CN101693796A - Seam crack-resisting putty - Google Patents
Seam crack-resisting putty Download PDFInfo
- Publication number
- CN101693796A CN101693796A CN200910193073A CN200910193073A CN101693796A CN 101693796 A CN101693796 A CN 101693796A CN 200910193073 A CN200910193073 A CN 200910193073A CN 200910193073 A CN200910193073 A CN 200910193073A CN 101693796 A CN101693796 A CN 101693796A
- Authority
- CN
- China
- Prior art keywords
- powder
- resisting
- percent
- seam crack
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a seam crack-resisting putty and aims at solving the problems that the existing similar seam crack-resisting putties have complex process, high cost, poor surface flatness after filling, repairing or finishing, and difficult polishing and finishing, and can not be applicable to wood or metal wall surfaces, table surfaces, furniture and other objects. The seam crack-resisting putty is characterized by being formed by the uniform mixing of a paste-shaped main agent and an auxiliary agent with the weight ratio of 1:0.5 to 2, wherein the main agent contains 63 to 84 percent of epoxy resin and 16 to 37 percent of plant powder with the particle size of less than 1 mm in percentage by weight. The auxiliary agent contains 63 to 84 percent of epoxy resin curing agent and 16 to 37 percent of plant powder with the particle size less than 1 mm in percentage by weight. 0.8 to 17 percent of toner can also be added to the main agent and the auxiliary agent in percentage by weight; and in percentage by weight the toner can be formed by uniform mixing of 1 to 99 percent of pigment powder and 1 to 99 percent of lithopone, titanium dioxide, talc powder, kaolin or bentonite, and the like.
Description
Technical field
The material of the present invention relates to that building decorating industry is filled up, repaired, finishing or bonding metope being used specifically is a kind of seam crack-resisting putty.Be specially adapted to the filling up of seam on wooden or metallic metope, table top, furniture and other article or slit, repair, finishing or bonding.
Background technology
The anti-crack mastic that building decorating industry is commonly used generally is the material that is used for traditional sand-cement slurry coat of plaster of alternative body of wall at present, avoid dry shrink of coat of plaster to cause be full of cracks, thereby avoid causing the appearance ornament layer crackle to occur, influence decorative effect, wall face also can cause infiltration.The anti-cracking powder putty that Chinese patent is 03108740.X number is this class technical scheme.Its technology constitutes by by weight percentage 3～4% polymer powders, 27～30% cement, 35～38% silica powders, 30～33% coarse whitings, 0.3～0.5% regulates material, 0.5～1.0% powder auxiliary and 0.5～1.0% fibrous, polymer powder is the multipolymer of acrylate, powder auxiliary is 60% dispersion agent and 40% defoamer, regulating material is the methylcellulose gum series products of about 15000～30000 molecular weight, and above-mentioned materials is allocated to appropriate viscosity with certain proportion with water at the construction field (site) and used.The defective of this class anti-cracking putty is: only be suitable for doing the big area coat of plaster, be not suitable for doing the filling up of local seam or slit, repair, finishing or bonding.
The seam crack-resisting putty that present building decorating industry is used is another kind of putty, be be specifically designed to the seam of metope or its decorative surface layer or place, slit fill up, repair, finishing or bonding material, technique effect requires to fill up, repairs, finishing or bonding after can not produce the crack.The anticracking joint putty that No. the 200810070869.8th, Chinese patent application is this class technical scheme.Its technology formation comprises host and solidifying agent, host is that 1～15 millimeter fiber, 5～20% wilkinites, 20～40% lime carbonate, 5～30% particle diameters are that 0.01～0.1 millimeter fine sand and 2～15% titanium dioxides are formed by 35～60% Resins, epoxy, 5～30% length, makes paste by stirring; Solidifying agent is that 1～15 millimeter fiber, 5～20% wilkinites, 20～40% lime carbonate, 5～30% particle diameters are that 0.01～0.1 millimeter fine sand and 2～15% titanium dioxides are formed by 35～60% polymeric amide, 5～30% length, makes the ointment shape by stirring; During use host and solidifying agent were mixed by weight 2: 1, be coated in seam crossing and get final product.The defective of this class seam crack-resisting putty is: the one, and material category is many, complex manufacturing technology, cost is higher; The 2nd, contain things such as fine sand, fiber, fill up, repair, finishing or bonding after surface finish poor, and be difficult to polish polishing; The 3rd, because surface finish is poor, be difficult to polish mill, so be suitable for requiring not have smooth slick surface, seam or slit are filled up, are repaired, finishing or bonding after must planeness good, and can polish wooden or metallic metope, table top, furniture and other article of polishing.
Summary of the invention
In order to overcome the existing existing complex process of similar seam crack-resisting putty, cost is higher, fill up, repair or repair the rear surface poor flatness, be difficult to polish polishing, be not suitable for the defective of wooden or metallic metope, table top, furniture and other thing, the purpose of this invention is to provide a kind of improved seam crack-resisting putty, can overcome the defective of prior art.
The technical solution adopted for the present invention to solve the technical problems is: a kind of seam crack-resisting putty, it is characterized in that: constitute by weight 1: 0.5～2 uniform mixing by unguinosus host and ingredients, wherein host contains the Resins, epoxy of weight percent 63～84% and 16～37% particle diameters less than 1 millimeter plant powder, and ingredients contains the epoxy curing agent of weight percent 63～84% and 16～37% particle diameters less than 1 millimeter plant powder.
In the host and ingredients of technique scheme, can also add the chromatic timing powder of weight percent 0.8～17%, with the allotment seam crack-resisting putty tone, make it with fill up, repair or repair the object color identical, near or be complementary.After adding chromatic timing powder, host contains the Resins, epoxy, 11～21% particle diameters of weight percent 63～84% less than 1 millimeter plant powder and 0.8～17% chromatic timing powder, and ingredients contains the epoxy curing agent, 10～20% particle diameters of weight percent 66～83% less than 1 millimeter plant powder and 0.8～17% chromatic timing powder.
The chromatic timing powder of technique scheme can be made up of the pigment powder of weight percent 1～99% and 1～99% zinc sulfide white, titanium dioxide, talcum powder, kaolin or wilkinite uniform mixing.
The plant powder of technique scheme can be bamboo powder, wood powder, straw powder, rattan reed powder, balloonflower powder, fruit shell powder or paper powder etc.
The epoxy curing agent of technique scheme can be alkaline solidifying agent, as aliphatic diamine, polyamines, aromatic polyamine, dicyandiamide, imidazoles, modified amine, Versamid etc.; Also can be acid curing agent, as organic acid anhydrides, boron trifluoride and complex compound etc.
The product of seam crack-resisting putty of the present invention generally is with host and ingredients separate packages and offer the user together, is using on-the-spot ability that host and ingredients are made into putty by weight 1: 0.5～2 uniform mixing.So host of the present invention and ingredients are provided simultaneously, the product of guiding people's deallocation system putty of the present invention should be considered as product manifestation of the present invention.
Beneficial effect of the present invention: the one, material category is few, and technology is simple, and making and adapted are convenient, and cost is lower; The 2nd, the additive in Resins, epoxy and the solidifying agent thereof all is a powder, to the filling up of slit, repair, finishing or bonding rear surface planeness be good, and can polish polishing with sand paper and so on; The 3rd, be applicable to that wooden or metallic metope, table top, furniture and other article carry out the filling up of seam or slit, repair, finishing or bonding; The 4th, whole additives are all nontoxic to environment and human body, so production and safe in utilization.
The invention will be further described below in conjunction with embodiment.Embodiment gives an example to of the present invention, is not the qualification to right of the present invention.
Embodiment
Embodiment one:
This seam crack-resisting putty, it is characterized in that: constitute by weight 1: 1 uniform mixing by unguinosus host and ingredients, wherein host contains the bisphenol A type epoxy resin of weight percent 74% and 26% particle diameter less than 1 millimeter bamboo powder, and ingredients contains the Versamid of weight percent 74% and 26% particle diameter less than 1 millimeter bamboo powder.
The Resins, epoxy of host and bamboo powder are uniformly mixed into the ointment shape, the Versamid of ingredients and bamboo powder also are uniformly mixed into the ointment shape, host and ingredients are separately packed, offer the user then together, using on-the-spot ability that host and ingredients are broken seal respectively, be made into putty by weight 1: 1 uniform mixing.
Embodiment two:
This seam crack-resisting putty, it is characterized in that: constitute by weight 1: 1.5 uniform mixing by unguinosus host and ingredients, wherein host contains the bisphenol A type epoxy resin, 30% particle diameter of weight percent 67% less than 1 millimeter wood powder and 3% chromatic timing powder, ingredients contains the phenol formaldehyde (PF) quadrol condenses (genus modified amine), 30% particle diameter of weight percent 67% less than 1 millimeter wood powder and 3% chromatic timing powder, and chromatic timing powder is made up of the pigment powder of weight percent 3% and 97% zinc sulfide white uniform mixing.
The Resins, epoxy of host, wood powder and chromatic timing powder are uniformly mixed into the ointment shape, phenol formaldehyde (PF) quadrol condenses, wood powder and the chromatic timing powder powder of ingredients also are uniformly mixed into the ointment shape, host and ingredients are separately packed, offer the user then together, using on-the-spot ability that host and ingredients are broken seal respectively, be made into putty by weight 1: 1.5 uniform mixing.
Claims (6)
1. seam crack-resisting putty, it is characterized in that: constitute by weight 1: 0.5～2 uniform mixing by unguinosus host and ingredients, wherein host contains the Resins, epoxy of weight percent 63～84% and 16～37% particle diameters less than 1 millimeter plant powder, and ingredients contains the epoxy curing agent of weight percent 63～84% and 16～37% particle diameters less than 1 millimeter plant powder.
2. by the described seam crack-resisting putty of claim 1, it is characterized in that adding in described host and the ingredients chromatic timing powder of weight percent 0.8～17%.
3. by the described seam crack-resisting putty of claim 2, it is characterized in that described host contains the Resins, epoxy of weight percent 63～84%, 11～21% particle diameters less than 1 millimeter plant powder and 0.8～17% chromatic timing powder, ingredients contains the epoxy curing agent, 10～20% particle diameters of weight percent 66～83% less than 1 millimeter plant powder and 0.8～17% chromatic timing powder.
4. by claim 2 or 3 described seam crack-resisting putties, it is characterized in that described chromatic timing powder is made up of the pigment powder of weight percent 1～99% and 1～99% zinc sulfide white, titanium dioxide, talcum powder, kaolin or wilkinite uniform mixing.
5. by claim 1 or 2 described seam crack-resisting putties, it is characterized in that described plant powder is bamboo powder, wood powder, straw powder, rattan reed powder, balloonflower powder, fruit shell powder or paper powder.
6. by claim 1 or 2 described seam crack-resisting putties, it is characterized in that described epoxy curing agent is alkaline solidifying agent or acid curing agent.