CN101538428A - 糯米凝胶建筑腻子粉 - Google Patents
糯米凝胶建筑腻子粉 Download PDFInfo
- Publication number
- CN101538428A CN101538428A CN200910031540A CN200910031540A CN101538428A CN 101538428 A CN101538428 A CN 101538428A CN 200910031540 A CN200910031540 A CN 200910031540A CN 200910031540 A CN200910031540 A CN 200910031540A CN 101538428 A CN101538428 A CN 101538428A
- Authority
- CN
- China
- Prior art keywords
- sticky rice
- rice gel
- powder
- lacquer putty
- putty powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种糯米凝胶建筑腻子粉，属建筑材料。由糯米凝胶、硅酸盐水泥、石英砂、海泡石粉、冷融聚乙烯醇胶粉、羟丙基甲基纤维素、聚丙烯短纤和木质纤维混合制成。用糯米凝胶、冷溶聚乙烯醇胶粉替代原有技术中的可分散聚醋酸乙烯乳胶干粉和羧甲基纤维素。使腻子的稳定性、耐老化性和耐水性大大提高。本发明的优点是，粘接强度高、耐水性好，并抗裂、抗老化、易施工。
Description
技术领域
本发明涉及化学建材类。具体是一种糯米凝胶建筑腻子粉。
背景技术
建筑腻子粉分为内墙建筑腻子粉和外墙建筑腻子粉。目前国内已公开的内墙建筑腻子粉以氢氧化钙、滑石粉、方解石粉、硫酸钙、可分散聚醋酸乙烯乳胶干粉和羧甲基纤维素等组成。其虽有一定的粘接强度和装饰性，但其耐水性能差，且易生霉。已公开的外墙建筑腻子粉以硅酸盐水泥、方解石粉、可分散聚醋酸乙烯乳胶干粉和羧甲基纤维素等组成，其虽有一定的粘接强度和装饰性，但其易开裂、易生霉、易空鼓，耐水性和耐老化性能一般。
发明内容
为解决上述技术问题，本发明提供一种糯米凝胶建筑腻子粉。选用符合环保要求的材料和辅助材料，使腻子的稳定性和耐老化性和耐水性大大提高。
本发明事宜如下技术方案实现的：一种糯米凝胶建筑腻子粉，其特征在于以下述重量份的原料混合制成：
糯米凝胶 3-40份
硅酸盐水泥 200-600份
石英砂 50-400份
海泡石粉 20-150份
冷融性聚乙烯醇胶粉 2-20份
羟丙基甲基纤维素 1-5份
聚丙烯短纤 1-6份
木质纤维 1-10份；
所述的糯米凝胶是用糯米为原料，用下述方法制作的：
1)糯米加水和明矾蒸煮至浆状；糯米、水和明矾三者的重量份是：糯米270-350份，水670份，明矾4.2份；
2)过滤，除去非浆状物；
3)干燥；
4)粉碎过筛，细度≤150目。
本发明的有益效果是：用糯米凝胶、冷溶聚乙烯醇胶粉替代可分散聚醋酸乙烯乳胶干粉和羧甲基纤维素。糯米凝胶与硅酸盐水泥中的氧化钙等碱性物质在水的条件下反应形成稳定的硅钙网状骨架结构，使腻子的稳定性和耐老化性和耐水性大大提高。糯米凝胶能辅助冷溶聚乙烯醇胶粉，提高其粘接性，改善腻子施工的平滑性。海泡石粉具有很强的吸水性，能控制施工中腻子水份的蒸发，使硅酸盐水泥与水充分水化反应，保证其强度达到最佳。添加聚丙烯短纤增强了腻子的抗裂性，避免腻子使用后的空鼓。
糯米凝胶建筑腻子粉使用时直接用水调和，保证了腻子调和的快捷和质量的一致性。
具体实施方式
下面结合实施例进一步说明本发明的效果。
实施例1
一、各种原料及配比(重量份)
糯米凝胶 20kg
硅酸盐水泥 500kg
石英砂 350kg
海泡石粉 110kg
冷融性聚乙烯醇胶粉 10kg
羟丙基甲基纤维素 3.5kg
聚丙烯短纤 3.2kg
木质纤维 5kg。
二)糯米凝胶制备：
1)糯米330kg加水670kg和明矾4.2kg；放入搪瓷反应釜中加热至100-120℃蒸煮约50分钟；取出；
2)用50目不锈钢过滤机过滤除去非浆状物；
3)用板式干燥器干燥；
4)粉碎过筛，细度≤150目，得腻子粉。
三)将各原料混合用干粉搅拌机搅拌成腻子粉
四)检测：经检测糯米凝胶建筑腻子各项技术指标均达到并优于《建筑外墙用腻子》JC/T157-2004国家建筑工业行业标准。
Claims (4)
1、一种糯米凝胶建筑腻子粉，其特征在于以下述重量份的原料混合制成：
糯米凝胶 3-40份
硅酸盐水泥 200-600份
石英砂 50-400份
海泡石粉 20-150份
冷融性聚乙烯醇胶粉 2-20份
羟丙基甲基纤维素 1-5份
聚丙烯短纤 1-6份
木质纤维 1-10份；
所述的糯米凝胶是用糯米为原料，用下述方法制作的：
1)糯米加水和明矾蒸煮至浆状；糯米、水和明矾三者的重量份是：糯米270-350份，水670份，明矾4.2份；
2)过滤，除去非浆状物；
3)干燥；
4)粉碎过筛，细度≤150目。
2、根据权利要求1所述的糯米凝胶建筑腻子粉，其特征在于糯米凝胶制备过程中的蒸煮工序的蒸煮温度为100-120度。
3、根据权利要求1所述的糯米凝胶建筑腻子粉，其特征在于糯米凝胶制备过程中的过滤工序采用50目过滤机过滤。
4、根据权利要求1所述的糯米凝胶建筑腻子粉，其特征在于糯米凝胶制备过程中的干燥工序采用板式干燥机。