CN101482481B - 包含疲劳载荷的金属结构日历寿命确定方法 - Google Patents

包含疲劳载荷的金属结构日历寿命确定方法 Download PDF

Info

Publication number
CN101482481B
CN101482481B CN2008100009015A CN200810000901A CN101482481B CN 101482481 B CN101482481 B CN 101482481B CN 2008100009015 A CN2008100009015 A CN 2008100009015A CN 200810000901 A CN200810000901 A CN 200810000901A CN 101482481 B CN101482481 B CN 101482481B
Authority
CN
China
Prior art keywords
test
corrosion
calendar life
fatigue load
spectrum
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2008100009015A
Other languages
English (en)
Other versions
CN101482481A (zh
Inventor
张福泽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
INST OF AVIATION EQUIPMENT ACADEMY OF AIRFORCE EQUIPMENT PLA
Original Assignee
INST OF AVIATION EQUIPMENT ACADEMY OF AIRFORCE EQUIPMENT PLA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by INST OF AVIATION EQUIPMENT ACADEMY OF AIRFORCE EQUIPMENT PLA filed Critical INST OF AVIATION EQUIPMENT ACADEMY OF AIRFORCE EQUIPMENT PLA
Priority to CN2008100009015A priority Critical patent/CN101482481B/zh
Publication of CN101482481A publication Critical patent/CN101482481A/zh
Application granted granted Critical
Publication of CN101482481B publication Critical patent/CN101482481B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

包含疲劳载荷的金属结构日历寿命确定方法，属材料失效与保护技术领域。它主要解决金属结构和设备在日历寿命确定中，如何考虑疲劳载荷的影响问题。它的技术方案是：①编制一年的使用温度谱和疲劳载荷谱；②确定腐蚀溶液成份和试验加速倍数；③在使用温度谱和疲劳载荷谱下，分别循环进行一级高浓度溶液的金属试件的腐蚀试验和疲劳试验，直至试件损伤达到临界损伤值Dc为止；④用模型(1)计算日历寿命Hc。
Figure B2008100009015A00011
模型(1)中的Dt是腐蚀和疲劳组合试验得到的，Dc是给定的临界腐蚀损伤值，dt是已知的试验溶液浓度，λ是由试验得到的试验循环周期数，是已知的使用温度谱，由此包含疲劳载荷的金属结构和设备日历寿命Hc可求出。

Description

包含疲劳载荷的金属结构日历寿命确定方法
所属技术领域
本发明属于材料失效与保护领域。
技术背景
由于一些金属结构和设备在使用中，它们不仅受到腐蚀环境的作用，而且还受到疲劳载荷的作用，因此在给这些结构和设备确定日历寿命时，只考虑腐蚀环境的作用，不考虑疲劳载荷的作用是不可靠的。目前国内外，如何考虑疲劳载荷在日历寿命确定中的影响，尚没有一种便于工程应用的方法。本发明方法解决了这一问题。
发明内容
本发明方法，在一级高浓度腐蚀溶液和一年的使用温度谱的试验中，将一年的使用疲劳载荷谱随机地加入其中，这样试验中的腐蚀损伤Dt就是腐蚀和疲劳载荷共同作用的结果。用由此获得的Dt算得的日历寿命就同时包含了腐蚀环境和疲劳载荷的作用，这样确定的日历寿命更可靠。
具体实施方案
1编制一年的使用温度谱。
2编制一年的使用疲劳载荷谱。
3确定腐蚀溶液成份和试验加速倍数。
4加工可施加疲劳载荷的腐蚀试验件。
5试验方法：
①在使用温度谱下，将一组试件放入选定的一级高浓度腐蚀溶液中进行试验，试验时间是一年使用温度谱中每级温度时间的
Figure S2008100009015D00011
的总和。
②取出上述腐蚀试验的全部试验件，分别对每个试验件进行一年使用疲劳载荷谱中每级频数的
Figure S2008100009015D00012
加载试验。
③重复循环上述腐蚀和疲劳两种试验，假设进行“λ”次循环后，达到临界损伤Dc，才停止试验。
6包含疲劳载荷的日历寿命计算
①取日历寿命计算模型(1)
H c = D c d t D t λ [ Σ t = 1 k h i ] - - - ( 1 )
②日历寿命Hc计算：
由于模型(1)中的Dt是腐蚀和疲劳组合试验得到的、Dc是给定的临界腐蚀损伤值、dt是已知的试验溶液浓度、λ是由试验得到的试验循环周期数、
Figure S2008100009015D00014
是已知的使用温度谱，由此包含疲劳载荷的金属结构和设备日历寿命Hc可求出。

Claims (1)

1.一种同时考虑使用腐蚀环境和疲劳载荷作用的金属结构和设备日历寿命确定方法，其特征在于日历寿命通过如下过程的组合试验以及计算模型(1)得到：
在使用温度谱下，将一组试件放入选定的一级高浓度腐蚀溶液中进行试验，试验时间是一年使用温度谱中每级温度时间的的总和；
取出上述腐蚀试验的全部试验件，分别对每个试验件进行一年使用疲劳载荷谱中每级频数的
Figure FSB00000870780100012
加载试验；
重复循环上述腐蚀和疲劳两种试验，假设进行“λ”次循环后，达到临界损伤Dc，才停止试验；
由模型(1)求包含疲劳载荷的金属结构日历寿命Hc，
H c = D c d t D t λ [ Σ i = 1 k h i ] - - - ( 1 )
式中，
Dc——给定的临界腐蚀损伤值；
dt——已知的腐蚀试验溶液浓度；
λ——由腐蚀和疲劳试验得到的试验循环周期数；
Figure FSB00000870780100014
——已知的使用温度谱；
Dt——由上述步骤的腐蚀和疲劳组合试验得到的腐蚀损伤值；
将Dc、dt、λ、Dt等参数代入模型(1)，便可获得包含疲劳载荷的金属结构日历寿命Hc。
CN2008100009015A 2008-01-07 2008-01-07 包含疲劳载荷的金属结构日历寿命确定方法 Expired - Fee Related CN101482481B (zh)