CN101455888A - 干粉灭火剂及其制备方法 - Google Patents
干粉灭火剂及其制备方法 Download PDFInfo
- Publication number
- CN101455888A CN101455888A CNA2007102029786A CN200710202978A CN101455888A CN 101455888 A CN101455888 A CN 101455888A CN A2007102029786 A CNA2007102029786 A CN A2007102029786A CN 200710202978 A CN200710202978 A CN 200710202978A CN 101455888 A CN101455888 A CN 101455888A
- Authority
- CN
- China
- Prior art keywords
- extinguishing agent
- percentage
- weight
- powder extinguishing
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种干粉灭火剂,其包括重量百分比55%至65%的氯化钠、重量百分比30%至45%的氯化镁、重量百分比0至8%的氯化钙及重量百分比0至3%的氧化镁。该干粉灭火剂具有灭镁合金金属火效果佳的优点。本发明另提供一种制备该灭火剂的方法。
Description
技术领域
本发明涉及一种干粉灭火剂及其制备方法,特别是涉及一种用于灭镁合金金属火的干粉灭火剂及其制备方法。
背景技术
镁合金在熔炼、铸造过程中,由于其具有较高的化学活性而易与空气中的氧气发生反应而燃烧起火,容易造成材料浪费甚至引发重大火灾事故。
现在技术中,镁合金燃烧时,常常需要用D级灭火器来灭火。D级灭火器通常使用的是氯化钠粉末。灭火过程中,氯化钠粉末沉积于着火的镁合金工件表面,对应区域与空气隔绝,工件中的镁因为没有氧气等氧化物质与其反应而停止燃烧,从而达到灭火的目的。
上述灭火过程是通过氯化钠粉末沉积于着火的镁合金工件表面,通过氯化钠粉末隔绝空气而起到灭火作用。由于氯化钠的熔点较高,其在镁合金的表面不能熔化,始终以固态粉末的形式沉积于着火的镁合金工件表面。而固态的粉末较难向四周进一步扩散,粉末的覆盖能力有限,造成未被覆盖或覆盖不好的镁合金工件表面的部份区域仍然会燃烧。而且,固态粉末之间较易存在的透气间隙,空气容易透过透气间隙与镁合金基体接触,从而导致镁合金氧化甚至燃烧。因此,该灭火器的灭火效果较差。
发明内容
鉴于上述状况,有必要提供一种灭镁合金金属火效果佳的干粉灭火剂及其制备方法。
一种干粉灭火剂,其包括重量百分比55%至65%的氯化钠、重量百分比30%至45%的氯化镁、重量百分比0至8%的氯化钙及重量百分比0至3%的氧化镁。
一种干粉灭火剂制备方法,其包括:提供一种混合物,该混合物包括重量百分比55%至65%的氯化钠、重量百分比30%至45%的氯化镁、重量百分比0至8%的氯化钙及重量百分比0至3%的氧化镁;加热混合物至熔化,搅拌均匀,浇注成干粉灭火剂块;将干粉灭火剂块磨成粉状。
上述干粉灭火剂包括氯化钠及氯化镁,使干粉灭火剂中存在MgCl2-NaCl二元系,MgCl2-NaCl二元系的存在使干粉灭火剂具有较低的熔点。因此,将干粉灭火剂的粉末喷向着火的镁合金工件表面时,干粉灭火剂的粉末受热后熔化,易于在镁合金工件表面流动并于镁合金工件表面形成均匀的覆盖层。该覆盖层为熔融的流体形成,中间不存在透气间隙,从而使空气无法通过该覆盖层与镁合金基本体接触,从而阻止镁合金燃烧,起到灭火的作用。并且,由于灭火粉末熔化后能在镁合金工件表面流动并向四周扩散,具有较高的覆盖能力,因而不存在部分区域未受到有效覆盖而继续燃烧的情况。因此,灭火器具有较好的灭火效果。
具体实施方式
下面将结合实施例对本发明干粉灭火剂及其制备方法做进一步详细说明。
实施例一:干粉灭火剂由重量百分比55%至65%的氯化钠(NaCl)与重量百分比35%至45%的氯化镁(MgCl2)组成。
由于熔融的氯化钠表面张力与粘度较小,具有降低熔融的干粉灭火剂的表面张力和粘度的作用,使熔融的干粉灭火剂具有较好的流动性,以便熔融的干粉灭火剂在镁合金工件表面形成连续的覆盖膜。
氯化镁使干粉灭火剂中存在MgCl2-NaCl二元系。MgCl2-NaCl二元系的存在使干粉灭火剂具有较低的熔点,干粉灭火剂的熔点为400摄氏度至500摄氏度,远低于单独采用氯化钠的灭火剂熔点801摄氏度。例如,干粉灭火剂只由重量百分比55%的氯化钠与重量百分比45%的氯化镁组成时,干粉灭火剂的熔点为460摄氏度;干粉灭火剂只由重量百分比65%的氯化钠与重量百分比35%的氯化镁组成时,干粉灭火剂的熔点为490摄氏度。
因此,将干粉灭火剂的粉末喷向着火的镁合金工件表面时,干粉灭火剂的粉末受热后熔化,易于在镁合金工件表面流动并于镁合金工件表面形成均匀的覆盖层。该覆盖层为熔融的流体形成,中间不存在透气间隙,从而使空气无法通过该覆盖层与镁合金基本体接触,从而阻止镁合金燃烧,起到灭火的作用。并且,由于灭火粉末熔化后能在镁合金工件表面流动并向四周扩散,具有较高的覆盖能力,因而不存在部分区域未受到有效覆盖而继续燃烧的情况。因此,灭火器具有较好的灭火效果。
此外,为使干粉灭火剂具有更佳的灭火效果,氯化钠与氯化镁组成的灭火剂中可同时或单独加入氯化钙与氧化镁,氯化钙可增加熔融的干粉灭火剂的比重,使干粉灭火剂具有更佳的灭火性能;氧化镁使熔融的干粉灭火剂具有一定的粘度,防止熔融的干粉灭火剂因流动性过大而不能完整覆盖一些表面,如侧面等。单独或同时加入氯化钙与氧化镁的干粉灭火剂实施例如下:
实施例二:干粉灭火剂由重量百分比57%的氯化钠、重量百分比40%的氯化镁及重量百分比3%的氯化钙组成。
实施例三:干粉灭火剂由重量百分比55%的氯化钠、重量百分比37%的氯化镁及重量百分比8%的氯化钙组成。
实施例四:干粉灭火剂由重量百分比59%的氯化钠、重量百分比40%的氯化镁及重量百分比1%的氧化镁组成。
实施例五:干粉灭火剂由重量百分比57%的氯化钠、重量百分比40%的氯化镁及重量百分比3%的氧化镁组成。
实施例六:干粉灭火剂由重量百分比65%的氯化钠、重量百分比30%的氯化镁、重量百分比4%的氯化钙及重量百分比1%的氧化镁组成。
实施例七:干粉灭火剂由重量百分比55%的氯化钠、重量百分比40%的氯化镁、重量百分比3%的氯化钙及重量百分比2%的氧化镁组成。
实施例八:干粉灭火剂由重量百分比59%的氯化钠、重量百分比30%的氯化镁、重量百分比8%的氯化钙及重量百分比3%的氧化镁组成。
在使用上述干粉灭火剂灭火时,可采用高压氩气带动干粉灭火剂粉末喷向镁合金工件表面。氩气本身是惰性气体。可以理解,氩气还可更换为不会与镁反应的其它惰性气体或非助燃气体。
本发明另提供一种制备上述干粉灭火剂的方法,其包括如下步骤:
提供一种混合物,该混合物包括重量百分比55%至65%的氯化钠、重量百分比30%至45%的氯化镁、重量百分比0至8%的氯化钙及重量百分比0至3%的氧化镁。
将混合物置于坩埚内,加热混合物升温到750摄氏度至800摄氏度熔化,搅拌均匀,浇注成干粉灭火剂块;
破碎后装入球磨机辊磨成粉状,装入密闭容器中备用。
另外,本领域技术人员还可在本发明精神内做其它变化,当然,这些依据本发明精神所做的变化,都应包含在本发明所要求保护的范围内。
Claims (6)
- 【权利要求1】一种干粉灭火剂,其特征在于包括重量百分比55%至65%的氯化钠、重量百分比30%至45%的氯化镁、重量百分比0至8%的氯化钙及重量百分比0至3%的氧化镁。
- 【权利要求2】如权利要求1所述的干粉灭火剂,其特征在于:该干粉灭火剂包括重量百分比55%至65%的氯化钠、重量百分比30%至40%的氯化镁、重量百分比3%至8%的氯化钙及重量百分比1%至3%的氧化镁。
- 【权利要求3】如权利要求1所述的干粉灭火剂,其特征在于:该干粉灭火剂的熔点范围为400摄氏度至500摄氏度。
- 【权利要求4】一种干粉灭火剂制备方法,其特征在于包括以下步骤:提供一种混合物,该混合物包括重量百分比55%至65%的氯化钠、重量百分比30%至45%的氯化镁、重量百分比0至8%的氯化钙及重量百分比0至3%的氧化镁;加热混合物至熔化,搅拌均匀,浇注成干粉灭火剂块;将干粉灭火剂块磨成粉状。
- 【权利要求5】如权利要求4所述的干粉灭火剂制备方法,其特征在于:加热混合物是在坩埚内进行,加热温度为750摄氏度至800摄氏度。
- 【权利要求6】如权利要求4所述的干粉灭火剂制备方法,其特征在于:将干粉灭火剂块磨成粉状是通过球磨机辊磨成。