CN101691304A - 高抗蚀石墨胶泥 - Google Patents

高抗蚀石墨胶泥 Download PDF

Info

Publication number
CN101691304A
CN101691304A CN200910172357A CN200910172357A CN101691304A CN 101691304 A CN101691304 A CN 101691304A CN 200910172357 A CN200910172357 A CN 200910172357A CN 200910172357 A CN200910172357 A CN 200910172357A CN 101691304 A CN101691304 A CN 101691304A
Authority
CN
China
Prior art keywords
graphite
corrosion resistant
high corrosion
parts
thermoplastic resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN200910172357A
Other languages
English (en)
Other versions
CN101691304B (zh
Inventor
叶乐
石立
肖国正
岳向旭
杜建超
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2009101723577A priority Critical patent/CN101691304B/zh
Publication of CN101691304A publication Critical patent/CN101691304A/zh
Application granted granted Critical
Publication of CN101691304B publication Critical patent/CN101691304B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种高抗蚀石墨胶泥，包括下述重量份原料：电解石墨粉20～35，膨胀石墨5～15，氧化硼5～20，氧化钛5～20，热固性树脂10～20，热塑性树脂1～6。本发明高抗蚀石墨胶泥提高了炭砖之间的粘结抗折强度；提高了石墨胶泥体积密度；提高了石墨胶泥抗铁水熔蚀指数。有利于炭砖内衬形成稳固的整体，并延长炉衬使用寿命。

Description

高抗蚀石墨胶泥
技术领域
本发明主要涉及一种炼铁高炉用石墨质结合剂，具体说是涉及一种适合用于高炉炉底、炉缸部位炭砖与炭砖之间的高抗蚀石墨胶泥。
背景技术
自1958年在炼铁高炉炉底、炉缸采用炭砖内衬以来，高炉炉底、炉缸的使用寿命已由2～3年延长至8～12年。高炉一代炉役结束后，经过多座炭砖内衬的破损调查，发现炭砖与炭砖之间的链接缝已成为影响内衬破损的重要因素之一。现有的炭素胶泥、细缝糊类产品已不能满足高炉长寿的实际需要。
发明内容
本发明所要解决的技术问题是提供一种高抗蚀石墨胶泥，该高抗蚀石墨胶泥的主要特点：1.粘结抗折强度高，由2～4MPa提高到4～6MPa；2.体积密度由1.2～1.3g/cm2提高到1.4～1.6g/cm2；3.铁水熔蚀指数小于40％。
为了解决以上技术问题采用以下方案：
一种高抗蚀石墨胶泥，包括下述重量份原料：
电解石墨粉20～35，膨胀石墨5～15，氧化硼5～20，氧化钛5～20，热固性树脂10～20，热塑性树脂1～6。
高抗蚀石墨胶泥，包括下述优选重量份原料：
电解石墨粉25～30，膨胀石墨8～12，氧化硼10～15，氧化钛10～15，热固性树脂13～17，热塑性树脂3～5。
高抗蚀石墨胶泥，包括下述具体重量份原料：
电解石墨粉27，膨胀石墨10，氧化硼12，氧化钛12，热固性树脂15，热塑性树脂4。
高抗蚀石墨胶泥，包括下述具体重量份原料：
电解石墨粉25，膨胀石墨10，氧化硼15，氧化钛15，热固性树脂15，热塑性树脂5。
本发明高抗蚀石墨胶泥提高了炭砖之间的粘结抗折强度；提高了石墨胶泥体积密度；提高了石墨胶泥抗铁水熔蚀指数。有利于炭砖内衬形成稳固的整体，并延长炉衬使用寿命。
具体实施方式
实施例1
一种高抗蚀石墨胶泥，包括下述重量份原料：
电解石墨粉20～35，膨胀石墨5～15，氧化硼5～20，氧化钛5～20，热固性树脂10～20，热塑性树脂1～6。
实施例2
一种高抗蚀石墨胶泥，包括下述优选重量份原料：
电解石墨粉25～30，膨胀石墨8～12，氧化硼10～15，氧化钛10～15，热固性树脂13～17，热塑性树脂3～5。
实施例3
一种高抗蚀石墨胶泥，包括下述具体重量份原料：
电解石墨粉27kg，膨胀石墨10kg，氧化硼12kg，氧化钛12kg，热固性树脂15kg，热塑性树脂4kg。
实施例4
一种高抗蚀石墨胶泥，包括下述具体重量份原料：
电解石墨粉25kg，膨胀石墨10kg，氧化硼15kg，氧化钛15kg，热固性树脂15kg，热塑性树脂5kg。
实施例5
一种高抗蚀石墨胶泥，包括下述重量份原料：
电解石墨粉20kg，膨胀石墨15kg，氧化硼5kg，氧化钛20kg，热固性树脂10kg，热塑性树脂6kg。
实施例6
一种高抗蚀石墨胶泥，包括下述重量份原料：
电解石墨粉35kg，膨胀石墨5kg，氧化硼20kg，氧化钛5kg，热固性树脂20kg，热塑性树脂1kg。
实施例7
一种高抗蚀石墨胶泥，包括下述重量份原料：
电解石墨粉300kg，膨胀石墨100kg，氧化硼150kg，氧化钛150kg，热固性树脂150kg，热塑性树脂30kg。
实施例8
一种高抗蚀石墨胶泥，包括下述重量份原料：
电解石墨粉25kg，膨胀石墨8kg，氧化硼17kg，氧化钛7kg，热固性树脂12kg，热塑性树脂5kg。
实施例9
一种高抗蚀石墨胶泥，包括下述重量份原料：
电解石墨粉20kg，膨胀石墨10kg，氧化硼7kg，氧化钛18kg，热固性树脂18kg，热塑性树脂3kg。
实施例10
一种高抗蚀石墨胶泥，包括下述重量份原料：
电解石墨粉33kg，膨胀石墨13kg，氧化硼8kg，氧化钛18kg，热固性树脂11kg，热塑性树脂4kg。
实施例11
一种高抗蚀石墨胶泥，包括下述重量份原料：
电解石墨粉280kg，膨胀石墨110kg，氧化硼130kg，氧化钛70kg，热固性树脂160kg，热塑性树脂30kg。
实施例12
一种高抗蚀石墨胶泥，包括下述优选重量份原料：
电解石墨粉25kg，膨胀石墨12kg，氧化硼10kg，氧化钛15kg，热固性树脂13kg，热塑性树脂5kg。
实施例13
一种高抗蚀石墨胶泥，包括下述优选重量份原料：
电解石墨粉30kg，膨胀石墨8kg，氧化硼15kg，氧化钛10kg，热固性树脂17kg，热塑性树脂3kg。

Claims (4)

1.一种高抗蚀石墨胶泥，其特征是包括下述重量份原料：
电解石墨粉20～35，膨胀石墨5～15，氧化硼5～20，氧化钛5～20，热固性树脂10～20，热塑性树脂1～6。
2.根据权利要求1所述的高抗蚀石墨胶泥，其特征是包括下述重量份原料：电解石墨粉25～30，膨胀石墨8～12，氧化硼10～15，氧化钛10～15，热固性树脂13～17，热塑性树脂3～5。
3.根据权利要求2所述的高抗蚀石墨胶泥，其特征是包括下述重量份原料：电解石墨粉27，膨胀石墨10，氧化硼12，氧化钛12，热固性树脂15，热塑性树脂4。
4.根据权利要求1所述的高抗蚀石墨胶泥，其特征是包括下述重量份原料：电解石墨粉25，膨胀石墨10，氧化硼15，氧化钛15，热固性树脂15，热塑性树脂5。
CN2009101723577A 2009-10-09 2009-10-09 高抗蚀石墨胶泥 Expired - Fee Related CN101691304B (zh)