CN101597540B - 一种适用于气门加工的防锈切削液 - Google Patents
一种适用于气门加工的防锈切削液 Download PDFInfo
- Publication number
- CN101597540B CN101597540B CN2009100407958A CN200910040795A CN101597540B CN 101597540 B CN101597540 B CN 101597540B CN 2009100407958 A CN2009100407958 A CN 2009100407958A CN 200910040795 A CN200910040795 A CN 200910040795A CN 101597540 B CN101597540 B CN 101597540B
- Authority
- CN
- China
- Prior art keywords
- cutting fluid
- rust
- phenylformic acid
- dibasic
- acid monoethanolamine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明是关于一种适用于气门加工的防锈切削液，以苯甲酸单乙醇胺为主要防锈剂，以烷基磺胺乙酸钠为主要切削润滑剂，并在其中加入其它配料配制而成的水溶液，所述切削液的各原料的重量百分数配比是：苯甲酸单乙醇胺1～2.2％；磷酸氢二钠0.2～0.8％；丙三醇0.1～0.9％；烷基磺胺乙酸钠0.5～2.0％；分子量400～600的聚乙二醇0.1～0.5％；去离子水余量。本发明的适用于气门加工的防锈切削液，既能满足气门切削加工要求，又能满足其防锈要求，且安全无毒。
Description
技术领域
本发明涉及一种金属切削加工使用的化学溶液组合物，特别是涉及一种适用于气门加工的防锈切削液。
背景技术
气门是发动机的一个关键部件，它加工时对切削液有着特殊的要求：1)所用切削液在加工时能满足表面粗糙度要求；2)切削加工后，在湿度95％以上，温度35℃左右时，气门材料防锈期要求能达到7天以上；3)切削液安全无毒；对工人无过敏；4)切削液稳定，不发生分解及霉变。
现有切削液存在的主要问题是：1)润滑能力不足，气门精加工时难以满足表面粗糙度要求；2)防锈能力不足：一般切削加工后，防锈期不足一天，必须另做工序间防锈，这给大批量生产气门带来很多不便；3)工人容易过敏；4)为防霉变，很多切削液加入了酚类物质，对人体有一定毒害。
发明内容
本发明的目的在于，克服现有的切削液存在的缺陷，而提供一种新的既能满足气门切削加工要求，又能满足其防锈要求的安全无毒防锈切削液。
本发明的目的及解决其技术问题是采用以下技术方案来实现的。依据本发明提出的一种适用于气门加工的防锈切削液，是以苯甲酸单乙醇胺为主要防锈剂，以烷基磺胺乙酸钠为主要切削润滑剂，并在其中加入其它配料配制而成的水溶液，所述切削液的各原料的重量百分数配比是：
苯甲酸单乙醇胺 1～2.2％
磷酸氢二钠 0.2～0.8％
丙三醇 0.1～0.9％
烷基磺胺乙酸钠 0.5～2.0％
分子量400～600的聚乙二醇 0.1～0.5％
去离子水 余量。
根据本发明实施例的防锈切削液，为了使效果更佳，气门半精加工时，所述各原料的重量百分数配比是：苯甲酸单乙醇胺：1.2-2％，磷酸氢二钠：0.3-0.7％，丙三醇：0.2-0.8％，烷基磺胺乙酸钠：0.5-0.9％，分子量400～600的聚乙二醇：0.1-0.3％，去离子水余量。
根据本发明实施例的防锈切削液，气门半精加工时，所述各原料的重量百分数配比是：苯甲酸单乙醇胺：1.6％，磷酸氢二钠：0.5％，丙三醇：0.5％，烷基磺胺乙酸钠：0.7％，分子量400～600的聚乙二醇：0.2％，去离子水余量。
根据本发明实施例的防锈切削液，气门精加工时，所述各原料的重量百分数配比是：苯甲酸单乙醇胺：1.2-2％，磷酸氢二钠：0.3-0.7％，丙三醇：0.2-0.8％，烷基磺胺乙酸钠：1.4-2％，分子量400～600的聚乙二醇：0.3-0.5％，去离子水余量。
根据本发明实施例的防锈切削液，气门精加工时，所述各原料的重量百分数配比是：苯甲酸单乙醇胺：1.6％，磷酸氢二钠：0.5％，丙三醇：0.5％，烷基磺胺乙酸钠：1.7％，分子量400～600的聚乙二醇：0.4％，去离子水余量。
借由上述技术方案，本发明一种适用于气门加工的防锈切削液具有的有益效果是：
1)切削液安全无毒，不发霉，对工人无过敏，防锈性能良好，切削润滑性能优越，苯甲酸单乙醇胺是主要的防锈剂，切削后，遗留在气门表面的苯甲酸单乙醇胺能在气门表面形成不溶性络合膜，起防锈作用；同时，苯甲酸单乙醇胺在切削液中有一定的杀菌作用，能抑制霉变，并减少对工人的过敏。
2)磷酸氢二钠起辅助防锈作用，气门切削加工中，切削液是流动和循环的，有溶解氧的存在，磷酸氢二钠能在气门表面形成γ-三氧化二铁和磷酸铁的混合性保护膜，起防锈作用。
上述说明仅是本发明技术方案的概述，为了能够更清楚了解本发明的技术手段，而可依照说明书的内容予以实施，并且为了让本发明的上述和其他目的、特征和优点能够更明显易懂，以下特举较佳实施例，详细说明如下。
具体实施方式
为更进一步阐述本发明为达成预定发明目的所采取的技术手段及功效，对依据本发明提出的一种适用于气门加工的防锈切削液其具体实施方式、方法、步骤、特征及其功效，详细说明如后。
本发明一种适用于气门加工的防锈切削液，安全无毒，不发霉，对工人无过敏，防锈性能良好，切削润滑性能优越。其中，苯甲酸单乙醇胺是主要的防锈剂，切削后，遗留在气门表面的苯甲酸单乙醇胺能在气门表面形成不溶性络合膜，起防锈作用，同时，苯甲酸单乙醇胺在切削液中有一定的杀菌作用，能抑制霉变，并减少对工人的过敏。
磷酸氢二钠起辅助防锈作用，气门切削加工中，切削液是流动和循环的，有溶解氧的存在，磷酸氢二钠能在气门表面形成γ-三氧化二铁和磷酸铁的混合性保护膜，起防锈作用。
丙三醇的主要作用是抗高温湿热氧化，它与磷酸氢二钠一起可有效抵抗气门在高温湿热天气的腐蚀。
烷基磺胺乙酸钠是主要的润滑剂，聚乙二醇是湿润剂，起辅助润滑作用，它们能使气门切削加工时润滑良好，精加工时，容易达到表面粗糙度的要求。
实施例1
以苯甲酸单乙醇胺为主要防锈剂，以烷基磺胺乙酸钠为主要切削润滑剂，并在其中加入其它配料配制而成的水溶液，各原料的重量配比是：苯甲酸单乙醇胺：1-2.2％，磷酸氢二钠：0.2-0.8％，丙三醇：0.1-0.9％，烷基磺胺乙酸钠：0.5-2.0％，分子量400～600的聚乙二醇：0.1-0.5％，去离子水93.6-98.1％。
实施例2
取去离子水：95.3-97.7％，苯甲酸单乙醇胺：1.2-2％，磷酸氢二钠：0.3-0.7％，丙三醇：0.2-0.8％，烷基磺胺乙酸钠：0.5-0.9％，分子量400～600的聚乙二醇：0.1-0.3％搅拌混合配制而成。
实施例3
取去离子水：96.5％，苯甲酸单乙醇胺：1.6％，磷酸氢二钠：0.5％，丙三醇：0.5％，烷基磺胺乙酸钠：0.7％，分子量400～600的聚乙二醇：0.2％搅拌混合配制而成。
实施例4
取去离子水：94-96.6％，苯甲酸单乙醇胺：1.2-2％，磷酸氢二钠：0.3-0.7％，丙三醇：0.2-0.8％，烷基磺胺乙酸钠：1.4-2％，分子量400～600的聚乙二醇：0.3-0.5％搅拌混合配制而成。
实施例5
取去离子水：95.3％，苯甲酸单乙醇胺：1.6％，磷酸氢二钠：0.5％，丙三醇：0.5％，烷基磺胺乙酸钠：1.7％，分子量400～600的聚乙二醇：0.4％搅拌混合配制而成。
以上所述，仅是本发明的较佳实施例而已，并非对本发明作任何形式上的限制，虽然本发明已以较佳实施例揭露如上，然而并非用以限定本发明，任何熟悉本专业的技术人员，在不脱离本发明技术方案范围内，当可利用上述揭示的技术内容作出些许更动或修饰为等同变化的等效实施例，但凡是未脱离本发明技术方案内容，依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰，均仍属于本发明技术方案的范围内。
Claims (5)
1.一种适用于气门加工的防锈切削液，其特征在于：以苯甲酸单乙醇胺为主要防锈剂，以烷基磺胺乙酸钠为主要切削润滑剂，并在其中加入其它配料配制而成的水溶液，所述切削液的各原料的重量百分数配比是：
苯甲酸单乙醇胺 1～2.2％
磷酸氢二钠 0.2～0.8％
丙三醇 0.1～0.9％
烷基磺胺乙酸钠 0.5～2.0％
分子量400～600的聚乙二醇 0.1～0.5％
去离子水 余量。
2.根据权利要求1所述的适用于气门加工的防锈切削液，其特征在于：各原料的重量百分数配比是：苯甲酸单乙醇胺：1.2-2％，磷酸氢二钠：0.3-0.7％，丙三醇：0.2-0.8％，烷基磺胺乙酸钠：0.5-0.9％，分子量400～600的聚乙二醇：0.1-0.3％，去离子水余量。
3.根据权利要求1所述的适用于气门加工的防锈切削液，其特征在于：各原料的重量百分数配比是：苯甲酸单乙醇胺：1.6％，磷酸氢二钠：0.5％，丙三醇：0.5％，烷基磺胺乙酸钠：0.7％，分子量400～600的聚乙二醇：0.2％，去离子水余量。
4.根据权利要求1所述的适用于气门加工的防锈切削液，其特征在于：各原料的重量百分数配比是：苯甲酸单乙醇胺：1.2-2％，磷酸氢二钠：0.3-0.7％，丙三醇：0.2-0.8％，烷基磺胺乙酸钠：1.4-2％，分子量400～600的聚乙二醇：0.3-0.5％，去离子水余量。
5.根据权利要求1所述的适用于气门加工的防锈切削液，其特征在于：各原料的重量百分数配比是：苯甲酸单乙醇胺：1.6％，磷酸氢二钠：0.5％，丙三醇：0.5％，烷基磺胺乙酸钠：1.7％，分子量400～600的聚乙二醇：0.4％，去离子水余量。