CN101525458A - Lava - Google Patents
Lava Download PDFInfo
- Publication number
- CN101525458A CN101525458A CN200810217370A CN200810217370A CN101525458A CN 101525458 A CN101525458 A CN 101525458A CN 200810217370 A CN200810217370 A CN 200810217370A CN 200810217370 A CN200810217370 A CN 200810217370A CN 101525458 A CN101525458 A CN 101525458A
- Authority
- CN
- China
- Prior art keywords
- parts
- quartzy mud
- lava
- quartzy
- mud
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to Lava, in particular to Lava which has good stretching effect and cannot be stuck to hands. The Lava contains polyvinyl alcohol solution which accounts for 20-60 portions of 100 portions of the total weight of the Lava; the Lava also comprises 30-60 portions of demineralized water, 0.5-2 portions of xanthan gum, 6-20 portions of propanetriol and 0.1-0.3 portion of borax, and the Lava is manufactured by stirring the composition. The invention has the advantages that: (1) the Lava enables children to practice the operation skill, promote the development of small muscle of hands and enhance the coordination ability of hands and eyes; (2) the capability of bravely expressing individual points of view and communicating and cooperating with other people of children is fostered; (3) membrane with the thickness smaller than 0.01 mm can be stretched, cannot break after being wound for 360 degrees, cannot be stuck to hands and can be used for blowing bubbles; (4) the Lava has better tenacity, enhanced stretching performance and very good elasticity and is not easy to stick to hands; and (5) shimmering powder in the shimmering powder Lava is not easy to sink.
Description
Technical field
The present invention relates to a kind of quartzy mud, refer more particularly to a kind of have good drawing effect and tack-free quartzy mud.
Background technology
Quartzy mud is also referred to as intention mud, is a kind of novel soft sculpture material of countries such as a kind of America and Europe of being popular in, Japan and Korea S., and this mud can oily hand, play cleaner, do not have the sort of oil sensation of general color mud, and be nonpoisonous and tasteless, feel very fine and smooth.Be the substitute products of traditional plasticine, compare that both differences just are with traditional plasticine:
1, quartzy mud does not have greasy feeling, and is nonpoisonous and tasteless, safety and Health.Traditional plasticine has the taste of essence, is regulated because it can add a large amount of flavouring agents in process of production, has a kind of oily sensation in the process of playing.2, intention mud is because easily moulding, easy gluing, and the mud of different color, different dry humidity is taken together and just can be cemented, and can arbitrarily stretch in the process of playing, crooked, winding and easy fracture not.
Common quartzy mud on the existing market is more crisp, and drawing effect is not so good, and elasticity is also relatively poor in addition, touches with one's hand than being easier to.Based on the weak point of existing quartzy mud, the inventor has designed a kind of have good drawing effect and tack-free " a kind of quartzy mud ".
Summary of the invention
The present invention is directed to above-mentioned the deficiencies in the prior art technical problem to be solved is: a kind of have good drawing effect and tack-free quartzy mud are provided.
The technical solution adopted for the present invention to solve the technical problems is:
A kind of quartzy mud, quartzy mud composition contains polyvinyl alcohol solution, it is 20-60 part of 100 parts that described polyvinyl alcohol solution accounts for quartzy mud gross weight, also include softening water 30-60 part, xanthan gum 0.5-2 part, glycerol 6-20 part and borax 0.5-3 part in the quartzy mud composition, quartzy mud is stirred by above-mentioned each composition and forms.
Described polyvinyl alcohol solution is made by following steps:
1), in parts by weight with 30 parts of polyvinyl alcohol and 100 parts of mixing of water;
2), mixed polyethylene alcohol and water is placed on is heated to 100 ℃ in the reactor;
3), under 100 ℃ constant temperature, stir the polyethylene alcohol and water then;
4), the cooling of the mixed solution after will stirring, promptly obtain polyvinyl alcohol solution.
Described polyethylene alcohol and water stirred 5 hours under 100 ℃ constant temperature in step 3).
Described each composition of quartzy mud obtains quartzy mud after stirring 2-3 hour at normal temperatures in the stirrer.
It is 100 parts 50 parts that described polyvinyl alcohol solution accounts for quartzy mud total amount, also includes 0.8 part of 36.2 parts of softening waters, 1 part of xanthan gum, 12 parts of glycerol and borax in the quartzy mud composition.
Also include the shimmering powder of 2.5-6 part in the described quartzy mud composition.
Described quartzy mud composition can also obtain the quartzy mud of shimmering powder by above-mentioned each composition for 3 parts of polyvinyl alcohol solution 48,37.4 parts of softening waters, 1 part of xanthan gum, 10 parts of glycerol, 0.6 part of borax and shimmering powders after stirring 2-3 hour at normal temperatures in the stirrer.
The beneficial effect of a kind of quartzy mud of the present invention is:
1), by go to rub with hand, rub with the hands, pinch, paste, insert, tear, turn round, twist, connect, carve, pressure, action such as bonding, can allow child practise operation skill, promote the development of the little muscle of hand, strengthen the ability of hand eye coordination.
2), the quartzy mud of different colours can make up, mould the article of different shapes and size, the imagination and the creativity that can inspire child.
3), father and mother and child play the recreation of mud skill together, need cooperate with one another in recreation, cultivate child and dare to expressing own viewpoint and link up the ability of cooperation with other people.
4), can to pull out thickness be the following film of 0.01mm, can twine 360 degree and not rupture, tack-free, and can blow bubbles.
5), compare the common quartzy mud on the existing market, the toughness that seems is better, tensile property also improves, elasticity is also very good in addition, and is not easy to touch with one's hand.
6), the shimmering powder in the quartzy mud of shimmering powder is not easy the situation of sinking to the bottom.
Embodiment
The present invention implements like this:
In embodiment 1, a kind of quartzy mud, quartzy mud composition contains polyvinyl alcohol solution, it is in 100 parts 50 parts that polyvinyl alcohol solution accounts for quartzy mud gross weight, softening water accounts for 36.2 parts, xanthan gum and accounts for 1 part, glycerol and account for 10 parts and borax and account for 0.6 part, and each composition of quartzy mud is obtained quartzy mud after stirring 2 hours at normal temperatures in the stirrer.
And polyvinyl alcohol solution is made by following steps:
1), in parts by weight with 30 parts of polyvinyl alcohol and 100 parts of mixing of water;
2), mixed polyethylene alcohol and water is placed on is heated to 100 ℃ in the reactor;
3), under 100 ℃ constant temperature, stirred the polyethylene alcohol and water 5 hours then;
4), the cooling of the mixed solution after will stirring, promptly obtain polyvinyl alcohol solution.
In embodiment 2, quartzy mud composition is 3 parts of 48 parts of polyvinyl alcohol solutions, 37.4 parts of softening waters, 1 part of xanthan gum, 10 parts of glycerol, 0.6 part of borax and shimmering powders, obtains the quartzy mud of shimmering powder by above-mentioned each composition after stirring 2-3 hour at normal temperatures in the stirrer.
Wherein quartzy mud composition can have the shimmering powder of 2.5-6 part, and the quartzy mud of the shimmering powder that obtains like this shimmering powder can not take place sinks to the bottom phenomenon.The above only be the preferred embodiment of a kind of quartzy mud of the present invention, and the content of each composition can be softening water 30-60 part, xanthan gum 0.5-2 part, glycerol 6-20 part, borax 0.5-3 part, polyvinyl alcohol solution 20-60 part, shimmering powder 2.5-6 part; Therefore the above embodiments are not that technical scope of the present invention is imposed any restrictions, and every foundation technical spirit of the present invention all still belongs in the scope of technical solution of the present invention above any trickle modification, equivalent variations and modification that embodiment did.
Claims (7)
1, a kind of quartzy mud, quartzy mud composition contains polyvinyl alcohol solution, it is characterized in that: it is 20-60 part of 100 parts that described polyvinyl alcohol solution accounts for quartzy mud gross weight, also include softening water 30-60 part, xanthan gum 0.5-2 part, glycerol 6-20 part and borax 0.1-0.3 part in the quartzy mud composition, obtain quartzy mud after above-mentioned each composition is stirred.
2, a kind of quartzy mud according to claim 1 is characterized in that described polyvinyl alcohol solution made by following steps:
1), in parts by weight with 30 parts of polyvinyl alcohol and 100 parts of mixing of water;
2), mixed polyethylene alcohol and water is placed on is heated to 100 ℃ in the reactor;
3), under 100 ℃ constant temperature, stir the polyethylene alcohol and water then;
4), the cooling of the mixed solution after will stirring, promptly obtain polyvinyl alcohol solution.
3, a kind of quartzy mud according to claim 2 is characterized in that described polyethylene alcohol and water stirred 5 hours under 100 ℃ constant temperature in step 3).
4, a kind of quartzy mud according to claim 1 is characterized in that described each composition of quartzy mud obtains quartzy mud after stirring 2-3 hour in the stirrer.
5, according to claim 1 or 2 or 3 described a kind of quartzy mud, it is characterized in that it is in 100 parts 50 parts that described polyvinyl alcohol solution accounts for quartzy mud gross weight, also include 0.8 part of 36.2 parts of softening waters, 1 part of xanthan gum, 12 parts of glycerol and borax in the quartzy mud composition.
6, a kind of quartzy mud according to claim 1 is characterized in that also including in the described quartzy mud composition shimmering powder of 2.5-6 part.
7, a kind of quartzy mud according to claim 5, it is characterized in that described quartzy mud composition includes 3 parts of 48 parts of polyvinyl alcohol solutions, 37.4 parts of softening waters, 1 part of xanthan gum, 10 parts of glycerol, 0.6 part of borax and shimmering powders, obtains the quartzy mud of shimmering powder by above-mentioned each composition after stirring 2-3 hour in the stirrer.