CN101468579A - Technique for repairing bronzing of historical building handicraft - Google Patents
Technique for repairing bronzing of historical building handicraft Download PDFInfo
- Publication number
- CN101468579A CN101468579A CNA2007101728389A CN200710172838A CN101468579A CN 101468579 A CN101468579 A CN 101468579A CN A2007101728389 A CNA2007101728389 A CN A2007101728389A CN 200710172838 A CN200710172838 A CN 200710172838A CN 101468579 A CN101468579 A CN 101468579A
- Authority
- CN
- China
- Prior art keywords
- coating
- beeswax
- bronzing
- gold lacquer
- lacquer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to bronzing technology, in particular to bronzing repair technology for historical building handicraft articles. The bronzing repair technology for the historical building handicraft articles is characterized by comprising the following steps: a) mixing bronze powder, lac lacquer and methylated spirit to prepare gold lacquer, using the gold lacquer to fully stipple the surface to be repaired to form a gold lacquer coating, stippling the surface to be repaired again when the gold lacquer is semi-dried, and generating texture on the gold lacquer coating; b) at least drying the gold lacquer coating in the air for 2 hours, coating beeswax which is diluted by turpentine and added with pigments on the gold lacquer coating to form a beeswax coating, using a solvent to wipe the beeswax coating, wiping off a great mass of beeswax, and exposing the gold lacquer coating; c) coating a second layer of beeswax after the solvent of the beeswax coating is completely volatized and hardened, and coating diluted beeswax; and d) placing products on a warm and dry place for drying in the air for at least 24 hours, volatilizing the solvent, and hardening the coating. The bronzing repair technology solves the problem of repairing defects of bronzing veneers of the prior historical buildings.
Description
Technical field
The present invention relates to a kind of technique for repairing bronzing, particularly a kind of technique for repairing bronzing of historical building handicraft.
Background technology
Make decoration at body surface with metal, have gold-plated, gild, mode such as bronzing.Bronzing is applied in the bigger place of area more, and the face of bronzing is as a whole, the vestige that the gold foil paper of not gilding is one one, but bigger with the gold amount.The technology of bronzing now at first will be broken gold size, then bronze is swept in the gold size surface gently with goat hair brush, makes the thickness uniformity, and it is real that bronze and gold size are glued, and will float bronze at last and sweep off.
Summary of the invention
The object of the present invention is to provide a kind of technique for repairing bronzing of historical building handicraft, to solve the present damaged reparation problem of historical building bronzing facing.
The present invention solves the problems of the technologies described above by the following technical programs:
Technique for repairing bronzing of historical building handicraft is characterized in that, may further comprise the steps:
A) with bronze powder, lacquer and methylated spirit mixing manufacture gold lacquer; Form the gold lacquer coating with the abundant stippling of gold lacquer surface to be repaired; When gold lacquer was half-dried, stippling surface to be repaired produced a little textures on the gold lacquer coating again;
B) dry 2 hours at least, smear the beeswax formation beeswax coating of diluting and added pigment with turpentine oil then, this beeswax is as polishing agent; Use the methyl alcohol wiping again, wipe most of beeswaxs then, appear the gold lacquer coating;
C) after by the time the methyl alcohol of beeswax coating vapors away fully and hardens, smear the second layer diluted and added pigment with turpentine oil beeswax;
D) goods are put into warm dry place and dried at least 24 hours, allow solvent evaporates, the coating sclerosis.
Further, before step d), sweep beeswax coating, and brush stippling this coating once with clean doing.Do several effects like this: the brush mark that stays in soft the smearing two kinds of scattered beeswax harmonious colours together, appears more following metal color.
Further, after step d), use sand papering surface, all veins of metal powder and projecting point below grinding.
Beneficial effect of the present invention is, make historical building protection and reparation have Echtheit, accomplished restoring the old as the old.
The specific embodiment
For technological means, creation characteristic that the present invention is realized, reach purpose and effect is easy to understand, below in conjunction with the specific embodiment, further set forth the present invention.
Technique for repairing bronzing of historical building handicraft, just golden earlier bronze powder, common brown lacquer and methylated spirit mixing manufacture gold lacquer; Form the gold lacquer coating with the abundant stippling of gold lacquer surface to be repaired; When gold lacquer was half-dried, stippling surface to be repaired produced a little textures on the gold lacquer coating again.
At least dried 2 hours, and smeared the beeswax formation beeswax coating of diluting and added pigment with turpentine oil then, beeswax is here as polishing agent.Pigment can use red ocher, and in fact any mineral color and most green all can be used.Wipe a few minutes with methyl alcohol again, wipe most of beeswaxs then, appear metal coating.
By the time the solvent of this beeswax coating vapor away fully and also harden (put into freeze case can reach this effect fast) after, smear the second layer diluted and added pigment with turpentine oil beeswax.Like this, the coating of back can not influence the coating of front.
Sweep beeswax coating, and brush stippling this coating once with clean doing.
Goods are put into warm dry place dried at least 24 hours, allow solvent evaporates, the coating sclerosis.
Use extremely meticulous sand papering surface, all veins of metal powder and projecting point below grinding.
More than show and described basic principle of the present invention, principal character and advantage of the present invention.The technical staff of the industry should understand; the present invention is not restricted to the described embodiments; that describes in the foregoing description and the specification just illustrates principle of the present invention; the present invention also has various changes and modifications without departing from the spirit and scope of the present invention, and these changes and improvements all fall in the claimed scope of the invention.The claimed scope of the present invention is defined by appending claims and equivalent thereof.
Claims (3)
1, technique for repairing bronzing of historical building handicraft is characterized in that, may further comprise the steps:
A) with bronze powder, lacquer and methylated spirit mixing manufacture gold lacquer; Form the gold lacquer coating with the abundant stippling of gold lacquer surface to be repaired; When gold lacquer was half-dried, stippling surface to be repaired produced a little textures on the gold lacquer coating again;
B) dry 2 hours at least, smear the beeswax formation beeswax coating of diluting and added pigment with turpentine oil then; Use solvent wiping again, wipe most of beeswaxs then, appear the gold lacquer coated substrate;
C) after by the time the solvent of beeswax coating vapors away fully and hardens, smear the second layer diluted and added pigment with turpentine oil beeswax;
D) goods are put into warm dry place and dried at least 24 hours, allow solvent evaporates, the coating sclerosis.
2, technique for repairing bronzing of historical building handicraft according to claim 1 is characterized in that: sweep beeswax coating before step d), and brush stippling this coating once with clean doing.
3, technique for repairing bronzing of historical building handicraft according to claim 1 is characterized in that: use the sand papering surface after step d).