CN101569920B - 一种用于发泡模具的转移涂料 - Google Patents
一种用于发泡模具的转移涂料 Download PDFInfo
- Publication number
- CN101569920B CN101569920B CN2009100626160A CN200910062616A CN101569920B CN 101569920 B CN101569920 B CN 101569920B CN 2009100626160 A CN2009100626160 A CN 2009100626160A CN 200910062616 A CN200910062616 A CN 200910062616A CN 101569920 B CN101569920 B CN 101569920B
- Authority
- CN
- China
- Prior art keywords
- percent
- paint
- preservative
- transfer
- mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种用于消失模铸造的转移涂料,其组分及质量百分比为:苯乙烯18~25%,成膜剂20~30%,丙酮15~20%g,消泡剂0.3~0.6%,防腐剂0.01~0.04%,余量为二氯乙烷。成膜剂为聚苯乙烯、硝酸纤维、聚甲基丙烯酸甲酯中的任一种或两种。防腐剂为苯甲酸钠、山黎酸钾类防腐剂中的任一种或两种。消泡剂为聚二甲基硅氧烷、聚氧乙烯聚氧丙醇胺醚,聚氧丙烯甘油醚的任一种。配制好的转移涂料具有强度适中、涂层均匀、优良的转移性能,可改变成分来调节涂料的粘度。涂层厚度可自由控制,喷涂在发泡模具上风干、固化后可用于模样发泡,涂料可与模样一起发出,用于消失模铸造,来改善铸件的表面的光洁度。该涂料制备简单,成本低,影响因素少,容易控制。
Description
技术领域
本发明属于金属材料加工和冶金类技术领域,涉及的是一种液态的消失模转移涂料,可以用作消失模铸件表面改性或改善表面光洁度,具有配制方便简单,成本较低,可以随时制备等优点。
背景技术
消失模铸造是一种经济有效的生产优质近净形、复杂铸件的绿色铸造工艺,是目前发展最快的新型铸造工艺,铸铁、铸钢件的消失模铸造工艺已得到广泛的应用,铝、镁合金的消失模铸造在欧洲和北美已成为生产汽车缸体、缸盖、变速箱壳体和进气歧管等产品的主要成形工艺。最近几年,国内外真对镁合金的消失模铸造技术进行了大量的研究,并已取得了不少成果。一般消失模铸造的主要对象是复杂零件,精确成形零件表面大部分是非加工面,且工作环境比较恶劣,因此如何提高消失模铸造镁合金表面性能至关重要。另外一方面,目前无论是铸铁、铸钢,还是镁、铝合金的消失模铸件的表面光洁度都有待提高,开发研究能提高消失模铸件表面质量的新工艺显得尤为重要。
发明内容
本发明的目的在于提供一种用于发泡模具的转移涂料,该转移涂料具有较好的成膜性和转移性。
其组分及质量百分比为:
苯乙烯18%~25%,成膜剂20%~30%,丙酮15%~20%,消泡剂0.3%~0.6%,粉末防腐剂0.01%~0.04%,余量为二氯乙烷;
所述成膜剂为聚苯乙烯、硝酸纤维和聚甲基丙烯酸甲酯中的任一种或两种;
所述粉末防腐剂为苯甲酸钠和山黎酸钾类防腐剂中的任一种或两种;
所述消泡剂为聚二甲基硅氧烷、聚氧乙烯聚氧丙醇胺醚,聚氧丙烯甘油醚的任一种。
本发明筛选了多种常见的、成本较低的材料配制成一种液态的发泡模具转移涂料。涂料使用前呈液态,具有使用简单方便、操作性强等优点。本发明具有强度高、涂层均匀、表面光洁、优良的转移性能,并且可以改变成分来调节涂料的粘度。在使用过程中可以根据用户不同的要求,可以控制涂层的厚度,在发泡模具上风干、固化后通过发泡工艺从模具型腔壁转移到模样表面,用于消失模铸造,由于在模样表面有一层光滑的转移涂料,因此可以提高铸件表面的光洁度,改善以往消失模铸件表面质量较低的情况。
具体实施方式
本发明的主要关键技术是配制性能优良的涂料,如较好的成膜性、强度适中、转移性优良。制好的转移涂料能均匀的喷涂在发泡模具型腔内壁,发泡时受热软化转移到泡沫模样表面,用于后续的消失模铸造,来改善铸件表面光洁度。
本发明转移涂料选用性能优异的成膜物质,选用丙酮、苯乙烯做溶剂,二氯乙烷做稀释剂,另外添加消泡剂、防腐剂,制备时首先溶解成膜剂,然后加稀释剂、消泡剂、防腐剂搅拌15~20分钟,即可使用。用喷枪喷涂在发泡模具内表面,通过控制流速和喷涂次数来控制涂料厚度,风干、固化后向模具充填发泡珠粒,在蒸缸内,蒸汽压力为2个大气压,发泡时间4分钟左右,即可取出,得到的泡沫模样表面有一层从模具上转移的涂料,模样在刷涂消失模涂料后直接可以用于消失模铸造。浇注的同时转移涂料裂解汽化,铸件表面光洁度可以得到大大提高。
通过借助以下实施例将更加详细说明本发明,且以下实施例仅是说明 性的,本发明并不受这些实施例的限制。
实施例1:
配制转移涂料时取苯乙烯25%(25g),聚苯乙烯20%(20g),丙酮20%(20g),二甲基硅氧烷消泡剂0.6%(0.6g),苯甲酸钠防腐剂0.03%(0.03g),山黎酸钾类防腐剂0.01%(0.01g),余量为二氯乙烷。
实施例2:
配制转移涂料时取苯乙烯20%(20g),硝酸纤维30%(30g),丙酮15%(15g),聚氧乙烯聚氧丙醇胺醚消泡剂0.5%(0.5g),山黎酸钾类防腐剂0.02%(0.02g),余量为二氯乙烷。
实施例3:
配制转移涂料时取苯乙烯18%(18g),聚苯乙烯15%(15g),硝酸纤维10%(10g),丙酮18%(18g),聚氧丙烯甘油醚消泡剂0.3%(0.3g),苯甲酸钠防腐剂0.04%(0.04g),余量为二氯乙烷。
实施例4:
配制转移涂料时取苯乙烯22%(22g),聚苯乙烯18%(18g),聚甲基丙烯酸甲酯12%(12g),丙酮15%(15g),聚氧乙烯聚氧丙醇胺醚消泡剂0.4%(0.4g),山黎酸钾类防腐剂0.03%(0.03g),余量为二氯乙烷。
实施例5:
配制转移涂料时取苯乙烯25%(25g),聚甲基丙烯酸甲酯25%(25g),丙酮18%(18g),聚氧乙烯聚氧丙醇胺醚消泡剂0.4%(0.4g),山黎酸钾类防腐剂0.04%(0.04g),余量为二氯乙烷。
实例操作相同,首先在丙酮里溶解成膜剂,然后加入稀释剂苯乙烯、二氯乙烷和消泡剂、防腐剂,搅拌大约10~20分钟即可使用,按照不同用户的要求,涂刷在发泡模具内壁,或者喷喷均匀,等其风干、固化后可以用于发泡,软化转移到模样表面,用于消失模铸造从而改善表面的光洁度。
以上所述为本发明的较佳实施例而已,但本发明不应该局限于该实施例所公开的内容。所以凡是不脱离本发明所公开的精神下完成的等效或修改,都落入本发明保护的范围。
Claims (1)
1.一种用于发泡模具的转移涂料,其组分及质量百分比为:
苯乙烯18%~25%,成膜剂20%~30%,丙酮15%~20%,消泡剂0.3%~0.6%,粉末防腐剂0.01%~0.04%,余量为二氯乙烷;
所述成膜剂为聚苯乙烯、硝酸纤维和聚甲基丙烯酸甲酯中的任一种或两种;
所述粉末防腐剂为苯甲酸钠和山黎酸钾类防腐剂中的任一种或两种;
所述消泡剂为聚二甲基硅氧烷、聚氧乙烯聚氧丙醇胺醚,聚氧丙烯甘油醚的任一种。