CN104130518A - High-temperature-resistant and flame-retardant stone floor - Google Patents
High-temperature-resistant and flame-retardant stone floor Download PDFInfo
- Publication number
- CN104130518A CN104130518A CN201410341038.5A CN201410341038A CN104130518A CN 104130518 A CN104130518 A CN 104130518A CN 201410341038 A CN201410341038 A CN 201410341038A CN 104130518 A CN104130518 A CN 104130518A
- Authority
- CN
- China
- Prior art keywords
- parts
- temperature
- resistant
- floor
- flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of floors, in particular to a high-temperature-resistant and flame-retardant stone floor. The high-temperature-resistant and flame-retardant stone floor is made by using a method comprising the following steps: uniformly mixing 35 parts of waste marble stone dust, 30 parts of a PVC (Polyvinyl Chloride) type V resin, 8 parts of an ACR processing aid, 10 parts of an aluminate coupling agent, 4 parts of paraffin, 8 parts of chlorinated polyethylene (CPE), 2 parts of stearic acid and 3 parts of a composite stable lubricating agent; extrusion and sizing: extruding the mixture at the temperature of 280-350 DEG C, sizing the mixture in vacuum, and cooling the mixture to form a semi-finished substrate; and surface treatment: planing and trimming the four sides of the substrate, and grinding the surface. The high-temperature-resistant and flame-retardant stone floor has the beneficial effects that the waste marble stone dust is taken as a filler, so that comprehensive treatment of marble stone waste residues is facilitated greatly, and an energy-saving ad emission-reducing comprehensive environment-friendly project is realized.
Description
Technical field
The present invention relates to field, floor, relate in particular to a kind of stone floor of heat-resistant fireproof.
Background technology
Present social people more and more focus on the health problem of interior decoration, floor has been the first-selection that flooring is decorated, but formaldehyde is the important killer of interior decoration health always, if the new room formaldehyde content of decorating is higher, can cause the generation of many diseases, even can cause death, in addition China's Floor Industry to the consumption of timber considerably beyond China trees total amounts of becoming a useful person, serious scarcity along with China's Forest Resources, add the overexploitation to forest, area of woods falls sharply, trees accumulation greatly reduces, at the northern area of China underground heat, gradually entered in the family of ordinary consumer, but floor is in the use procedure of underground heat, there is crucial effect, floor on the market can not meet the needs of ordinary consumer, in addition the moist quantity of precipitation in south China area is large again, floor can be out of shape under long-term wet air, mouldy, infested, this product Shi Wo company is to reduce environmental pollution, the pollution of forest exploitation and interior decoration formaldehyde, without timber, just can effectively save the forest reserves, containing formaldehyde, can effectively not improve the health of people's living environment, performance is catered to huge numbers of families, the needs that meet greatly market, the world development trend of board industry conformably, it is the once technical reform of interior decoration Floor Industry.
Summary of the invention
The object of invention: for a kind of stone floor of powerful heat-resistant fireproof is provided, specific purposes are shown in a plurality of essence technique effects of concrete implementation section.
In order to reach as above object, the present invention takes following technical scheme:
A stone floor for heat-resistant fireproof, is characterized in that, adopts with the following method and is prepared from,
Batch mixing: by the mixing of materials of following parts by weight: 35 parts of marble stone flours, 30 parts of PVC five type resins, 8 parts of ACR processing aids, 10 parts of aluminate coupling agents, 4 parts, paraffin, 8 parts of CPE chlorinatedpolyethylenees, 3 parts of 2 parts of stearic acid, stable composition lubricant mix;
Be extruded to shape: by the material mixing in 280~350 degrees Celsius push, Vacuum shaping, cooling, form work in-process base material;
Surface treatment; Base material is carried out to four side moulder trimming process step, polished in surface.
The further technical scheme of the present invention is, the complete rear stamp plating of surface finish is on plate face.
Adopting as above the present invention of technical scheme, with respect to prior art, have following beneficial effect: this product serves as weighting material by marble stone flour, be greatly conducive to the comprehensive improvement to marble wastes waste residue, is the comprehensive environmental protection project of energy-saving and emission-reduction; This product is to combine solid wooden floor board, composite floor board, and consolidated floor, the every advantage of ceramic floor and make a kind of brand-new environmentfriendly products, is the once technical reform in Floor Industry.
Accompanying drawing explanation
In order to further illustrate the present invention, below in conjunction with accompanying drawing, further describe:
Fig. 1 is invented technology schematic diagram;
Fig. 2 is the main TV structure schematic diagram of invention;
Fig. 3 is invention backsight structural representation;
Fig. 4 is invention plan structure schematic diagram;
The left TV structure schematic diagram of Fig. 5;
Fig. 6 is a kind of section structure schematic diagram of implementing structure.
Embodiment
Below in conjunction with accompanying drawing, embodiments of the invention are described, embodiment is not construed as limiting the invention:
A stone floor for heat-resistant fireproof, is characterized in that, adopts with the following method and is prepared from,
Batch mixing: by the mixing of materials of following parts by weight: 35 parts of marble stone flours, 30 parts of PVC five type resins, 8 parts of ACR processing aids, 10 parts of aluminate coupling agents, 4 parts, paraffin, 8 parts of CPE chlorinatedpolyethylenees, 3 parts of 2 parts of stearic acid, stable composition lubricant mix;
Be extruded to shape: by the material mixing in 280~350 degrees Celsius push, Vacuum shaping, cooling, form work in-process base material;
Surface treatment; Base material is carried out to four side moulder trimming process step, polished in surface.
The complete rear stamp plating of surface finish is on plate face.Such as, can, by carrying out surface printing technique, can also add that imitative wood grain is printed on floor.
? | Solid wooden floor board | Consolidated floor | Ceramic floor | This patent |
Feel elasticity | Good | Generally | Poor | Better |
Aesthetic property | Good | Generally | Generally | Good |
Surface abrasion resistance | Poor | Good | Good | Good |
Waterproof and dampproof preventing deformation | Poor | Special poor | Good | Better |
Explosion-proof impacts | Poor | Special poor | Poor | Special good |
The anti-arch camber of going mouldy | Poor | Special poor | Good | Special good |
High temperature resistant, low temperature | Special poor | Poor | Good | Special good |
Fire-retardant | Special poor | Generally | Good | Special good |
Anti-skidding sound insulation | Generally | Good | Special poor | Good |
Popular wood grain | Good | Special poor | Poor | Special good |
Health environment-friendly | Generally | Special poor | Generally | Special good |
Executive cost | Greatly | Little | Greatly | Little |
Recycle | Can not | Can not | Can not | Energy |
When using: the in the situation that of Land leveling, spread moistureproof cushion, link floor draw-in groove, is used according to the assembled laying of assembled mode, and specifically, the decorative pattern that Fig. 6 and Fig. 3 show can block with the draw-in groove of below or directly spread.
The projection that Fig. 2 represents to Fig. 5 and depression can block each other and, easy for installation.
Stable composition lubricant in literary composition, ACR processing aid, PVC five type resins composition are separately as follows: compounded lubricant main component has one of any or part combination of calcium stearate, ricinolic acid calcium, Zinic stearas, zinc ricinate and epoxy soybean oil, UV light absorber.
ACR processing aid is the multipolymer of methyl methacrylate and acrylate, is white charge of flowable solids powder.
PVC five type resin compositions are polyvinyl chloride.
More than show and described ultimate principle of the present invention, principal character and advantage of the present invention.Those skilled in the art should understand the present invention and not be restricted to the described embodiments; that in above-described embodiment and specification sheets, describes just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in claimed scope.
Claims (2)
1. a stone floor for heat-resistant fireproof, is characterized in that, adopt with the following method and be prepared from,
Batch mixing: by the mixing of materials of following parts by weight: 35 parts of marble stone flours, 30 parts of PVC five type resins, 8 parts of ACR processing aids, 10 parts of aluminate coupling agents, 4 parts, paraffin, 8 parts of CPE chlorinatedpolyethylenees, 3 parts of 2 parts of stearic acid, stable composition lubricant mix;
Be extruded to shape: by the material mixing in 280~350 degrees Celsius push, Vacuum shaping, cooling, form work in-process base material;
Surface treatment; Base material is carried out to four side moulder trimming process step, polished in surface.
2. the stone floor of a kind of heat-resistant fireproof as claimed in claim 1, is characterized in that, the complete rear stamp plating of surface finish is on plate face.