CN101579869A - 一种抗静电装饰板 - Google Patents

一种抗静电装饰板 Download PDF

Info

Publication number
CN101579869A
CN101579869A CNA2009100946173A CN200910094617A CN101579869A CN 101579869 A CN101579869 A CN 101579869A CN A2009100946173 A CNA2009100946173 A CN A2009100946173A CN 200910094617 A CN200910094617 A CN 200910094617A CN 101579869 A CN101579869 A CN 101579869A
Authority
CN
China
Prior art keywords
antistatic
resin glue
decorated board
board
board according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2009100946173A
Other languages
English (en)
Inventor
邱天祥
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
YUNNAN YUNG LIFA FOREST GROUP Ltd
Original Assignee
YUNNAN YUNG LIFA FOREST GROUP Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by YUNNAN YUNG LIFA FOREST GROUP Ltd filed Critical YUNNAN YUNG LIFA FOREST GROUP Ltd
Priority to CNA2009100946173A priority Critical patent/CN101579869A/zh
Publication of CN101579869A publication Critical patent/CN101579869A/zh
Pending legal-status Critical Current

Abstract

一种抗静电装饰板,涉及一种人造板材,尤其是一种竹或木材料制作,具有抗静电功能装饰板。本发明的一种抗静电装饰板,以刨花板、定向结构刨花板或纤维板为基材,采用装饰浸渍纸作面层和底层,通过热压胶合而成,其特征在于刨花板、定向结构刨花板或纤维板中加入了抗静电材料,面层和底层装饰浸渍纸的浸渍材料是抗静电树脂胶,抗静电装饰板的表面电阻小于1010欧姆。本发明的抗静电装饰板外形美观,保持结构板的相应性能,又具有双重抗静电效果,成本低、耐腐蚀,板面电阻小于1010欧姆,是最佳的电子环境装饰板材选择。

Description

一种抗静电装饰板
技术领域
本发明涉及一种人造板材,尤其是一种竹或木材料制作,具有抗静电功能装饰板。
背景技术
在现代化电子计算机房、控制中心、军工厂、医院手术室、油气轮船、邮电通信、电台、电视台、会议室、油气田等场所,一般都布置有大量的电子设备,为保证信息传输的稳定和可靠性,因此要求场所装饰板材料都需要具备防静电的功能,确保其防火、防爆、不引起触电事故等静电灾害的发生。
目前,在电子工程技术领域环境中使用的抗静电装饰板的种类有木质地板、钢制冲压地板、铸铝地板和混凝土抗静电地板。其中,木质地板在温湿度变化中容易出现严重变形而使铺设不平的情况。钢制冲压及铸铝地板则制作成本高,承载能力不足,有严重锈蚀、变形情况,其产生的金属粉尘也对计算机有危害。而混凝土抗静电地板极易吸潮或在有水渗入后,使混凝土中的钢筋和钢网发生氧化反应,使钢部件生锈,进而使其机械强度逐渐降低。
发明内容
本发明所要解决的就是现有的抗静电装饰板不耐变形、强度低、成本高的问题,提供一种性能优良的抗静电装饰板。
本发明的一种抗静电装饰板,以刨花板、定向结构刨花板或纤维板为基材,采用装饰浸渍纸作面层和底层,通过热压胶合而成,其特征在于刨花板、定向结构刨花板或纤维板中加入了抗静电材料,面层和底层装饰浸渍纸的浸渍材料是抗静电树脂胶,抗静电装饰板的表面电阻小于1010欧姆。
所述的刨花板、定向结构刨花板或纤维板中加入的抗静电材料是碳纤维,其直径为7~12μm,纤维强度为350~550Mpa,加入的量为每100kg刨花板、定向结构刨花板或纤维板中加入15~18kg碳纤维。
所述的抗静电材料是在刨花板、定向结构刨花板或纤维板拌胶工序中加入。
所述的抗静电树脂胶是在树脂胶中加入了2-70wt-%非导电热固性粉末形成,2-70wt-%非导电热固性粉末是ATO或ITO微粒子,其粒径是10~20nm。
所述的刨花板、定向结构刨花板或纤维板是木质、竹质材料或是秸秆碎料制作而成。
所述的树脂胶是酚醛树脂胶、三聚氢胺树脂胶、脲醛树脂胶,装饰浸渍纸采用80~300g/m2的装饰纸通过在浸渍液中浸渍形成。
所述的面层和底层装饰浸渍纸的抗静电树脂胶是经过以下的工艺步骤制得:
a、将树脂胶反应完成,温度降至50℃;
b、向树脂胶中加氧化锡和石墨粉,按重量,加入比例为,树脂胶∶氧化锡∶石墨粉=100∶12∶18;
c、将加入氧化锡和石墨粉的树脂胶充分搅拌,反应15分钟后将树脂胶的温度降到30℃以下,存放至少24h。
本发明的抗静电树脂胶中加入了一种2-7wt%-d的非导电热固性粉末材料,如:氧化锡和石墨粉。氧化锡是金属氧化系填充型防静电材料的新品种,其性能比金属填充型材料略差一些,但性价比好。它是金属氧化系里性能和价格均佳的,它色相较淡,粒径很小,在0.1μm以下,其化学性质也较稳定,经过我们用多种金属氧化物试验,只有用氧化锡和石墨粉按一定的比例制成的树脂胶,其抗静电效果比较理想。
另外,为了使装饰板的抗静电效果达到最好,除了在生产装饰浸渍纸的环节中加入抗静电材料外,还在生产刨花板、定向结构刨花板或纤维板的拌胶工序中,添加了碳纤维。这样可以在当抗静电装饰板的面底层被破环时,装饰板的抗静电效果仍然存在。碳纤维是含碳量高于90%的无机高分子纤维,其中,含碳量高于99%的称石墨纤维。碳纤维的轴向强度和模量高,无蠕变,耐疲劳性好,比热及导电性介于非金属和金属之间,热膨胀系数小,耐腐蚀性好,纤维的密度低,X射线透过性好。因此在刨花板、定向结构刨花板或纤维板拌胶工序中,添加了碳纤维不仅能有效的起到抗静电的作用,也不会影响结构板的性能。
本发明的抗静电装饰板外形美观,保持结构板的相应性能,又具有双重抗静电效果,成本低、耐腐蚀,板面电阻小于1010欧姆,是最佳的电子环境装饰板材选择。
具体实施方式
实施例1:一种抗静电竹质定向结构刨花板装饰板,首先制作抗静电树脂胶,先制作300kg酚醛树脂胶,在反应完成,降温到50℃时,加入2-7wt%-d氧化锡36kg,石墨粉54kg,充分搅拌并保温15分钟,再降温到30℃,存放24小时。然后再将120g/m2的装饰纸通过浸胶机在制得的抗静电酚醛树脂胶中充分浸渍,再经干燥机在65℃~90℃温度下干燥,制成抗静电酚醛树脂浸渍装饰纸。
在生产竹质定向结构刨花板拌胶工序时,将碳纤维按每100kg竹刨花加入直径为7μm,纤维强度为550Mpa的碳纤维15kg,充分搅拌混合后,再经热压形成竹质定向结构刨花基板。
将基板砂光处理,基板厚度偏差不大于±0.2mm,然后把抗静电酚醛树脂浸渍装饰纸平整铺在基板上,经热压制成抗静电竹质定向结构装饰板,其板面电阻小于1010欧姆。
实施例2:一种抗静电木质刨花装饰板,首先制作抗静电树脂胶,先制作200kg脲醛树脂胶,在反应完成,降温到50℃时,按重量比加入2-7wt%-d氧化锡24kg,石墨粉36kg,充分搅拌并保温15分钟,再降温到30℃以下,存放24小时。然后再将125g/m2的装饰纸通过浸胶机在制得的抗静电脲醛树脂胶中充分浸渍,再经干燥机在65℃~90℃温度下干燥,制成抗静电脲醛树脂装饰纸。
在生产木质刨花板拌胶工序时,将碳纤维按每100kg木刨花加入直径为12μm,纤维强度为550Mpa的碳纤维15kg,并充分搅拌混合后,再经热压成抗静电木质刨花板装饰板。
将木质刨花板砂光基本处理,基板厚度偏差不大于±0.2mm,把抗静电脲醛树脂浸渍装饰纸平整铺在基板上,经热压制成抗静电装饰板,其板面电阻小于1010欧姆。
实施例3:一种抗静电中密度纤维装饰板,首先制作抗静电树脂胶,先制作150kg三聚氰胺树脂胶,在反应完成,降温到50℃时,按重量比加入2-7wt%-d氧化锡18kg,石墨粉27kg,充分搅拌并保温15分钟,再降温到30℃以下,存放24小时。然后将140g/m2的装饰纸通过浸胶机在制得的抗静电三聚氰胺树脂胶中充分浸渍,再经干燥机在65℃~90℃温度下干燥,制成抗静电三聚氰胺树脂浸渍装饰纸。
在生产中密度纤维板拌胶工序时,将碳纤维按每100kg加入纤维中加入直径为12μm,纤维强度为350Mpa碳纤维18kg,并充分搅拌混合后,再经热压制成中密度纤维基板。
将中密度纤维基板砂光处理,基板厚度偏差不大于±0.2mm,把抗静电三聚氰胺树脂浸渍装饰纸平整铺在人造板基板上,经热压制成抗静电装饰板,其板面电阻小于1010欧姆。

Claims (10)

1、一种抗静电装饰板,以刨花板、定向结构刨花板或纤维板为基材,采用装饰浸渍纸作面层和底层,通过热压胶合而成,其特征在于刨花板、定向结构刨花板或纤维板中加入了抗静电材料,面层和底层装饰浸渍纸的浸渍材料是抗静电树脂胶,抗静电装饰板的表面电阻小于1010欧姆。
2、根据权利要求1所述的一种抗静电装饰板,其特征在于所述的刨花板、定向结构刨花板或纤维板中加入的抗静电材料是碳纤维,其直径为7~12μm,纤维强度为350~550Mpa,加入的量为每100kg刨花板、定向结构刨花板或纤维板中加入15~18kg碳纤维。
3、根据权利要求1所述的一种抗静电装饰板,其特征在于所述的抗静电材料是在刨花板、定向结构刨花板或纤维板拌胶工序中加入。
4、根据权利要求1所述的一种抗静电装饰板,其特征在于所述的抗静电树脂胶是在树脂胶中加入了2-70wt-%非导电热固性粉末形成。
5、根据权利要求4所述的一种抗静电装饰板,其特征在于所述2-70wt-%非导电热固性粉末是ATO或ITO微粒子。
6、根据权利要求4所述的一种抗静电装饰板,其特征在于所述2-70wt-%非导电热固性粉末的粒径是10~20nm。
7、根据权利要求1所述的一种抗静电装饰板,其特征在于所述的刨花板、定向结构刨花板或纤维板是木质、竹质材料或是秸秆碎料的。
8、根据权利要求1或4所述的一种抗静电装饰板,其特征在于所述的树脂胶是酚醛树脂胶、三聚氢胺树脂胶、脲醛树脂胶。
9、根据权利要求1所述的一种抗静电装饰板,其特征在于所述的装饰浸渍纸采用80~300g/m2的装饰纸。
10、根据权利要求1所述的一种抗静电装饰板,其特征在于所述的面层和底层装饰浸渍纸的抗静电树脂胶是经过以下的工艺步骤制得:
c、将树脂胶反应完成,温度降至50℃;
d、向树脂胶中加氧化锡和石墨粉,按重量,加入比例为,树脂胶∶氧化锡∶石墨粉=100∶12∶18;
c、将加入氧化锡和石墨粉的树脂胶充分搅拌,反应15分钟后将树脂胶的温度降到30℃以下,存放至少24h。
CNA2009100946173A 2009-06-19 2009-06-19 一种抗静电装饰板 Pending CN101579869A (zh)