CN101514096A - 新型环保防火嵌缝石膏 - Google Patents

新型环保防火嵌缝石膏 Download PDF

Info

Publication number
CN101514096A
CN101514096A CNA2008100579466A CN200810057946A CN101514096A CN 101514096 A CN101514096 A CN 101514096A CN A2008100579466 A CNA2008100579466 A CN A2008100579466A CN 200810057946 A CN200810057946 A CN 200810057946A CN 101514096 A CN101514096 A CN 101514096A
Authority
CN
China
Prior art keywords
gypsum
environment
friendly fireproof
percent
filleting
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2008100579466A
Other languages
English (en)
Other versions
CN101514096B (zh
Inventor
周梦文
冯菊莲
周建中
颜博渊
杨青
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BNBM Suzhou Co Ltd
Original Assignee
Beijing New Building Material Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beijing New Building Material Group Co Ltd filed Critical Beijing New Building Material Group Co Ltd
Priority to CN2008100579466A priority Critical patent/CN101514096B/zh
Publication of CN101514096A publication Critical patent/CN101514096A/zh
Application granted granted Critical
Publication of CN101514096B publication Critical patent/CN101514096B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种环保型防火嵌缝石膏，包括：非金属矿物防火材料0.2～8％、调整剂0.1～5％、保水增稠剂0.01～0.8％、粘接剂0.01～0.2％、缓凝剂0.01～0.5％、增强剂0.1～2％、余量为建筑石膏粉；其中，所述百分比为重量百分比。本发明由于添加了云母粉或蛭石等非金属矿物防火材料，配以增强剂、调整剂等，既保证了嵌缝石膏的基本性能，同时还具有防火、抗龟裂、环保无毒、无刺激等特点。

Description

新型环保防火嵌缝石膏
技术领域
本发明涉及一种环保型防火嵌缝石膏，特别是具有防火、抗龟裂、环保无毒、无刺激等特点的新型环保防火嵌缝石膏。
背景技术
嵌缝石膏是在建筑施工过程中用于填充地砖或是墙体石膏板之间缝隙的材料。由于缝隙所占地面或是墙体的面积很少，因此人们普遍认为用普通的不具有防火功能的嵌缝石膏填充该缝隙就可以了，即使发生火灾该嵌缝也起不到什么实质的作用。因此，目前的嵌缝石膏仍然是常规石膏。
然而，由于现有的嵌缝石膏不具有防火功能，因此当火灾发生时虽然石膏板墙体一般不会发生龟裂、火焰穿透等现象，但往往会在板缝之间的缝隙发生龟裂，并有火焰穿透现象发生。
发明内容
本发明要解决的技术问题是提供一种新型环保防火嵌缝石膏，当火灾发生时，该嵌缝石膏能够防止板缝之间发生龟裂及火焰穿透。
为了解决上述问题，本发明提供了一种环保型防火嵌缝石膏包括：
非金属矿物防火材料0.2～8％、调整剂0.1～5％、保水增稠剂0.01～0.8％、粘接剂0.01～0.2％、缓凝剂0.01～0.5％、增强剂0.1～2％、余量为建筑石膏粉；其中，所述百分比为重量百分比。
优选地，所述非金属矿物防火材料为云母粉、蛭石粉中的至少一种。
优选地，所述调整剂为磺酸盐。
优选地，所述缓凝剂为柠檬酸。
优选地，所述保水增稠剂为甲基纤维素、羧甲基纤维素钠或纤维素醚。
优选地，所述粘接剂为胶粉。
优选地，所述增强剂为硼砂或硼酸。
本发明由于添加了云母粉或蛭石等非金属矿物防火材料，配以增强剂、调整剂等，既保证了嵌缝石膏的基本性能，同时还具有防火、抗龟裂、环保无毒、无刺激等特点。
具体实施方式
实施例1
本实施例的具体制备工艺如下：
步骤1：首先按照如下配比称取各组分：建筑石膏粉91.3％、云母粉0.2％、调整剂5％、保水增稠剂0.8％、粘接剂0.2％、缓凝剂0.5％、增强剂2％；其中，上述百分比为重量百分比；
步骤2：将建筑石膏粉加入到混料机，同时将云母粉及上述其它外加剂也加入到混料机，混匀后按一定重量进行包装即成产品。
调整剂选用磺酸盐，缓凝剂选用柠檬酸，保水增稠剂选用甲基纤维素，粘接剂选用胶粉，增强剂选用硼酸。
本实施例制备出的防火嵌缝石膏，其主要技术指标满足如下要求：初凝时间为40～70分钟，终凝时间为50～80分钟，0.2mm筛余小于1％，抗折强度不低于1.5MPa，抗压强度不低于3.0MPa，耐火时间不低于1小时。
实施例2
本实施例的具体制备工艺如下：
步骤1：首先按照如下配比称取各组分：建筑石膏粉91.77％、蛭石粉8％、调整剂0.1％、保水增稠剂0.01％、粘接剂0.01％、缓凝剂0.01％、增强剂0.1％；其中，上述百分比为重量百分比；
步骤2：将建筑石膏粉加入到混料机，同时将蛭石粉及上述其它外加剂也加入到混料机，混匀后按一定重量进行包装即成产品。
调整剂选用磺酸盐，缓凝剂选用柠檬酸，保水增稠剂选用纤维素醚，粘接剂选用胶粉，增强剂选用硼酸。
本实施例制备出的防火嵌缝石膏，其主要技术指标满足如下要求：初凝时间为40～70分钟，终凝时间为50～80分钟，0.2mm筛余小于1％，抗折强度不低于1.5MPa，抗压强度不低于3.0MPa，耐火时间不低于2小时。
实施例3
本实施例的具体制备工艺如下：
步骤1：首先按照如下配比称取各组分：建筑石膏粉90.2％、蛭石粉3％、云母粉2.5％、调整剂2.5％、保水增稠剂0.4％、粘接剂0.1％、缓凝剂0.3％、增强剂1％；其中，上述百分比为重量百分比；
步骤2：将建筑石膏粉加入到混料机，同时将蛭石粉及上述其它外加剂也加入到混料机，混匀后按一定重量进行包装即成产品。
调整剂选用磺酸盐，缓凝剂选用柠檬酸，保水增稠剂选用羧甲基纤维素钠，粘接剂选用胶粉，增强剂选用硼酸。
本实施例制备出的防火嵌缝石膏，其主要技术指标满足如下要求：初凝时间为40～70分钟，终凝时间为50～80分钟，0.2mm筛余小于1％，抗折强度不低于1.5MPa，抗压强度不低于3.0MPa，耐火时间不低于3小时。

Claims (7)

1、一种环保型防火嵌缝石膏，其特征在于，包括：
非金属矿物防火材料0.2～8％、调整剂0.1～5％、保水增稠剂0.01～0.8％、粘接剂0.01～0.2％、缓凝剂0.01～0.5％、增强剂0.1～2％、余量为建筑石膏粉；其中，所述百分比为重量百分比。
2、如权利要求1所述的环保型防火嵌缝石膏，其特征在于，所述非金属矿物防火材料为云母粉、蛭石粉中的至少一种。
3、如权利要求1或2所述的环保型防火嵌缝石膏，其特征在于，所述调整剂为磺酸盐。
4、如权利要求1或2所述的环保型防火嵌缝石膏，其特征在于，所述缓凝剂为柠檬酸。
5、如权利要求1或2所述的环保型防火嵌缝石膏，其特征在于，所述保水增稠剂为甲基纤维素、羧甲基纤维素钠或纤维素醚。
6、如权利要求1或2所述的环保型防火嵌缝石膏，其特征在于，所述粘接剂为胶粉。
7、如权利要求1或2所述的环保型防火嵌缝石膏，其特征在于，所述增强剂为硼砂或硼酸。
CN2008100579466A 2008-02-21 2008-02-21 环保防火嵌缝石膏 Active CN101514096B (zh)