CN101672094A - 一种紫晶红石天然色复合砖 - Google Patents

一种紫晶红石天然色复合砖 Download PDF

Info

Publication number
CN101672094A
CN101672094A CN200910083676A CN200910083676A CN101672094A CN 101672094 A CN101672094 A CN 101672094A CN 200910083676 A CN200910083676 A CN 200910083676A CN 200910083676 A CN200910083676 A CN 200910083676A CN 101672094 A CN101672094 A CN 101672094A
Authority
CN
China
Prior art keywords
amethyst
natural color
color composite
red stone
cement
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN200910083676A
Other languages
English (en)
Inventor
苑敏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BEIJING NAITE TONGDA SCIENCE AND TECHNOLOGY DEVELOPMENT Co Ltd
Original Assignee
BEIJING NAITE TONGDA SCIENCE AND TECHNOLOGY DEVELOPMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BEIJING NAITE TONGDA SCIENCE AND TECHNOLOGY DEVELOPMENT Co Ltd filed Critical BEIJING NAITE TONGDA SCIENCE AND TECHNOLOGY DEVELOPMENT Co Ltd
Priority to CN200910083676A priority Critical patent/CN101672094A/zh
Publication of CN101672094A publication Critical patent/CN101672094A/zh
Pending legal-status Critical Current

Abstract

本发明一种紫晶红石天然色复合砖是一种双层砖，表面层是釉面免烧彩瓷砖，基础层是廉价免烧砖。的制作方法，基础层的原料比例为水泥∶砂子∶矿粉∶碎石∶水＝1∶1.44∶1.15∶3.16∶0.30，面料层的原料的配方是用20％氯化镁溶液，30％氧化镁，5％滑石粉，10％硅灰石粉，10％乳液，15％水，5％水泥，5％颜料及助剂(按重量比计算)。本发明的产品表面色泽艳丽，基础部分透气性良好，具有良好的抗压、抗折、抗冻等性能。本发明的方法工艺简单，可以保证生产出来的产品具有良好的质量。

Description

一种紫晶红石天然色复合砖
技术领域
本发明涉及一种紫晶红石天然色复合砖。
技术背景
近年来随着建筑装饰材料的不断发展，各种内外墙瓷砖的广泛应用，目前流行的瓷砖多以粘土为原料，先制成砖坯，再上釉层，最后高温烧制而成。其不足之处是工艺复杂浪费能源，成本高。城市道路的人行道上，都要铺设步道砖。最常见的步道砖是用混凝土压制成型的方形板材。这种方形板材的强度较低，铺装过程及使用过程中的破损率很高。虽然它的材料及制作成本较低，但实际成本却很高。另外它的最大不足是色调灰暗、单一，不利于城市的美化。为了提高步道板对城市的美化作用，出现了彩色步道板。现有的彩色步道板主要有彩色釉面砖、瓷质砖等，使得步道板即具有美观的色彩，又具有光滑的表面。这种彩色步道板虽然具有很多优点，但是也带来了一些新的问题。其中之一是表面过于光滑，不适合于在北方地区使用。因为在北方的冬季，当地面上会有雪、或者是霜，这时行人踏在由釉面砖、瓷质砖铺设的人行道上会感到很滑，经常发生行人在步道板上滑倒摔伤的现象。其二是釉面砖、瓷质砖的表面比较密实，其透水性、透气性均较差，铺装这种步道板的人行道，在雨季渗入的水分很难挥发出来，在寒冷的冬季，会因为步道板下的土地中的含水量较高，而使步道板膨胀破损。
发明内容
本发明的目的是克服了现有技术的缺点，提供了一条不用烧制，不用上釉的方法，它采用几种普通原料经混合搅拌，灌模成形，工艺简单，节约能源，成本低。具体方法是：
一种紫晶红石天然色复合砖，它用双层复合结构，基础层采用水泥∶砂子∶矿粉∶碎石∶水构成。
用氯化镁溶液、氧化镁、滑石粉、石粉、水泥、乳液、颜料及助剂，按一定比例混合、灌模形成表面。
石粉是紫晶红石粉。
基础层的原料为水泥∶砂子∶矿粉∶碎石∶水＝1∶1.44∶1.15∶3.16∶0.30。
面料层原料中所用水泥是白水泥。
每一块产品的边缘处有倒角。
制好面料层原料，搅拌均匀，先向自动成型机的底模中加入底料，振动使之密实，在加入面料层原料，振动使之密实，脱模后进行养护处理成产品。
面料层加入了荧光剂。
面料加入了防霉剂。
表面进行了抛光处理。
以上配料，先做基础层，然后再做表面层。
具体实施方式
基础层制作：按砂子∶矿粉∶碎石∶水＝1∶1.44∶1.15∶3.16∶0.30的比例配制好底料层原料，搅拌均匀，先向自动成型机的底模中加入底料层原料，振动使之密实，在加入面料层原料，振动使之密实，脱模后按照水泥制品的养护方法进行养护处理，制成产品。其中面料层原料中所用的水泥是白水泥。根据产品需求，可以在每一块产品的边缘处有倒角。
有益效果
本发明的产品不易破损、表面色泽艳丽、基础部分透气性良好，具有良好的抗压、抗折、抗冻等性能。本发明的方法工艺简单，可以保证生产出来的产品具有良好的质量。

Claims (10)

1、一种紫晶红石天然色复合砖，它用双层复合结构，其特征在于基础层采用水泥∶砂子∶矿粉∶碎石∶水构成。
2、根据权利要求1所述的一种紫晶红石天然色复合砖，其特征在于用氯化镁溶液、氧化镁、滑石粉、石粉、水泥、乳液、颜料及助剂，按一定比例混合、灌模形成表面。
3、根据权利要求1、2所述的一种紫晶红石天然色复合砖，其特征在于所述的石粉是翠绿石粉。
4、根据权利要求1、2所述的一种紫晶红石天然色复合砖，其特征在于所述的基础层的原料为水泥∶砂子∶矿粉∶碎石∶水＝1∶1.44∶1.15∶3.16∶0.30。
5、根据权利要求1所述的一种紫晶红石天然色复合砖，其特征是：其中面料层原料中所用水泥是白水泥。
6、根据权利要求1、2所述的一种紫晶红石天然色复合砖，其特征是：每一块产品的边缘处有倒角。
7、根据权利要求1、2所述的一种紫晶红石天然色复合砖，其特征在于制好面料层原料，搅拌均匀，先向自动成型机的底模中加入底料，振动使之密实，在加入面料层原料，振动使之密实，脱模后进行养护处理成产品。
8、据权利要求1所述的一种紫晶红石天然色复合砖，其特征在于面料层加入了荧光剂。
9、据权利要求1所述的一种紫晶红石天然色复合砖，其特征在于面料加入了防霉剂。
10、权利要求1所述的一种紫晶红石天然色复合砖，其特征在于表面进行了抛光处理。
CN200910083676A 2009-05-06 2009-05-06 一种紫晶红石天然色复合砖 Pending CN101672094A (zh)