CN101555118A - Inorganic tile powder - Google Patents

Inorganic tile powder Download PDF

Info

Publication number
CN101555118A
CN101555118A CNA2009100618821A CN200910061882A CN101555118A CN 101555118 A CN101555118 A CN 101555118A CN A2009100618821 A CNA2009100618821 A CN A2009100618821A CN 200910061882 A CN200910061882 A CN 200910061882A CN 101555118 A CN101555118 A CN 101555118A
Authority
CN
China
Prior art keywords
parts
inorganic tile
powder
inorganic
tile powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2009100618821A
Other languages
Chinese (zh)
Inventor
邱杰儒
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
QIUSHI HUBEI ENERGY SAVING BUILDING HI-TECH DEVELOPMENT Co Ltd
Original Assignee
QIUSHI HUBEI ENERGY SAVING BUILDING HI-TECH DEVELOPMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by QIUSHI HUBEI ENERGY SAVING BUILDING HI-TECH DEVELOPMENT Co Ltd filed Critical QIUSHI HUBEI ENERGY SAVING BUILDING HI-TECH DEVELOPMENT Co Ltd
Priority to CNA2009100618821A priority Critical patent/CN101555118A/en
Publication of CN101555118A publication Critical patent/CN101555118A/en
Pending legal-status Critical Current

Abstract

The invention relates to inorganic tile powder; the powder is characterized by comprising the following materials according to parts by weight: 290-310 parts of Portland cement, 600-630 parts of quartz sand, 2.9-3.1 parts of wooden fibre, 16-20 parts of RE5044 re-dispersible rubber powder, 11-13 parts of P1551Z re-dispersible rubber powder, 2.8-3.2 parts of hydroxypropyl methylcellulose, 2.5 parts of water reducing agent, 2.3-2.7 parts of air entraining agent, 1 part of moisture repel, and 20-60 parts of iron oxide pigment. The inorganic tile powder can be applied to a building wall face, which has the characteristics of good water resistance, high bonding strength, alkaline and impact and flushing resistance, anti-fouling property, self-cleaning function, air penetration property, freezing and thawing resistance, and good shrinkage ratio, and without cracking, blasting, flaking, and stripping.

Description

Inorganic tile powder
Technical field
The invention belongs to building material technical field, be specifically related to a kind of inorganic tile powder.
Background technology
In recent years, building wall adopts the porcelain brick sticking face; It is not high to exist cohesive strength, easy to crack, easy explosion, phenomenon such as easily flake, easily come off, and water-repellancy is bad.
Summary of the invention
The object of the present invention is to provide a kind of inorganic tile powder, this inorganic tile powder is applied to the characteristics that building wall has good waterproof performance.
To achieve these goals, technical scheme provided by the invention is: inorganic tile powder, it is characterized in that it is by ordinary Portland cement, quartz sand, wood fibre, the RE5044 re-dispersible glue powder, the P1551Z re-dispersible glue powder, Vltra tears, water reducer, air entrapment agent, hydrophober, the iron oxide pigment raw material mixes, and the shared mass fraction of each raw material is: 290~310 parts of ordinary Portland cements, 600~630 parts of quartz sands, 2.9~3.1 parts of wood fibres, 16~20 parts of RE5044 re-dispersible glue powders, 11~13 parts of P1551Z re-dispersible glue powders, 2.8~3.2 parts of Vltra tearss, 2.5 parts of water reducers, 2.3~2.7 parts of air entrapment agents, 1 part of hydrophober, 20~60 parts of iron oxide pigments.
The shared mass fraction of described each raw material is: 300 parts of ordinary Portland cements, 618 parts of quartz sands, 3 parts of wood fibres, 18 parts of RE5044 re-dispersible glue powders, 12 parts of P1551Z re-dispersible glue powders, 3 parts of Vltra tearss, 2.5 parts of water reducers, 2.5 parts of air entrapment agents, 1 part of hydrophober, 40 parts of iron oxide pigments.
Can use (constituting the inorganic tile slurry) after inorganic tile powder adds entry and stirs during use; The inorganic tile slurry is made up of inorganic tile powder and water, and the weight ratio of inorganic tile powder and water is 1: 0.2~0.4.
The invention has the beneficial effects as follows when this inorganic tile powder is applied to building wall:
1). this inorganic tile powder is applied to building wall to have: good waterproof performance, the cohesive strength height, do not ftracture, not explosion, do not flake, adeciduate characteristics; The water that has thoroughly solved tiling, brickwork joint is penetrated into indoor, destroys upholstery, the indoor attractive in appearance and sanitary difficult problem of influence;
2). can be in special-shaped metope moulding;
3). alkaline-resisting, shock resistance, washability, anti-contamination, have self-cleaning function;
4). ventilative, waterproof, freeze-thaw-, shrinking percentage are better;
5). color is abundant, and the color that can like according to oneself is selected;
6). easy construction is quick, labor and material saving;
7). belong to inorganic materials, nontoxic, tasteless, pollution-free, safety and environmental protection.
End-use: this product is constructed well than ceramics brick, is better than the water-proof function of ceramic tile, is applicable to the facing decoration of bodies of wall such as thermal insulation wall of exterior wall, concrete, aerated blocks, flyash brick, also can be used for promptly having the wall decoration of building renovation; Alleviate load to body of wall, more attractive in appearance than ceramics brick decorative wall, be lower than the cost of high price ceramics brick, with the same life-span of body of wall, be the most competitive of fine quality, inexpensive, the decoration of exterior wall product that thing is beautiful on the current market.
Embodiment
In order to understand the present invention better, further illustrate content of the present invention below in conjunction with embodiment, but content of the present invention not only is confined to the following examples.
Embodiment 1:
Inorganic tile powder, it is by ordinary Portland cement, quartz sand, wood fibre, the RE5044 re-dispersible glue powder, the P1551Z re-dispersible glue powder, Vltra tears, water reducer, air entrapment agent, hydrophober, the iron oxide pigment raw material mixes, and the shared mass fraction of each raw material of dry powder is: 300 parts of ordinary Portland cements, 618 parts of quartz sands, 3 parts of wood fibres, 18 parts of RE5044 re-dispersible glue powders, 12 parts of P1551Z re-dispersible glue powders, 3 parts of Vltra tearss, 2.5 parts of water reducers, 2.5 parts of air entrapment agents, 1 part of hydrophober, 40 parts of iron oxide pigments.
Described ordinary Portland cement is that Huaxin Concrete Co., Ltd produces model 42.5 normal silicate white cements.
Described quartz sand is that the refining quartz sand factory in Hubei produces model: 40~120 orders.
Described wood fibre is that Beijing Jin Lida light building material factory produces model: 500um.
Described RE5044 re-dispersible glue powder is that German Wa Ke company produces model: PE5044.
Described P1551Z re-dispersible glue powder is that German Wa Ke company produces model: R1551Z.
Described Vltra tears is that Mierocrystalline cellulose company limited of Jinzhou City HTC produces model: 100000S.
Described water reducer is that German Kening Co.,Ltd produces model: L-D.
Described air entrapment agent is that German Kening Co.,Ltd produces model: 712.
Described hydrophober is produced model: SHP50 for sky, the Shanghai worker company limited that formats.
Described iron oxide pigment is that Bayer A.G produces model: 4915.
Can use (constituting the inorganic tile slurry) after inorganic tile powder adds entry and stirs during use; The weight ratio of inorganic tile powder and water is 1: 0.35.
Constructional method: blade coating, brushing, spraying.
The material preparation:
1) the thick rubber powder of levelling: the thick rubber powder of cracking resistance levelling and clear water by 1: 0.3 weight ratio, are poured into water in the spice bucket earlier, after the thick rubber powder powder of cracking resistance levelling is poured into, fully stir into evenly to paste with electric mixer again, can criticize and scrape.
2) priming paint, finish paint stir direct use before using.
3) inorganic tile slurry: (press 1 during spraying: 0.3-0.4) dry powder and the clear water of inorganic tile powder are pressed 1: 0.35 weight ratio, (during blade coating) presses 1 with inorganic tile powder and clear water: the 0.2-0.25 weight ratio; Earlier water is poured in the spice bucket, after inorganic tile powder is poured into, fully stir into evenly to mobile bigger inorganic tile slurry with electric mixer again, can use.
Sequence of construction: reaching on the relevant criterion basic unit body of wall of national regulation, the thick putty of the supporting levelling of blade coating one time---brushing/spraying is supporting after 24 hours has color bottom paint one time---went out the ceramic tile lines with line of ink marker lattice after 24 hours, and T-me line paper self-adhesive tape---spraying/blade coating inorganic tile slurry---sprays/brush supporting finish paint after 48 hours
Construction environment: temperature is not less than 5 ℃, and relative humidity is not higher than 85%, and severe weather should be avoided construction.
The packed protection against the tide of package storage: 25kg, rainproof/18kg barreled are not deposited cool place, cleaning, exsiccant place, and product of the present invention belongs to the asepsis environment-protecting product, and be quick-fried, do not burn, be easy to carry about with one, transport.
The performance test experiment: control piece is existing common finished product ceramic tile.
1, the inorganic tile slurry of embodiment being made (dry powder of inorganic tile powder is mixed by 1: 0.35 weight ratio with clear water) is sprayed on building wall (groove shape internal surface, inorganic tile slurry coating thickness is 2-3mm), ceramic tile is attached to building wall (groove shape internal surface).The infiltration phenomenon appears in the experiment (discharging water in the groove) of soaking under same condition, control piece after 1 day, and the product of invention does not have the phenomenon of infiltration after 1 year.Illustrate that this inorganic tile powder is applied to the characteristics that building wall has good waterproof performance.
2, the inorganic tile slurry of embodiment being made (dry powder of inorganic tile powder is mixed by 1: 0.35 weight ratio with clear water) is sprayed on building wall (coating thickness is 2-3mm), and ceramic tile is attached to building wall.Control piece cracking, explosion occur, flakes after 1 year, obscission, and the product of invention did not ftracture after 1 year, not explosion, do not flake, do not come off.
3, alkali resistance test: spraying inorganic tile slurry (dry powder of inorganic tile powder is mixed by 1: 0.35 weight ratio with clear water, and coating thickness is 2-3mm) on 150mm * 70mm * 3mm uralite when temperature is 25 ℃, begins test after dry 28 days; After pressing the regulation off-test of GB/T9265, test plate surface is not had hollowing, ftractures, peels off, and compares with not soaking part, and color has slight variation.Illustrate that alkali resistance of the present invention is good.
4, impact resistance test: spraying inorganic tile slurry (mixes with clear water the dry powder of inorganic tile powder by 1: 0.35 weight ratio on 430mm * 150mm * 3mm uralite, coating thickness is 2-3mm), when temperature is 25 ℃, begin test after dry 28 days, the spherical counterweight that with weight is 530g lands from height 300mm, the Impact Test plate, peels off and is out of shape the flawless that detects by an unaided eye on the test panel.Good impact resistance of the present invention is described.
5, washability test: spraying inorganic tile slurry (mixes with clear water the dry powder of inorganic tile powder by 1: 0.35 weight ratio on 430mm * 150mm * 3mm uralite, coating thickness is 2-3mm), when temperature is 25 ℃, begin test after dry 28 days, washing powder with 0.5% and water sepage, its pH value is 10, scrubs the test plate (panel) surface and does not have for 5000 times damaged.Illustrate that abrasion resistance of the present invention is good.
6, contamination resistance test: spraying inorganic tile slurry (mixes with clear water the dry powder of inorganic tile powder by 1: 0.35 weight ratio on 150mm * 70m * 3mm uralite, coating thickness is 2-3mm), when temperature is 25 ℃, begin test after dry 28 days, after stirring with 100g flyash and 100ML water, with banister brush with the water of coal ash brushing at the test plate (panel) coatingsurface, water flushing behind the seasoning 2h, plate face and water column angle at 45, wash the seasoning 4h that finishes, the test plate (panel) surface reflectance is greater than 8%.Illustrate that contamination resistance of the present invention is good.
Embodiment 2:
Substantially the same manner as Example 1, difference is the shared mass fraction difference of each raw material, present embodiment: the shared mass fraction of each raw material is: 290 parts of ordinary Portland cements, 600 parts of quartz sands, 2.9 parts of wood fibres, 16 parts of RE5044 re-dispersible glue powders, 11 parts of P1551Z re-dispersible glue powders, 2.8 parts of Vltra tearss, 2.5 parts of water reducers, 2.3 parts of air entrapment agents, 1 part of hydrophober, 20 parts of iron oxide pigments.
Embodiment 3:
Substantially the same manner as Example 1, difference is the shared mass fraction difference of each raw material, present embodiment: the shared mass fraction of each raw material is: 310 parts of ordinary Portland cements, 630 parts of quartz sands, 3.1 parts of wood fibres, 20 parts of RE5044 re-dispersible glue powders, 13 parts of P1551Z re-dispersible glue powders, 3.2 parts of Vltra tearss, 2.5 parts of water reducers, 2.7 parts of air entrapment agents, 1 part of hydrophober, 60 parts of iron oxide pigments.
All ordinary Portland cements, quartz sand, wood fibre, re-dispersible glue powder, Vltra tears, water reducer, air entrapment agent, hydrophober, iron oxide pigment raw material all are applicable to the present invention, do not enumerate embodiment one by one at this.

Claims (10)

1. inorganic tile powder, it is characterized in that it is by ordinary Portland cement, quartz sand, wood fibre, the RE5044 re-dispersible glue powder, the P1551Z re-dispersible glue powder, Vltra tears, water reducer, air entrapment agent, hydrophober, the iron oxide pigment raw material mixes, and the shared mass fraction of each raw material is: 290~310 parts of ordinary Portland cements, 600~630 parts of quartz sands, 2.9~3.1 parts of wood fibres, 16~20 parts of RE5044 re-dispersible glue powders, 11~13 parts of P1551Z re-dispersible glue powders, 2.8~3.2 parts of Vltra tearss, 2.5 parts of water reducers, 2.3~2.7 parts of air entrapment agents, 1 part of hydrophober, 20~60 parts of iron oxide pigments.
2. inorganic tile powder according to claim 1 is characterized in that: the shared mass fraction of described each raw material is: 300 parts of ordinary Portland cements, 618 parts of quartz sands, 3 parts of wood fibres, 18 parts of RE5044 re-dispersible glue powders, 12 parts of P1551Z re-dispersible glue powders, 3 parts of Vltra tearss, 2.5 parts of water reducers, 2.5 parts of air entrapment agents, 1 part of hydrophober, 40 parts of iron oxide pigments.
3. inorganic tile powder according to claim 1 is characterized in that: described quartz sand is that the refining quartz sand factory in Hubei produces model: 40~120 orders.
4. inorganic tile powder according to claim 1 is characterized in that: described wood fibre is that Beijing Jin Lida light building material factory produces model: 500um.
5. inorganic tile powder according to claim 1 is characterized in that: described RE5044 re-dispersible glue powder is that German Wa Ke company produces model: PE5044; Described P1551Z re-dispersible glue powder is that German Wa Ke company produces model: R1551Z.
6. inorganic tile powder according to claim 1 is characterized in that: described Vltra tears is that Mierocrystalline cellulose company limited of Jinzhou City HTC produces model: 100000S.
7. inorganic tile powder according to claim 1 is characterized in that: described water reducer is that German Kening Co.,Ltd produces model: L-D.
8. inorganic tile powder according to claim 1 is characterized in that: described air entrapment agent is that German Kening Co.,Ltd produces model: 712.
9. inorganic tile powder according to claim 1 is characterized in that: described hydrophober is that German Kening Co.,Ltd produces model: SHP50.
10. inorganic tile powder according to claim 1 is characterized in that: described iron oxide pigment is that Bayer A.G produces model: 4915.
CNA2009100618821A 2009-04-28 2009-04-28 Inorganic tile powder Pending CN101555118A (en)