CN102557522B

CN102557522B - Material for building decoration and artificial floor manufactured by material for building decoration

Info

Publication number: CN102557522B
Application number: CN201010605040.0A
Authority: CN
Inventors: 陈中武; 陈中平
Original assignee: ANSHUN XIXIU DISTRICT BOJI BOARD Co Ltd
Current assignee: The central Guizhou energy group bogy Xixiu District of Anshun city industry limited liability company
Priority date: 2010-12-26
Filing date: 2010-12-26
Publication date: 2014-05-07
Anticipated expiration: 2030-12-26
Also published as: CN102557522A

Abstract

The invention discloses a material for building decoration. The material for building decoration is prepared by the following raw materials in parts by weight: 40-60 parts of calcite, 40-60 parts of PVC (Poly Vinyl Chloride), 1-2 parts of sodium chloride, 1-3 parts of paraffin wax and 1-2 parts of stabilizer. The main materials of the material for building decoration include the calcite and the PVC, and the specific weight of the calcite and the PVC accounts for above 93% of that of all the raw materials, and a base material prepared by the calcite and the PVC has the most direct advantages of being lighter than a ceramic tile and being non-deformed and difficultly corroded in a wet environment and the like; the decoration material prepared by the base material can be recovered, crushed, squeezed and granulated for continuous use after being used for a certain time, and has the advantages of energy saving and environmental friendliness, and a stone material is mixed with large amounts of PVC, so that the ice-cold feel of the decoration material can be reduced, and the insulation effect is enhanced; and the decoration material cannot be broken in case of collision, so that the base material can be squeezed to obtain a variety of decoration materials, such as floor tiles, wall tiles, ceilings and the like.

Description

Architectural decoration material and with the artificial floor of its making

Technical field

The present invention relates to a kind of material of construction and floor, particularly a kind of architectural decoration material and with the artificial floor of its making.

Background technology

Timber floor is broadly divided into three major types: solid wooden floor board, solid wooden compound floor and laminated flooring.The main raw on above-mentioned three class floors all belongs to natural materials, have comfortable foot feeling, attractive in appearance, be convenient to processing, the advantage such as cool in summer and warm in winter.Although wood floors have above advantage, but also there are some unvanquishable shortcomings, as large in wooden consumed resource, easy care etc. not, particularly in the larger place of some humidity, exist floor width to produce with relative humidity variations the deficiency that large-size changes, and easily there is rotten, distortion in timber floor in a humid environment, can significantly reduce floor work-ing life; The timber floor of simultaneously damaging also cannot recycling.And at present the conventional finishing material with moisture effect mostly is floor tile or wall brick, floor tile and wall brick are to fire and form, and exist visual impression, sense of touch ice-cold, and heat retaining property is poor, and frangible, quality is the shortcoming such as heavily.

Summary of the invention

The technical problem to be solved in the present invention is: a kind of recyclable recycling is provided, is not afraid of that tide, quality are light, the architectural decoration material of constant product quality and with the artificial floor of its making, can overcome the deficiencies in the prior art

Technical scheme of the present invention is: architectural decoration material, it is to make with the raw material of following weight proportion, calcite 40-60 part, PVC 40-60 part, sodium-chlor 1-2 part, paraffin 1-3 part, stablizer 1-2 part.

In described calcite, calcium carbonate content is greater than 80%.

Described stablizer is high-efficiency compound stabilizer.

Described stablizer is PVC high-efficiency compound stabilizer.

The making method of building and ornament materials: it comprises the following steps:

A, calcite, PVC, paraffin, sodium-chlor, the stablizer of specifying component mixed and be crushed to 200 orders more than;

B, the mixture after the fragmentation in step a is sent into the base material that worm conveyor Squeezinggranulator obtains rod-shpaed particle;

Architectural decoration material producer is in the making method on floor:

A, base material is sent into single-lead-screw extruding briquetting machine, after cooling, cutting substrate;

B, the utilization material identical with substrate add the two ends of the middle part perforate on substrate stifled, and offer end and carve mouth, obtain artificial floor main body;

C, to the artificial floor main body japanning of polishing, and top layer lacquer painting is carried out to ultraviolet light polymerization paint baking.

Compared with the prior art, the main material of these building and ornament materials is calcite and PVC, both proportion accounts for the more than 93% of whole material, and the most direct advantage of base material making with calcite and PVC is for weighing less than ceramic tile, indeformable in wet environment, be difficult for burn into fire prevention etc.; The finishing material making with it can also reclaim after using certain hour, as base material, continue to use after broken, extruder grain, there are energy-conserving and environment-protective, and because be mixed with a large amount of PVC in stone material, can reduce the coolness of finishing material like this, increase heat insulation effect, and run into also can be broken collide with in the situation that, so this base material can obtain all kinds of finishing material by the method for extruding, as floor tile, wall brick, furred ceiling etc.The making method of this finishing material is also simpler, energy-conservation simultaneously.With this material making artificial floor, when extrusion molding, by its floor middle part perforate, there is like this quality of alleviating, save material, utilize base material to add stifled two ends, mouth is carved at the two ends that so just can be convenient to offer artificial floor, can not affect the property easy for installation on floor; Top layer lacquer painting is carried out to ultraviolet light polymerization paint baking, so not only can prevent that lacquer painting from coming off, and can Anti-scratching, increase wear resistance.

Embodiment

Embodiment 1: it comprises the following steps the making method of architectural decoration material:

A, get calcium carbonate content and be greater than more than 1 part of 80% 1 part, 1 part, 40 parts of 40 parts, calcite, PVC, sodium-chlor, paraffin, stablizer mixes and be crushed to 200 orders;

B, the mixture after the fragmentation in step a is sent into worm conveyor Squeezinggranulator obtain rod-shpaed particle and obtain base material.Described stablizer used is high-efficiency compound stabilizer, preferably PVC high-efficiency compound stabilizer.

It comprises the following steps the making method of embodiment 2, architectural decoration material:

A, get calcium carbonate content and be greater than more than 2 parts of 80% 3 parts, 2 parts, 60 parts of 60 parts, calcite, PVC, sodium-chlor, paraffin, stablizers mix and be crushed to 200 orders;

It comprises the following steps the making method of embodiment 3, architectural decoration material:

A, get calcium carbonate content and be greater than 2 parts of 80% 3 parts, 2 parts, 40 parts of 60 parts, calcite, PVC, sodium-chlor, paraffin, stablizers and mix and be crushed to below 200 orders;

It comprises the following steps the making method of embodiment 4, architectural decoration material:

A, get calcium carbonate content and be greater than 2 parts of 80% 1 part, 1 part, 60 parts of calcite, PVC, sodium-chlor, paraffin, stablizers and mix and be crushed to below 200 orders.

It comprises the following steps the making method of embodiment 5, architectural decoration material:

A, get calcium carbonate content and be greater than 2 parts of 80% 1.5 parts, 2 parts, 50 parts of calcite, PVC, sodium-chlor, paraffin, stablizers and mix and be crushed to below 200 orders;

Utilize the method on above-mentioned gained base material making artificial floor to be:

A, base material is sent into single-lead-screw extruding briquetting machine, after cooling, cutting substrate; Push the substrate of gained at the disposable wedge mouth that offers of length direction, and when extrusion molding, utilize forming mould to go out longitudinal hole in longitudinal extrusion molding of substrate, the uniform quantity of through hole is 6-9;

B, the utilization material identical with substrate add the two ends of the through hole on substrate stifled, and with necking tool, offer end and carve mouth, obtain artificial floor main body;

C, to the artificial floor main body japanning of polishing, and top layer lacquer painting carried out to ultraviolet light polymerization processing obtain this product.

Claims

1. an architectural decoration material, is characterized in that: it is to make with the raw material of following weight proportion,

Calcite 40-60 part, PVC 40-60 part, sodium-chlor 1-2 part, paraffin 1-3 part, stablizer 1-2 part;

It comprises the following steps its preparation technology:

A, calcite, PVC, paraffin, sodium-chlor, the stablizer of specifying deal mixed and be crushed to 200 orders more than;

In described calcite, calcium carbonate content is greater than 80%; Described stablizer is PVC high-efficiency compound stabilizer.

2. utilize the method on the architectural decoration material making artificial floor described in claim 1: it is characterized in that: it comprises the following steps: