CN101746997B - 一种海贝泥、硅藻泥墙面装饰壁材及其生产施工方法 - Google Patents
一种海贝泥、硅藻泥墙面装饰壁材及其生产施工方法 Download PDFInfo
- Publication number
- CN101746997B CN101746997B CN 200810188543 CN200810188543A CN101746997B CN 101746997 B CN101746997 B CN 101746997B CN 200810188543 CN200810188543 CN 200810188543 CN 200810188543 A CN200810188543 A CN 200810188543A CN 101746997 B CN101746997 B CN 101746997B
- Authority
- CN
- China
- Prior art keywords
- orders
- following
- parts
- powder
- wall surface
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种海贝泥、硅藻泥墙面装饰壁材及其生产施工方法，装饰壁材包括贝壳粉20-98份，二氧化硅硅石8-30份，硅藻土4-100份，麦饭石2-20份，云母粉3.8-48份，富镁硅酸盐2-10份，钙沸石6-26份，水合硅酸盐1.5-36份，二氧化钛粉末0-50份，碳酸钙2-50份，植物纤维0.1-0.3份，颜料1-30份，海带粉4.8-40份，冷溶型聚乙烯醇粉1-30份，羟丙基甲基纤维素1-20份；生产施工方法包括将各组分原料放入搅拌机中搅拌均匀；装入塑料袋中，装箱密封后入库；加水搅拌均匀；置于待装饰墙面上，做成各种肌理图案。本发明取得的有益效果是：(1)质地柔软、无毒害和不褪色不剥落开裂；(2)具有消除室内污染、调节室内湿度、消除异味、隔离噪音和肌理感强的特点；(3)防火阻燃；(4)色彩丰富。
Description
技术领域
本发明涉及一种墙面装饰壁材及其生产施工方法，特别是一种海贝泥、硅藻泥墙面装饰壁材及其生产施工方法。
背景技术
随着我国经济的高速发展，人们对自己居所的要求也越来越高，在墙面装修方面，从过去的用石灰刷墙和用报纸糊墙，到现在的用乳胶漆、墙纸、装饰布和装饰板来装饰墙面，充分体现了人们对墙面美观的需求，但是，目前广泛使用的墙面装饰涂料所带来的空气污染已成为严重影响人们身体健康的杀手，因此市场上出现了一种墙面装饰涂料，该涂料以无机料状骨材、粉体和无机多孔粉体为主要成份，其优点是不会损害人们的身体健康，但同时由于用料配比不当以及自身的原因，也存在不少缺陷：1)颜色单一，只有灰白色一种颜色，无法满足人们对多采多姿墙面的追求；2)肌理感差，手感粗糙、生硬，容易伤及人们的皮肤；3)吸附性差，不能对室内其它设施释放的有害气体进行吸附；4)长期使用后，容易出现开裂和脱落的现象。
发明内容
本发明要解决的问题是：提供一种海贝泥、硅藻泥墙面装饰壁材，该墙面装饰壁材以海洋生物中的藻类和贝类作为主要原料，使用该壁材装饰后的墙面，能消除室内污染、呼吸调节室内湿度、防火阻燃、隔离噪音，消除异味、保湿隔热、色彩丰富、机理感强、质地柔软且长期使用不褪色、不剥落开裂。
为了解决上述技术问题，本发明的海贝泥、硅藻泥墙面装饰壁材，各组分的重量份数比为：
800目以下的贝壳粉20-98份；
二氧化硅硅石8-30份；
2000目以下的硅藻土4-100份；
10-120目的麦饭石2-20份；
100目以下的云母粉3.8-48份
2000目以下的富镁硅酸盐2-10份；
200目以下的钙沸石6-26份；
100目以下的水合硅酸盐1.5-36份；
二氧化钛粉末10-50份；
200目以下的碳酸钙2-50份；
植物纤维0.1-0.3份
颜料1-30份；
20-200目的海带粉4.8-40份；
冷溶型聚乙烯醇粉1-30份；
羟丙基甲基纤维素1-20份。
本发明的海贝泥、硅藻泥墙面装饰壁材，优选的各组分的重量份数比为：
800目以下的贝壳粉30-90份；
二氧化硅硅石10-25份；
2000目以下的硅藻土8-60份；
10-120目的麦饭石5-15份；
100目以下的云母粉8-30份；
2000目以下的富镁硅酸盐3-8份；
200目以下的钙沸石8-25份；
100目以下的水合硅酸盐5-24份；
二氧化钛粉末20-40份；
200目以下的碳酸钙5-35份；
植物纤维0.15-0.25份
颜料3-25份；
20-200目的海带粉9-33份；
冷溶型聚乙烯醇粉5-25份；
羟丙基甲基纤维素2-18份。
本发明的海贝泥、硅藻泥墙面装饰壁材，更优的各组分的重量份数比为：
800目以下的贝壳粉40-70份；
二氧化硅硅石15-20份；
2000目以下的硅藻土15-45份；
10-120目的麦饭石10-12份；
100目以下的云母粉10-25份
2000目以下的富镁硅酸盐4-6份；
200目以下的钙沸石12-20份；
100目以下的水合硅酸盐8-16份；
二氧化钛粉末25-35份；
200目以下的碳酸钙10-25份；
植物纤维0.18-0.22份
颜料10-20份；
20-200目的海带粉13-22份；
冷溶型聚乙烯醇粉10-20份；
羟丙基甲基纤维素5-15份。
本发明的海贝泥、硅藻泥墙面装饰壁材，所述二氧化硅硅石的二氧化硅含量≥95％。
本发明要解决的另外一个问题是：提供一种海贝泥、硅藻泥墙面装饰壁材的生产施工方法。
为了解决上述技术问题，本发明的海贝泥、硅藻泥墙面装饰壁材生产施工方法，主要包括如下步骤：
1)将各组分的原料放入搅拌机中搅拌均匀，搅拌均匀后的材料即为海贝泥、硅藻泥墙面装饰壁材；
2)将搅拌好的壁材装入塑料袋中，转箱密封后，入库；
3)将壁材倒入桶中，加入适量的水，搅拌均匀，搅拌均匀后的壁材呈粘稠状；
4)采用喷涂或刮批的方式将粘稠状壁材置于待装饰墙面上，并做成各种肌理图案。
本发明取得的有益效果是：(1)贝壳粉具有质地柔软，白度好、无毒、粘结性好和抗腐蚀能量强的特点，因此，在本壁材中加入贝壳粉，使得本壁材具有质地柔软、无毒害和长期使用不褪色不剥落开裂的特点；(2)硅藻土具有很强的吸附力、隔音效果好的特点，而且可以调节涂层的光洁度和辉度，因而具有消除室内污染、调节室内湿度、消除异味、隔离噪音和肌理感强的特点；(3)本壁材的各组分燃点较高，因而具有防火阻燃的作用；(4)本壁材的各种组分可以跟多种颜色的颜料相融合，因而具有色彩丰富的特点。
具体实施方式：
实施例1
本实施例的海贝泥、硅藻泥墙面装饰壁材，各组分的重量份数比为：
800目以下的贝壳粉25份，
二氧化硅硅石25份，
2000目以下的硅藻土10份，
10-120目的麦饭石16份，
100目以下的云母粉5份，
2000目以下的富镁硅酸盐8份，
200目以下的钙沸石23份，
100目以下的水合硅酸盐2份，
二氧化钛粉末46份，
200目以下的碳酸钙4份，
植物纤维0.3份，
颜料5份，
20-200目的海带粉7份，
冷溶型聚乙烯醇粉27份，
羟丙基甲基纤维素2份；
二氧化硅硅石的二氧化硅含量为96.5％。
本实施例的海贝泥、硅藻泥墙面装饰壁材的生产施工方法，主要包括如下步骤：
1)将各组分的材料放入搅拌机中搅拌均匀，搅拌均匀后的材料即为海贝泥、硅藻泥墙面装饰壁材；
2)将搅拌好的壁材装入塑料袋中，装箱密封后，入库；
3)将壁材倒入桶中，加入适量的水，搅拌均匀，搅拌均匀后的壁材呈粘稠状；
4)采用喷涂或刮批的方式将粘稠状壁材置于待装饰墙面上，并做成各种肌理图案。
实施例2
本实施例的海贝泥、硅藻泥墙面装饰壁材，各组分的重量份数比为：
800目以下的贝壳粉35份，
二氧化硅硅石22份，
2000目以下的硅藻土10份，
10-120目的麦饭石14份，
100以下的云母粉9份，
2000目以下的富镁硅酸盐7份，
200目以下的钙沸石10份，
100目以下的水合硅酸盐22份，
二氧化钛粉末21份，
200目以下的碳酸钙33份，
植物纤维0.15份，
颜料23份，
20-200目的海带粉30份，
冷溶型聚乙烯醇粉23份，
羟丙基甲基纤维素13份；
二氧化硅硅石的二氧化硅含量为97.2％。
本实施例的海贝泥、硅藻泥墙面装饰壁材的生产施工方法，与实施例1相同。实施例3
本实施例的海贝泥、硅藻泥墙面装饰壁材，各组分的重量份数比为：
800目以下的贝壳粉45份，
二氧化硅硅石18份，
2000目以下的硅藻土30份，
10-120目的麦饭石11份，
100目以下的云母粉17份，
2000目以下的富镁硅酸盐5份，
200目以下的钙沸石16份，
100目以下的水合硅酸盐12份，
二氧化钛粉末30份，
200目以下的碳酸钙18份，
植物纤维0.20份，
颜料18份，
20-200目的海带粉19份，
冷溶型聚乙烯醇粉25份，
羟丙基甲基纤维素5份；
二氧化硅硅石的二氧化硅含量为98.8％。
本实施例的海贝泥、硅藻泥墙面装饰壁材的生产施工方法，与实施例1相同。
Claims (5)
1.一种海贝泥、硅藻泥墙面装饰壁材，其特征在于，是由按重量份数比计的以下组分组成：
800目以下的贝壳粉20-98份；
二氧化硅硅石8-30份；
2000目以下的硅藻土4-100份；
10-120目的麦饭石2-20份；
100目以下的云母粉3.8-48份
2000目以下的富镁硅酸盐2-10份；
200目以下的钙沸石6-26份；
100目以下的水合硅酸盐1.5-36份；
二氧化钛粉末10-50份；
200目以下的碳酸钙2-50份；
植物纤维0.1-0.3份
颜料1-30份；
20-200目的海带粉4.8-40份；
冷溶型聚乙烯醇粉1-30份；
羟丙基甲基纤维素1-20份。
2.根据权利要求1所述的海贝泥、硅藻泥墙面装饰壁材，其特征在于，是由按重量份数比计的以下组分组成：
800目以下的贝壳粉30-90份；
二氧化硅硅石10-25份；
2000目以下的硅藻土8-60份；
10-120目的麦饭石5-15份；
100目以下的云母粉8-30份；
2000目以下的富镁硅酸盐3-8份；
200目以下的钙沸石8-25份；
100目以下的水合硅酸盐5-24份；
二氧化钛粉末20-40份；
200目以下的碳酸钙5-35份；
植物纤维0.15-0.25份
颜料3-25份；
20-200目的海带粉9-33份；
冷溶型聚乙烯醇粉5-25份；
羟丙基甲基纤维素2-18份。
3.根据权利要求2所述的海贝泥、硅藻泥墙面装饰壁材，其特征在于，是由按重量
份数比计的以下组分组成：
800目以下的贝壳粉40-70份；
二氧化硅硅石15-20份；
2000目以下的硅藻土15-45份；
10-120目的麦饭石10-12份；
100目以下的云母粉10-25份
2000目以下的富镁硅酸盐4-6份；
200目以下的钙沸石12-20份；
100目以下的水合硅酸盐8-16份；
二氧化钛粉末25-35份；
200目以下的碳酸钙10-25份；
植物纤维0.18-0.22份
颜料10-20份；
20-200目的海带粉13-22份；
冷溶型聚乙烯醇粉10-20份；
羟丙基甲基纤维素5-15份。
4.根据权利要求1-3任一项所述的海贝泥、硅藻泥墙面装饰壁材，其特征在于：所述二氧化硅硅石的二氧化硅含量≥95％。
5.一种根据权利要求1所述的海贝泥、硅藻泥墙面装饰壁材的生产施工方法，其特征在于：包括如下具体步骤：
1)将各组分的原料放入搅拌机中搅拌均匀，搅拌均匀后的材料即为海贝泥、硅藻泥墙面装饰壁材；
2)将搅拌好的涂料装入塑料袋中，装箱密封后，入库；
3)将涂料倒入桶中，加入适量的水，搅拌均匀，搅拌均匀后的涂料呈粘稠状；
4)采用喷涂或刮批的方式将粘稠状涂料置于待装饰墙面上，并做成各种肌理图案。