CN101575396B - 水性凹版油墨共聚乳液的加工工艺 - Google Patents
水性凹版油墨共聚乳液的加工工艺 Download PDFInfo
- Publication number
- CN101575396B CN101575396B CN2009103031496A CN200910303149A CN101575396B CN 101575396 B CN101575396 B CN 101575396B CN 2009103031496 A CN2009103031496 A CN 2009103031496A CN 200910303149 A CN200910303149 A CN 200910303149A CN 101575396 B CN101575396 B CN 101575396B
- Authority
- CN
- China
- Prior art keywords
- gram
- water
- aqueous solution
- gravure ink
- ammonium persulfate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种水性凹版油墨共聚乳液的加工工艺，先将烯丙氧基羟丙基磺酸钠与水混溶后，加入一定量的由醋酸乙烯酯、叔癸酸乙烯酯、亚甲基丁二酸、丙烯酸羟乙酯和十二烷硫醇组成的混合液升温至60-70℃，然后加入一定量的过硫酸铵水溶液，反应至78-82℃回流停时开始滴加余下的混合液，每滴加一小时加入过硫酸铵水溶液，滴加结束后加入余下的过硫酸铵水溶液在90-95℃的温度下保温，然后冷却制成乳液。该材料主要用来制作应用在水松纸上的水性凹版油墨连接料。制成的连接料一方面节省大量的粮食，另一方面减少使用有机溶剂，有效地避免了有机溶剂型所不可避免的易燃易爆、污染环境和危害生产工人健康等缺点，使其符合环保的要求。
Description
技术领域
本发明涉及一种粘胶剂，尤其是涉及到一种香烟过滤嘴用水松纸的粘接剂乳液的加工工艺，属于粘接剂技术领域。
背景技术
醇溶型烟咀纸胶液作为烟咀纸--水松纸凹版印刷油墨的连接料，其原理是利用聚醋酸乙烯易溶于含部分水的乙醇中的性质，同时通过乳液共聚引入丙烯酸丁酯增塑、甲基丙烯酸助溶，壬基酚聚氧乙烯醚增溶的多种因素作用下制取了醇溶性烟咀纸(水松纸)凹版印刷油墨的连接料，每吨连接料耗用95％食用乙醇600公斤左右，而且在配制油墨时还要使用大量的乙醇，这类溶剂虽然无毒，但仍然属于挥发性有机物之类。上世纪九十年代初，为了节省大量的食用乙醇，开始研制无乙醇粘接剂，如中国发明专利申请CN90109256.8，公开了一种《新型水松纸水溶性涂料粘合剂》，采用褐藻酸钠、三聚磷酸钠、油酸钠、尿素、丁苯胶乳、甲醛、水和消泡剂按一定比例混合而成，该粘合剂的使用虽然节约了大量的食用乙醇，但是采用了现在不符合环保要求的甲醛等材料，在香烟有害健康的基础上，又增加了致癌物质，长期接触会严重危害生产工人和烟民的健康，在许多国家已被禁止使用。随着现代社会对环保和安全意识日益增强，近几年来为了减少或不用有机溶剂、节能降耗、减少大气污染、印刷室内环境清洁和避免火灾危害，国内外研究人员都在研究开发新一代水松纸用粘合剂。
发明内容
通常制备水溶性共聚树脂有两种方法：共聚单体在有机溶剂中共聚成稠状共聚树脂，然后进行碱解制得水溶性共聚树脂，还有共聚单体组成中加入含羧基单体在有机溶剂中共聚成酸性稠状共聚树脂，加胺中和成盐而获得水溶性。
本发明的目的在于克服现有技术的不足，提供一种制备新型水溶性热固性粘合剂乳液--水性凹版油墨共聚乳液的加工工艺，一方面节省大量的粮食，另一方面减少使用有机溶剂，使粘合剂符合环保的要求。
实现本发明的技术方案是这样实现的：
水性凹版油墨共聚乳液的加工工艺，其特征在于：先把0.45-0.55克烯丙氧基羟丙基磺酸钠与100克水投入烧瓶中搅拌混溶后，加入由醋酸乙烯酯65-75克、叔癸酸乙烯酯8-12克、亚甲基丁二酸8-12克、丙烯酸羟乙酯8-12克、十二烷硫醇0.08-0.12克组成的混合液8-12克升温 至60-70℃，然后加入20克水中含过硫酸铵0.25-0.35克的水溶液5-8克，反应至78-82℃回流停时开始滴加余下的上述混合液，滴加温度控制在78-82℃，每滴加一小时加入上述过硫酸铵水溶液2-3克，滴加结束后加入余下的过硫酸铵水溶液在90-95℃的温度下保温1-3小时，然后冷却至室温制成乳液。
上述滴加时间为3.5-4.5小时。
本发明与现有技术相比具有如下优点：
1.采用该工艺制备成的新型水溶性热固性粘合剂的共聚乳液，一方面节省大量的粮食，另一方面减少使用有机溶剂，有效地避免了有机溶剂型所不可避免的易燃易爆、污染环境和危害生产工人健康等缺点，使制成的粘合剂符合环保的要求。
2.对卷烟过滤嘴棒用粘接剂有两点基本要求，一是粘接剂的粘度必须足够低，以满足嘴棒高速生产线的需要；二是确保包裹嘴棒的水松纸不产生发皱变形，由于嘴棒用水松纸很薄并具很强的吸水性很容易吸水发皱变形，而采用本发明工艺制成乳液来加工的连接料，粘度为90-150秒，具有的强吸水性和缓释功能，可确保水松纸不吸水变形，能够满足嘴棒生产的要求。
3.该工艺步骤简单、使用方便，无需对设备进行改造，在原有的设备上可以直接进行生产。
具体实施方式
水性凹版油墨共聚乳液的加工工艺：先把0.45-0.55克烯丙氧基羟丙基磺酸钠与100克水投入烧瓶中搅拌混溶后，加入由醋酸乙烯酯65-75克、叔癸酸乙烯酯8-12克、亚甲基丁二酸8-12克、丙烯酸羟乙酯8-12克、十二烷硫醇0.08-0.12克组成的混合液8-12克缓慢升温至60-70℃，然后加入20克水中含过硫酸铵0.25-0.35克的水溶液5-8克，反应至78-82℃回流停时开始滴加余下的上述混合液，滴加时间为3.5-4.5小时，每滴加一小时加入上述过硫酸铵水溶液2-3克，滴加结束后加入余下的过硫酸铵水溶液在90-95℃的温度下保温1-3小时，然后冷却至室温制成乳液。
将乳液和蒸馏水混合后加入有机胺或氨水将pH值调至8-9，然后加入食用乙醇1混合助溶即得微黄色透明粘稠、带乙醇味的水性凹版油墨连接料。
上述连接料加入铁黄、铁红、碳酸钙和蒸馏水后研磨可制得水性凹版水松纸印刷油墨。
Claims (2)
1.水性凹版油墨共聚乳液的加工工艺，其特征在于：先把0.45-0.55克烯丙氧基羟丙基磺酸钠与100克水投入烧瓶中搅拌混溶后，加入由醋酸乙烯酯65-75克、叔癸酸乙烯酯8-12克、亚甲基丁二酸8-12克、丙烯酸羟乙酯8-12克、十二烷硫醇0.08-0.12克组成的混合液8-12克，升温至60-70℃，然后加入20克水中含过硫酸铵0.25-0.35克的水溶液5-8克，反应至78-82℃回流停时开始滴加余下的上述混合液，每滴加一小时加入上述过硫酸铵水溶液2-3克，滴加结束后加入余下的过硫酸铵水溶液在90-95℃的温度下保温1-3小时，然后冷却至室温制成乳液。
2.根据权利要求1所述的水性凹版油墨共聚乳液的加工工艺，其特征在于：所述的滴加时间为3.5-4.5小时。