CN101649550B - 一种聚丙烯除味剂 - Google Patents
一种聚丙烯除味剂 Download PDFInfo
- Publication number
- CN101649550B CN101649550B CN200910307900XA CN200910307900A CN101649550B CN 101649550 B CN101649550 B CN 101649550B CN 200910307900X A CN200910307900X A CN 200910307900XA CN 200910307900 A CN200910307900 A CN 200910307900A CN 101649550 B CN101649550 B CN 101649550B
- Authority
- CN
- China
- Prior art keywords
- polypropylene
- parts
- deodorant
- product
- districts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及小苯体聚丙烯除异味的除味剂，特别指一种聚丙烯除味剂。本发明是由下列重量份的原料制成：单硬脂酸甘油酯10-20份，乙撑双硬脂酰胺4-8份，重质碳酸钙10-15份，白油0.5-1份，高融聚丙烯5-10份，其余成份为聚丙烯。本发明能有效去除小苯体聚丙烯粉料的异味，在小苯体聚丙烯产品内添加1-2%的本发明产品，在纺粘无纺布设备上生产丙纶纺粘无纺布，就能较好的除去无纺布产品异味，满足了医卫材料的使用要求，从而扩大了产品的使用范围，同时满足了环保要求。
Description
技术领域
本发明涉及小苯体聚丙烯除异味的除味剂，特别指一种聚丙烯除味剂。
背景技术
小苯体聚丙烯装置生产的聚丙烯由于受其工艺本身的限制，在氢调、反应聚合取热过程中存在控制难度大，致使其产品分子量分布比较宽，同时会形成部分低分子混合物，低分子混合物随着含量的不同表现在产品上会出现不同程度的刺激性气味，大大限制了其产品的特殊用途。
发明内容
本发明的目的是针对背景技术中存在的缺点和问题加以改进、创新，提供一种针对小苯体聚丙烯产品在无纺布上的应用来解决异味问题的聚丙烯除味剂。
本发明是由下列重量份的原料制成：
单硬脂酸甘油酯10-20份，乙撑双硬脂酰胺4-8份，重质碳酸钙10-15份，白油0.5-1份，高融聚丙烯5-10份，其余成份为聚丙烯。
本发明各原料的最佳重量份为：
单硬脂酸甘油酯15份，乙撑双硬脂酰胺6份，重质碳酸钙12份，白油0.8份，高融聚丙烯8份，其余成份为聚丙烯。
本发明所述的高融聚丙烯为1500-2000融指。
本发明的制作方法是：将单硬脂酸甘油酯、乙撑双硬脂酰胺、重质碳酸钙、白油、高融聚丙烯和聚丙烯配比后，放置于高速搅拌机内搅拌5-8分钟，然后加入双螺杆挤出机，其中温度控制为一区200℃±2℃，二区210℃±2℃，三区210℃±2℃，四区215℃±2℃，五区210℃±2℃，六区200℃±2℃，七区190℃±2℃，同时保持抽真空设备运行平稳，确保一定的真空度；搅拌完成后冷却、拉条切粒、干燥，最后得成品包装入库。
本发明各原料的作用：
单硬脂酸甘油酯简称单甘脂，主要作用是排除低分子混合物，同时具有润滑、抗缩和抗静电作用。乙撑双硬脂酰胺即EBS，主要起协同作用，同时还起抗结块和防腐蚀作用。重质碳酸钙可以改善调整无纺布质量。白油主要起润滑作用。高融聚丙烯可以改善融体流动性。
本发明的优点及有益效果：
本发明能有效去除小苯体聚丙烯粉料的异味，在小苯体聚丙烯产品内添加1-2%的本发明产品，在纺粘无纺布设备上生产丙纶纺粘无纺布，就能较好的除去无纺布产品异味，满足了医卫材料的使用要求，从而扩大了产品的使用范围，同时满足了环保要求。
具体实施方式
实施例一：
取单硬脂酸甘油酯10kg、乙撑双硬脂酰胺4kg、重质碳酸钙10kg、白油0.5kg、高融聚丙烯5kg和聚丙烯170.5kg配比后，放置于高速搅拌机内搅拌5分钟，然后加入双螺杆挤出机，其中温度控制为一区198℃，二区208℃，三区208℃，四区213℃，五区208℃，六区198℃，七区188℃，同时保持抽真空设备运行平稳，确保一定的真空度；搅拌完成后冷却、拉条切粒、干燥，最后得成品包装入库。
实施例二：
取单硬脂酸甘油酯15kg、乙撑双硬脂酰胺6kg、重质碳酸钙12kg、白油0.8kg、高融聚丙烯8kg和聚丙烯158.5kg配比后，放置于高速搅拌机内搅拌6分钟，然后加入双螺杆挤出机，其中温度控制为一区200℃，二区210℃，三区210℃，四区215℃，五区210℃，六区200℃，七区190℃，同时保持抽真空设备运行平稳，确保一定的真空度；搅拌完成后冷却、拉条切粒、干燥，最后得成品包装入库。
实施例三：
取单硬脂酸甘油酯20kg、乙撑双硬脂酰胺8kg、重质碳酸钙15kg、白油1kg、高融聚丙烯10kg和聚丙烯146kg配比后，放置于高速搅拌机内搅拌8分钟，然后加入双螺杆挤出机，其中温度控制为一区202℃，二区212℃，三区212℃，四区217℃，五区212℃，六区202℃，七区192℃，同时保持抽真空设备运行平稳，确保一定的真空度；搅拌完成后冷却、拉条切粒、干燥，最后得成品包装入库。
本发明所述的实施例仅仅是对本发明的优选实施方式进行的描述，并非对本发明构思和范围进行限定，在不脱离本发明设计思想的前提下，本领域中工程技术人员对本发明的技术方案作出的各种变型和改进，均应落入本发明的保护范围，本发明请求保护的技术内容，已经全部记载在权利要求书中。
Claims (2)
1.一种聚丙烯除味剂，其特征在于它是由下列重量份的原料制成：
单硬脂酸甘油酯10-20份，乙撑双硬脂酰胺4-8份，重质碳酸钙10-15份，白油0.5-1份，高融聚丙烯5-10份，其余成份为聚丙烯；
所述的高融聚丙烯为1500-2000融指。
2.根据权利要求1所述的一种聚丙烯除味剂，其特征在于它是由下列重量份的原料制成：
单硬脂酸甘油酯15份，乙撑双硬脂酰胺6份，重质碳酸钙12份，白油0.8份，高融聚丙烯8份，其余成份为聚丙烯。