CN101709168A - 一种吸收环境腐蚀物质转化防腐蚀增强型涂料 - Google Patents
一种吸收环境腐蚀物质转化防腐蚀增强型涂料 Download PDFInfo
- Publication number
- CN101709168A CN101709168A CN200910102830A CN200910102830A CN101709168A CN 101709168 A CN101709168 A CN 101709168A CN 200910102830 A CN200910102830 A CN 200910102830A CN 200910102830 A CN200910102830 A CN 200910102830A CN 101709168 A CN101709168 A CN 101709168A
- Authority
- CN
- China
- Prior art keywords
- film
- corrosive substances
- resin
- coating
- absorbing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种除成膜树脂外，体系中同时存在一定量的非芳香含π键物质，非芳香含π键物质能吸收环境中腐蚀物(卤化氢、卤气等)发生反应转化为成膜物质的一部分，使漆膜中的含卤量更高，填充了膜中空位，使膜的空隙率、吸水率和渗透性大幅度降低，从而提高了涂膜的防腐蚀能力的一种增强新型防腐蚀涂层。
Description
技术领域
本发明涉及一种防腐蚀涂料，特别涉及一种涂膜中的含非芳香π键高分子化合物含能与卤化氢、卤素单体等腐蚀性物质发生反应，最终涂膜体系中树脂含卤量增加，涂膜更加致密，提高了涂膜机械性能和防腐性能的吸收转化防腐蚀增强型涂料。
背景技术
在氯碱制造工业、钛化工冶炼、生产使用及产生卤化氢和卤素单质气体的工厂，厂房设备在强氧化剂和氢卤酸工作环境下腐蚀一直给防腐工作带来极大的麻烦，如采取涂层增厚、多道施工及PE、PVC收缩膜进行包覆均取得了一定效果。但受溶剂挥发残余空隙和渗透压作用的影响，卤化氢、卤素单质气体(特别是氯气)等工作环境中逸出的物质有极高的渗透力和强腐蚀性，使抗腐蚀效果不甚理想，同时施工困难，施工中漆膜存在的弊病瑕疵，导致成膜树脂内部及成膜树脂与基体间结合键的破坏而迅速被腐蚀，难以达到设计使用年限的要求。
发明内容
本发明的目的是当外界腐蚀气体渗透进涂层时，非芳香含π键物质能迅速开键与卤化氢、卤素气体发生加成反应，而将这些腐蚀物质转化为成膜树脂的成份。
本发明所述的一种吸收环境腐蚀物质转化防腐蚀增强型涂料，其组成由成膜树脂、含非芳香π键高分子化合物、防锈颜填料、溶剂及各类助剂组成。
本发明所述的一种吸收环境腐蚀物质转化防腐蚀增强型涂料，其组分重量百分比为：成膜树脂15.0-20.0，非芳香含π键高分子化合物5.0-10.0，防锈颜填料30.0-45.0，溶剂11.0-26.0，助剂2.0-8.5。
本发明所述的含非芳香π键高分子化合物能吸收卤化氢、卤素单体等腐蚀性物质发生反应。
本发明所述的涂料涂膜通过吸收卤化氢、卤素单体等腐蚀性物质发生反应，最终涂膜体系中树脂含氯量增加，涂膜更加致密，提高了涂膜的机械性能和防腐性能。
本发明所述的成膜树脂为丙烯酸树脂、苯丙树脂、二甲苯树脂、氯化橡胶、聚乙烯高氯化树脂、过氯乙烯树脂、环氧酯树脂、环氧树脂、醇酸树脂的一种或多种。
本发明所述的非芳香π键高分子化合物为天然橡胶、丁腈橡胶、顺丁橡胶、聚戊二烯橡胶、氯丁橡胶或改性氯丁橡胶、亚麻油、桐油、梓油、花生油、棉子油、松香、松香甘油脂、松香季戊脂、三丙烯酸甘油醇、四甲基丙烯酸季戊四酯、(甲)丙烯酸乙二酯、(甲基)丙烯酸聚乙二醇酯、环氧丙烯酸酯、顺丁二酸辛酯、顺丁二酸丁酯、丙烯酸辛酯中的一种或多种。
本发明给出的这种吸收环境腐蚀物质转化防腐蚀增强型涂料经制膜分析检测，检测结果如下：
| 项目 | 指标 | 试验方法 |
| 漆膜外观 | 平整光滑 | GB/T1729-1979 |
| 固体含量，％ | ≥50 | GB/T1725-1979 |
| 柔韧性，mm | 1 | GB/T1731-1993 |
| 铅笔硬度 | HB | GB/T6739-1996 |
| 附着力(划圈法) | 1 | GB/T1720-1979 |
| 冲击强度，kg.cm | 50 | GB/T1732-1993 |
| 耐水性，3d | 不起泡，不脱落 | GB/T1733-1979 |
| 耐盐水性(3％)，48h | 不起泡，不脱落 | GB/T1763-1979 |
| 耐中性盐雾性，1000h | 通过 | GB/T1771-1991 |
| 漆膜吸收转化率(m/m)，％ | 2.5～3.8 | 自测 |
与现有技术相比，本发明的有益效果为：
1、本发明配方设计中让成膜物质余留大量不饱和非芳香π键物质，成膜后无催干剂的加入，在常温被氧气氧化形成氧桥的速度极慢，同时成膜树脂的总体玻璃化温度高，溶剂挥发后即可成膜。
2、含非芳香π键物质通过吸收卤化氢、卤素等腐蚀性物质发生加成反应，如下：
①-CH＝CH-+HX→-CH2-CHX-
使涂膜质量增加，即漆膜体积也相应增加，膜空隙被占据填充，透水、透气率下降，同时不同树脂渗透性是有很大的差异的，含卤量增大腐蚀渗透率就会小，同时自由基可能诱发的聚合反应使膜的交联密度加大，如下：
X2→X·+X·HX→H·+X·
漆膜的物理性能更好，玻璃态温度更高，亲水性降低，渗透率也降低，因此产生的多重效应，使腐蚀介质在漆膜中的渗透率大幅降低，从而防腐性得到提高。
具体实施方式
实施例1：
50％的氯化橡胶二甲苯树脂液20kg和60％油度的50％的桐油酸环氧酯二甲苯溶液30kg混合，加入铁钛料10kg，钛白粉10kg，沉淀硫酸钡13kg，高速分散1小时，分散均匀后，研磨至细度小于25μm，补加剩4.2kg的助剂，搅拌均匀，制得成品吸收环境腐蚀物质转化防腐蚀增强型涂料。
实施例2：
丙烯酸树脂10kg，过氯乙烯树脂20kg，顺丁二酸辛酯5kg，6101环氧二丙烯酸酯20kg，分别投入到10kg二甲苯，醋酸丁酯5kg、环己酮5kg，搅拌完全溶解，在低搅拌下分别加入云母氧化铁红15kg，滑石粉20kg，高速搅拌1小时后研磨至细度小于30μm后，投入助剂3.2kg，搅拌均匀，制得成品吸收环境腐蚀物质转化防腐蚀增强型涂。
Claims (6)
1.一种吸收环境腐蚀物质转化防腐蚀增强型涂料，其特征在于该涂料由成膜树脂和含非芳香π键高分子化合物、防锈颜填料、溶剂及各类助剂组成。
2.一种吸收环境腐蚀物质转化防腐蚀增强型涂料，其特征在于该涂料组分及其配方的重量份数比为：成膜树脂15.0-20.0，非芳香π键的天然化合物或高分子化合物5.0-10.0，防锈颜填料30.0-35.0，溶剂11.0-31.0，助剂2.0-8.5。
3.按照权利要求1中所述的一种吸收环境腐蚀物质转化防腐蚀增强型涂料，其特征在于所述的含非芳香π键高分子化合物能吸收卤化氢、卤素单体等腐蚀性物质发生反应。
4.按照权利要求1中所述的一种吸收环境腐蚀物质转化防腐蚀增强型涂料，其特征在于所述的涂膜通过吸收卤化氢、卤素单体等腐蚀性物质发生反应，最终涂膜体系中树脂含氯量增加，涂膜更加致密，提高了涂膜的机械性能和防腐性能。
5.按照权利要求1中所述的一种吸收环境腐蚀物质转化防腐蚀增强型涂料，其特征在于所述的成膜树脂为丙烯酸树脂、苯丙树脂、二甲苯树脂、氯化橡胶、高氯化树脂、环氧酯树脂、环氧树脂、醇酸树脂的一种或多种。
6.按照权利要求1中所述的一种吸收环境腐蚀物质转化防腐蚀增强型涂料，其特征在于所述的含非芳香π键高分子化合物为天然橡胶、丁腈橡胶、顺丁橡胶、聚戊二烯橡胶、氯丁橡胶或改性氯丁橡胶、亚麻油、桐油、梓油、花生油、棉子油、松香、松香甘油脂、松香季戊脂、三丙烯酸甘油醇、四甲基丙烯酸季戊四酯、(甲)丙烯酸乙二酯、(甲基)丙烯酸聚乙二醇酯、环氧丙烯酸酯、顺丁二酸辛酯、顺丁二酸丁酯、丙烯酸辛酯中的一种或多种。