CN101717223A - Decorative material and preparation method thereof - Google Patents
Decorative material and preparation method thereof Download PDFInfo
- Publication number
- CN101717223A CN101717223A CN200910309887A CN200910309887A CN101717223A CN 101717223 A CN101717223 A CN 101717223A CN 200910309887 A CN200910309887 A CN 200910309887A CN 200910309887 A CN200910309887 A CN 200910309887A CN 101717223 A CN101717223 A CN 101717223A
- Authority
- CN
- China
- Prior art keywords
- resin
- preparation
- processing
- extrusion molding
- surface treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of the decoration and fitment material production process, in particular to a decorative material and a preparation method thereof. The decorative material is characterized by comprising the materials in percentage by weight: 60-80% of glass fiber and 20-40% of resin. The preparation method of the decorative material is characterized by comprises the following steps: preparing the materials in proportion; putting the prepared resin in a melting device and heating the resin at a controlled temperature of 60-90 DEG C to melt the resin; soaking the glass fiber in the resin solution; taking out and drying; conveying the dried product into a die; heaing, drawing and extruding at a controlled heating temperature of 60-140 DEG C; cutting the extruded and molded product according to needed areas; and processing the surface. The invention has the remarkable advantages of environmental protection, waterproofness, insulation, fire resistance, high strength, convenient transportation, and the like.
Description
Technical field:
The present invention relates to the decorating and renovating material technical field of producing, specifically a kind of finishing material and preparation method thereof.
Background technology:
Finishing material is meant and is used to fit up all kinds of civil construction things to improve its functions of use and attractive in appearance; the protection stability of agent structure under various environmental factorss and the material of construction and the goods thereof of weather resistance; mainly be divided into the two parts by use occasion; a part is outdoor material; a part is an indoor material; indoor material is further divided into real material; sheet material; sheet material; section bar; five types of wire rod; finishing material mainly contains grass; wood; stone; sand; brick; watt; cement; gypsum; asbestos; lime; glass; mosaic; pottery; paint; paper; metal; plastics; fabric etc., and various composite product.
Common floor decorative material mainly contains: (1) cement mortar surface, its advantage is that wear resisting property is good, use the widest, but there is sound insulation poor, nonelastic, shortcomings such as thermal conductivity is big, (2) marble ground, clean mark is attractive in appearance, be usually used in public areas such as luxurious hotel, but stone material Heavy Weight, folding strength is low, often there is harmful radiativity in stone material simultaneously, (3) timber floor, high resilience, thermal conductivity is little, give warm soft sensation, checker parquet flooring, durable in use, be used for the gymnasium more, studio, stage, banquet hall, yet timber floor can not be prevented fires, and can't satisfy the requirement of people for finishing material fire prevention aspect, and the facing plate is meant various wall slabs in the interior wall facial ornament material, wood dado or skin plate, material therefor has glued board, plastic plate etc., in recent years, the fire proof construction finishing material comes into the market successively, especially the glass magnesium plate formation fire partition that is applied to combining with keel, yet glass magnesium plate exists always and returns halogen, scum, thin-skinnedization of plate, and anti-folding, tension, shortcomings such as indexs such as resistance to impact shock are low.
Summary of the invention:
The present invention is in order to overcome the deficiencies in the prior art, at the present situation that has the finishing material production technology both at home and abroad now, provide a kind of can satisfy window limit, door limit, windowsill, payment to a porter and base plate decorate needs, have finishing material of multinomial advantages such as fire prevention, waterproof, insulation, exhausted combustion, shock resistance be strong and preparation method thereof simultaneously.
The technical measures that the present invention adopts are:
A kind of finishing material is characterized in that its component comprises glass fibre and resin, and each compositions in weight percentage is: glass fibre 60%-80%, resin 20%-40%.
A kind of preparation method of finishing material is characterized in that comprising the steps:
Steps A: get material by proportioning, getting resin is dropped in the melting appartus, resin is heated, temperature is controlled at 60 ℃-90 ℃, makes the resin fusing,
Step B: leached glass fiber is gone in the resin liquation, and after taking-up, dry processing,
Step C: will dry the back product and send in the mould, heat and pultrusion processing, in this process heating and temperature control at 60 ℃-140 ℃,
Step D: the product of extrusion molding is cut on demand, and carry out surface treatment.
The preparation method of a kind of device materials of the present invention is characterized in that step B can be braiding netted leached glass fiber and go in the resin liquation, and dry processing after taking-up.
The preparation method of a kind of device materials of the present invention is characterized in that the described surface treatment of step D is for carrying out surperficial roll printing decorative pattern processing to extrusion molding product among the step C.
The preparation method of a kind of device materials of the present invention is characterized in that the described surface treatment of step D is for carrying out the surface lacquer processing to extrusion molding product among the step C.
The preparation method of a kind of device materials of the present invention is characterized in that the described surface treatment of step D is for carrying out surperficial baking vanish processing to extrusion molding product among the step C.
The present invention adopts the glass fibre preparation finishing material that combines with resin, be mainly used in window limit, windowsill, door limit, the decoration needs on payment to a porter, floor etc., compared with prior art, can effectively avoid shortcomings such as environmental pollution, generation rubbish, transportation inconvenience, have significant advantages such as the equipment input is low, good product quality, waterproof, insulation, exhausted combustion, intensity height, non-modification.
Embodiment:
The present invention is in order to overcome the deficiencies in the prior art, at the present situation of existing finishing material production technology both at home and abroad, provides a kind of finishing material that has multinomial advantages such as fire prevention, waterproof, insulation, exhausted combustion, shock resistance be strong simultaneously and preparation method thereof.
The technical measures that the present invention adopts are:
A kind of finishing material is characterized in that its component comprises glass fibre and resin, and each compositions in weight percentage is: glass fibre 60%-80%, resin 20%-40%.
A kind of preparation method of finishing material is characterized in that comprising the steps:
Steps A: get material by proportioning, getting resin is dropped in the melting appartus, resin is heated, temperature is controlled at 60 ℃-90 ℃, makes the resin fusing,
Step B: leached glass fiber is gone in the resin liquation, and after taking-up, dry processing,
Step C: will dry the back product and send in the mould, heat and pultrusion processing, in this process heating and temperature control at 60 ℃-140 ℃,
Step D: the product of extrusion molding is cut on demand, and carry out surface treatment.
The preparation method of a kind of device materials of the present invention is characterized in that step B can be braiding netted leached glass fiber and go in the resin liquation, and dry processing after taking-up.
The preparation method of a kind of device materials of the present invention is characterized in that the described surface treatment of step D is for carrying out surperficial roll printing decorative pattern processing to extrusion molding product among the step C.
The preparation method of a kind of device materials of the present invention is characterized in that the described surface treatment of step D is for carrying out the surface lacquer processing to extrusion molding product among the step C.
The preparation method of a kind of device materials of the present invention is characterized in that the described surface treatment of step D is for carrying out surperficial baking vanish processing to extrusion molding product among the step C.
The present invention adopt glass fibre be combined with resin-phase the preparation ornament materials, be mainly used in the decoration needs on window limit, windowsill, door limit, baseboard, floor etc., compared with prior art, can effectively avoid the shortcomings such as environmental pollution, generation rubbish, transportation inconvenience, have the significant advantages such as equipment input is low, good product quality, waterproof, insulation, absolutely combustion, intensity height, non-modification.
Claims (5)
1. a finishing material is characterized in that its component comprises glass fibre and resin, and each compositions in weight percentage is: glass fibre 60%-80%, resin 20%-40%.
2. the preparation method of a finishing material is characterized in that comprising the steps:
Steps A: get material by proportioning, getting resin is dropped in the melting appartus, resin is heated, temperature is controlled at 60 ℃-90 ℃, makes the resin fusing,
Step B: glass fiber yarn is immersed in the resin liquation, and after taking-up, dry processing,
Step C: will dry the back product and send in the mould, heat and pultrusion processing, in this process heating and temperature control at 60 ℃-140 ℃,
Step D: the product of extrusion molding is cut on demand, and carry out surface treatment.
3. the preparation method of a kind of device materials according to claim 2 is characterized in that the described surface treatment of step D is for carrying out surperficial roll printing decorative pattern processing to extrusion molding product among the step C.
4. the preparation method of a kind of device materials according to claim 2 is characterized in that being that the described surface treatment of step D is for carrying out the surface lacquer processing to extrusion molding product among the step C.
5. the preparation method of a kind of device materials according to claim 2 is characterized in that the described surface treatment of step D is for carrying out surperficial baking vanish processing to extrusion molding product among the step C.