背景技术
传统钛合金法兰是通过自由锻造或者模锻加工，由于钛材的特性，表面容易氧化变硬，造成加工过程中产生折叠，形成裂纹，成品必须去除这些裂纹，既增加了加工成本又增加了原材料成本。
目前的自由锻造及模锻加工只能提供低端的民用标准产品。而对于高端的宇航标准却无能为力。
发明内容
本发明目的是提供一种钛及钛合金法兰加工工艺，针对宇航标准法兰的生产，提高标准的同时，达到降低生产成本，减少加工环节，节约加工时间，显著提高经济效益的目的。
实现本发明目的的钛及钛合金法兰加工工艺，其按照如下步骤实施：
(1)在中空钛锭或钛合金锭表面包厚度不大于0.8mm的铜板，并焊接固定；
(2)包裹铜板的中空钛锭或钛合金锭加热至500度以上，通过大型油压挤压机或者大型水压挤压机按照法兰的外径及壁厚挤压成为管型坯料；
(3)管型坯料按法兰的厚度通过线切割或者带锯切片，通过精加工---检验---成品。
在钛合金锭外同时包厚度不大于0.8mm铜板和相同厚度的不锈钢板并焊接固定。
挤压步骤中使用玻璃保护润滑剂。
本发明加工方法能够使金属间的结晶充分结合，形成致密的金属结构，从而增加了金属抗拉强度及使用寿命。完全可以满足宇航标准对金属结晶，高低倍，抗拉强度以及探伤的检测要求，同时提高了效率大幅度降低了成本。
本发明还可应用于其他金属以及大型环型金属的加工。
具体实施方式
本发明通过大型油压挤压机或者大型水压挤压机，使用中空钛锭表面包0.8mm铜板，钛合金需要包0.8mm铜板和相同厚度的不锈钢板，焊接固定。或者使用玻璃保护润滑剂。加热至500度以上，按照法兰的外径及壁厚挤压成为管型坯料。按法兰的厚度通过线切割或者带锯切片，精加工---检验---成品。

Claims (3)

1.钛及钛合金法兰加工工艺，其特征是按照如下步骤实施：
(1)在中空钛锭或钛合金锭表面包厚度不大于0.8mm的铜板，并焊接固定；
(2)包裹铜板的中空钛锭或钛合金锭加热至500度以上，通过大型油压挤压机或者大型水压挤压机按照法兰的外径及壁厚挤压成为管型坯料；
(3)管型坯料按法兰的厚度通过线切割或者带锯切片，通过精加工---检验---成品。
2.根据权利要求1所述的钛及钛合金法兰加工工艺，其特征是在钛合金锭外同时包厚度不大于0.8mm铜板和相同厚度的不锈钢板并焊接固定。
3.根据权利要求1所述的钛及钛合金法兰加工工艺，其特征是挤压步骤中使用玻璃保护润滑剂。
CN2009102544108A 2009-12-12 2009-12-12 钛及钛合金法兰加工工艺 Expired - Fee Related CN101758369B (zh)