CN103862539A - Wood repairing agent - Google Patents
Wood repairing agent Download PDFInfo
- Publication number
- CN103862539A CN103862539A CN201210548256.7A CN201210548256A CN103862539A CN 103862539 A CN103862539 A CN 103862539A CN 201210548256 A CN201210548256 A CN 201210548256A CN 103862539 A CN103862539 A CN 103862539A
- Authority
- CN
- China
- Prior art keywords
- healant
- timber
- percentage composition
- quality percentage
- floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a wood repairing agent. The wood repairing agent comprise 40%-50% by mass of floor priming paint debris, 30%-40% by mass of alpha- ethyl cyanoacrylate, 1%-2% by mass of gas-phase silicon dioxide, 1%-2% of acrylic-styrene copolymer, 1%-3% of benzotriazole, 3%-5% of soft resin, 0.5%-2% of a carbonate, wherein the floor priming paint debris is obtained by employing an abrasive belt to perform sanding treatment on priming-paint-coated floor, and the priming paint comprises artificially synthesized resin and 15%-20% by mass of talcum powder. The wood repairing agent disclosed by the invention has good repairing effect and high repairing efficiency on wooed floor.
Description
Technical field
The present invention relates to a kind of timber healant.
Background technology
In the production process of solid wooden floor board, it is a very important link that defects in timber are repaired, and along with timber resources is more and more nervous, it is an important process of Floor Industry that defective timber is repaired.In addition, antique imitation process floor more and more gets consumer reception, can be by timber healant for floor archaizing processing technology, the art up processing of repairing can promote the aesthetic feeling modelled after an antique on floor, thereby makes defective timber process by antique imitation process the good result that reaching defect is nature aesthetic feeling.
In the time carrying out floor defect mending, because the defect of timber is various, such as cracking, small holes caused by worms, medullary spots, fast knot, cavity, damaged etc., if make that repair efficiency is good, repairing efficiency is high, need a kind of good timber healant.Various timber healants are sold in the market, but these healants all have weak point, therefore, this area is needed a kind of timber healant all having premium properties aspect repairing quality, resistance to water, intensity, adhesive force and polishing processing badly.
Summary of the invention
The object of the present invention is to provide a kind of timber healant, described timber healant contains following composition:
Quality percentage composition is 40% to 50% the broken end of ground electroplate primer,
Quality percentage composition is 30% to 40% ECA,
Quality percentage composition is 1% to 2% aerosil,
Quality percentage composition is acrylic acid/styrol copolymer emulsion of 1% to 2%,
Quality percentage composition is 1% to 3% BTA,
Quality percentage composition is 3% to 5% soft resin,
Quality percentage composition is 0.5% to 2% carbonate,
Wherein, electroplate primer broken end in described ground is by using abrasive band to carry out sanding processing and obtain being coated with the floor of priming paint, and it is 15% to 20% talcum powder that described priming paint comprises artificial synthetic resin and quality percentage composition.
Preferably, described carbonate is selected from sodium carbonate, calcium carbonate and magnesium carbonate, described talcous 1250 orders that are of a size of, and the particle size on described abrasive band is more than 240 orders, the color at the broken end of electroplate primer, described ground is white or faint yellow.
In the time repairing high rigidity timber, described timber healant also can comprise that quality percentage composition is 5% to 10% the broken end of di-iron trioxide.Preferably, more than the broken end of described di-iron trioxide is of a size of 500 orders.Described high rigidity timber is preferably teak, Pometia spp, locust tree, oak, rosewood, face cream pigeonpea, two wing beans, red acid branch, Mani Kara spp, Bai Lamu, maple, birch, white phellem.
Timber healant of the present invention is owing to containing the broken end of ground electroplate primer that strengthens filling effect, there is efficient fusible ECA, promote the aerosil of viscosity, acrylic acid/styrol copolymer emulsion that resistance to water is stronger and stabilizing agent BTA, improve flexible soft resin and the basic carbonate for dry and mildew-resistant, therefore it has the following advantages with respect to commercially available timber healant tool: fast drying, be difficult for mouldy, the property filled up is good, do not shrink, repairing quality is good, water-tolerant, intensity is high, after repairing, adhesive force is good, difficult drop-off, and good polishing processing characteristics.
Detailed description of the invention
For making the object, technical solutions and advantages of the present invention clearer, below in conjunction with specific embodiment, further the present invention is described in detail.Following examples, only for illustrating, do not form any restriction to the present invention.
Embodiment 1
In every 80 grams of white artificial synthetic resin's priming paint, add 20 gram of 1250 object talcum powder, with being added with talcous priming paint, priming paint processing is carried out in floor, then carry out sanding processing with 240 object abrasive bands, retain the broken end of white primer.Get broken last 47 grams of this priming paint, 40 grams of ECAs, 2 grams of aerosils, 2 grams of acrylic acid/styrol copolymer emulsions, 3 grams of BTAs, 4 grams of soft resins, 2 grams, sodium carbonate, stirs and evenly mixs, and makes timber healant.The timber healant that use makes is repaired the white timber floor of cracking, by healant full-filling in ground plank split, after full-filling, become dry less than 1 minute healant, be bonded into one with floor, significantly do not repair vestige, and repair part water-tolerant, intensity is high, healant does not shrink, difficult drop-off, sanding property are good.
Embodiment 2
In every 85 grams of faint yellow artificial synthetic resin's priming paint, add 15 gram of 1250 object talcum powder, with being added with talcous priming paint, priming paint processing is carried out in floor, then carry out sanding processing with 240 object abrasive bands, retain the broken end of faint yellow priming paint.Get broken last 49.5 grams of this priming paint, 34 grams of ECAs, 1.5 grams of aerosils, 1 gram of acrylic acid/styrol copolymer emulsion, 3 grams of BTAs, 5 grams of soft resins, 1 gram, magnesium carbonate, 5 grams, the broken end of di-iron trioxide (being of a size of 500 orders), stirs and evenly mixs, and makes timber healant.The timber healant that use makes is repaired the small holes caused by worms on faint yellow oak floors, in small holes caused by worms by healant full-filling on floor, after full-filling, 50 seconds healants become dry, be bonded into one with floor, significantly do not repair vestige, and repair part water-tolerant, intensity is high, healant does not shrink, difficult drop-off, sanding property are good.
Embodiment 3
In every 83 grams of faint yellow artificial synthetic resin's priming paint, add 17 gram of 1250 object talcum powder, with being added with talcous priming paint, priming paint processing is carried out in floor, then carry out sanding processing with 250 object abrasive bands, retain the broken end of faint yellow priming paint.Get broken last 50 grams of this priming paint, 30 grams of ECAs, 1 gram of aerosil, 2 grams of acrylic acid/styrol copolymer emulsions, 2 grams of BTAs, 4 grams of soft resins, 1 gram, calcium carbonate, 10 grams, the broken end of di-iron trioxide (being of a size of 600 orders), stirs and evenly mixs, and makes timber healant.By conventional method to the timber healant the making processing of mixing colours, it is approached red, with toning after timber healant the cavity in red two wing beans timber floors is repaired, in cavity by healant full-filling on floor, after full-filling, become dry less than 1 minute healant, be bonded into one with floor, significantly do not repair vestige, and repair part water-tolerant, intensity is high, healant does not shrink, difficult drop-off, sanding property are good.
Embodiment 4
In every 85 grams of faint yellow artificial synthetic resin's priming paint, add 15 gram of 1250 object talcum powder, with being added with talcous priming paint, priming paint processing is carried out in floor, then carry out sanding processing with 270 object abrasive bands, retain the broken end of faint yellow priming paint.Get broken last 46 grams of this priming paint, 40 grams of ECAs, 2 grams of aerosils, 2 grams of acrylic acid/styrol copolymer emulsions, 3 grams of BTAs, 5 grams of soft resins, 2 grams, sodium carbonate, stirs and evenly mixs, and makes timber healant.By conventional method to the timber healant the making processing of mixing colours, make it approach brown, with toning after timber healant the breach in brown timber floor is repaired, by healant full-filling in the breach of floor, after full-filling, 40 seconds healants become dry, and are bonded into one with floor, significantly do not repair vestige, and repair part water-tolerant, intensity is high, healant does not shrink, difficult drop-off, sanding property are good.
Embodiment 5
In every 85 grams of white artificial synthetic resin's priming paint, add 15 gram of 1250 object talcum powder, with being added with talcous priming paint, priming paint processing is carried out in floor, then carry out sanding processing with 280 object abrasive bands, retain the broken end of white primer.Get broken last 49 grams of this priming paint, 35 grams of ECAs, 2 grams of aerosils, 2 grams of acrylic acid/styrol copolymer emulsions, 1 gram of BTA, 3 grams of soft resins, 0.5 gram, sodium carbonate, 7.5 grams, the broken end of di-iron trioxide (being of a size of 700 orders), stirs and evenly mixs, and makes timber healant.The timber healant that use makes is repaired the breach in the white cured timber floor of white, by healant full-filling in the breach of floor, after full-filling, 50 seconds healants become dry, be bonded into one with floor, significantly do not repair vestige, and repair part water-tolerant, intensity is high, healant does not shrink, difficult drop-off, sanding property are good.
Embodiment 6
In every 85 grams of white artificial synthetic resin's priming paint, add 15 gram of 1250 object talcum powder, with being added with talcous priming paint, priming paint processing is carried out in floor, then carry out sanding processing with 280 object abrasive bands, retain the broken end of white primer.Get broken last 50 grams of this priming paint, 40 grams of ECAs, 1 gram of aerosil, 1.5 grams of acrylic acid/styrol copolymer emulsions, 2 grams of BTAs, 5 grams of soft resins, 0.5 gram, sodium carbonate, stirs and evenly mixs, and makes timber healant.The timber healant that use makes is repaired the medullary spots in white timber floor, by healant full-filling in medullary spots place, floor, after full-filling, become dry less than 1 minute healant, be bonded into one with floor, significantly do not repair vestige, and repair part water-tolerant, intensity is high, healant does not shrink, difficult drop-off, sanding property are good.
Embodiment 7
In every 85 grams of white artificial synthetic resin's priming paint, add 15 gram of 1250 object talcum powder, with being added with talcous priming paint, priming paint processing is carried out in floor, then carry out sanding processing with 280 object abrasive bands, retain the broken end of white primer.Get broken last 40 grams of this priming paint, 40 grams of ECAs, 2 grams of aerosils, 2 grams of acrylic acid/styrol copolymer emulsions, 3 grams of BTAs, 3 grams of soft resins, 1 gram, sodium carbonate, 9 grams, the broken end of di-iron trioxide (being of a size of 600 orders), stirs and evenly mixs, and makes timber healant.The timber healant that use makes is repaired the breach on white maple floor, by healant full-filling in the breach of floor, after full-filling, 30 seconds healants become dry, be bonded into one with floor, significantly do not repair vestige, and repair part water-tolerant, intensity is high, healant does not shrink, difficult drop-off, sanding property are good.
Describe the present invention in conjunction with detailed description of the invention above; these detailed description of the invention are only exemplary; can not limit protection scope of the present invention with this, those skilled in the art can carry out various amendments, variation or replacement under the prerequisite that does not depart from essence of the present invention.Therefore, the various equivalent variations of doing according to the present invention, still belong to the scope that the present invention is contained.
Claims (7)
1. a timber healant, described timber healant contains following composition:
Quality percentage composition is 40% to 50% the broken end of ground electroplate primer,
Quality percentage composition is 30% to 40% ECA,
Quality percentage composition is 1% to 2% aerosil,
Quality percentage composition is acrylic acid/styrol copolymer emulsion of 1% to 2%,
Quality percentage composition is 1% to 3% BTA,
Quality percentage composition is 3% to 5% soft resin,
Quality percentage composition is 0.5% to 2% carbonate,
Wherein, electroplate primer broken end in described ground is by using abrasive band to carry out sanding processing and obtain being coated with the floor of priming paint, and it is 15% to 20% talcum powder that described priming paint comprises artificial synthetic resin and quality percentage composition.
2. timber healant as claimed in claim 1, wherein, described carbonate is selected from sodium carbonate, calcium carbonate and magnesium carbonate.
3. timber healant as claimed in claim 1, wherein, described talcous 1250 orders that are of a size of.
4. timber healant as claimed in claim 1, wherein, the particle size on described abrasive band is more than 240 orders.
5. timber healant as claimed in claim 1, wherein, the color at the broken end of electroplate primer, described ground is white or faint yellow.
6. timber healant as claimed in claim 1, wherein, described timber healant also comprises that quality percentage composition is 5% to 10% the broken end of di-iron trioxide.
7. timber healant as claimed in claim 6, wherein, more than the broken end of described di-iron trioxide is of a size of 500 orders.