CN101508598A - 稀土钕红变色釉颜料及其制备方法 - Google Patents

稀土钕红变色釉颜料及其制备方法 Download PDF

Info

Publication number
CN101508598A
CN101508598A CNA2009100475705A CN200910047570A CN101508598A CN 101508598 A CN101508598 A CN 101508598A CN A2009100475705 A CNA2009100475705 A CN A2009100475705A CN 200910047570 A CN200910047570 A CN 200910047570A CN 101508598 A CN101508598 A CN 101508598A
Authority
CN
China
Prior art keywords
glaze
red
neodymium
color
changing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2009100475705A
Other languages
English (en)
Other versions
CN101508598B (zh
Inventor
白皓
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2009100475705A priority Critical patent/CN101508598B/zh
Publication of CN101508598A publication Critical patent/CN101508598A/zh
Application granted granted Critical
Publication of CN101508598B publication Critical patent/CN101508598B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种能在不同光源下变色的稀土陶瓷釉颜料。本发明所说的稀土钕红变色釉颜料，由重量百分比为17－29％的变色钕红颜料和83－71％的长石釉组成；其中变色钕红颜料的重量组成为：SiO2 42－50％、Al2O3 16－24％、CaO6％、ZnO 5％、B2O3 3％、Nd2O3 12－15％、Er2O35－8％。本发明的稀土钕红变色釉，将变色颜料于釉料瓷质结合成为变色釉产品，其在不同光源照射下显示不同的颜色。如在日光灯下显淡蓝色，自然光下显丁香红色，节能灯下则显淡绿色。本发明的稀土钕红变色釉还可减轻釉面上的碎裂性，改善釉面光泽度，提高强度，化学稳定性，硬度等。

Description

稀土钕红变色釉颜料及其制备方法
技术领域
本发明属于一种能在不同光源下变色的稀土陶瓷釉颜料及其制备方法技术领域。
背景技术
稀土变色釉早在我国古代1404年就有制品，如山西省(明代汾州府)的钕红制品最具代表性。从二十世纪九十年代，随着稀土开发研究，在陶瓷中应用已有：变色釉瓷塑(潮州)，彩色变色玲珑釉装饰工艺品(景德镇)，变色颜料，变色釉料(唐山)销售及变色杯、装饰工艺品等皆为钕紫。
对比现有各种釉料的种种缺陷，现从我经历多年的研究——稀土钕红变色釉颜料配方实验成果中筛选出呈色最佳、变色明快、成本较低，方法简便可行的方案：稀土钕红变色釉颜料及其制备方法。
发明内容
本发明的目的就是提供一种新型稀土钕红变色釉颜料，该变色釉颜料可广泛应用于建筑饰材，如瓷砖等；生活用品，如各种陶瓷器皿、工艺品等。
稀土钕红发光变色原理：在高温下，氧化硅、氧化铝生成针网状胎体骨架(2SiO2·3AlO3)的载色母体复合分子色料发光，在不同光源照射下变色。因此原料的选用、量比、直接影响生成物化学结构和颜色效果。
本发明所说的稀土钕红变色釉颜料，由重量百分比为17—29％的变色钕红颜料和83—71％的长石釉组成；其中变色钕红颜料的重量组成为：SiO2 42—50％、Al2O3 16—24％、CaO 6％、ZnO 5％、B2O3 3％、Nd2O3 12—15％、Er2O3 5—8％。
上述变色釉颜料的各种原料，包括钕红颜料的各个组分和长石釉成分原料均市售可得。
上述稀土钕红变色釉颜料的制备方法，其方法是先准确称量变色钕红颜料各原料，然后用球磨机湿法细混合，过滤(200目)，干燥后在1200—1300℃煅烧0.5—1.5小时，冷却后干法细粉碎，过200目筛；最后与长石釉混合即可。
本发明的稀土钕红变色釉，可在建筑砖釉、花瓶、酒瓶、装饰工艺品等陶瓷制品釉中广泛应用，也可用作变色釉面卫生砖，建筑陶瓷用。
本发明有益效果：
1、本发明的稀土钕红变色釉，将变色颜料于釉料瓷质结合成为变色釉产品，其在不同光源照射下显示不同的颜色。如在日光灯下显淡蓝色，自然光下显丁香红色，节能灯下则显淡绿色。
2、本发明的稀土钕红变色釉还可减轻釉面上的碎裂性，改善釉面光泽度，提高强度，化学稳定性，硬度等。
具体实施方式
实施例1
称量各原料：SiO2 42kg、Al2O3 24kg、CaO 6kg(也可以是等摩尔质量的碳酸钙)、ZnO 5kg、B2O3 3kg(也可以是等摩尔质量的硼酸等)、Nd2O3 12kg、Er2O3 8kg和长石釉488kg。
将变色钕红颜料的原料放入湿式球磨机混合，细磨一段时间，过滤(200目)，干燥后在1200—1300℃煅烧1小时，冷却，最后干法粉碎，过筛(200目)。最后将过200目筛的变色钕红颜料与长石釉搅拌混合。
实施例2
称量各原料：SiO2 50kg、Al2O3 16kg、CaO6kg(也可以是等摩尔质量的碳酸钙)、ZnO 5kg、B2O3 3kg(也可以是等摩尔质量的硼酸等)、Nd2O3 15kg、Er2O 5kg和长石釉245kg。
将上述原料放入湿式球磨机混合，细磨一段时间，过滤(200目)，干燥后在1200—1300℃煅烧1小时，冷却，最后干法粉碎，过筛(200目)即可。最后将过200目筛的变色钕红颜料与长石釉搅拌混合。
将实施例1制作的钕红变色釉用于花瓶表面釉料，在日光灯下显淡蓝色，自然光下显丁香红色，节能灯下显淡绿色。且釉面异常光洁，有质感。

Claims (2)

1.稀土钕红变色釉颜料，由重量百分比为17—29％的变色钕红颜料和83—71％的长石釉组成；其中变色钕红颜料的重量组成为：SiO2 42—50％、Al2O3 16—24％、CaO 6％、ZnO 5％、B2O3 3％、Nd2O3 12—15％、Er2O35—8％。
2.权利要求1所述的稀土钕红变色釉颜料的制备方法，该方法是先准确称量变色钕红颜料各原料，然后用球磨机湿法细混合，过200筛；干燥后在1200—1300℃煅烧0.5—1.5小时，冷却后干法细粉碎，过200目筛；最后与长石釉混合。
CN2009100475705A 2009-03-13 2009-03-13 稀土钕红变色釉颜料及其制备方法 Expired - Fee Related CN101508598B (zh)