CN101469436A - 在环保型三价铬镀液中制备铬基复合镀层的方法 - Google Patents

在环保型三价铬镀液中制备铬基复合镀层的方法 Download PDF

Info

Publication number
CN101469436A
CN101469436A CN 200710308580 CN200710308580A CN101469436A CN 101469436 A CN101469436 A CN 101469436A CN 200710308580 CN200710308580 CN 200710308580 CN 200710308580 A CN200710308580 A CN 200710308580A CN 101469436 A CN101469436 A CN 101469436A
Authority
CN
China
Prior art keywords
chromium
plating
based composite
composite coating
trivalent chromium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200710308580
Other languages
English (en)
Inventor
张俊彦
曾志翔
梁爱民
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lanzhou Institute of Chemical Physics LICP of CAS
Original Assignee
Lanzhou Institute of Chemical Physics LICP of CAS
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lanzhou Institute of Chemical Physics LICP of CAS filed Critical Lanzhou Institute of Chemical Physics LICP of CAS
Priority to CN 200710308580 priority Critical patent/CN101469436A/zh
Publication of CN101469436A publication Critical patent/CN101469436A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种在环保型三价铬镀液中制备铬基复合镀层的方法。本发明在含氯化铬的基础电解液中，添加不同的颗粒，通过选择适当的工艺条件，制备出表面平整，与底材结合牢固铬基复合镀层。其优点在于制备出的铬基复合镀层厚度大于50μm。复合镀层有比六价铬电镀镀层更高的硬度和与之相当的摩擦学性能，可在各种摩擦工况条件下代替传统的六价铬电镀工艺。

Description

在环保型三价铬镀液中制备铬基复合镀层的方法
技术领域
本发明涉及在环保型三价铬镀液中制备铬基复合镀层的电沉积方法。
背景技术
硬铬镀层由于具有高硬度、良好的耐磨性能及耐腐蚀性能而成为工业界应用最广泛的电镀层。但是长期以来，传统的六价铬镀液存在很多难以克服的缺点，如电流效率低、电镀温度高、污染严重等。在电镀硬铬的过程中，废水和废气中大量的六价铬对环境造成很大的污染，六价铬可以造成人体肾功能衰竭，心率衰竭，白血病，并可强烈引发癌症。目前，世界卫生组织和世界各国对六价铬电镀工艺的污染问题越来越重视，从1997年起，欧洲和北美规定六价铬在空气中的最大排放量为0.001mg/m3。我国自2003年实施《清洁生产促进法》以来，逐步减少并最终禁止六价铬镀液的使用。因此，当前替代六价铬电沉积技术研究已经成为电镀行业的研究的热点和难点之一。
目前，替代六价铬电镀技术主要有三种：气相沉积铬镀层、电沉积合金镀层、三价铬电沉积镀层。气相沉积技术优点在于污染小、沉积均匀，但是其成本高、不能用于大规模的工业生产；电沉积合金代铬镀层主要包括Zn-Sn-Co、Ni-P、Ni-W及其他三元合金。此种方法污染小，但是镀液稳定性差，可操作条件窄。相比之下，三价铬电沉积溶液毒性只有六价铬溶液的1％，且能耗少，效率高，但是其致命的缺点就是不能镀厚，且硬度低，因此只能用作装饰性镀层而不能用作耐磨镀层和修复镀层。
为了减少环境的污染，减少在镀铬方面中国对外国的技术依赖，克服绿色贸易的堡垒，迫切需要开发出三价铬电镀厚铬工艺。
发明内容
本发明的目的在于提供一种在环保型三价铬镀液中制备铬基复合镀层的方法。
本发明通过如下措施来实现：
一种在环保型三价铬镀液中制备铬基复合镀层的方法，采用电镀法制备，其特征在于每升电解液中含有六水合氯化铬100～210g，溴化铵40～50g，氯化钠20～35g，硼酸20～30g，甲酸、乙酸、乙二酸、氨基乙酸、甲酸盐、乙酸盐或乙二酸盐0.3～1.0mol，氧化铝、碳化硅、氧化锆、金刚石、二氧化硅、石墨、聚四氟乙烯或二硫化钼颗粒10～100g；电镀时高纯石墨或钛板为阳极，将经过常规镀前预处理后的钢铁或铜工件作阴极；气体搅拌或机械搅拌；电解液pH值控制在1-2，控制施镀温度在20～40℃，沉积过程中通过控制阴极电流密度为10～50A/dm2，电沉积时间为20～120分钟即可沉积出厚度为15μm～100μm的铬基复合镀层。
按本发明制备的铬基复合镀层无裂纹，表面粗糙度Ra≤0.6μm。
按本发明制备的铬基陶瓷颗粒复合镀层耐磨性能优于传统的六价铬电镀镀层。
按本发明制备的铬基石墨复合镀层在干摩擦条件下的摩擦系数小于0.3。
按本发明制备的铬基聚四氟乙烯复合镀层干摩擦条件下的摩擦系数小于0.3，并具有疏水性能(和纯水的接触角大于120度)。
本发明中镀液的毒性仅为六价铬镀液的1％，因此属于《清洁生产法》规定的环保型清洁生产工艺配方。
本发明公开的三价铬电镀铬基复合镀层工艺，能生产出厚度达到50μm以上的复合镀层。此工艺溶液配制简单，可操作条件宽，有望在电镀厚铬方面取代污染环境却广泛应用的六价铬电镀工艺。
本发明实现了三价铬镀液中电沉积铬基复合镀层，其镀层的厚度达到50μm以上，复合粒子的体积含量为5～20％，表面平整，镀层和底材具有较高的结合强度。适当的热处理后，复合镀层的耐磨性能与六价铬电镀镀层相当或优于六价铬电镀镀层。
本发明的最大突破点为：1.在三价铬电镀体系中实现了三价铬电镀的复合镀；2.提供了一种能使铬镀层具有更多功能(如超高硬度、自润滑、疏水等性能)的方法；3.能在比较宽的操作条件范围内，在三价铬镀液中快速沉积厚度为50μm的复合镀层；4.镀层中可以含有各种粒子，且结合良好；5.按本发明制备的铬基陶瓷复合镀层在适当的热处理后，其耐磨性能优于传统的六价铬电镀镀层。
本发明可以在镀厚铬方面部分取代传统的六价铬电镀技术。
具体实施方式
为了更好的理解本发明，通过实施例进行说明。
实施例1
在金属如钢或铜工件表面采用本发明电沉积方法施镀，工件的镀前预处理采用常规的镀前预处理工艺。三价铬电沉积铬基复合镀层镀液配方是：每升电解液中含有六水合氯化铬为100～210g，溴化铵40～50g，氯化钠20～35g，硼酸20～30g，甲酸(或乙酸、乙二酸、氨基乙酸、甲酸盐、乙酸盐、乙二酸盐)0.3～1.0mol，颗粒10～100g。颗粒为氧化铝、碳化硅、氧化锆、金刚石、二氧化硅、石墨、聚四氟乙烯或二硫化钼。电镀时高纯石墨为阳极或钛板，将经过常规镀前预处理后的钢铁或铜工件作阴极；电解液pH值控制在1-2，利用恒温装置控制施镀温度在20～40℃，搅拌速度适当，沉积过程中控制阴极电流为10～50A/dm2之间，电流密度太小或太大镀层的质量都不好。电沉积时间为20～120分钟，即可沉积出厚度为15～100μm的铬基复合镀层。

Claims (1)

1、一种在环保型三价铬镀液中制备铬基复合镀层的方法，采用电镀法制备，其特征在于每升电解液中含有六水合氯化铬100～210g，溴化铵40～50g，氯化钠20～35g，硼酸20～30g，甲酸、乙酸、乙二酸、氨基乙酸、甲酸盐、乙酸盐或乙二酸盐0.3～1.0mol，氧化铝、碳化硅、氧化锆、金刚石、二氧化硅、石墨、聚四氟乙烯或二硫化钼颗粒10～100g；电镀时高纯石墨或钛板为阳极，将经过常规镀前预处理后的钢铁或铜工件作阴极；气体搅拌或机械搅拌；电解液pH值控制在1-2，控制施镀温度在20～40℃，沉积过程中通过控制阴极电流密度为10～50A/dm2，电沉积时间为20～120分钟即可沉积出厚度为15μm～100μm的铬基复合镀层。
CN 200710308580 2007-12-25 2007-12-25 在环保型三价铬镀液中制备铬基复合镀层的方法 Pending CN101469436A (zh)